WO2016042530A1 - Virtual cathode deposition (vcd) for thin film manufacturing - Google Patents
Virtual cathode deposition (vcd) for thin film manufacturing Download PDFInfo
- Publication number
- WO2016042530A1 WO2016042530A1 PCT/IB2015/057205 IB2015057205W WO2016042530A1 WO 2016042530 A1 WO2016042530 A1 WO 2016042530A1 IB 2015057205 W IB2015057205 W IB 2015057205W WO 2016042530 A1 WO2016042530 A1 WO 2016042530A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- thin film
- hollow cathode
- target
- film deposition
- deposition apparatus
- Prior art date
Abstract
Description
Claims