WO2016198886A1 - Dispositifs et procédés d'enregistrement magnétique - Google Patents

Dispositifs et procédés d'enregistrement magnétique Download PDF

Info

Publication number
WO2016198886A1
WO2016198886A1 PCT/GB2016/051721 GB2016051721W WO2016198886A1 WO 2016198886 A1 WO2016198886 A1 WO 2016198886A1 GB 2016051721 W GB2016051721 W GB 2016051721W WO 2016198886 A1 WO2016198886 A1 WO 2016198886A1
Authority
WO
WIPO (PCT)
Prior art keywords
magnetic
wire
electrodes
storage device
strain
Prior art date
Application number
PCT/GB2016/051721
Other languages
English (en)
Inventor
Andrew William RUSHFORTH
Jan Zemen
Duncan Edward PARKES
Original Assignee
The University Of Nottingham
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from GBGB1510098.5A external-priority patent/GB201510098D0/en
Priority claimed from GBGB1604999.1A external-priority patent/GB201604999D0/en
Application filed by The University Of Nottingham filed Critical The University Of Nottingham
Publication of WO2016198886A1 publication Critical patent/WO2016198886A1/fr

Abstract

L'invention se rapporte à l'enregistrement d'informations à l'aide de domaines magnétiques ou de parois de domaines magnétiques, et concerne des procédés permettant de déplacer, de créer, de détecter et de transformer la structure des parois de domaines magnétiques à l'aide d'une contrainte mécanique induite par des champs électriques. Des applications comprennent des dispositifs d'enregistrement et de traitement d'informations ayant une haute efficacité énergétique et des petites dimensions. Les modes de réalisation illustratifs comprennent un dispositif d'enregistrement magnétique (100) comprenant : un élément électroactif (103) comprenant un élément piézoélectrique ou électrostrictif ayant des première et seconde électrodes (101) agencé pour appliquer un champ électrique à l'élément électroactif (103) de façon à induire une contrainte ; et un fil magnétique (102) ayant une pluralité de domaines magnétiques séparés par des parois de domaines, le fil magnétique (102) étant aligné le long d'un axe et accouplé mécaniquement à l'élément électroactif (103) ; les première et seconde électrodes (101) étant agencées de telle sorte que le champ électrique soit aligné sur une direction comportant une composante orthogonale à l'axe (104) du fil magnétique (102), une grandeur du champ électrique ayant un gradient le long de l'axe (104) du fil magnétique (102) pour provoquer le déplacement des domaines magnétiques le long de l'axe (104) du fil magnétique (102).
PCT/GB2016/051721 2015-06-10 2016-06-10 Dispositifs et procédés d'enregistrement magnétique WO2016198886A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
GB1510098.5 2015-06-10
GBGB1510098.5A GB201510098D0 (en) 2015-06-10 2015-06-10 Electric field control of magnetic domain walls for information storage and logical processing
GB1604999.1 2016-03-24
GBGB1604999.1A GB201604999D0 (en) 2016-03-24 2016-03-24 Electric field control of the chirality and polarity of vortex magnetic domain walls for information storage and logical processing

Publications (1)

Publication Number Publication Date
WO2016198886A1 true WO2016198886A1 (fr) 2016-12-15

Family

ID=56131566

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2016/051721 WO2016198886A1 (fr) 2015-06-10 2016-06-10 Dispositifs et procédés d'enregistrement magnétique

Country Status (1)

Country Link
WO (1) WO2016198886A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109103329A (zh) * 2018-08-15 2018-12-28 中国科学技术大学 一种电控自旋阀结构及非易失存储器件
CN112002798A (zh) * 2020-08-03 2020-11-27 中国计量大学 一种连续可控磁畴壁移动和钉扎的器件和方法
CN112002361A (zh) * 2020-08-03 2020-11-27 中国计量大学 一种基于多铁异质结构的磁畴壁写入单元及方法
CN112712830A (zh) * 2020-12-09 2021-04-27 中国人民解放军国防科技大学 电压诱导的纳米点磁化单轴到涡旋态的非易失调控方法
CN114532983A (zh) * 2022-01-17 2022-05-27 中国科学院电工研究所 一种磁声成像系统及方法
US11362268B2 (en) 2017-10-30 2022-06-14 Taiwan Semiconductor Manufacturing Company Ltd. Semiconductor structure and associated operating and fabricating method
US11487508B2 (en) 2019-04-15 2022-11-01 International Business Machines Corporation Magnetic tunnel junction based true random number generator

Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6531723B1 (en) 2001-10-16 2003-03-11 Motorola, Inc. Magnetoresistance random access memory for improved scalability
US6545906B1 (en) 2001-10-16 2003-04-08 Motorola, Inc. Method of writing to scalable magnetoresistance random access memory element
US6834005B1 (en) 2003-06-10 2004-12-21 International Business Machines Corporation Shiftable magnetic shift register and method of using the same
US6898132B2 (en) 2003-06-10 2005-05-24 International Business Machines Corporation System and method for writing to a magnetic shift register
US6920062B2 (en) 2003-10-14 2005-07-19 International Business Machines Corporation System and method for reading data stored on a magnetic shift register
US7236386B2 (en) 2004-12-04 2007-06-26 International Business Machines Corporation System and method for transferring data to and from a magnetic shift register with a shiftable data column
WO2007132174A1 (fr) 2006-05-09 2007-11-22 Ingenia Holdings (Uk) Limited Dispositif et procédé de stockage de données
GB2465370A (en) 2008-11-13 2010-05-19 Ingenia Holdings Magnetic data storage comprising a synthetic anti-ferromagnetic stack arranged to maintain solitons
WO2012035355A2 (fr) 2010-09-16 2012-03-22 Cambridge Enterprise Ltd Mise en mémoire magnétique
US20120250398A1 (en) * 2011-03-28 2012-10-04 Kabushiki Kaisha Toshiba Magnetic storage element, magnetic storage device, and magnetic memory
US20130163313A1 (en) * 2010-06-18 2013-06-27 Ecole Centrale De Lille Magnetoelectric memory
US20130250668A1 (en) * 2012-03-23 2013-09-26 Kabushiki Kaisha Toshiba Magnetic memory element, magnetic memory, and magnetic memory device

Patent Citations (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6531723B1 (en) 2001-10-16 2003-03-11 Motorola, Inc. Magnetoresistance random access memory for improved scalability
US6545906B1 (en) 2001-10-16 2003-04-08 Motorola, Inc. Method of writing to scalable magnetoresistance random access memory element
US6834005B1 (en) 2003-06-10 2004-12-21 International Business Machines Corporation Shiftable magnetic shift register and method of using the same
US6898132B2 (en) 2003-06-10 2005-05-24 International Business Machines Corporation System and method for writing to a magnetic shift register
US7031178B2 (en) 2003-06-10 2006-04-18 International Business Machines Corporation Magnetic shift register with shiftable magnetic domains between two regions, and method of using the same
US6920062B2 (en) 2003-10-14 2005-07-19 International Business Machines Corporation System and method for reading data stored on a magnetic shift register
US7236386B2 (en) 2004-12-04 2007-06-26 International Business Machines Corporation System and method for transferring data to and from a magnetic shift register with a shiftable data column
WO2007132174A1 (fr) 2006-05-09 2007-11-22 Ingenia Holdings (Uk) Limited Dispositif et procédé de stockage de données
EP2016592B1 (fr) 2006-05-09 2009-09-16 Ingenia Holdings (UK)Limited Dispositif et procédé de stockage de données
GB2465370A (en) 2008-11-13 2010-05-19 Ingenia Holdings Magnetic data storage comprising a synthetic anti-ferromagnetic stack arranged to maintain solitons
US20130163313A1 (en) * 2010-06-18 2013-06-27 Ecole Centrale De Lille Magnetoelectric memory
WO2012035355A2 (fr) 2010-09-16 2012-03-22 Cambridge Enterprise Ltd Mise en mémoire magnétique
US20120250398A1 (en) * 2011-03-28 2012-10-04 Kabushiki Kaisha Toshiba Magnetic storage element, magnetic storage device, and magnetic memory
US20130250668A1 (en) * 2012-03-23 2013-09-26 Kabushiki Kaisha Toshiba Magnetic memory element, magnetic memory, and magnetic memory device

Non-Patent Citations (81)

* Cited by examiner, † Cited by third party
Title
"Emerging Research Devices", 2007, article "International Technology Roadmap for Semiconductors"
"Mills and Bland", 2006, ELSEVIER, article "Nanomagnetism - Ultrathin films, multilayers and nanostructures"
A. BRANDLMAIER ET AL., PHYS. REV. B, vol. 77, 2008, pages 104445
A. CHUNG ET AL., NANOTECHNOLOGY, vol. 21, 2010, pages 412001
A. JAVED ET AL., J. APPL. PHYS., vol. 107, 2010, pages 09A944
A. W. RUSHFORTH; E. DE RANIERI; J. ZEMEN ET AL., PHYS. REV. B, vol. 78, 2008, pages 085314
BEACH ET AL., NATURE MATERIALS, vol. 4, 2005, pages 741
BRINTLINGER, T.; LIM, S-H.; BALOCH, K. H.; ALEXANDER, P.; QI, Y.; BARRY, J.; MELNGAILIS, J.; SALAMANCA-RIBA, L.; TAKEUCHI, I.; CUM: "In Situ Observation of Reversible Nanomagnetic Switching Induced by Electric Fields", NANO. LETT., vol. 10, 2010, pages 1219
BRYAN ET AL., APPLIED PHYSICS LETTERS, vol. 91, 2007, pages 142502
BUZZI, M.; CHOPDEKAR, R. V.; HOCKEL, J. L.; BUR, A.; WU, T.; PILET, N.; WARNICKE, P.; CARMAN, G. P.; HEYDERMAN, L. J.; NOLTING, F.: "Single Domain Spin Manipulation by Electric Fields in Strain Coupled Artificial Multiferroic Nanostructures", PHYS. REV. LETT., vol. 111, 2013, pages 027204
C. ZINONI ET AL., PHYS. REV. LETT., vol. 107, 2011, pages 207204
C.H. MARROWS, ADVANCES IN PHYSICS, vol. 54, 2005, pages 585
CHIN-JUI HSU; JOSHUA L. HOCKEL; GREGORY P. CARMAN, APPL. PHYS. LETT., vol. 100, 2012, pages 092902
CHU ET AL., NATURE MATERIALS, vol. 7, 2008, pages 478
CHUNG ET AL., APPL. PHYS. LETT., vol. 94, 2009, pages 132501
D. A. ALLWOOD ET AL., APPL. PHYS. LETT., vol. 85, 2004, pages 2848
D. ATKINSON ET AL., NATURE MATERIALS, vol. 2, 2003, pages 85
D. BONDURANT ET AL., PORTABLE DESIGN, July 2008 (2008-07-01), pages 16
D.A. ALLWOOD ET AL., SCIENCE, vol. 296, 2002, pages 2003
D.A. ALLWOOD; G. XIONG; C.C. FAULKNER ET AL., SCIENCE, vol. 309, 2005, pages 1688
D.E. PARKES, APPL. PHYS. LETT., vol. 101, 2012, pages 072402
DE RANIERI, E.; ROY, P. E.; FANG, D.; VEHSTHEDT, E. K.; IRVINE, A. C.; HEISS, D., CASIRAGHI; A., CAMPION; R. P., GALLAGHER; B. L.,: "Piezoelectric control of the mobility of a domain wall driven by adiabatic and non-adiabatic torques", NATURE MATERIALS, vol. 12, 2013, pages 808
DEAN J ET AL: "Stress-based control of magnetic nanowire domain walls in artificial multiferroic systems", JOURNAL OF APPLIED PHYSICS, AMERICAN INSTITUTE OF PHYSICS, US, vol. 109, no. 2, 24 January 2011 (2011-01-24), pages 23915-1 - 23915-5, XP012147375, ISSN: 0021-8979, DOI: 10.1063/1.3532041 *
DEAN, J. ET AL.: "Stress-based control of magnetic nanowire domain walls in artificial multiferroic systems", J. APP. PHYS., vol. 109, 2011, pages 023915
E. R. LEWIS ET AL., NAT. MAT., vol. 9, 2010, pages 980
E. RAPOPORT; D. MONTANA; G. S. D. BEACH, LAB CHIP, vol. 12, 2012, pages 4433 - 4440
E. SAITOH ET AL., NATURE, vol. 432, 2004, pages 203
ELIZABETH RAPOPORT; GEOFFREY S. D. BEACH, APPL. PHYS. LETT., vol. 100, 2012, pages 082401
FERROMAGNETISM, BOZORTH, 1951
FRANKE, K. J. A.; VAN DE WIELE, B.; SHIRAHATA, Y.; HAMALAINEN, S. J.; TANIYAMA, T.; VAN DIJKEN, S.: "Reversible Electric-Field-Driven Magnetic Domain-Wall Motion", PHYS. REV., vol. X 5, 2015, pages 011010
FRANKEN ET AL., NATURE NANOTECHNOLOGY, vol. 7, 2012, pages 499 - 503
FUKAMI, S. ET AL.: "Low-current perpendicular domain wall motion cell for scalable high-speed MRAM", SYMPOSIUM ON VLSI TECHNOLOGY, 2009
G. VIEIRA ET AL., PHYSICAL REVIEW LETTERS, vol. 103, 2009, pages 128101
GALLAGHER; PARKIN, IBM J. RES. & DEV., vol. 1, 2006, pages 5
H. BOUKARI; C. CAVACO; W. EYCKMANS ET AL., J. APPL. PHYS., vol. 101, 2007, pages 054903
HU, J-M.; LI, Z.; CHEN, L-Q.; NAN, C-W.: "High-density magnetoresistive random access memory operating at ultralow voltage at room temperature", NATURE. COMMUNICATIONS, vol. 2, 2011, pages 553
HUAI, Y. M.: "Spin-transfer torque MRAM: challenges and prospects", AAPPS BULLETIN, vol. 18, 2008, pages 33 - 40, XP008158056
HUANG T. ZENG; D. READ; L. O'BRIEN ET AL., APPL. PHYS. LETT., vol. 96, 2010, pages 262510
J L LEAL; M H KRYDER, J. APPL. PHYS., vol. 83, 1998, pages 3720
J. L. HOCKEL; A. BUR; T WU ET AL., APPL. PHYS. LETT., vol. 100, 2012, pages 022401
K. A. OMARI; T. J. HAYWARD, PHYSICAL REVIEW APPLIED, vol. 2, 2014, pages 044001
KENT, A. D.; WORLEDGE, D. C.: "A new spin on magnetic memories", NATURE NANOTECHNOLOGY, vol. 10, 2015, pages 187
KISELEV ET AL., NATURE, vol. 425, 2003, pages 380
L. ALVAREZ ET AL., PHYS. REV. LETT., vol. 104, 2010, pages 137205
L.K. BOGART ET AL., APPL. PHYS. LETT., vol. 94, 2011, pages 042511
LEE ET AL., APPL. PHYS. LETT., vol. 82, 2003, pages 2458
LEI ET AL., NAT. COMMS., 2013, pages 2386
LUC THOMAS ET AL., SCIENCE, vol. 330, 2010, pages 1810
M. DONAHUE; D. G. PORTER: "Interagency Report NISTIR 6376", September 1999, NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY, article "OOMMF User's Guide, Version 1.0"
M. GHIDINI; R. PELLICELLI; J.L. PRIETO ET AL., NAT. COMMS., 2013, pages 2398
M. LIU, J. APPL. PHYS., vol. 112, 2012, pages 063917
M. OVERBY; A. CHERNYSHOV; L.P. ROKHINSON ET AL., APPL. PHYS. LETT., vol. 92, 2008, pages 192501
M. WEILER; A. BRANDLMAIER; S. GEPRAGS ET AL., N. J. PHYS., vol. 11, 2009, pages 013021
M.T. BRYAN ET AL., APPL. PHYS. LETT., vol. 91, 2007, pages 142502
M.T. BRYAN ET AL., J. APPL. PHYS., vol. 103, 2008, pages 073906
M.T. BRYAN ET AL., J. PHYS. CONDENS. MATTER., vol. 24, 2012, pages 024205
NA LEI ET AL: "Strain-controlled magnetic domain wall propagation in hybrid piezoelectric/ferromagnetic structures", NATURE COMMUNICATIONS, vol. 4, 22 January 2013 (2013-01-22), United Kingdom, pages 1 - 7, XP055300354, ISSN: 2041-1723, DOI: 10.1038/ncomms2386 *
OHNO, H. ET AL., NATURE, vol. 408, 2000, pages 944 - 946
P.E. ROY ET AL., APPL. PHYS. LETT., vol. 99, 2011, pages 122504
PARKIN ET AL., SCIENCE, vol. 320, 2008, pages 190
PUSHP, A.; PHUNG, T.; RETTNER, C.; HUGHES, B. P.; YANG, S-H.; THOMAS, L.; PARKIN, S. S. P.: "Domain wall trajectory determined by its fractional topological edge defects", NAT. PHYS., vol. 9, 2013, pages 505
R. LAVRIJSEN ET AL., NATURE, vol. 493, 2013, pages 647
RAFALOVSKYI, I.; GUENNOU, M.; GREGORA, I.; HLINKA, J.: "Macroscopic lamellar heterophase pattern in Pb(Mgl/3Nb2/3)03-PbTi03 single crystals", PHYS. REV. B, vol. 93, 2016, pages 064110
S. KANAI ET AL., APPL. PHYS. LETT., vol. 101, 2012, pages 122403
S. MCGROUTHER ET AL., APPL. PHYS. LETT., vol. 91, 2007, pages 022506
S.A. CAVILL ET AL., APPL. PHYS. LETT., vol. 102, 2013, pages 032405
S.S.P. PARKIN ET AL., PHYS. REV. LETT., vol. 64, 1990, pages 2304
SATO, Y.; HIRAYAMA, T.; IKUHARA, Y.: "Real-time direct observations of polarisation reversal in a piezoelectric crystal: Pb(Mgl/3Nb2/3)03-PbTi03 studied via in situ electrical biasing transmission electron microscopy", PHYS. REV. LETT., vol. 107, 2011, pages 187601
SOHN ET AL.: "Electrically Driven Magnetic Domain Wall Rotation in Multiferroic Heterostructures to Manipulate Suspended On-Chip Magnetic Particles", ACS NANO, vol. 9, 2015, pages 4814
STOLICHNOV ET AL., NATURE MATERIALS, vol. 7, 2008, pages 464
SUN, IBM J. RES. & DEV., vol. 1, 2006, pages 80
T. B. GOENNENWEIN; M. ALTHAMMER; C. BIHLER ET AL., PHYS. STATUS SOLIDI RRL, vol. 2, 2008, pages 96
T. KOYAMA ET AL., NATURE MATERIALS, vol. 10, 2011, pages 194
T. MARUYAMA ET AL., NATURE NANOTECH., vol. 4, 2009, pages 158
TUOMAS H. E. LAHTINEN; KEVIN J. A. FRANKE; SEBASTIAAN VAN DIJKEN, SCI. REP., vol. 2, 2012, pages 258
U. RUEDIGER ET AL., PHYS. REV. LETT., vol. 80, 1998, pages 5639
UWE BAUER ET AL., APPL. PHYS. LETT., vol. 101, 2012, pages 172403
W. EERENSTEIN ET AL., NATURE, vol. 442, 2006, pages 759 - 765
WU, T.; ZHAO, P.; BAO, M.; BUR, A.; HOCKEL, J. L.; WONG, K.; MOHANCHANDRA, K. P.; LYNCH, C. S.; CARMAN, G. P.: "Domain engineered switchable strain states in ferroelectric (O11)[Pb(Mgl/3Nb2/3)03](1-x)-[PbTi03]x (PMN-PT, x=0.32) single crystals", J. APPL. PHYS., vol. 109, 2011, pages 124101, XP012147238, DOI: doi:10.1063/1.3595670
Y. NAKATANI ET AL., NATURE MATERIALS, vol. 2, 2003, pages 521
YOICHI SHIOTA ET AL., NATURE MATERIALS, vol. 11, 2012, pages 39

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11362268B2 (en) 2017-10-30 2022-06-14 Taiwan Semiconductor Manufacturing Company Ltd. Semiconductor structure and associated operating and fabricating method
TWI783018B (zh) * 2017-10-30 2022-11-11 台灣積體電路製造股份有限公司 半導體結構以及相關操作和製造方法
CN109103329A (zh) * 2018-08-15 2018-12-28 中国科学技术大学 一种电控自旋阀结构及非易失存储器件
US11487508B2 (en) 2019-04-15 2022-11-01 International Business Machines Corporation Magnetic tunnel junction based true random number generator
CN112002798A (zh) * 2020-08-03 2020-11-27 中国计量大学 一种连续可控磁畴壁移动和钉扎的器件和方法
CN112002361A (zh) * 2020-08-03 2020-11-27 中国计量大学 一种基于多铁异质结构的磁畴壁写入单元及方法
CN112002361B (zh) * 2020-08-03 2022-06-24 中国计量大学 一种基于多铁异质结构的磁畴壁写入单元及方法
CN112002798B (zh) * 2020-08-03 2022-10-04 中国计量大学 一种连续可控磁畴壁移动和钉扎的器件和方法
CN112712830A (zh) * 2020-12-09 2021-04-27 中国人民解放军国防科技大学 电压诱导的纳米点磁化单轴到涡旋态的非易失调控方法
CN112712830B (zh) * 2020-12-09 2022-05-13 中国人民解放军国防科技大学 电压诱导的纳米点磁化单轴到涡旋态的非易失调控方法
CN114532983A (zh) * 2022-01-17 2022-05-27 中国科学院电工研究所 一种磁声成像系统及方法
CN114532983B (zh) * 2022-01-17 2023-12-29 中国科学院电工研究所 一种磁声成像系统及方法

Similar Documents

Publication Publication Date Title
Guo et al. Ferroic tunnel junctions and their application in neuromorphic networks
Xiong et al. Antiferromagnetic spintronics: An overview and outlook
WO2016198886A1 (fr) Dispositifs et procédés d'enregistrement magnétique
Wang et al. Electric-field control of spin-orbit interaction for low-power spintronics
US10460786B2 (en) Systems and methods for reducing write error rate in magnetoelectric random access memory through pulse sharpening and reverse pulse schemes
Yao et al. Electrically driven reversible magnetic rotation in nanoscale multiferroic heterostructures
JP5414681B2 (ja) 電流によって誘起されるスピン運動量移動に基づいた、高速かつ低電力な磁気デバイス
EP2446471B1 (fr) Dispositifs magnétiques basse puissance grande vitesse basés sur un transfert de moment de spin induit par courant
JP5431400B2 (ja) 磁気記憶素子
US20160276006A1 (en) Circuits and devices based on spin hall effect to apply a spin transfer torque with a component perpendicular to the plane of magnetic layers
KR101559216B1 (ko) 바이폴라 스핀-전달 스위칭
Tian et al. Topological domain states and magnetoelectric properties in multiferroic nanostructures
JPWO2016159017A1 (ja) 磁気抵抗効果素子、磁気メモリ装置、製造方法、動作方法、及び集積回路
JP5508868B2 (ja) 磁気抵抗素子
KR20090007201A (ko) 자기저항 디바이스
JP2007080952A (ja) 多値記録スピン注入磁化反転素子およびこれを用いた装置
Ren et al. Efficient Spin–Orbit Torque Switching in a Perpendicularly Magnetized Heusler Alloy MnPtGe Single Layer
Liang et al. Deterministic switching of a magnetoelastic single-domain nano-ellipse using bending
Gong et al. A new pathway towards all-electric spintronics: electric-field control of spin states through surface/interface effects
KR102073467B1 (ko) 교류전류를 이용한 스핀 궤도 토크 자기 메모리 소자
JP5576960B2 (ja) 磁気記憶素子、磁気記憶装置、および磁気メモリ
Tiercelin et al. Strain mediated magnetoelectric memory
Li et al. Direct observation of magnetic vortex behavior in an ordered La 0.7 Sr 0.3 MnO 3 dot arrays
Chen et al. Electric-Field-Enhanced Bulk Perpendicular Magnetic Anisotropy in GdFe/Pb (Mg1/3Nb2/3) 0.7 Ti0. 3O3 Multiferroic Heterostructure
Peng et al. Electric-field-driven Deterministic and Robust 120° magnetic rotation in a concave triangular nanomagnet

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16729344

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16729344

Country of ref document: EP

Kind code of ref document: A1