WO2015112478A1

WO2015112478A1 - Photosensitive resin composition

Info

Publication number: WO2015112478A1
Application number: PCT/US2015/011988
Authority: WO
Inventors: Kyle P. BALDWIN; Miguel A. BARBOZA; Kerry O'brate; Rogelio Sanchez
Original assignee: Macdermid Printing Solutions, Llc
Priority date: 2014-01-22
Filing date: 2015-01-20
Publication date: 2015-07-30
Also published as: CN105980930B; CN105980930A; TWI598228B; US10025183B2; JP2017506360A; EP3097453A4; US20150205199A1; EP3097453A1; ES2896049T3; TW201545872A; EP3097453B1

Abstract

A photosensitive printing blank having is described. The photosensitive printing blank comprises at least one photocurable layer that is capable of being selectively crosslinked and cured upon exposure to actinic radiation at a desired wavelength region comprising (a) at least one elastomeric binder, (b) at least one ethylenically unsaturated monomer, (c) a photoinitiator having a favorable absorption profile in the desired wavelength region used for exposing the at least one photocurable layer to actinic radiation, and (d) a dye, wherein the dye exhibits a suitable percent transmission as measured with a UV spectrophotometer at the desired wavelength region used for exposing the at least one photocurable layer to actinic radiation, and optionally an infrared ablatable layer disposed on the at least one photocurable layer. A method of making a relief image printing element from the photosensitive printing blank is also described.

Description

PHOTOSENSITIVE RESIN COMPOSITION

FIELD OF THE INVENTION

The present invention relates generally to a method of making a flexographic printing element having improved exposure latitude,

BACKGROUND OF THE INVENTION

Flexography is a method of printing that is commonly used for high-volume runs. Flexography is employed for printing on a variety of substrates such as paper, paperboard stock, corrugated board, films, foils and laminates. Newspapers and grocery bags are prominent examples. Coarse surfaces and stretch films can be economically printed only by means of flexography.

Flexographic printing plates are relief plates with image elements raised above open areas. Generally, the plate is somewhat soft, and flexible enough to wrap around a printing cylinder, and durable enough to print over a million copies. Such plates offer a number of advantages to the printer, based chiefly on their durability and the ease with which they can be made. A typical flexographic printing plate as delivered by its manufacturer is a multilayered article made of, in order, a backing or support layer; one or more unexposed photocurable layers; optionally a protective layer or slip film; and often, a protective cover sheet.

The support (or backing) layer lends support to the plate. The support layer can be formed from a transparent or opaque material such as paper, cellulose film, plastic, or metal. Preferred materials include sheets made from synthetic polymeric materials such as polyesters, polystyrene, polyolefin, polyamides, and the like, including polyethylene terephthalate (PET), polyethylene naphthalate (PEN), and polybutylene terephthalate (PBT). The support may be in sheet form or in cylindrical form, such as a sleeve. The sleeve may be formed from single layer or multiple layers of flexible material. Flexible sleeves made of polymeric films are preferred, as they typically are transparent to ultraviolet radiation and thereby accommodate backflash exposure for building a floor in the cylindrical printing element. One widely used support layer is a flexible film of polyethylene terephthalate. The photocurable layer(s) can include any of the known photopolymers, monomers, initiators, reactive or non-reactive diluents, fillers, processing aids, UV absorbers and dyes. As used herein, the term "photocurable" refers to a composition which undergoes polymerization, cross-linking, or any other curing or hardening reaction in response to actinic radiation with the result that the unexposed portions of the material can be selectively separated and removed from the exposed (cured) portions to form a three-dimensional relief pattern of cured material. Exemplary photocurable materials are disclosed in European Patent Application Nos. 0 456 336 A2 and 0 640 878 Al to Goss, et al., British Patent No. 1,366,769, U.S. Pat. No. 5,223,375 to Berrier, et al., U.S. Pat. No. 3,867,153 to MacLahan, U.S. Pat. No. 4,264,705 to Allen, U.S. Pat. Nos. 4,323,636, 4,323,637, 4,369,246, and 4,423,135 all to Chen, et al, U.S. Pat. No. 3,265,765 to Holden, et al., U.S. Pat. No. 4,320,188 to Heinz, et al., U.S. Pat. No. 4,427,759 to Gruetzmacher, et al., U.S. Pat. No. 4,622,088 to Min, and U.S. Pat. No. 5,135,827 to Bohm, et al., the subject matter of each of which is herein incorporated by reference in its entirety. More than one photocurable layer may also be used. The photocurable layer(s) may be applied directly on the support. In the alternative, the photocurable layer(s) may be applied on top of an adhesion layer and/or resilient under layer.

Photocurable materials generally cross-link (cure) and harden through radical polymerization in at least some actinic wavelength region. As used herein, "actinic radiation" is radiation that is capable of polymerizing, crosslinking or curing the photocurable layer. Actinic radiation includes, for example, amplified (e.g., laser) and non-amplified light, particularly in the UV and violet wavelength regions.

The slip film is a thin layer, which protects the photopolymer from dust and increases its ease of handling. In a conventional ("analog") plate making process, the slip film is transparent to UV light, and the printer peels the cover sheet off the printing plate blank, and places a negative on top of the slip film layer. The plate and negative are then subjected to flood-exposure by UV light through the negative. The areas exposed to the light cure, or harden, and the unexposed areas are removed (developed) to create the relief image on the printing plate. In the alternative, a negative may be placed directly on the at least one photocurable layer. In a "digital" or "direct to plate" process, a laser is guided by an image stored in an electronic data file, and is used to create an in situ negative in a digital (i.e., laser ablatable) masking layer, which is generally a slip film which has been modified to include a radiation opaque material. Portions of the laser ablatable layer are then ablated by exposing the masking layer to laser radiation at a selected wavelength and power of the laser. Thereafter, the at least one photocurable layer with the in situ negative thereon, is subjected to flood-exposure by UV light through the in situ negative. The areas exposed to the light cure, or harden, and the unexposed areas are removed (developed) to create the relief image on the printing plate. Selective exposure to the source of actinic radiation can be achieved using either the analog or digital method. Examples of laser ablatable layers are disclosed, for example, in U.S. Pat. No. 5,925,500 to Yang, et al., and U.S. Pat. Nos. 5,262,275 and 6,238,837 to Fan, the subject matter of each of which is herein incorporated by reference in its entirety.

Processing steps for forming relief image printing elements typically include the following: 1) Image generation, which may be mask ablation for digital "computer to plate" printing plates or negative production for conventional analog plates;

2) Face exposure through the mask (or negative) to selectively crosslink and cure portions of the photocurable layer not covered by the mask, thereby creating the relief image;

3) Back exposure to create a floor layer in the photocurable layer and establish the depth of relief. It is preferred to face expose the plate before flipping it for back exposure. Doing the back exposure first may result in damaging the black mask during the plate handling, thus contributing to image degradation. Some exposing systems can also run both exposure systems simultaneously, which also preserves the image integrity;

4) Development to remove unexposed photopolymer by solvent (including water) or dry "thermal" development; and

5) If necessary, post exposure and detackification. Removable coversheets may be provided to protect the photocurable printing element from damage during transport and handling. Useful cover sheets include flexible polymeric films, e.g., polystyrene, polyethylene, polypropylene, polycarbonate, fluoropolymers, polyamide or polyesters. Polyesters, especially polyethylene terephthalate, are commonly used.

Prior to processing the printing elements, the coversheet(s) are removed and the photosensitive surface is exposed to actinic radiation in an imagewise fashion. Upon imagewise exposure to actinic radiation, polymerization, and hence, insolubilization of the photopolymerizable layer occurs in the exposed areas. Treatment with a suitable developer solvent (or thermal development) removes the unexposed areas of the photopolymerizable layer, leaving a printing relief that can be used for flexographic printing.

As used herein "back exposure" refers to a blanket exposure to actinic radiation of the photopolymerizable layer on the side opposite that which does, or ultimately will, bear the relief. This step is typically accomplished through a transparent support layer and is used to create a shallow layer of photocured material, i.e., the "floor," on the support side of the photocurable layer. The purpose of the floor is generally to sensitize the photocurable layer and to establish the depth of relief.

Prior to the brief back exposure step (i.e., brief as compared to the imagewise exposure step), an imagewise exposure is performed utilizing a digitally-imaged mask or a photographic negative mask, which is in contact with the photocurable layer and through which actinic radiation is directed.

The type of radiation used is dependent in part on the type of photoinitiator in the photopolymerizable layer. The digitally-imaged mask or photographic negative prevents the material beneath from being exposed to the actinic radiation and hence those areas covered by the mask do not polymerize, while the areas not covered by the mask are exposed to actinic radiation and polymerize. Any conventional sources of actinic radiation can be used for this exposure step. Examples of suitable visible and UV sources include carbon arcs, mercury-vapor arcs, fluorescent lamps, electron flash units, electron beam units, photographic flood lamps, and, more recently, light emitting diodes (LEDs), which emit UV light. The use of ultraviolet mercury arc lamps that emit ultraviolet light suitable to cure photocurable layers is well known. Ultraviolet arc lamps emit light by using an electric arc to excite mercury that resides inside an inert gas (e.g., argon) environment to generate ultraviolet light which effectuates curing. Alternatively, microwave energy can also be used to excite mercury lamps in an inert gas medium to generate the ultraviolet light. However, the use of ultraviolet mercury lamps as a radiation source suffers from several disadvantages including environmental concerns from mercury and the generation of ozone as a by-product. Further, mercury lamps typically have lower energy conversion ratio, require warm-up time, generate heat during operation, and consume a large amount of energy when compared with LEDs. In addition, mercury lamps are characterized by a broad spectral output, in addition to the UV radiation, much of which is not useful for curing and can damage substrates and presents hazards to personnel.

LEDs are semiconductor devices which use the phenomenon of electroluminescence to generate light. LEDs consist of a semiconducting material doped with impurities to create a p-n junction capable of emitting light as positive holes join with negative electrons when voltage is applied. The wavelength of emitted light is determined by the materials used in the active region of the semiconductor. Typical materials used in semiconductors of LEDs include, for example, elements from Groups (III) and (V) of the periodic table. These semiconductors are referred to as III-V semiconductors and include, for example, GaAs, GaP, GaAsP, AlGaAs, InGaAsP, AlGalnP and InGaN semiconductors. The choice of materials is based on multiple factors including desired wavelength of emission, performance parameters and cost.

It is possible to create LEDs that emit light anywhere from a low of about 100 nm to a high of about 900 nm. Currently, known LED UV light sources emit light at wavelengths between about 300 and about 475 nm, with 365 nm, 390 nm and 395 nm being common peak spectral outputs. When using LED lamps for curing photocurable compositions, the photoinitiator is the coating composition is selected to be responsive to the wavelength of light emitted by the LED lamp.

LED offer several advantages over mercury lamps in curing applications. For example, LEDs do not use mercury to generate UV light and are typically less bulky than mercury UV arc lamps. In addition, LEDs are instant on/off sources requiring no warm-up time, which contributes to LED lamps' low energy consumption. LEDs also generate much less heat, with higher energy conversion efficiency, have longer lamp lifetimes, and are essentially monochromatic emitting a desired wavelength of light which is governed by the choice of semiconductor materials employed in the LED.

In the analog flexographic printing element world, higher UV doses are often required to hold finer highlight dots. If a desired dot level would not hold, then the operator would increase the dose by increasing the amount of time that the plate was exposed. This would work for most plate formulation types. However, the downside is that as exposure times are increased to hold finer dots, reverses often start to close up. This is commonly referred to as the plate's exposure latitude." Therefore, one can increase the dot sensitivity only to the point where the reverses stay open. Thus, there remains a need in the art for an improved photocurable composition that can be imagewise exposed to actinic radiation from an LED source at a chosen wavelength while exhibiting a good exposure latitude.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide a photocurable composition that exhibits good exposure latitude.

It is another object of the present invention to provide a photocurable resin composition that can be exposed to actinic radiation from an LED source at a chosen wavelength while exhibiting good exposure latitude.

It is still another object of the present invention to provide a photocurable resin composition that achieves fine highlight dots while not filling plate reverses.

To that end, in one embodiment, the present invention relates generally to a photosensitive printing blank having improved exposure latitude, the photosensitive printing blank comprising: a) a support; b) at least one photocurable layer disposed on the support wherein the at least one photocurable layer is capable of being selectively crosslinked and cured upon exposure to actinic radiation at a desired wavelength region, the at least one photocurable layer comprising:

1) at least one elastomeric binder;

2) at least one ethylenically unsaturated monomer;

3) a photoinitiator having a favorable absorption profile in the desired wavelength region used for exposing the at least one photocurable layer to actinic radiation;

4) a dye, wherein the dye exhibits a suitable percent transmission as measured with a UV spectrophotometer at the desired wavelength region used for exposing the at least one photocurable layer to actinic radiation; and c) optionally, a laser ablatable mask layer disposed upon the at least one photocurable layer.

In another embodiment, the present invention relates generally to a method of making a photosensitive relief image printing element from a photosensitive printing blank, wherein the photosensitive printing blank comprises a support, at least one photocurable layer upon the support, wherein the at least one photocurable layer is capable of being selectively crosslinked and cured upon exposure to actinic radiation at a desired wavelength region and wherein the at least one photocurable layer comprises (a) at least one elastomeric binder, (b) at least one ethylenically unsaturated monomer, (c) a photoinitiator having a favorable absorption profile in the desired wavelength region used for exposing the at least one photocurable layer to actinic radiation, and (d) a dye, wherein the dye exhibits a suitable percent transmission as measured with a UV spectrophotometer at the desired wavelength region used for exposing the at least one photocurable layer to actinic radiation, and optionally an infrared ablatable layer disposed on the at least one photocurable layer; the method comprising the steps of: a) imagewise exposing the at least one photocurable layer to actinic radiation at the desired wavelength region to selectively cross link and cure the at least one photocurable layer; and b) developing the photocurable layer to remove uncured portions of the at least one photocurable layer; wherein the presence of the dye exhibiting a suitable percent transmission at the desired wavelength region used for exposure of the least one photocurable layer to actinic radiation results in a relief image in the printing element having improved exposure latitude.

BRIEF DESCRIPTION OF THE FIGURES

Figure 1 depicts UV-Vis plots for Pylam Green and Savinyl Red dyes.

Figure 2 depicts reverses of 15 mil reverses of dyes having a 30% absorption and an 80% absorption at 4J and 8J.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention relates generally to a method of making a photosensitive relief image printing element from a photosensitive printing blank, wherein the photosensitive printing blank comprises a support, at least one photocurable layer upon the support, wherein the at least one photocurable layer is capable of being selectively crosslinked and cured upon exposure to actinic radiation at a desired wavelength region and wherein the at least one photocurable layer comprises (a) at least one elastomeric binder, (b) at least one ethylenically unsaturated monomer, (c) a photoinitiator having a favorable absorption profile in the desired wavelength region used for exposing the at least one photocurable layer to actinic radiation, and (d) a dye, wherein the dye exhibits a suitable percent transmission as measured with a UV spectrophotometer at the desired wavelength region used for exposing the at least one photocurable layer to actinic radiation, and optionally an infrared ablatable layer disposed on the at least one photocurable layer; the method comprising the steps of: a) imagewise exposing the at least one photocurable layer to actinic radiation at the desired wavelength region to selectively cross link and cure the at least one photocurable layer; and b) developing the photocurable layer to remove uncured portions of the at least one photocurable layer; wherein the presence of the dye exhibiting a suitable percent transmission at the desired wavelength region used for exposure of the least one photocurable layer to actinic radiation results in a relief image in the printing element having an improved exposure latitude. The present invention also describes the use of LEDs operating within a desired wavelength region for face exposure (i.e., imagewise exposure) of at least one photocurable layer to actinic radiation to selectively crosslink and cure portions of the photocurable layer.

The inventors of the present invention investigated the exposure latitude of various photosensitive resin compositions. Based thereon, the inventors of the present invention experimented with various ingredients in the photocurable composition to try to improve the exposure latitude of the photocurable composition.

The inventors discovered that choosing particular dyes for use in the photocurable composition (such as switching from Savinyl Red dye to Pylam green dye) resulted in a much wider exposure latitude. Initially, it was believed that the improvement latitude could be due to the actual color of the dye, so a number of green dyes were evaluated. However, the results did not correlate specifically to green dyes and thus UV-Vis plots were measured for both the Savinyl Red and Pylam green dyes as shown in Figure 1.

The UV-Vis spectra of these two dyes displayed a different percent transmission at the 395 nm wavelength (i.e. the peak wavelength used to imagewise expose the photopolymer layer) While Savinyl red was recorded to have 73.0% transmission at 395 nm, the Pylam green dye had only 40.9% transmission at 395 nm. As the 395 nm wavelength does not contribute to the "green" color, a series of dyes was analyzed for their UV-Vis spectra. Each dye was made up at a concentration of 2.0x10^"5 g/mL and was tested on a Perkin Elmer Lambda 35 UV-Vis spectrophotometer. The procedure of making the solution was to dissolve 0.1 grams of dye in 100 mL of acetone solvent. The solution was then further diluted by mixing 2.0 mL of this solution in 100 mL of additional acetone solvent. The results are presented in Table 1 which shows the absorbance, percent transmission and percent absorption for each of the dyes at 365 nm and at 395 nm.

The inventors found that various dyes yield favorable results when used in relief image printing plate formulations cured with a 395 nm LED array. It was determined that the actual color of the dye did not matter nearly as much as how the dye absorbed in the 395 nm region. Furthermore, it is noted that while the present invention is described as it relates to the absorption/transmission of dyes in a particular wavelength region, the invention is not limited to dyes. That is, any material that absorbs/transmits at the desired level within the chosen wavelength region (including, for example, 395 nm) would be usable in the present invention.

The lower transmitting dyes at 395 nm were made into flexographic printing elements and were exposed with a 395 nm LED array at two exposure levels. Cross sections of the reverses of the imaged and exposed printing elements were then studied.

It was observed that the dyes with a percent transmission of less than 50% started to show an image latitude advantage when curing with 395 nm LEDs and that dyes with a percent transmission of less than 80% showed the greatest imaging latitude. The dye concentration in the formulation showed a formulation at a concentration as low as 0.01% and as high as 0.1% by weight, preferably between about 0.02% and about 0.05% by weight. Dyes made at a concentration of 2x10^"5 g/mL that transmit at less than 20% on a UV spectrophotometer were found to offer excellent imaging latitude when made into a flexographic printing element formulation at 0.02% when curing with a 395 nm LED array.

Table 1. Absorbance, % Transmission and % Absorption for selected dyes

Dye Absor jancc % Transmission % Absorption

365 395 365 395 365 395

Flexo Violet 615 0.130 0.050 74.100 89.080 25.900 10.920

HS 400 Violet R 0.1 15 0.060 76.720 87.030 23.280 12.970

LX 1926 Polykrome Violet 0.153 0.096 70.340 80.180 29.660 19.820

Methyl Violet Base FN 0.172 0.071 67.330 84.950 32.670 15.050

Methyl Violet Base 0.123 0.058 75.260 87.440 24.740 12.560

Orasol Violet RN 0.317 0.231 48.240 58.740 51.760 41.260

Pylam Krome Violet 0.137 0.092 72.930 80.930 27.070 19.070

Sandoplast HS 400 0.121 0.063 75.620 86.400 24.380 13.600

Savinyl Dark Violet R 0.341 0.274 45.630 53.270 54.370 46.730

Zapon Violet 500 0.043 0.040 90.470 91.250 9.530 8.750

Waxoline Rubin TR 0.415 0.071 38.430 84.970 61.570 15.030

Blues

Solvent Blue 67 0.583 0.155 26.140 69.920 73.860 30.080

Polycent Blue RLS 0.131 0.106 73.980 78.420 26.020 21.580

Pylam new Royal blue 0.388 0.142 40.910 72.120 59.090 27.880

Basic Blue 47 0.1 10 0.096 77.620 80.230 22.380 19.770

Hecto Blue 0.386 0.265 41.100 54.350 58.900 45.650

HS 500 Blue B 0.269 0.165 53.880 68.380 46.120 31.620

LX 9544 Pylam Cyan 0.588 0.173 25.820 67.170 74.180 32.830

Microlith Blue 4 GK 0.581 0.212 26.230 61.430 73.770 38.570

Microlith Blue A3 RK 0.167 0.093 68.020 80.640 31.980 19.360

Orasol Blue GL 0.560 0.149 27.560 70.980 72.440 29.020

Orasol Blue GN 0.625 0.163 23.730 68.700 76.270 31.300

Phthalo Blue LX 10394 0.583 0.173 26.150 67.220 73.850 32.780

Pylakrome Bright Blue 0.068 0.056 85.510 87.950 14.490 12.050

Phthalo Blue 40591 1 0.506 0.142 31.190 72.060 68.810 27.940

Phthalo Blue 405912 0.277 0.094 52.860 80.630 47.140 19.370

Savinyl Blue RLS 0.134 0.105 73.520 78.580 26.480 21.420

Solvent Blue 67 0.583 0.155 26.140 69.920 73.860 30.080

Victoria Pure Blue 0.315 0.143 48.380 71.990 51.620 28.010

Greens

Pylam New D Green 0.541 0.388 28.770 40.940 71.230 59.060

Acid Green 25 0.177 0.255 66.520 55.620 33.480 44.380

Lissamine Green 0.173 0.217 67.100 60.710 32.900 39.290

Macroflex Green 0.164 0.255 68.550 55.560 31.450 44.440

Methylene Green 0.210 0.166 61.590 68.220 38.410 31.780

Naphtoluene Green 0.299 0.207 50.180 62.090 49.820 37.910

Pylam Old Dark Green 0.519 0.422 30.260 37.880 69.740 62.120

Sandoplast Green 2GS 0.247 0.342 56.580 45.530 43.420 54.470

Savinyl Green 2GLS 0.521 0.228 30.110 59.150 69.890 40.850

Savinyl Green GLS 0.496 0.229 31.910 59.00 68.090 41.000

Waxoline Green 5G FW 0.139 0.209 72.560 61.760 27.440 38.240 Dye Absor jance % Transmission % Absorption

365 395 365 395 365 395

Waxoline Green 6 GFW 0.142 0.221 72.060 60.170 27.940 39.830

Waxoline Green GFW 0.227 0.310 59.240 48.990 40.760 51.010

Yellows

Orasol Yellow 4GN 0.139 0.467 72.620 34.130 27.380 65.870

Morton Yellow 0.534 0.792 29.250 16.140 70.750 83.860

Neptune Yellow 078 0.130 0.473 74.170 33.680 25.830 66.320

Orasol Orange G 0.555 0.643 27.890 22.740 72.1 10 77.260

Orasol Yellow 2 GLN 0.384 0.564 41.270 27.290 58.730 72.710

Orasol Yellow 2 RLN 0.256 0.255 55.510 55.540 44.490 44.460

Orasol Yellow 3 R 0.461 0.710 34.570 19.490 65.430 80.510

Orasol Yellow 152 0.422 0.622 37.840 23.870 62.160 76.130

Solvent Yellow 83 0.424 0.609 37.660 24.610 62.340 75.390

Reds

Savinyl Red 3 BLS 0.179 0.136 66.250 73.030 33.750 26.970

LX 1903 Pylakrome Red 0.827 0.636 14.910 23.140 85.090 76.860

LX 5988 Pylakrome Bright Red 0.763 0.612 17.270 24.430 82.730 75.570

LX 10096 Pylakrome Red 0.057 0.068 87.620 85.580 12.380 14.420

Moreplas Red 46 0.065 0.070 86.190 85.120 13.810 14.880

Moreplas Red III 0.064 0.084 86.360 82.320 13.640 17.680

Neozapon Red 355 0.408 0.519 39.040 30.250 60.960 69.750

Neozapon Red 365 0.323 0.353 47.510 44.340 52.490 55.660

Neozapon Red 471 0.305 0.219 49.560 60.440 50.440 39.560

Neozapon Rot 335 0.540 0.538 28.820 29.000 71.180 71.00

Neozapon Rot 395 0.574 0.498 26.640 31.790 73.360 68.210

Orasol Red 3 GL 0.429 0.309 37.280 49.110 62.720 50.890

Orasol Red BL 0.565 0.488 27.200 32.480 72.800 67.520

Orcosolve Fire Red G 0.483 0.568 32.870 27.060 67.130 72.940

Permalex Red MC-91 0.402 0.268 39.660 53.980 60.340 46.020

Savinyl Red 3 GLS 0.332 0.435 46.600 36.740 53.400 63.260

Savinyl Rouge 3 BLS 0.325 0.216 47.280 60.830 52.720 39.170

Solvaperm Red 2G 0.592 0.208 25.570 61.880 74.430 38.120

Waxoline Red MPWF 0.060 0.079 87.180 83.420 12.820 16.580

Moreplas Red 240 0.793 0.582 16.090 26.170 83.910 73.830

The dyes were sorted in order of percent absorption. Certain dyes were then selected at specific intervals of percent absorption to be tested in a photosensitive printing plate formulation as shown below in Table 2: Table 2. Exam le Formulation

Commercially available LEDs for imagewise exposure of flexographic printing elements are typically available at a wavelength of 395 ran with a UV power between 1-4 W/cm . Generally speaking, the intensity of the UV LEDs used in accordance with the invention is greater than 100 mW/cm², preferably greater than 150 mW/cm², more preferably greater than 200 mW/cm², measured at the surface of the flexographic printing plate.

As described herein, the photocurable layer(s) can include any of the known elastomeric binders, monomers, photoinitiators, reactive or non-reactive diluents, fillers, processing aids, UV absorbers and dyes. As used herein, the term "photocurable" refers to a composition which undergoes polymerization, cross-linking, or any other curing or hardening reaction in response to actinic radiation with the result that the unexposed portions of the material can be selectively separated and removed from the exposed (cured) portions to form a three-dimensional relief pattern of cured material. Elastomeric binders are generally known to those skilled in the art, including, for example, styrene-diene block copolymers, ethylene-acrylic acid copolymers, polyethylene oxide- polyvinyl alcohol graft copolymers, natural rubber, polybutadiene, polyisoprene, styrene- butadiene rubber, nitrile-butadiene rubber, butyl rubber, styrene-isoprene rubber, styrene- butadiene-isoprene rubber, polynorbomene rubber, and ethylene-propylene-diene rubber (EPDM), among others.

The elastomeric binder is preferably a thermoplastically elastomeric block copolymer of alkenylaromatics and 1,3-dienes and may be a linear, branched, or radial block copolymer. Suitable examples include triblock copolymers of the A-B-A type, diblock polymers of the A-B type, or copolymers having two or more alternating elastomeric and thermoplastic blocks, e.g., A-B-A-B-A, and combinations of one or more of the foregoing. The total amount of binder in the photocurable layer(s) is typically in the range of about 40% to 90% by weight, based on the total weight of the photocurable composition, more preferably 45% to 75% by weight.

The photocurable composition also comprises at one ethylenically unsaturated compound that is compatible with the elastomeric binder(s). Suitable compounds have at least one ethylenically unsaturated double bond and are polymerizable. These ethylenically unsaturated compounds (also referred to as monomers) include, for example, esters or amides of acrylic acid or of methacrylic acid with mono- or polyfunctional alcohols, amines, amino alcohols or hydroxylethers and hydroxyl esters, esters of fumaric or maleic acid, vinyl ethers, vinyl esters, or allyl compounds, among others. Preferred examples of suitable monomers include butyl acrylate, 2-ethylhexyl acrylate, lauryl acrylate, tetradecyl acrylate, 1 ,4-butanediol diacrylate, 1,6- hexanediol diacrylate, 1 ,6-hexanediol dimethacrylate, 1 ,9-nonanediol diacrylate, trimethylolpropane tri(meth)acrylate, dioctyl fumarate, and N-dodecylmaleimide, and combinations of one or more of the foregoing. The amount of monomer in the photocurable composition is preferably less than about 25% by weight, preferably between about 5% and about 20% by weight, based on the total weight of the photocurable composition.

The photocurable composition also includes a photoinitiator having a favorable absorption profile in the desired LED wavelength region. Suitable photoinitiators having a favorable absorption profile in the 395 nm region, including bis-acyl phosphine oxide (BAPO), 2,4,6-trimethylbenzoylethoxyphenylphosphine oxide (TPO), Irgacure-369 and Irgacure-379, among others. The amount of photoinitiator in the photocurable composition is typically in the range of from about 0.1% to 5% by weight, based on the total weight of the photocurable composition.

The photocurable composition may also optionally contain one or more plasticizers. Examples of suitable plasticizers include modified and unmodified natural oils and natural resins, such as high-boiling paraffinic, naphthenic, or aromatic mineral oils, synthetic oligomers or resins such as oligostyrene, high-boiling esters, oligomeric styrene-butadiene copolymers, oligomeric α-methylstyrene/p-methylstyrene copolymers, liquid oligobutadienes, , or liquid oligomeric acrylonitrile-butadiene copolymers or oligomeric ethylene-propylene-diene copolymers, among others. Preference is given to polybutadiene oils, more particularly those having a molecular weight of between 500 and 5000 g/mol, high-boiling aliphatic esters such as, more particularly, esters of alkylmonocarboxylic and dicarboxylic acids, examples being stearates or adipates, and mineral oils. The amount of an optionally present plasticizer is preferably in the range of about 0% to 50% by weight, based upon the total weight of the photocurable composition.

The photocurable composition may also contain various fillers, processing aids, UV absorbers and dyes.

As to the dyes, as described herein, the inventors have found that the use of a specific dye in the photocurable composition produces a photocurable printing element having an improved exposure latitude. More specifically, the present invention contemplates the use of a dye in the photocurable composition having a % transmission of less than about 50% at 395 nm, more preferably a % transmission of less than about 40% at 395 nm and most preferably a % transmission of less than about 20% at 395 when running UV-Vis at a dye concentration of 2x10^" ⁵ g/mL. The dye is typically present in the photocurable composition at a concentration of between about 0.005 and 0.1% by weight, more preferably between about 0.01 and 0.05% by weight, based upon the total weight of the photocurable composition. Table 3. Set of Dyes with increasing percent absorption

Each of the dyes in Table 3 was then made into the example formulation. Each formulation was then made into flexographic printing plates. Then, UV dosing levels of 4J and 8J were conducted on plates of each dye type. The plates were then developed to remove uncured portions of the one or more photocurable layers by processing in Solvit 100 (available from MacDermid Printing Solutions) and then dried. The reverse depths at each dosing level for each dye are shown in Tables 4 and 5 below. Table 4. 30 mil reverse depths for each dye at 4 J and 8 J dosing levels

Thus, dyes having a lower percent transmission at 395 nm yielded deeper reverses. At the same dosing levels, plates made yielded 1% highlight dots at 150 LPI when exposed at 8 J dosing levels, meaning that it produced a usable printing element. Figure 2 shows reverses of 15 mil reverses of dyes having a 30% absorption and an 80% absorption at 4J and 8J. As seen in Figure 2, the formulation that contains a dye having an 80% absorption demonstrates much deeper reverses than the formulation having a 30% absorption. It is believed that transmissions of less than 50% at 395 nm are required to see a usable benefit, while a greater benefit is observed with transmissions of less than 41% and the best benefit at transmissions of less than 20% when running UV-Vis at a dye concentration of 2x10^"5 g/mL.

Based on the results provided herein, the preferred dye list (with % Absorption is as follows):

1) Orasol Red 3GL (50.9% A) 2) Waxolin Green GFW (51.0% A)

3) Sandoplast Green 2GS (54.5% A)

4) Neozapon Red 365 (55.7% A)

5) Pylam New D Green (59.1% A)

6) Pylam Old Dark Green (62.1% A)

7) Savinyl Red 3 GLS (63.3% A)

8) Orasol Yellow 4GN (65.9 %A)

9) Neptune Yellow 078 (66.3% A)

10) Orasol Red BL (67.5% A)

11) Neozapon Red 395 (68.2% A)

12) Neozapon Red 355 (69.8% A)

13) Neozapon Red 335 (71.0% A)

14) Orasol Yellow 2GLN (72.7% A)

15) Orcosolve Fire Red G (72.9% A)

16) Moreplas Red 240 (73.8% A)

17) Solvent Yellow 83 (75.4% A)

18) Pylakrome Bright Red LX 5988 (75.6% A)

19) Orasol Yellow 152 (76.1% A)

20) Pylakrome Red LX 1903 (76.9% A)

21) Orasol Orange G (77.3% A)

22) Orasol Yellow 3R (80.5% A)

23) Morton Orange (83.9% A)

It should further be apparent that one skilled in the art could readily identify dyes other than those listed that would have the desired percent transmission/percent absorption and that would be usable in the photocurable layers described herein.

It should also be understood that the following claims are intended to cover all of the generic and specific features of the invention described herein and all statements of the scope of the invention that as a matter of language might fall therebetween.

Claims

WHAT IS CLAIMED IS;

1. A photosensitive printing blank having improved exposure latitude, the photosensitive printing blank comprising: a) a support; b) at least one photocurable layer disposed on the support wherein the at least one photocurable layer is capable of being selectively crosslinked and cured upon exposure to actinic radiation at a desired wavelength, the at least one photocurable layer comprising:

1) at least one elastomeric binder;

2) at least one ethylenically unsaturated monomer;

4) a dye, wherein the dye exhibits the characteristic of measuring less than 50 percent transmittance, at the peak wavelength of the actinic radiation used to cure the photocurable layer, when measured in a U.V. spectrometer at a concentration of 2 x 10 ^*5 gr/ml; c) optionally, a laser ablatable mask layer disposed upon the at least one photocurable layer.

2. The photosensitive printing blank according to claim 1 , wherein the desired wavelength of the actinic radiation used for imagewise exposing the at least one photocurable layer to actinic radiation is 395 nm.

3. The photosensitive printing blank according to claim 2, wherein the dye exhibits a percent transmission of less than about 50% at 395 nm wavelength.

4. The photosensitive printing blank according to claim 3, wherein the dye exhibits a percent transmission of less than about 40% at 395 nm wavelength.

5. The photosensitive printing blank according to claim 4, wherein the dye exhibits a percent transmission of less than about 20% at 395 nm wavelength.

6. The photosensitive printing blank according to claim 1, wherein the dye is present in the photocurable layer at a concentration of between about 0.01 and 0.1 percent by weight.

7. The photosensitive printing blank according to claim 6, wherein the dye is present in the photocurable layer at a concentration of between about 0.02 and 0.05 percent by weight.

8. A method of making a photosensitive relief image printing element from a photosensitive printing blank, wherein the photosensitive printing blank comprises a support, at least one photocurable layer upon the support, wherein the at least one photocurable layer is capable of being selectively crosslinked and cured upon exposure to actinic radiation at a desired wavelength and wherein the at least one photocurable layer comprises (a) at least one elastomeric binder, (b) at least one ethylenically unsaturated monomer, (c) a photoinitiator having a favorable absorption profile in the desired wavelength region used for exposing the at least one photocurable layer to actinic radiation, and (d) a dye, wherein the dye exhibits the characteristic of measuring less than 50 percent transmittance, at the peak wavelength of the actinic radiation used to cure the photocurable layer, when measured in a U.V. spectrometer at a concentration of 2 x 10 ^"3 gr/ml; , and optionally an infrared ablatable layer disposed on the at least one photocurable layer; the method comprising the steps of: a) imagewise exposing the at least one photocurable layer to actinic radiation at the desired wavelength to selectively cross link and cure the at least one photocurable layer; and b) developing the photocurable layer to remove uncured portions of the at least one photocurable layer; wherein the presence of the dye results in a relief image in the printing element having an improved exposure latitude.

9. The method according to claim 8, wherein the at least one photocurable layer is exposed to actinic radiation using a light emitting diode operating at the desired wavelength.

10. The method according to claim 9, wherein the desired wavelength is 395 nm.

11. The method according to claim 10, wherein the dye exhibits a percent transmission of less than about 50% at 395 nm wavelength.

12. The method according to claim 1 1, wherein the dye exhibits a percent transmission of less than about 40% at 395 nm wavelength.

13. The method according to claim 12, wherein the dye exhibits a percent transmission of less than about 20% at 395 nm wavelength.

14. The method according to claim 8, wherein the dye is present in the photocurable layer at a concentration of between about 0.01 and 0.1 percent by weight.

15. The method according to claim 14, wherein the dye is present in the photocurable layer at a concentration of between about 0.02 and 0.05 percent by weight.

16. The method according to claim 10, wherein the light emitting diode comprises an array of light emitting diodes and the intensity of each light emitting diode in the array is greater than 100 mW/cm².