WO2015138449A1 - High temperature non-crosslinked polyethylene-based foam and methods of making the same - Google Patents
High temperature non-crosslinked polyethylene-based foam and methods of making the same Download PDFInfo
- Publication number
- WO2015138449A1 WO2015138449A1 PCT/US2015/019705 US2015019705W WO2015138449A1 WO 2015138449 A1 WO2015138449 A1 WO 2015138449A1 US 2015019705 W US2015019705 W US 2015019705W WO 2015138449 A1 WO2015138449 A1 WO 2015138449A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- low density
- linear low
- density polyethylene
- foam
- temperature
- Prior art date
Abstract
Description
Claims