WO2015126252A1 - Composition d'asphalte et procédé de préparation d'une telle composition - Google Patents
Composition d'asphalte et procédé de préparation d'une telle composition Download PDFInfo
- Publication number
- WO2015126252A1 WO2015126252A1 PCT/NL2015/050111 NL2015050111W WO2015126252A1 WO 2015126252 A1 WO2015126252 A1 WO 2015126252A1 NL 2015050111 W NL2015050111 W NL 2015050111W WO 2015126252 A1 WO2015126252 A1 WO 2015126252A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- particles
- aggregates
- elastic
- binder material
- gap
- Prior art date
Abstract
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP15710943.0A EP3107973A1 (fr) | 2014-02-21 | 2015-02-20 | Composition d'asphalte et procédé de préparation d'une telle composition |
JP2016570756A JP2017509818A (ja) | 2014-02-21 | 2015-02-20 | アスファルト組成物及びこの組成物の調製方法 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
NL2012307A NL2012307C2 (en) | 2014-02-21 | 2014-02-21 | Asphalt composition and process for preparing such a composition. |
NL2012307 | 2014-02-21 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2015126252A1 true WO2015126252A1 (fr) | 2015-08-27 |
Family
ID=50440788
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/NL2015/050111 WO2015126252A1 (fr) | 2014-02-21 | 2015-02-20 | Composition d'asphalte et procédé de préparation d'une telle composition |
Country Status (4)
Country | Link |
---|---|
EP (1) | EP3107973A1 (fr) |
JP (1) | JP2017509818A (fr) |
NL (1) | NL2012307C2 (fr) |
WO (1) | WO2015126252A1 (fr) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN107988877A (zh) * | 2017-11-28 | 2018-05-04 | 重庆合泽道路工程有限公司 | 一种沥青发泡装置 |
CN110734742A (zh) * | 2019-09-09 | 2020-01-31 | 安徽省交通控股集团有限公司 | 一种新旧路面接缝处治材料及其制备方法和施工方法 |
WO2021019482A1 (fr) * | 2019-07-31 | 2021-02-04 | Alessandro Mondini | Conglomérat pour la fabrication de revêtements de chaussées, composé pour la fabrication du conglomérat et procédé de production associé |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB1325916A (en) | 1970-01-20 | 1973-08-08 | Mobil Oil Corp | Method and apparatus for producing foamed materials |
US3999743A (en) | 1975-08-11 | 1976-12-28 | Mendenhall Robert Lamar | Asphalt-aggregate recycle process and apparatus |
US4096588A (en) | 1975-08-11 | 1978-06-20 | Mendenhall Robert Lamar | Recycled asphalt-aggregate process and apparatus |
US20040044104A1 (en) | 2000-12-28 | 2004-03-04 | Mitsuaki Maeda | Elastic pavement material containing waste rubber |
EP1767581A1 (fr) | 2005-09-26 | 2007-03-28 | Koninklijke BAM Groep nv | Procédé pour la production d'une composition d'asphalte et son utilisation |
JP2007154539A (ja) | 2005-12-06 | 2007-06-21 | Bridgestone Corp | 低騒音舗装体 |
WO2011074003A2 (fr) | 2009-12-14 | 2011-06-23 | Bharat Petroleum Corporation Ltd. | Compositions de bitume modifié à la poudrette de caoutchouc et procédé associé |
Family Cites Families (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4548962A (en) * | 1981-12-29 | 1985-10-22 | All Seasons Surfacing Corporation | Rubberized asphaltic concrete composition |
JP3059566B2 (ja) * | 1992-02-14 | 2000-07-04 | 大林道路株式会社 | 舗設方法 |
JP3243631B2 (ja) * | 1994-12-08 | 2002-01-07 | 日本鋪道株式会社 | 人工骨材を使用した舗装体 |
JP2002371505A (ja) * | 2001-06-19 | 2002-12-26 | Obayashi Road Corp | 舗装構造及びアスファルト舗装材 |
JP4204424B2 (ja) * | 2003-09-19 | 2009-01-07 | 株式会社フコク | 多孔質弾性舗装材及びその多孔質弾性舗装材を用いた多孔質弾性舗装用パネルの作製方法 |
-
2014
- 2014-02-21 NL NL2012307A patent/NL2012307C2/en active
-
2015
- 2015-02-20 JP JP2016570756A patent/JP2017509818A/ja active Pending
- 2015-02-20 WO PCT/NL2015/050111 patent/WO2015126252A1/fr active Application Filing
- 2015-02-20 EP EP15710943.0A patent/EP3107973A1/fr not_active Withdrawn
Patent Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB1325916A (en) | 1970-01-20 | 1973-08-08 | Mobil Oil Corp | Method and apparatus for producing foamed materials |
US3999743A (en) | 1975-08-11 | 1976-12-28 | Mendenhall Robert Lamar | Asphalt-aggregate recycle process and apparatus |
US4096588A (en) | 1975-08-11 | 1978-06-20 | Mendenhall Robert Lamar | Recycled asphalt-aggregate process and apparatus |
US20040044104A1 (en) | 2000-12-28 | 2004-03-04 | Mitsuaki Maeda | Elastic pavement material containing waste rubber |
EP1767581A1 (fr) | 2005-09-26 | 2007-03-28 | Koninklijke BAM Groep nv | Procédé pour la production d'une composition d'asphalte et son utilisation |
JP2007154539A (ja) | 2005-12-06 | 2007-06-21 | Bridgestone Corp | 低騒音舗装体 |
WO2011074003A2 (fr) | 2009-12-14 | 2011-06-23 | Bharat Petroleum Corporation Ltd. | Compositions de bitume modifié à la poudrette de caoutchouc et procédé associé |
Non-Patent Citations (18)
Title |
---|
A. VON MEIER ET AL: "A noise-absorbing road surface made of poroelastic asphaltic concrete (GB-HR-35-01)", 1 January 1986 (1986-01-01), pages 1 - 114, XP055134362, Retrieved from the Internet <URL:http://www.asphaltrubber.org/ARTIC/International/RPA_A1148.pdf> [retrieved on 20140812] * |
ANONYMOUS: "Aggregate Gradation", STUDENT HANDOUT, 11 June 2014 (2014-06-11), pages 1 - 31, XP055134130, Retrieved from the Internet <URL:http://www.ce.memphis.edu/3137/Powerpoint Handouts/2 - Aggregate Gradation and Sampling.pdf> [retrieved on 20140811] * |
ANONYMOUS: "Crumb Rubber Modifier, Workshop Notes", 1 January 1993 (1993-01-01), pages 1 - 295, XP055031446, Retrieved from the Internet <URL:http://isddc.dot.gov/OLPFiles/FHWA/013377.pdf> [retrieved on 20120702] * |
ANONYMOUS: "The Double Barrel Aggregate Dryer/Drum Mixer", 12 August 2010 (2010-08-12), pages 1 - 20, XP055134416, Retrieved from the Internet <URL:http://www.astecinc.com/images/file/literature/Astec_Double_Barrel.pdf> [retrieved on 20140812] * |
BAOSHAN HUANG ET AL: "Louisiana Experience with Crumb Rubber-Modified Hot-Mix Asphalt Pavement", TRANSPORTATION RESEARCH RECORD, vol. 1789, no. 1, 1 January 2002 (2002-01-01), pages 1 - 13, XP055134402, ISSN: 0361-1981, DOI: 10.3141/1789-01 * |
F. OLARD ET AL: "LOW EMISSION & LOW ENERGY ASPHALTS FOR SUSTAINABLE ROAD CONSTRUCTION: THE EUROPEAN EXPERIENCE OF LEA PROCESS", 1 January 2011 (2011-01-01), pages 1 - 10, XP055078773, Retrieved from the Internet <URL:http://www.aapaq.org/q/2011st/CAPSA2011/FA1_05_107_1111.pdf> [retrieved on 20130911] * |
FEIPENG XIAO ET AL: "Laboratory Investigation of Dimensional Changes of Crumb Rubber Reacting with Asphalt Binder", ROAD MATERIALS AND PAVEMENT DESIGN. VOLUME X - NO. X/2006, 1 January 2006 (2006-01-01), pages 1 - 21, XP055056634, Retrieved from the Internet <URL:http://www.clemson.edu/ces/arts/Dimensional Changes of Crumb Rubber Binder.pdf> [retrieved on 20130314] * |
JENKINS K J: "Mix design considerations for cold and half-warm bituminous mixes with emphasis on foamed bitumen", 1 September 2000 (2000-09-01), pages I - XVII,1, XP008125845, Retrieved from the Internet <URL:http://www.tudelft.nl/live/ServeBinary?id=f3ab4a9e-2345-4fe9-874f-0e92b59eb89b&binary=/doc/Jerkins+-+Complete+PhD+Jenkins.pdf> * |
JULIEN BUISSON ET AL: "The Mastic Asphalt Industry - A Global Perspective The Mastic Asphalt Industry - A Global Perspective", 1 November 2010 (2010-11-01), pages 1 - 29, XP055117933, Retrieved from the Internet <URL:http://www.mastic-asphalt.eu/fileadmin/user_upload/pdf/Health___Safety/EMAA_global_perspective_mastic_asphalt.pdf> [retrieved on 20140514] * |
MARK S. BUNCHER: "Evaluating the Effects of the Wet and Dry Process for Inclusding Crumb Rubber Modifier in Hot Mix Asphalt", DISSERTATION, 30 August 1995 (1995-08-30), Auburn, Alabama, USA, pages 1 - 186, XP055034600, Retrieved from the Internet <URL:http://asphaltrubber.org/ARTIC/RPA_A1059.pdf> [retrieved on 20120803] * |
NILS ULMGREN ET AL: "Quiet City Transport, Vehicle/Infrastructure interface related noise, Refine and optimize the road surface, D3.18 Studies of poroelastic road surfaces in a lab-scale. (TIP4-CT-2005-516420)", PROJECT FUNDED BY THE EUROPEAN COMMUNITY UNDER THE SIXTH FRAMEWORK PROGRAMME PRIORITY 6 SUSTAINABLE DEVELOPMENT, GLOBAL CHANGE & ECOSYSTEMS, 15 February 2006 (2006-02-15), pages 1 - 64, XP055134373, Retrieved from the Internet <URL:http://www.qcity.org/downloads/SP3/D3-18_NCC_12M.pdf> [retrieved on 20140812] * |
PASQUINI E ET AL: "Performance evaluation of gap graded Asphalt Rubber mixtures", CONSTRUCTION AND BUILDING MATERIALS, ELSEVIER, NETHERLANDS, vol. 25, no. 4, 1 April 2011 (2011-04-01), pages 2014 - 2022, XP027581632, ISSN: 0950-0618, [retrieved on 20101231] * |
R GO?EBIEWSKI ET AL: "Traffic noise reduction due to the porous road surface", APPLIED ACOUSTICS 64 (2003) 481-494, 1 January 2003 (2003-01-01), pages 481 - 494, XP055134360, Retrieved from the Internet <URL:http://www.sciencedirect.com/science/article/pii/S0003682X0200124X/pdf?md5=dacacc1018615f7c7aae2fa31eb276ac&pid=1-s2.0-S0003682X0200124X-main.pdf> [retrieved on 20140812] * |
See also references of EP3107973A1 |
SHEN D H ET AL: "Properties of gap-aggregate gradation asphalt mixture and permanent deformation", CONSTRUCTION AND BUILDING MATERIALS, ELSEVIER, NETHERLANDS, vol. 19, no. 2, 1 March 2005 (2005-03-01), pages 147 - 153, XP027787782, ISSN: 0950-0618, [retrieved on 20050301] * |
TONGSHENG ZHANG ET AL: "A new gap-graded particle size distribution and resulting consequences on properties of blended cement", CEMENT AND CONCRETE COMPOSITES, vol. 33, no. 5, 1 May 2011 (2011-05-01), pages 543 - 550, XP055064277, ISSN: 0958-9465, DOI: 10.1016/j.cemconcomp.2011.02.013 * |
ULF SANDBERG ET AL: "The Poroelastic Road Surface - Results of an Experiment in Stockholm", FORUMACUSTICUM 2005, 1 January 2005 (2005-01-01), pages 1205 - 1210, XP055134355, Retrieved from the Internet <URL:http://www.conforg.fr/acoustics2008/cdrom/data/fa2005-budapest/paper/834-0.pdf> [retrieved on 20140812] * |
ULF SANDBERG ET AL: "Tyre/road noise reduction of poroelastic road surface tested in a laboratory", PROCEEDINGS OF ACOUSTICS 2013 - VICTOR HARBOR, AUSTRALIA, 20 November 2013 (2013-11-20), pages 1 - 8, XP055134357, Retrieved from the Internet <URL:http://www.acoustics.asn.au/conference_proceedings/AAS2013/papers/p98.pdf> [retrieved on 20140812] * |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN107988877A (zh) * | 2017-11-28 | 2018-05-04 | 重庆合泽道路工程有限公司 | 一种沥青发泡装置 |
WO2021019482A1 (fr) * | 2019-07-31 | 2021-02-04 | Alessandro Mondini | Conglomérat pour la fabrication de revêtements de chaussées, composé pour la fabrication du conglomérat et procédé de production associé |
CN110734742A (zh) * | 2019-09-09 | 2020-01-31 | 安徽省交通控股集团有限公司 | 一种新旧路面接缝处治材料及其制备方法和施工方法 |
Also Published As
Publication number | Publication date |
---|---|
JP2017509818A (ja) | 2017-04-06 |
NL2012307C2 (en) | 2015-08-25 |
EP3107973A1 (fr) | 2016-12-28 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
Mashaan et al. | A review on using crumb rubber in reinforcement of asphalt pavement | |
RU2468049C2 (ru) | Модификаторы асфальта для применения в "теплых смесях", включающие промотор адгезии | |
US11142667B2 (en) | Asphalt additive compositions and methods of making and using thereof | |
CN103282441B (zh) | 使用重油飞灰来改进沥青粘结剂和沥青混凝土性能 | |
NL2010586C2 (en) | Mastic composition for asphalt mixtures and process for making such a mastic composition. | |
RU2733749C2 (ru) | Битумная композиция, содержащая смесь восков, состоящую из нефтяного сырого парафина и воска фишера-тропша, применение смеси восков в битумных композициях, применение битумной композиции в асфальтовых композициях, асфальтовые композиции, содержащие битумную композицию, и способ изготовления асфальтовых покрытий из них | |
KR101511236B1 (ko) | 인도네시아 부톤 천연 아스팔트를 이용한 저비용 및 친환경 구스 아스팔트 포장용 아스팔트 바인더 조성물 및 그 제조방법 | |
KR100986718B1 (ko) | 폐이피디엠분말을 이용한 개질 아스팔트의 제조방법 | |
Akisetty | Evaluation of warm asphalt additives on performance properties of CRM binders and mixtures | |
NL2012307C2 (en) | Asphalt composition and process for preparing such a composition. | |
KR102225398B1 (ko) | 아스팔트 혼합물용 개질 첨가제 및 이를 첨가한 개질 아스팔트 혼합물 | |
RU2740062C1 (ru) | Каучуковый композиционный материал и способ его получения | |
KR102226750B1 (ko) | 순환 아스팔트 혼합물용 개질 첨가제 및 이를 첨가한 순환 개질 아스팔트 혼합물 | |
US11945953B2 (en) | Ground tire rubber density modification using elastomeric polymers | |
Batari et al. | Rutting assessment of crumb rubber modifier modified warm mix asphalt incorporating warm asphalt additive | |
US10407557B2 (en) | Sulfur extended asphalt modified with crumb rubber for paving and roofing | |
KR101511237B1 (ko) | 인도네시아 부톤 천연 아스팔트를 이용한 저비용 및 친환경 구스 아스팔트 포장용 아스팔트 혼합물 및 그 제조방법 | |
Singh et al. | Experimental study on the behavior of modified bituminous concrete mix developed using plastic waste and scrapped rubber tyre | |
WO2015023494A1 (fr) | Asphalte enrichi en soufre modifié au moyen d'un granulé de caoutchouc pour chaussée et toiture | |
Hamdou et al. | Effect of polymers on permanent deformation of flexible pavement | |
Zolfaghari et al. | Modification of Bitumen by Varying Size of the Crumb Rubber in Coarse Graded Aggregates | |
Mallick et al. | Specialty Applications | |
Ahmad | Using Crumb Rubber (CR) of Scrap Tire in Hot Mix Asphalt Design | |
Abdullah Al Hossain | Study on the rheological properties of polymer modified bituminous binder and mixes | |
Yousef | Influence Of Clay and Rubber On The Performance Of Egyptian Asphalt |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 15710943 Country of ref document: EP Kind code of ref document: A1 |
|
DPE1 | Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101) | ||
ENP | Entry into the national phase |
Ref document number: 2016570756 Country of ref document: JP Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
REEP | Request for entry into the european phase |
Ref document number: 2015710943 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |