WO2016020668A1 - Membrane - Google Patents
Membrane Download PDFInfo
- Publication number
- WO2016020668A1 WO2016020668A1 PCT/GB2015/052253 GB2015052253W WO2016020668A1 WO 2016020668 A1 WO2016020668 A1 WO 2016020668A1 GB 2015052253 W GB2015052253 W GB 2015052253W WO 2016020668 A1 WO2016020668 A1 WO 2016020668A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- electrolyte membrane
- nanofibres
- membrane according
- membrane
- polymer
- Prior art date
Abstract
Description
Claims