WO2015098803A1 - Composition de résine dégradable pour la solidification et le moulage par extrusion, produit moulé, produit moulé secondaire, outil de forage ou membre de celui-ci et procédé de récupération d'hydrocarbures - Google Patents

Composition de résine dégradable pour la solidification et le moulage par extrusion, produit moulé, produit moulé secondaire, outil de forage ou membre de celui-ci et procédé de récupération d'hydrocarbures Download PDF

Info

Publication number
WO2015098803A1
WO2015098803A1 PCT/JP2014/083847 JP2014083847W WO2015098803A1 WO 2015098803 A1 WO2015098803 A1 WO 2015098803A1 JP 2014083847 W JP2014083847 W JP 2014083847W WO 2015098803 A1 WO2015098803 A1 WO 2015098803A1
Authority
WO
WIPO (PCT)
Prior art keywords
decomposable resin
molded product
resin composition
extrusion molding
solidified
Prior art date
Application number
PCT/JP2014/083847
Other languages
English (en)
Japanese (ja)
Inventor
大倉正之
▲高▼橋健夫
西條光
佐藤浩幸
Original Assignee
株式会社クレハ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社クレハ filed Critical 株式会社クレハ
Publication of WO2015098803A1 publication Critical patent/WO2015098803A1/fr

Abstract

La présente invention concerne une composition de résine dégradable pour la solidification et le moulage par extrusion, la composition de résine comprenant 60 à 97 % en masse d'une résine dégradable, 3 à 37 % en masse d'un matériau de renforcement et de 0 à 3,5 % en masse d'un agent améliorant l'endurance (100 % en masse en tout de la résine dégradable, du matériau de renforcement et de l'agent d'amélioration de l'endurance), la composition de résine présentant une résistance au choc sur barreau entaillé d'après Izod (pas d'entaille) de 500 J/m ou plus, une résistance au choc sur barreau entaillé d'après Izod (entaille) de 50 J/m ou plus et une résistance à la traction de 135 MPa ou plus. L'invention concerne également un produit moulé en résine dégradable solidifié et extrudé et un produit moulé secondaire formé à partir de ladite composition de résine dégradable pour solidification et moulage par extrusion ; un outil de forage ou un membre de celui-ci formé à partir du produit moulé (secondaire) en résine ; et un procédé de récupération d'hydrocarbures.
PCT/JP2014/083847 2013-12-26 2014-12-22 Composition de résine dégradable pour la solidification et le moulage par extrusion, produit moulé, produit moulé secondaire, outil de forage ou membre de celui-ci et procédé de récupération d'hydrocarbures WO2015098803A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013268784 2013-12-26
JP2013-268784 2013-12-26

Publications (1)

Publication Number Publication Date
WO2015098803A1 true WO2015098803A1 (fr) 2015-07-02

Family

ID=53478657

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/083847 WO2015098803A1 (fr) 2013-12-26 2014-12-22 Composition de résine dégradable pour la solidification et le moulage par extrusion, produit moulé, produit moulé secondaire, outil de forage ou membre de celui-ci et procédé de récupération d'hydrocarbures

Country Status (1)

Country Link
WO (1) WO2015098803A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
USRE46028E1 (en) 2003-05-15 2016-06-14 Kureha Corporation Method and apparatus for delayed flow or pressure change in wells
US9708878B2 (en) 2003-05-15 2017-07-18 Kureha Corporation Applications of degradable polymer for delayed mechanical changes in wells
WO2018216334A1 (fr) * 2017-05-25 2018-11-29 株式会社クレハ Composition de gomme pour outils de forage et élément pour outils de forage
US10829614B2 (en) 2015-12-25 2020-11-10 Kureha Corporation Composition, composition for downhole tools, degradable rubber member for downhole, downhole tool, and method for well drilling
CN112679927A (zh) * 2020-12-24 2021-04-20 海南赛诺实业有限公司 一种具有较高货架期的改性pga材料及其制备方法
US20230174777A1 (en) * 2021-12-08 2023-06-08 Cnpc Usa Corporation Modified polyglycolic acid and molded articles for degradable downhole tools application

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000176879A (ja) * 1998-12-15 2000-06-27 Kureha Chem Ind Co Ltd 生分解性切断部材及びそれを備えた包装用容器
JP2008031472A (ja) * 2006-07-05 2008-02-14 Mitsubishi Plastics Ind Ltd 生分解性樹脂製管状成形体
JP2010069718A (ja) * 2008-09-18 2010-04-02 Kureha Corp ポリグリコール酸固化押出成形物及びその製造方法
WO2014010267A1 (fr) * 2012-07-10 2014-01-16 株式会社クレハ Élément d'outil de fond de puits pour la récupération de ressources en hydrocarbures
WO2014109347A1 (fr) * 2013-01-11 2014-07-17 株式会社クレハ Article solidifié et moulé par extrusion d'acide poly-l-lactique, son procédé de production et ses applications d'utilisation
WO2014192885A1 (fr) * 2013-05-31 2014-12-04 株式会社クレハ Tampon de forage comprenant un mandrin formé d'un matériau dégradable

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000176879A (ja) * 1998-12-15 2000-06-27 Kureha Chem Ind Co Ltd 生分解性切断部材及びそれを備えた包装用容器
JP2008031472A (ja) * 2006-07-05 2008-02-14 Mitsubishi Plastics Ind Ltd 生分解性樹脂製管状成形体
JP2010069718A (ja) * 2008-09-18 2010-04-02 Kureha Corp ポリグリコール酸固化押出成形物及びその製造方法
WO2014010267A1 (fr) * 2012-07-10 2014-01-16 株式会社クレハ Élément d'outil de fond de puits pour la récupération de ressources en hydrocarbures
WO2014109347A1 (fr) * 2013-01-11 2014-07-17 株式会社クレハ Article solidifié et moulé par extrusion d'acide poly-l-lactique, son procédé de production et ses applications d'utilisation
WO2014192885A1 (fr) * 2013-05-31 2014-12-04 株式会社クレハ Tampon de forage comprenant un mandrin formé d'un matériau dégradable

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
USRE46028E1 (en) 2003-05-15 2016-06-14 Kureha Corporation Method and apparatus for delayed flow or pressure change in wells
US9708878B2 (en) 2003-05-15 2017-07-18 Kureha Corporation Applications of degradable polymer for delayed mechanical changes in wells
US10280703B2 (en) 2003-05-15 2019-05-07 Kureha Corporation Applications of degradable polymer for delayed mechanical changes in wells
US10829614B2 (en) 2015-12-25 2020-11-10 Kureha Corporation Composition, composition for downhole tools, degradable rubber member for downhole, downhole tool, and method for well drilling
GB2575573B (en) * 2017-05-25 2020-10-14 Kureha Corp Rubber composition for downhole tools and member for downhole tools
GB2575573A (en) * 2017-05-25 2020-01-15 Kureha Corp Rubber composition for downhole tools and member for downhole tools
CN110431178A (zh) * 2017-05-25 2019-11-08 株式会社吴羽 井下工具用橡胶组合物以及井下工具用构件
WO2018216334A1 (fr) * 2017-05-25 2018-11-29 株式会社クレハ Composition de gomme pour outils de forage et élément pour outils de forage
CN110431178B (zh) * 2017-05-25 2021-02-02 株式会社吴羽 井下工具用橡胶组合物以及井下工具用构件
US11059952B2 (en) 2017-05-25 2021-07-13 Kureha Corporation Rubber composition for downhole tools and member for downhole tools
CN112679927A (zh) * 2020-12-24 2021-04-20 海南赛诺实业有限公司 一种具有较高货架期的改性pga材料及其制备方法
US20230174777A1 (en) * 2021-12-08 2023-06-08 Cnpc Usa Corporation Modified polyglycolic acid and molded articles for degradable downhole tools application
US11827780B2 (en) * 2021-12-08 2023-11-28 Cnpc Usa Corporation Modified polyglycolic acid and molded articles for degradable downhole tools application

Similar Documents

Publication Publication Date Title
WO2015098803A1 (fr) Composition de résine dégradable pour la solidification et le moulage par extrusion, produit moulé, produit moulé secondaire, outil de forage ou membre de celui-ci et procédé de récupération d'hydrocarbures
JP6207529B2 (ja) ポリ−ｌ−乳酸固化押出成形物の応用及びポリ−ｌ−乳酸固化押出成形物の製造方法
CA2891507C (fr) Article moule solidifie extrude fait d'acide polyglycolique et sa methode de fabrication
Leong et al. Comparison of the mechanical properties and interfacial interactions between talc, kaolin, and calcium carbonate filled polypropylene composites
CA2931282C (fr) Outil de fond de trou ou element d'outil de fond de trou, composition de resine degradable et procede de recuperation de ressources d'hydrocarbures
Adak et al. Polyurethane/clay nanocomposites with improved helium gas barrier and mechanical properties: Direct versus master‐batch melt mixing route
US20180291702A1 (en) Solidification- and extrusion-molded article of polyglycolic acid and method for manufacturing same
KR101154107B1 (ko) 충전제?유리 함유 수지 성형체
Yeniova Erpek et al. Effects of halloysite nanotubes on the performance of plasticized poly (lactic acid)‐based composites
Sánchez‐Safont et al. PHBV/TPU/cellulose compounds for compostable injection molded parts with improved thermal and mechanical performance
Dong et al. The study on polypropylene applied in fused deposition modeling
CN104736635B (zh) 耐热、阻燃聚乳酸配混物
Kumar et al. Mechanical properties of modified biofiller‐polypropylene composites
US20180094132A1 (en) Polyglycolic acid resin composition, molded product for well drilling, and downhole tool member
Nayani et al. Synthesis and Characterization of Polyurethane‐Nanoclay Composites
JP5066790B2 (ja) 樹脂組成物
Lucchetta et al. Self‐reinforced composites based on commercial PP woven fabrics and a random PP copolymer modified with quartz
JP2007161791A (ja) 樹脂組成物
Ghaisas et al. Blends of plasticized poly (vinyl chloride) and waste flexible poly (vinyl chloride) with waste nitrile rubber powder
KR20180055401A (ko) 폴리올레핀계 수지 조성물, 폴리올레핀계 마스터배치, 이의 제조 방법 및 이를 이용한 성형품
Chaiwutthinan et al. Influence of poly (butylene terephthalate) and wollastonite on properties of recycled poly (ethylene terephthalate) preforms
Mohamed et al. Enhancing 3D printing sustainability: Reinforcing thermoplastic polyurethane with recycled polyurethane foam for durable applications in orthopedic footwear
JP2016047874A (ja) 樹脂組成物およびそれからなる成形品
Wei et al. POLYPROPYLENE HYBRID COMPOSITES BASED ON TALC AND CALCIUM CARBONATE

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14875192

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14875192

Country of ref document: EP