WO2015111572A1 - Gas barrier film - Google Patents
Gas barrier film Download PDFInfo
- Publication number
- WO2015111572A1 WO2015111572A1 PCT/JP2015/051367 JP2015051367W WO2015111572A1 WO 2015111572 A1 WO2015111572 A1 WO 2015111572A1 JP 2015051367 W JP2015051367 W JP 2015051367W WO 2015111572 A1 WO2015111572 A1 WO 2015111572A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- gas barrier
- silicon
- atom
- barrier film
- Prior art date
Abstract
Description
本発明のガスバリア性フィルムは、高分子基材の少なくとも片面に、ガスバリア層が配されたガスバリア性フィルムであって、該ガスバリア層は、酸化亜鉛と二酸化ケイ素とを含む第1層とケイ素化合物を含む第2層とが高分子基材から見てこの順に接して配されており、X線光電子分光法により測定される前記第1層と前記第2層との界面におけるSi2p軌道の結合エネルギーが、前記第1層におけるSi2p軌道の結合エネルギーより大きく、かつ前記第2層におけるSi2p軌道の結合エネルギーより小さいガスバリア性フィルムである。なお、「酸化亜鉛と二酸化ケイ素とを含む第1層」を、単に「第1層」と、「ケイ素化合物を含む第2層」を、単に「第2層」と略記することもある。 [Gas barrier film]
The gas barrier film of the present invention is a gas barrier film in which a gas barrier layer is disposed on at least one surface of a polymer substrate, and the gas barrier layer comprises a first layer containing zinc oxide and silicon dioxide, and a silicon compound. And the second layer including the second layer is in contact with the polymer base material in this order, and the binding energy of the Si2p orbit at the interface between the first layer and the second layer measured by X-ray photoelectron spectroscopy is The gas barrier film is larger than the binding energy of Si2p orbitals in the first layer and smaller than the binding energy of Si2p orbitals in the second layer. The “first layer containing zinc oxide and silicon dioxide” may be simply abbreviated as “first layer” and the “second layer containing silicon compound” may be simply abbreviated as “second layer”.
本発明に用いられる高分子基材は、柔軟性を確保する観点からフィルム形態を有することが好ましい。フィルムの構成としては、単層フィルムでもよいし、2層以上の、例えば、共押し出し法で製膜したフィルムであってもよい。フィルムの種類としては、一軸方向あるいは二軸方向に延伸されたフィルム等を使用してもよい。 [Polymer substrate]
The polymer substrate used in the present invention preferably has a film form from the viewpoint of ensuring flexibility. As a structure of a film, a single layer film may be sufficient and the film formed by the coextrusion method of two or more layers may be sufficient. As the type of film, a film stretched in a uniaxial direction or a biaxial direction may be used.
本発明のガスバリア性フィルムは、ガスバリア層が酸化亜鉛と二酸化ケイ素とを含む第1層を有することによって高いガスバリア性を発現することができる。酸化亜鉛と二酸化ケイ素とを含む第1層を適用することによりガスバリア性が良好となる理由は、結晶質の酸化亜鉛成分とガラス質の二酸化ケイ素成分とを共存させることによって、微結晶を生成しやすい酸化亜鉛の結晶成長が抑制され、酸化亜鉛の粒子径が小さくなるため、層が緻密化し、水蒸気の透過が抑制されるためと推測している。また、酸化亜鉛および二酸化ケイ素を含む層は、酸化アルミニウム、酸化チタン、酸化ジルコニウム等の一つの金属元素のみからなる酸化物で形成された薄膜よりも膜の柔軟性が優れるため、熱や外部からの応力に対してクラックが生じにくく、ガスバリア性の低下を抑制できると考えられる。 [First layer containing zinc oxide and silicon dioxide]
The gas barrier film of the present invention can exhibit high gas barrier properties when the gas barrier layer has the first layer containing zinc oxide and silicon dioxide. The reason why the gas barrier property is improved by applying the first layer containing zinc oxide and silicon dioxide is that the crystalline zinc oxide component and the vitreous silicon dioxide component coexist to produce microcrystals. It is presumed that the crystal growth of zinc oxide, which is easy, is suppressed and the particle diameter of zinc oxide is reduced, so that the layer is densified and the permeation of water vapor is suppressed. In addition, the layer containing zinc oxide and silicon dioxide is superior in flexibility to a thin film formed of an oxide composed of only one metal element such as aluminum oxide, titanium oxide, zirconium oxide, etc. It is considered that cracks are less likely to occur with respect to the stress of and that it is possible to suppress a decrease in gas barrier properties.
第1層として好適に用いられる酸化亜鉛、二酸化ケイ素および酸化アルミニウムからなる層について詳細を説明する。なお、「酸化亜鉛、二酸化ケイ素および酸化アルミニウムからなる層」を「酸化亜鉛-二酸化ケイ素-酸化アルミニウム層」または「ZnO-SiO2-Al2O3層」と略記することもある。 [Zinc oxide-silicon dioxide-aluminum oxide layer]
Details of the layer made of zinc oxide, silicon dioxide, and aluminum oxide that are suitably used as the first layer will be described. Note that “a layer made of zinc oxide, silicon dioxide and aluminum oxide” may be abbreviated as “zinc oxide-silicon dioxide-aluminum oxide layer” or “ZnO—SiO 2 —Al 2 O 3 layer”.
次に、ケイ素化合物を含む第2層について詳細を説明する。本発明における第2層は、ケイ素化合物を含む層であり、ケイ素化合物として、ケイ素酸化物、ケイ素窒化物、ケイ素炭化物、ケイ素酸窒化物または、それらの混合物を含んでいてもよい。特に、ケイ素化合物が、二酸化ケイ素、炭化ケイ素、窒化ケイ素および酸窒化ケイ素からなる群より選ばれる少なくとも一つを含むことが好ましい。 [Second layer containing silicon compound]
Next, the details of the second layer containing a silicon compound will be described. The second layer in the present invention is a layer containing a silicon compound, and the silicon compound may contain silicon oxide, silicon nitride, silicon carbide, silicon oxynitride, or a mixture thereof. In particular, the silicon compound preferably contains at least one selected from the group consisting of silicon dioxide, silicon carbide, silicon nitride, and silicon oxynitride.
ガスバリア性フィルムには、ガスバリア性向上および耐屈曲性向上のため、前記高分子基材と前記第1層との間に芳香族環構造を有するポリウレタン化合物を架橋して得られる構造を含むアンダーコート層が設けられることが好ましい。この態様のガスバリア性フィルムの一例を図2に示す。アンダーコート層3を有することによって、高分子基材1の表面に突起や傷が存在しても、平坦化することができ、ガスバリア層が偏りなく均一に成長するため、より高いガスバリア性を発現するガスバリア性フィルムとなる。また、高分子基材と第1層との熱寸法安定性差が大きい場合も、アンダーコート層を設けることにより、ガスバリア性や耐屈曲性の低下を防ぐことができるので好ましい。 [Undercoat layer]
The gas barrier film includes an undercoat including a structure obtained by crosslinking a polyurethane compound having an aromatic ring structure between the polymer base material and the first layer in order to improve gas barrier properties and flex resistance. A layer is preferably provided. An example of the gas barrier film of this embodiment is shown in FIG. By having the
d=6/ρs (1)
ρ:密度
に適用することで求められる粒子直径dを指す。 As the inorganic silicon compound, silica particles are preferable from the viewpoint of surface protection performance and transparency. The primary particle diameter of the silica particles is preferably in the range of 1 to 300 nm, more preferably in the range of 5 to 80 nm. In addition, the primary particle diameter here is the specific surface area s obtained by the gas adsorption method as shown in the following formula (1).
d = 6 / ρs (1)
ρ: The particle diameter d obtained by applying to the density.
本発明のガスバリア性フィルムの最表面の上には、ガスバリア性が低下しない範囲で耐擦傷性の向上を目的としたハードコート層を形成してもよいし、有機高分子化合物からなるフィルムをラミネートしてもよい。なお、ここでいう最表面とは、第1層と接していない側の第2層の表面をいう。 [Other layers]
On the outermost surface of the gas barrier film of the present invention, a hard coat layer may be formed for the purpose of improving scratch resistance as long as the gas barrier property does not deteriorate, or a film made of an organic polymer compound is laminated. May be. The outermost surface here refers to the surface of the second layer that is not in contact with the first layer.
本発明のガスバリア性フィルムは高いガスバリア性を有するため、様々な電子デバイスに用いることができる。例えば、太陽電池のバックシートやフレキシブル回路基板のような電子デバイスに好適に用いることができる。また、高いガスバリア性を活かして、電子デバイス以外にも、食品や電子部品の包装用フィルム等として好適に用いることができる。 [Usage]
Since the gas barrier film of the present invention has a high gas barrier property, it can be used in various electronic devices. For example, it can be suitably used for an electronic device such as a back sheet of a solar cell or a flexible circuit board. Moreover, it can utilize suitably for a packaging film of foodstuffs, an electronic component, etc. besides an electronic device taking advantage of high gas barrier property.
まず、各実施例および比較例における評価方法を説明する。評価n数は、特に断らない限り、n=5とし平均値を求めた。 [Evaluation methods]
First, an evaluation method in each example and comparative example will be described. The number of evaluation n was n = 5 and the average value was obtained unless otherwise specified.
断面観察用サンプルを、マイクロサンプリングシステム((株)日立製作所製 FB-2000A)を使用してFIB法により(具体的には「高分子表面加工学」(岩森暁著)p.118~119に記載の方法に基づいて)作製した。透過型電子顕微鏡((株)日立製作所製 H-9000UHRII)により、加速電圧300kVとして、観察用サンプルの断面を観察し、第1層、第2層およびアンダーコート層の厚みを測定した。 (1) Layer thickness Samples for cross-sectional observation are obtained by the FIB method using a microsampling system (FB-2000A, manufactured by Hitachi, Ltd.) (specifically, “Surface Polymer Processing”) (by Satoshi Iwamori) (p. 118-119). Using a transmission electron microscope (H-9000UHRII, manufactured by Hitachi, Ltd.), the cross section of the observation sample was observed at an acceleration voltage of 300 kV, and the thicknesses of the first layer, the second layer, and the undercoat layer were measured.
三次元表面粗さ測定機(小坂研究所社製)を用いて、以下の条件で各層表面について測定した。
システム:三次元表面粗さ解析システム「i-Face model TDA31」
X軸測定長さ/ピッチ:500μm/1.0μm
Y軸測定長さ/ピッチ:400μm/5.0μm
測定速度:0.1mm/s
測定環境:温度23℃、相対湿度65%、大気中。 (2) Center plane average roughness SRa
Using a three-dimensional surface roughness measuring machine (manufactured by Kosaka Laboratory), the surface of each layer was measured under the following conditions.
System: Three-dimensional surface roughness analysis system “i-Face model TDA31”
X-axis measurement length / pitch: 500 μm / 1.0 μm
Y-axis measurement length / pitch: 400 μm / 5.0 μm
Measurement speed: 0.1 mm / s
Measurement environment: temperature 23 ° C., relative humidity 65%, in air.
特許第4407466号に記載のカルシウム腐食法により、温度40℃、湿度90%RHの雰囲気下での水蒸気透過度を測定した。水蒸気透過度を測定するためのサンプル数は水準当たり2検体とし、測定回数は各検体について5回とし、得られた10点の平均値を水蒸気透過度(g/(m2・24hr・atm))とした。 (3) Water vapor permeability (g / (m 2 · 24 hr · atm))
By the calcium corrosion method described in Japanese Patent No. 4407466, the water vapor permeability was measured in an atmosphere at a temperature of 40 ° C. and a humidity of 90% RH. The number of samples for measuring the water vapor transmission rate is 2 samples per level, the number of measurement is 5 times for each sample, and the average value of the obtained 10 points is the water vapor transmission rate (g / (m 2 · 24 hr · atm) ).
第1層、第2層の組成分析およびSi2p軌道の結合エネルギー、Zn2p3/2軌道の結合エネルギーピークの半値幅は、X線光電子分光法(XPS法)により行った。各層の厚みが1/2となる位置まで、表層からアルゴンイオンエッチングにより層を除去して下記の条件で測定した。また、第1層と第2層との界面におけるSi2p軌道の結合エネルギーおよびZn2p3/2軌道の結合エネルギーピークの半値幅は、第2層表面から第1層方向に向けて、(1)に記載の方法で透過型電子顕微鏡による断面観察により確認される第1層と第2層との界面までアルゴンエッチングにより第2層を除去し、第2層が除去された第1層表面をX線光電子分光法(XPS法)により下記の条件で測定した。
装置:Quantera SXM (PHI社製)
励起X線:monochromatic Al Kα1,2線(1486.6eV)
X線径:100μm
光電子脱出角度(試料表面に対する検出器の傾き):45°
イオンエッチング:Ar+ ion 2kV
raster サイズ : 2mm×2mm。 (4) Composition and Si2p orbital binding energy, half width of Zn2p3 / 2 orbital binding energy peak Composition analysis of first layer and second layer and Si2p orbital binding energy and Zn2p3 / 2 orbital half-value width of binding energy peak Was performed by X-ray photoelectron spectroscopy (XPS method). The layers were removed from the surface layer by argon ion etching until the thickness of each layer became 1/2, and the measurement was performed under the following conditions. Further, the Si2p orbital binding energy and the Zn2p3 / 2 orbital half-value width at the interface between the first layer and the second layer are described in (1) from the surface of the second layer toward the first layer. The second layer is removed by argon etching up to the interface between the first layer and the second layer, which is confirmed by cross-sectional observation using a transmission electron microscope, and the surface of the first layer from which the second layer has been removed is X-ray photoelectron. It was measured under the following conditions by spectroscopic method (XPS method).
Device: Quantera SXM (PHI)
Excitation X-ray: monochromatic Al Kα1,2 line (1486.6 eV)
X-ray diameter: 100 μm
Photoelectron escape angle (inclination of detector relative to sample surface): 45 °
Ion etching: Ar + ion 2 kV
Raster size: 2 mm x 2 mm.
JIS K7361:1997に基づき、濁度計NDH2000(日本電色工業(株)製)を用いて測定した。測定は、縦50mm、横50mmのサイズに切り出したフィルム3枚について行い、測定回数は各サンプルにつき5回とし、合計15回測定の平均値を全光線透過率とした。 (5) Total light transmittance Based on JIS K7361: 1997, it measured using the turbidimeter NDH2000 (made by Nippon Denshoku Industries Co., Ltd.). The measurement was performed on three films cut into a size of 50 mm in length and 50 mm in width, the number of measurements was 5 times for each sample, and the average value of 15 times in total was the total light transmittance.
JIS K7136:2000に基づき、濁度計NDH2000(日本電色工業(株)製)を用いて測定した。測定は、縦50mm、横50mmのサイズに切り出したフィルム3枚について行い、測定回数は各サンプルにつき5回とし、合計15回測定の平均値をヘイズ値とした。 (6) Haze Based on JIS K7136: 2000, the haze was measured using a turbidimeter NDH2000 (manufactured by Nippon Denshoku Industries Co., Ltd.). The measurement was performed on three films cut into a size of 50 mm in length and 50 mm in width, the number of measurements was 5 times for each sample, and the average value of 15 measurements in total was taken as the haze value.
(第1層の形成)
高分子基材1として、厚み50μmのポリエチレンテレフタレートフィルム(東レ株式会社製“ルミラー”(登録商標)U48)を用いた。 Example 1
(Formation of the first layer)
As the
図5に示す構造のスパッタ・CVD装置を使用し、上記の工程により得られた第1層が形成されたフィルムの第1層の上に、ヘキサメチルジシラザンを原料とした化学気相蒸着(以降、CVDと略す)を実施し、第2層としてSiO2層を厚み100nmとなるように設けた。 (Formation of the second layer)
Chemical vapor deposition using hexamethyldisilazane as a raw material on the first layer of the film on which the first layer obtained by the above process is formed using the sputtering / CVD apparatus having the structure shown in FIG. Hereinafter, the abbreviated CVD) was performed, and a SiO 2 layer was provided as a second layer so as to have a thickness of 100 nm.
(芳香族環構造を有するポリウレタン化合物の合成)
5リットルの4つ口フラスコに、ビスフェノールAジグリシジルエーテルアクリル酸付加物(共栄社化学社製、商品名:エポキシエステル3000A)を300質量部および酢酸エチル710質量部を入れ、内温60℃になるよう加温した。合成触媒としてジラウリン酸ジ-n-ブチル錫0.2質量部を添加し、攪拌しながらジシクロヘキシルメタン4,4’-ジイソシアネート(東京化成工業社製)200質量部を1時間かけて滴下した。滴下終了後2時間反応を続行し、続いてジエチレングリコール(和光純薬工業社製)25質量部を1時間かけて滴下した。滴下後5時間反応を続行し、重量平均分子量20,000の芳香族環構造を有するポリウレタン化合物を得た。 (Example 2)
(Synthesis of polyurethane compounds having an aromatic ring structure)
300 parts by weight of bisphenol A diglycidyl ether acrylic acid adduct (trade name: Epoxy ester 3000A) and 710 parts by weight of ethyl acetate are placed in a 5-liter four-necked flask, and the internal temperature reaches 60 ° C. So warmed. As a synthesis catalyst, 0.2 part by mass of di-n-butyltin dilaurate was added, and 200 parts by mass of
高分子基材1として、厚み50μmのポリエチレンテレフタレートフィルム(東レ株式会社製“ルミラー”(登録商標)U48)を用いた。 (Formation of undercoat layer)
As the
導入ガス:N2(窒素イナートBOX)
紫外線発生源:マイクロ波方式無電極ランプ
積算光量:400mJ/cm2
試料温調:室温。 Ultraviolet treatment device: LH10-10Q-G (manufactured by Fusion UV Systems Japan)
Introduced gas: N 2 (nitrogen inert BOX)
Ultraviolet light source: Microwave type electrodeless lamp Integrated light quantity: 400 mJ / cm 2
Sample temperature control: room temperature.
第1層としてZnO-SiO2-Al2O3層を厚み450nmとなるよう設けた以外は、実施例2と同様にしてガスバリア性フィルムを得た。 Example 3
A gas barrier film was obtained in the same manner as in Example 2 except that a ZnO—SiO 2 —Al 2 O 3 layer having a thickness of 450 nm was provided as the first layer.
第1層としてZnO-SiO2-Al2O3層を厚み100nmとなるよう設けた以外は、実施例2と同様にしてガスバリア性フィルムを得た。 Example 4
A gas barrier film was obtained in the same manner as in Example 2 except that a ZnO—SiO 2 —Al 2 O 3 layer having a thickness of 100 nm was provided as the first layer.
第2層としてSiO2層を厚み400nmとなるよう設けた以外は、実施例2と同様にしてガスバリア性フィルムを得た。 (Example 5)
A gas barrier film was obtained in the same manner as in Example 2 except that a SiO 2 layer having a thickness of 400 nm was provided as the second layer.
第2層としてSiO2層を厚み70nmとなるよう設けた以外は、実施例2と同様にしてガスバリア性フィルムを得た。 (Example 6)
A gas barrier film was obtained in the same manner as in Example 2 except that a SiO 2 layer having a thickness of 70 nm was provided as the second layer.
第2層形成時のメインドラム温度を110℃として、SiO2層を厚み300nmとなるよう設けた以外は、実施例2と同様にしてガスバリア性フィルムを得た。 (Example 7)
A gas barrier film was obtained in the same manner as in Example 2 except that the main drum temperature at the time of forming the second layer was 110 ° C., and the SiO 2 layer was provided to a thickness of 300 nm.
第2層としてSiO2層を形成しない以外は、実施例1と同様にしてガスバリア性フィルムを得た。 (Comparative Example 1)
A gas barrier film was obtained in the same manner as in Example 1 except that the SiO 2 layer was not formed as the second layer.
第1層としてZnO-SiO2-Al2O3層を形成しないで、高分子基材の表面に直接、SiO2層を厚み100nmとなるように設けた以外は、実施例1と同様にしてガスバリア性フィルムを得た。 (Comparative Example 2)
Except that the ZnO—SiO 2 —Al 2 O 3 layer was not formed as the first layer, and the SiO 2 layer was provided directly on the surface of the polymer substrate so as to have a thickness of 100 nm, the same as in Example 1. A gas barrier film was obtained.
第2層としてSiO2層を形成しない以外は、実施例2と同様にしてガスバリア性フィルムを得た。 (Comparative Example 3)
A gas barrier film was obtained in the same manner as in Example 2 except that the SiO 2 layer was not formed as the second layer.
第1層の形成条件として、メインドラム10の温度を25℃とし、直流パルス電源の投入電力を1,500Wとし、さらに第2層の形成条件としてメインドラム10の温度を25℃とし、CVD電極の誘導コイルの投入電力を500Wとした以外は実施例2と同様にしてガスバリア性フィルムを得た。 (Comparative Example 4)
As the formation condition of the first layer, the temperature of the
第1層としてZnO-SiO2-Al2O3層を厚み450nmとなるよう設け、さらに第2層の形成条件としてメインドラム10の温度を25℃とし、CVD電極の誘導コイルの投入電力を500Wとした以外は実施例2と同様にしてガスバリア性フィルムを得た。 (Comparative Example 5)
A ZnO—SiO 2 —Al 2 O 3 layer having a thickness of 450 nm is provided as the first layer, and the temperature of the
第1層としてSiO2層を厚み100nmとなるよう形成し、第2層としてZnO-SiO2-Al2O3層を厚み150nmとなるよう形成した以外は実施例2と同様にしてガスバリア性フィルムを得た。 (Comparative Example 6)
Gas barrier film in the same manner as in Example 2 except that a SiO 2 layer having a thickness of 100 nm was formed as the first layer and a ZnO—SiO 2 —Al 2 O 3 layer having a thickness of 150 nm was formed as the second layer. Got.
第2層の形成条件としてメインドラム10の温度を25℃とし、CVD電極の誘導コイルの投入電力を500Wとして、SiO2層の厚みを400nmとなるように形成した以外は実施例2と同様にしてガスバリア性フィルムを得た。 (Comparative Example 7)
The second layer was formed in the same manner as in Example 2 except that the temperature of the
第2層のSiO2層に代えて、Al2O3層を厚み100nmとなるよう設けた以外は、実施例2と同様にしてガスバリア性フィルムを得た。なお、Al2O3層は、ZnO-SiO2-Al2O3層形成時の酸化亜鉛と二酸化ケイ素と酸化アルミニウムで形成された混合焼結材であるスパッタターゲットを、純度99.99質量%のアルミニウムからなるスパッタターゲットに代えてスパッタ電極12に設置した以外は実施例2の第1層と同様にして形成した。この第2層の組成は、Al原子濃度が37.5atom%、O原子濃度が62.5atom%であった。 (Comparative Example 8)
A gas barrier film was obtained in the same manner as in Example 2 except that an Al 2 O 3 layer having a thickness of 100 nm was provided instead of the second SiO 2 layer. The Al 2 O 3 layer is made of a sputter target that is a mixed sintered material formed of zinc oxide, silicon dioxide, and aluminum oxide at the time of forming the ZnO—SiO 2 —Al 2 O 3 layer, and has a purity of 99.99 mass%. It was formed in the same manner as the first layer of Example 2 except that it was placed on the
実施例2において、第1層として純度99.99質量%のアルミニウムからなるスパッタターゲットを使用して、Al2O3層を厚み150nmとなるよう設けた以外は、実施例2と同様にしてガスバリア性フィルムを得た。この第1層の組成は、Al原子濃度が37.5atom%、O原子濃度が62.5atom%であった。 (Comparative Example 9)
In Example 2, a gas barrier was used in the same manner as in Example 2 except that a sputter target made of aluminum having a purity of 99.99% by mass was used as the first layer and the Al 2 O 3 layer was provided to a thickness of 150 nm. A characteristic film was obtained. The composition of the first layer was an Al atom concentration of 37.5 atom% and an O atom concentration of 62.5 atom%.
実施例2において、第1層として純度99.99質量%の酸化亜鉛からなるスパッタターゲットを使用して、ZnO層を厚み150nmとなるよう設けた以外は、実施例2と同様にしてガスバリア性フィルムを得た。この第1層の組成は、Zn原子濃度が48.9atom%、O原子濃度が51.1atom%であった。 (Comparative Example 10)
In Example 2, a gas barrier film was used in the same manner as in Example 2 except that a sputter target made of zinc oxide having a purity of 99.99% by mass was used as the first layer and the ZnO layer was provided to a thickness of 150 nm. Got. The composition of the first layer was such that the Zn atom concentration was 48.9 atom% and the O atom concentration was 51.1 atom%.
2 ガスバリア層
2a 酸化亜鉛と二酸化ケイ素とを含む第1層
2b ケイ素化合物を含む第2層
3 アンダーコート層
4 巻き取り式スパッタリング・化学気相蒸着装置
5 巻き取り室
6 巻き出しロール
7、8、9 巻き出し側ガイドロール
10 メインドラム
11 スパッタ電極
12、13、14 巻き取り側ガイドロール
15 巻き取りロール
16 CVD電極
17 誘導コイル DESCRIPTION OF
Claims (8)
- 高分子基材の少なくとも片面に、ガスバリア層が配されたガスバリア性フィルムであって、該ガスバリア層は、酸化亜鉛と二酸化ケイ素とを含む第1層とケイ素化合物を含む第2層とが高分子基材から見てこの順に接して配されており、X線光電子分光法により測定される前記第1層と前記第2層との界面におけるSi2p軌道の結合エネルギーが、前記第1層におけるSi2p軌道の結合エネルギーより大きく、かつ前記第2層におけるSi2p軌道の結合エネルギーより小さいガスバリア性フィルム。 A gas barrier film having a gas barrier layer disposed on at least one surface of a polymer substrate, wherein the gas barrier layer is composed of a first layer containing zinc oxide and silicon dioxide and a second layer containing a silicon compound. The bonding energy of the Si2p orbitals at the interface between the first layer and the second layer measured by X-ray photoelectron spectroscopy is the Si2p orbital in the first layer. A gas barrier film that is larger than the binding energy of Si2p and smaller than the binding energy of Si2p orbitals in the second layer.
- X線光電子分光法により測定される前記第1層と前記第2層との界面の、Zn2p3/2軌道の結合エネルギーピークの半値幅が2.5eV以上である請求項1に記載のガスバリア性フィルム。 The gas barrier film according to claim 1, wherein a half-value width of a binding energy peak of Zn2p3 / 2 orbit at the interface between the first layer and the second layer measured by X-ray photoelectron spectroscopy is 2.5 eV or more. .
- 前記ケイ素化合物が、二酸化ケイ素、炭化ケイ素、窒化ケイ素および酸窒化ケイ素からなる群より選ばれる少なくとも一つを含む請求項1または2に記載のガスバリア性フィルム。 The gas barrier film according to claim 1 or 2, wherein the silicon compound contains at least one selected from the group consisting of silicon dioxide, silicon carbide, silicon nitride, and silicon oxynitride.
- 前記第1層が、アルミニウム、ガリウム、チタン、ジルコニウム、スズ、インジウム、ニオブ、モリブデンおよびタンタルからなる群より選ばれる少なくとも一つの元素をさらに含む請求項1~3のいずれかに記載のガスバリア性フィルム。 The gas barrier film according to any one of claims 1 to 3, wherein the first layer further contains at least one element selected from the group consisting of aluminum, gallium, titanium, zirconium, tin, indium, niobium, molybdenum and tantalum. .
- 前記高分子基材と前記第1層との間にアンダーコート層をさらに有し、該アンダーコート層が芳香族環構造を有するポリウレタン化合物を架橋して得られる構造を含む請求項1~4のいずれかに記載のガスバリア性フィルム。 5. The structure according to claim 1, further comprising an undercoat layer between the polymer substrate and the first layer, wherein the undercoat layer includes a structure obtained by crosslinking a polyurethane compound having an aromatic ring structure. The gas barrier film according to any one of the above.
- 前記第1層が、酸化亜鉛、二酸化ケイ素および酸化アルミニウムからなる請求項1~5のいずれかに記載のガスバリア性フィルム。 The gas barrier film according to any one of claims 1 to 5, wherein the first layer comprises zinc oxide, silicon dioxide, and aluminum oxide.
- 前記第1層は、X線光電子分光法により測定される亜鉛原子濃度が10~35atom%、ケイ素原子濃度が7~25atom%、アルミニウム原子濃度が0.5~5atom%、酸素原子濃度が45~70atom%である請求項1~6のいずれかに記載のガスバリア性フィルム。 The first layer has a zinc atom concentration measured by X-ray photoelectron spectroscopy of 10 to 35 atom%, a silicon atom concentration of 7 to 25 atom%, an aluminum atom concentration of 0.5 to 5 atom%, and an oxygen atom concentration of 45 to 45%. The gas barrier film according to any one of claims 1 to 6, which is 70 atom%.
- 前記第2層は、X線光電子分光法により測定されるケイ素原子濃度が25~45atom%、酸素原子濃度が55~75atom%である請求項1~7のいずれかに記載のガスバリア性フィルム。 The gas barrier film according to any one of claims 1 to 7, wherein the second layer has a silicon atom concentration of 25 to 45 atom% and an oxygen atom concentration of 55 to 75 atom% as measured by X-ray photoelectron spectroscopy.