WO2016010343A1 - 은 부직포 및 그 제조방법 - Google Patents
은 부직포 및 그 제조방법 Download PDFInfo
- Publication number
- WO2016010343A1 WO2016010343A1 PCT/KR2015/007304 KR2015007304W WO2016010343A1 WO 2016010343 A1 WO2016010343 A1 WO 2016010343A1 KR 2015007304 W KR2015007304 W KR 2015007304W WO 2016010343 A1 WO2016010343 A1 WO 2016010343A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- silver
- nonwoven fabric
- production method
- producing
- drying
- Prior art date
Abstract
본 발명은 은을 함유하는 은 부직포 및 은 부직포 제조방법에 관한 것으로서, 섬유 제조용 폴리머에 은입자가 콜로이드 고착시켜 방취 항균 성질의 은(Ag)을 섬유에 고착하는 제조방법을 얻기 위한 것이 바, 장마철의 하우스 포장물로 사용되는 부직포에서 곰팡이 발생을 현저히 줄이고 인체접속부위에 사용되는 은 부직포는 음이온 발생으로 피부에 친환경 상태가 될 뿐 아니라 항균 방취 기능이 있어 병원의 침대보, 의사, 간호사, 환자의 가운, 수건, 마스크, 일회용 수건 브레지어, 기저귀, 생리대 등을 만들면 질병으로부터 매우 안전하고 위생적인 으로 사용할 수 있는 효과가 있는 발명인 것이다.
Description
본 발명은 은을 함유하는 은 부직포 및 은 부직포 제조방법에 관한 것으로서, 더욱 상세하게는 섬유 제조용 폴리머에 은입자가 콜로이드 고착시켜 방취 항균 성질의 은(Ag)을 섬유에 고착하는 제조방법에 관한 것이다.
종래의 섬유는 섬유제품에 미생물이 발생번식하면 섬유의 취화와 변색현상이 발생되고 동시에 악취를 내고 인체피부에 염증을 유발시키게 된다. 즉, 미생물은 그의 성장 및 증식에 필요한 영양분을 얻기 위해 유기물에 기생하면서 세포로부터 효소를 밖으로 내보내어 단백질이나 탄수화물등을 아미노산이나 글루코스 등으로 변화시켜서 세포막내로 흡수시키고 단백질과 탄수화물로 재합성하면서 증식되어간다. 섬유는 호제, 가공제 및 땀에 의하여 미생물의 번식이 되는데 특히 땀은 수분, 염분 및 뇨소를 함유하며 발생초기에는 pH3.8-6.4이지만 미생물에 의한 뇨소분해로 다량의 암모니아가 발생되어 pH가 급격히 상승되고 미생물의 신진대사 과정에 따른 젖산, 초산 및 규산생성으로 인하여 그 특유한 냄새를 풍기게 되는 원인이 되고
있는 것이며 또 피부를 자극하여 염증을 유발시키는 것이다. 따라서, 섬유제품에 미생물이 번식하지 못하도록 위생사를 제조하는 방법이 알려지고 있는 바, 종래에 알려지고 있는 위생사를 제조하는 방법으로는 N,N-디데실-N-메틸-3(트리메톡시실릴)족 염화암모늄이나 5-클로로-2(2,4-디클로로페녹실) 페놀 등을 후가공해서 처리하는 방법이 알려지고 있다. 그러나, 이러한 방법은 후가공이라는 공법상의 특성 때문에 제조된 제품에 내구성이 없고 가격도 비싸며 또 음이온 또는 양이온 가공제와 혼용할 수 없는 등 가공 상의 문제점도 많은 것이었다. 다음으로 은(銀)은 예로부터 자연항생제로 사용하였으며, 수용액상태의 은용액을 만들어 음용하기도 하였다. 또한, 근래에는 은(銀)의 항균효과와 해독작용이 밝혀지면서 다양한 실험과 함께 그 적용분야를 넓혀가고 있는 실정이다.
비스코스 레이온, 폴리에스터, 폴리푸로피렌, 폴리에치렌, 단독 또는 2가지 이상 섞어 제조되는 부직포는 환자, 의사 가운에서부터 생리대, 기저귀, 천막, 건축자재 등 매우 광범위하게 사용되고 있다. 그러나 인체 접촉하는 부분 사용될 때는 양전하 상태가 되어 피부에 알레르기 피부병도 되고 하여 천연섬유를 선호하고 있다. 인체 접촉부분을 은을 함유한 부직포를 만들면 음전하가 발생되어 친화적 기능이 되고 항균 방취 기능도 있게 되어 가격이 면 섬유보다 저렴하면서도 대량생산기능도 있게 된다.
일반적으로 은(Ag)은 독소를 제거할 뿐만 아니라, 바이러스 및 세균성 감염병 등을 포함하여 약 650 종류의 병을 치료할 수 있으며, 세균의 신진대사 작용을 하는 효소를 무력화시켜 탁월한 항균 효과를 지닌 것으로 밝혀졌다. 이러한 효과 때문에 은(Ag)은 식기 또는 장신구 등으로 사용되어 왔으며, 최근에는 항생제, 정수기의 필터 등에 응용되고 있다.
종래에 은을 이용하여 제조하는 살균성 섬유는 소정의 섬유제조용 칩과 고체인 미세한 은입자를 혼합하여 섬유를 제조하거나, 단순히 섬유의 표면에 은입자를 코팅하여 제조하였다. 그러나, 섬유제조용 칩과 은입자를 혼합하여 섬유를 제조하는 방법은 고체의 은입자를 이용하기 때문에 단순히 미세한 은입자가 섬유조직 내에 함몰되어 있을 뿐이고, 은입자를 균일하게 섬유조직에 분산시키지 못하는 단점이 있었다. 또한, 섬유의 표면에 은입자를 코팅하는 방법은 견고한 결합관계를 형성하지 못하기 때문에 세탁 등의 과정을 통해 쉽게 탈피될 수 있어 초기에 갖고 있는 살균력이 그대로 유지되기 어려운 단점이 있었다.
본 발명은 종래의 문제점을 개선한 것으로 습기 있는 곳에서 곰팡이 발생을 현저히 감소시키고 음전하를 발생케 되어 친환경적이면서 항균 방취 기능을 갖게하는데 그 목적이 있다.
또한 본 발명의 다른 목적은 섬유에 은입자(나노입자)를 고루게 고착할 수 있는 은 부직포 및 그 제조방법을 제공하는 데 있다.
본 발명의 과제의 해결수단은 은 부직포는 종래 부직포를 완성단계에서 배출시나 별도 권취된 부직포를 8에서 10PPM 은 이은수를 만드는 저수통에 침적과 탈수를 하여 통과케 하여 은 부직포를 제조하여 달성하였다.
본 발명의 효과는 장마철의 하우스 포장물로 사용되는 부직포에서 곰팡이 발생을 현저히 줄이고 인체접속부위에 사용되는 은 부직포는 음이온 발생으로 피부에 친환경 상태가 될 뿐 아니라 항균 방취 기능이 있어 병원의 침대보, 의사, 간호사, 환자의 가운, 수건, 마스크, 일회용 수건 브레지어, 기저귀, 생리대를 만들면 질병으로부터 매우 안전하고 위생적인 효과가 있는 발명인 것이다.
도 1은 본 발명의 바람직한 실시예의 은 부직포 및 그 제조방법의 상태도.
도 2는 본 발명으로 제조한 은 부직포의 사시도.
이하, 본 발명의 바람직한 실시예를 첨부된 도면을 참조하여 상세히 설명한다.
명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정 해석되지 아니하며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.
따라서, 본 명세서에 기재된 실시예와 도면에 도시된 구성은 본 발명의 가장 바람직한 일 실시예에 불과할 뿐이고 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다.
도 1에 도시한 본 발명의 은 부직포 및 그 제조방법은
비스코스 레이온, 폴리에스터, 폴리푸로피렌, 폴리에치렌 중에 단독 또는 2가지 이상으로 합성된 부직포;
상기 부직포를 40℃~50℃ 온도를 유지하면서 다수개의 은에 전원을 공급하되 전원을 (+),(-)를 번갈아 가면서 전원을 24V공급하여 은(Ag)이 8~10PPM 용출되게 하고, 상기 수조에 0.3~2% 명반을 혼합하여 교반한 후, 부직포를 수조내에서 함침되어 탈수를 거친 후에 건조하여 생산되는 특징이 있다.
상기 부직포는 비스코스 레이온, 폴리에스터, 폴리푸로필렌, 폴리에치렌을 단독 또는 2종 이상을 섞어 부직포를 제조 배출 단계에서 또는 별도 권취된 부직포(100)를 합성수지 수조(2)를 구조하고 수중 초음파(3)가 작동되어 교반이 잘이루어지도록 형성한 특징이 있다.
상기 수조에 은 이온수에 0.3~1% 명반을 혼합하여, 상기 부직포에 은(銀)입자가 고착이 잘 이루어지도록 매염제인 명반을 공급하였다.
또한 상기 수조의 온도를 일정하게 유지하도록 히터를 내장되어 온도가 일정하게 유지될 수 있도록 형성한 특징이 있다.
상기 수조의 온도는 40℃~50℃로 유지하면서 은(봉)전극 24V로 작동되는 은전극(50)이 연결된 은 이온수제조 장치(5)를 내부에 설치하여 나노화 된 은이 8~10PPM 용출케 하여 수조내에 은이온이 함유케 하였다.
상기 부직포의 생산을 위해 롤에 감겨진 부직포를 수저에 함침되어 이동될 수 있도록 롤러를 다수개 배열하고, 상기 배열된 롤러의 상부에는 부직포를 탈 수 하기 위한 압착하는 탈수 롤러가 형성된다.
상기와 같이 탈수 롤러를 통과한 부직포를 건조 히터와 건조 송풍기를 형성한 건조부를 통과하여 건조가 이루어지도록 형성한 특징이 있다.
상기와 같이 부직포를 건조하기 위한 저수조(2) 말미에 실리콘이나 합성수지로 된 탈수 롤러(60)(60)'로 탈수 후 건조 히터(30)(30)'와 건조 송풍기(40)에 의해 건조 이송케 하여 제조가 이루어진다.
상기 건조 히터, 건조 송풍기, 은전극, 수중 초음파기에 전원을 공급하도록 전원공급선이 연결되어 전원을 공급하도록 형성하였다.
상기 은(Ag) 이온수제조 장치(5)는 은전극에 전원을 (+),(-)를 교차하여 전원을 공급하여 두 전극에 은전극이 전기분해되어 물에 이온화가 이루어지도록 형성하였다.
상기와 같이 은용액을 형성한 상기 수조의 온도는 40℃~50℃로 유지하면서 은(봉)전극 24V로 작동되는 은전극(50)이 연결된 은 이온수제조 장치(5)를 내부에 설치하여 나노화 된 은이 8~10PPM 용출케 하여 수조 내에 은이온이 함유케 하였다.
증류수에 은(Ag)을 전해방법으로 8~10PPM 콜로이드 이온화시킨 용액 20에 은이온수가 일반세균등 650여 가지의 탁월한 살균소독 기능으로 인한 근본적이고 효과적인 살균과 전염성 예방에 효과와 재생에 탁월한 기능이 있다.
이와 같은 본 발명의 시험성적결과는 다음과 같다.
표 1 
Claims (5)
- 비스코스 레이온, 폴리에스터, 폴리푸로피렌, 폴리에치렌 중에 단독 또는 2가지 이상으로 합성된 부직포;상기 부직포를 40℃~50℃ 온도를 유지하면서 다수개의 은(銀)에 전원을 공급하되 전원을 (+),(-)를 번갈아 가면서 전원을 24V공급하여 은(Ag)이 8~10PPM 용출되게 하고, 상기 수조에 0.3~2% 명반을 혼합하여 교반한 후,부직포를 수조 내에서 함침되어 탈수를 거친 후에 건조하여 생산되는 것을 특징으로 하는 은 부직포 제조방법.
- 제 1항에 있어서, 상기 수조에 침적된 상태는 1분~20분을 함침하고, 수중초음파를 이용하여 부직포와 은용액의 고착이 잘 이루어지도록 진동발생케 것을 특징으로 하는 은 부직포 제조방법.
- 제 1항에 있어서,상기 부직포(100)가 2초에서 5초간 수조에서 침적상태를 유지케 한 후 배출부쪽에서 실리콘이나 합성수지로 된 탈수로라(60)(60')를 거쳐 건조히터(30)(30'), 건조 송풍기(40)를 거처 건조된 부직포가 연속적으로 제조하는 것을 특징으로 하는 은 부직포 제조방법.
- 제 1항에 있어서, 상기 합성된 부직포를 직조섬유로 대처하여 처한 것을 특징으로 하는 은 부직포 제조방법.
- 제 1항에 의해 제조된 은 부직포.