WO2017107822A1 - Method for preparing helical milling cutter - Google Patents

Method for preparing helical milling cutter Download PDF

Info

Publication number
WO2017107822A1
WO2017107822A1 PCT/CN2016/109889 CN2016109889W WO2017107822A1 WO 2017107822 A1 WO2017107822 A1 WO 2017107822A1 CN 2016109889 W CN2016109889 W CN 2016109889W WO 2017107822 A1 WO2017107822 A1 WO 2017107822A1
Authority
WO
WIPO (PCT)
Prior art keywords
mass
parts
grinding
milling cutter
cutting
Prior art date
Application number
PCT/CN2016/109889
Other languages
French (fr)
Chinese (zh)
Inventor
周静波
Original Assignee
苏州三骏工具科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 苏州三骏工具科技有限公司 filed Critical 苏州三骏工具科技有限公司
Publication of WO2017107822A1 publication Critical patent/WO2017107822A1/en

Abstract

A method for preparing a helical milling cutter, comprising the following steps: 1) subjecting steel blanks to outer circle grinding, heat treatment, acid washing, drying, and groove cutting; 2) adding 3.5 parts by mass of dibasic anhydride, 1.7 parts by mass of sodium dodecylbenzenesulfonate, 1.3 parts by mass of borate, and 2.6 parts by mass of a cycloalkyl oil to 10.8 parts by mass of deionized water, and mixing thoroughly, and then adding in sequence 0.8 parts by mass of boric acid, 2.5 parts by mass of cellulose hydroxyethyl ether, and 2.9 parts by mass of di-n-butyl phosphite, and mixing uniformly to obtain a working fluid for grinding and cutting; 3) grinding and cutting the milling cutter blanks, using the grinding and cutting fluid during said grinding and cutting process; and 4) implementing light wave heating and eliminating thermal stress. The milling cutter prepared using the present method for preparing a helical milling cutter has high surface quality and a long service life, and the milling cutter is sharp.

Description

一种螺旋铣刀的制备方法Method for preparing spiral milling cutter 技术领域Technical field
本发明涉及一种螺旋铣刀的制备方法。The invention relates to a method for preparing a spiral milling cutter.
背景技术Background technique
现有螺旋铣刀的制备方法，其制备的铣刀，尺寸精度、稳定性、表面质量都有待提高，使用寿命还有继续提供的空间。The preparation method of the existing spiral milling cutter, the milling cutter prepared thereof, the dimensional accuracy, the stability, the surface quality have to be improved, and the service life has a space to continue to provide.
发明内容Summary of the invention
本发明的目的在于提供一种螺旋铣刀的制备方法，其制备的铣刀具有较高的表面质量，铣刀锋利，使用寿命长。The object of the present invention is to provide a method for preparing a spiral milling cutter, which has a high surface quality, a sharp milling cutter and a long service life.
为了实现上述目的，本发明的技术方案是设计一种螺旋铣刀的制备方法，包括如下步骤：In order to achieve the above object, the technical solution of the present invention is to design a method for preparing a spiral milling cutter, comprising the following steps:
1)将钢材坯料经过外圆打磨、热处理、酸洗、烘干、切削沟槽；1) The steel billet is subjected to external grinding, heat treatment, pickling, drying, and cutting grooves;
2)在10.8质量份去离子水中投入3.5质量份二元酸酐、1.7质量份十二烷基苯磺酸钠、1.3质量份硼酸盐、2.6质量份环烷基油，搅拌混合充分，再依次加入0.8质量份硼酸、2.5质量份纤维素羟乙基醚、2.9质量份亚磷酸二正丁酯，充分搅拌均匀，得研磨切削工作液；2) 3.5 parts by mass of a dibasic acid anhydride, 1.7 parts by mass of sodium dodecylbenzenesulfonate, 1.3 parts by mass of borate, and 2.6 parts by mass of a naphthenic oil are added in 10.8 parts by mass of deionized water, stirred and mixed well, and then sequentially 0.8 parts by mass of boric acid, 2.5 parts by mass of cellulose hydroxyethyl ether, and 2.9 parts by mass of di-n-butyl phosphite are added, and the mixture is thoroughly stirred to obtain a grinding cutting working solution;
3)对铣刀坯料进行研磨切削，研磨切削过程中使用上述研磨切削液；4)行光波加热，消除热应力。 3) Grinding and cutting the milling cutter blank, using the above grinding cutting fluid in the grinding cutting process; 4) heating the light wave to eliminate thermal stress.
本发明的优点和有益效果在于：提供一种螺旋铣刀的制备方法，其制备的铣刀具有较高的表面质量，铣刀锋利，使用寿命长。The invention has the advantages and advantageous effects of providing a method for preparing a spiral milling cutter, which has a high surface quality, a sharp milling cutter and a long service life.
具体实施方式detailed description
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。The specific embodiments of the present invention are further described below in conjunction with the embodiments. The following examples are only intended to more clearly illustrate the technical solutions of the present invention, and are not intended to limit the scope of the present invention.
本发明具体实施的技术方案是：The technical solution specifically implemented by the present invention is:
一种螺旋铣刀的制备方法，包括如下步骤：A method for preparing a spiral milling cutter includes the following steps:
1)将钢材坯料经过外圆打磨、热处理、酸洗、烘干、切削沟槽；1) The steel billet is subjected to external grinding, heat treatment, pickling, drying, and cutting grooves;
2)在10.8质量份去离子水中投入3.5质量份二元酸酐、1.7质量份十二烷基苯磺酸钠、1.3质量份硼酸盐、2.6质量份环烷基油，搅拌混合充分，再依次加入0.8质量份硼酸、2.5质量份纤维素羟乙基醚、2.9质量份亚磷酸二正丁酯，充分搅拌均匀，得研磨切削工作液；2) 3.5 parts by mass of a dibasic acid anhydride, 1.7 parts by mass of sodium dodecylbenzenesulfonate, 1.3 parts by mass of borate, and 2.6 parts by mass of a naphthenic oil are added in 10.8 parts by mass of deionized water, stirred and mixed well, and then sequentially 0.8 parts by mass of boric acid, 2.5 parts by mass of cellulose hydroxyethyl ether, and 2.9 parts by mass of di-n-butyl phosphite are added, and the mixture is thoroughly stirred to obtain a grinding cutting working solution;
3)对铣刀坯料进行研磨切削，研磨切削过程中使用上述研磨切削液；4)行光波加热，消除热应力。3) Grinding and cutting the milling cutter blank, using the above grinding cutting fluid in the grinding cutting process; 4) heating the light wave to eliminate thermal stress.
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。 The above description is only a preferred embodiment of the present invention, and it should be noted that those skilled in the art can make several improvements and retouchings without departing from the technical principles of the present invention. It should also be considered as the scope of protection of the present invention.

Claims (1)

  1. 一种螺旋铣刀的制备方法，其特征在于，包括如下步骤：A method for preparing a spiral milling cutter, comprising the steps of:
    1)将钢材坯料经过外圆打磨、热处理、酸洗、烘干、切削沟槽；1) The steel billet is subjected to external grinding, heat treatment, pickling, drying, and cutting grooves;
    2)在10.8质量份去离子水中投入3.5质量份二元酸酐、1.7质量份十二烷基苯磺酸钠、1.3质量份硼酸盐、2.6质量份环烷基油，搅拌混合充分，再依次加入0.8质量份硼酸、2.5质量份纤维素羟乙基醚、2.9质量份亚磷酸二正丁酯，充分搅拌均匀，得研磨切削工作液；2) 3.5 parts by mass of a dibasic acid anhydride, 1.7 parts by mass of sodium dodecylbenzenesulfonate, 1.3 parts by mass of borate, and 2.6 parts by mass of a naphthenic oil are added in 10.8 parts by mass of deionized water, stirred and mixed well, and then sequentially 0.8 parts by mass of boric acid, 2.5 parts by mass of cellulose hydroxyethyl ether, and 2.9 parts by mass of di-n-butyl phosphite are added, and the mixture is thoroughly stirred to obtain a grinding cutting working solution;
    3)对铣刀坯料进行研磨切削，研磨切削过程中使用上述研磨切削液；3) grinding and cutting the milling cutter blank, and using the above grinding cutting fluid in the grinding cutting process;
    4)行光波加热，消除热应力。 4) Light wave heating to eliminate thermal stress.
PCT/CN2016/109889 2015-12-25 2016-12-14 Method for preparing helical milling cutter WO2017107822A1 (en)