WO2015093783A1 - 글라스 프릿 및 이를 이용한 발광 다이오드 - Google Patents

글라스 프릿 및 이를 이용한 발광 다이오드 Download PDF

Info

Publication number
WO2015093783A1
WO2015093783A1 PCT/KR2014/012187 KR2014012187W WO2015093783A1 WO 2015093783 A1 WO2015093783 A1 WO 2015093783A1 KR 2014012187 W KR2014012187 W KR 2014012187W WO 2015093783 A1 WO2015093783 A1 WO 2015093783A1
Authority
WO
WIPO (PCT)
Prior art keywords
glass frit
emitting diode
light emitting
phosphor
light
Prior art date
Application number
PCT/KR2014/012187
Other languages
English (en)
French (fr)
Inventor
오윤석
이기연
신희균
김보미
김지만
양춘봉
Original Assignee
코닝정밀소재 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 코닝정밀소재 주식회사 filed Critical 코닝정밀소재 주식회사
Publication of WO2015093783A1 publication Critical patent/WO2015093783A1/ko

Abstract

본 발명은 글라스 프릿 및 이를 이용한 발광 다이오드에 관한 것으로서, 더욱 상세하게는 형광체에 혼합되는 글라스 프릿 및 이를 이용한 발광 다이오드에 관한 것이다. 이를 위해, 본 발명은 7.49 ~ 39.11 mol%의 Bi2O3 및 20 ~ 70 mol%의 B2O3를 포함하는 것을 특징으로 하는 글라스 프릿을 제공한다.

Description

글라스 프릿 및 이를 이용한 발광 다이오드
본 발명은 글라스 프릿 및 이를 이용한 발광 다이오드에 관한 것으로서, 더욱 상세하게는 형광체가 혼합되는 글라스 프릿 및 이를 이용한 발광 다이오드에 관한 것이다.
발광 다이오드(light emission diode; LED)는 반도체의 p-n 접합 구조를 이용하여 주입된 소수 캐리어(전자 또는 정공)를 만들고 이들의 재결합에 의하여 소정의 빛을 발산하는 소자를 지칭한다.
발광 다이오드는 소비 전력이 적고 수명이 길며, 협소한 공간에 설치 가능하고, 또한 진동에 강한 특성을 갖는다. 이러한 발광 다이오드는 표시 소자 및 백라이트로 이용되고 있으며, 최근 일반 조명 용도로 이를 적용하기 위해 활발한 연구가 진행 중이다. 최근에는 단일 색성분 예를 들어, 적색, 청색, 또는 녹색 발광 다이오드 외에 백색 발광 다이오드들이 출시되고 있다. 백색 발광 다이오드는 자동차용 및 조명용 제품에 응용되면서, 그 수요가 급속히 증가할 것으로 예상된다.
발광 다이오드 기술에서 백색을 구현하는 방식은 크게 두 가지로 구분 가능하다. 첫번째는 적색, 녹색, 청색 발광 다이오드 칩을 인접하게 설치하고, 각 소자의 발광을 혼색시켜 백색을 구현하는 방식이다. 그러나, 각 발광 다이오드 칩은 열적 또는 시간적 특성이 상이하기 때문에 사용 환경에 따라 색조가 변하고 특히, 색얼룩이 발생하는 등 균일한 혼색을 구현하지 못하는 문제점이 있다.
두번째는 형광체를 발광 다이오드 칩에 배치시켜, 발광 다이오드 칩의 1차 발광의 일부와 형광체에 의해 파장 변환된 2차 발광이 혼색되어 백색을 구현하는 방식이다. 예를 들어 청색으로 발광하는 발광 다이오드 칩 상에 그 광의 일부를 여기원으로서 황록색 또는 황색 발광하는 형광체를 분포시켜 발광 다이오드 칩의 청색 발광과 형광체의 황록색 또는 황색 발광에 의해 백색을 얻을 수 있다. 현재는 이와 같이 청색 발광 다이오드 칩과 형광체를 이용하여 백색광을 구현하는 방법이 보편화되어 있다.
한편, 이와 같은 발광 다이오드에서 형광체는 글라스 프릿에 혼합되어 사용될 수 있는데, 이 경우 글라스 프릿과 형광체와의 굴절률 차이에 의한 광손실에 의해 발광 다이오드의 광 추출 효율이 저하된다는 문제가 발생한다.
[선행기술문헌]
대한민국 공개특허공보 제10-2013-0070043호(2013.06.27)
본 발명은 상술한 바와 같은 종래기술의 문제점을 해결하기 위해 안출된 것으로서, 본 발명의 목적은 형광체와 혼합되는 글라스 프릿에서 발광 다이오드의 광 추출 효율을 향상시킬 수 있는 글라스 프릿 및 이를 이용한 발광 다이오드를 제공하는 것이다.
이를 위해, 본 발명은 7.49 ~ 39.11 mol%의 Bi2O3 및 20 ~ 70 mol%의 B2O3를 포함하는 것을 특징으로 하는 글라스 프릿을 제공한다.
그리고, 상기 글라스 프릿은 10 ~ 60 mol%의 ZnO를 더 포함할 수 있다.
또한, 상기 글라스 프릿은 V2O5, MgO, 및 TeO2 중 적어도 하나를 더 포함할 수 있다. 이때, 상기 글라스 프릿의 소결 온도는 550℃ 이하일 것이다.
바람직하게, 상기 글라스 프릿은 PbO와 Na2O를 실질적으로 포함하지 않을 것이다.
그리고, 상기 글라스 프릿의 입경은 100㎛ 이하일 것이다.
또한, 본 발명은 본체; 상기 본체에 실장되는 발광 다이오드 칩; 및 상기 발광 다이오드 칩의 상부에 배치되며, 본체를 밀봉하는 커버 플레이트를 포함하되, 상기 커버 플레이트는, 기판; 및 상기 본체의 내부를 향하는 상기 기판의 일면에 형성되되, 형광체와 상술한 글라스 프릿이 혼합되어 이루어진 형광체층을 포함하여 이루어지는 발광 다이오드를 제공한다.
여기서, 상기 기판은 소다 라임(soda-lime) 유리로 이루어질 수 있다.
바람직하게, 상기 발광 다이오드 칩은 청색 발광 다이오드 칩이고, 상기 형광체는 황색 형광체일 것이다.
본 발명에 따르면, 발광 다이오드의 광 추출 효율을 향상시킬 수 있다.
또한, 소성 시 형광체의 조성 및 품질의 변화를 억제할 수 있다.
또한, 글라스 프릿을 친환경적으로 제조할 수 있다.
도 1은 본 발명에 따른 발광 다이오드의 개략적인 단면도.
도 2는 본 발명에 따른 발광 다이오드의 파장별 광량을 나타낸 그래프.
이하에서는 첨부된 도면들을 참조하여 본 발명의 실시 예에 따른 글라스 프릿 및 이를 이용한 발광 다이오드에 대해 상세히 설명한다.
아울러, 본 발명을 설명함에 있어서, 관련된 공지 기능 혹은 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단된 경우 그 상세한 설명은 생략한다.

본 발명에 따른 글라스 프릿(glass frit)은 미분쇄를 통해 얻어진 유리 분말로서, 7.49 ~ 39.11 mol%의 Bi2O3 및 20 ~ 70 mol%의 B2O3를 포함하여 이루어진다.
글라스 프릿이 이와 같은 조성으로 이루어짐으로써 본 발명에 따른 글라스 프릿은 1.9 이상의 굴절률을 가질 수 있다.
[표 1]은 글라스 프릿의 조성별 함유량(mol%)에 따른 굴절률을 나타낸 표이다.
No. 1 2 3 4 5 6 7 8 9 10
Bi2O3 5.07 31.45 39.11 31.39 6 7.49 33.3 30.6 32.9
B2O3 33.65 64.58 31.22 36.36 24.74 30.14 28.9 66.7 55.3 57.2
SiO2 9.87 14.33 9.98 10.6 9.94
Al2O3
ZnO 50.63 29.67 32.25 52.02 52.8 51.9 14.2
V2O5 0.79 1.1 1.16
MgO 8.9
TeO2 3.97
굴절율 1.756 1.925 2.199 2.165 1.653 1.791 1.9 1.9 1.9 1.9
[표 1]에 나타난 바와 같이, 7.49 ~ 39.11 mol%의 Bi2O3 및 20 ~ 70 mol%의 B2O3를 포함하여 이루어진 글라스 프릿은 1.9 이상의 굴절률을 갖는 반면, 그렇지 않은 글라스 프릿은 이보다 낮은 굴절률을 가짐을 알 수 있다.
이에 본 발명에 따른 글라스 프릿을 형광체와 혼합한 후 발광 다이오드의 형광층을 구성하는데 사용하는 경우, 발광 다이오드의 광 추출 효율을 향상시킬 수 있다. 즉, 일반적으로 형광체는 1.7 ~ 1.8의 굴절률을 가지므로 이와 혼합되는 글라스 프릿이 이보다 높은 1.9 이상의 굴절률을 갖도록 함으로써, 글라스 프릿에 의해 산란된 후 발광 다이오드의 외부로 발광하지 못하는 광량을 감소시킬 수 있고 이에 의해 발광 다이오드의 광 추출 효율을 향상시킬 수 있다.
또한, 본 발명에 따른 글라스 프릿은 형광체와의 반응성이 적어 형광체와 혼합된 글라스 프릿의 소성 시 형광체의 조성 변화를 방지할 수 있다.
그리고, 본 발명에 따른 글라스 프릿은 더 큰 굴절률을 갖기 위해 10 ~ 60 mol%의 ZnO를 더 포함할 수 있다.
또한, 본 발명에 따른 글라스 프릿은 V2O5, MgO, 및 TeO2 중 적어도 하나를 더 포함할 수 있다.
글라스 프릿에 V2O5, MgO, 및 TeO2 중 적어도 하나를 더 포함시킴으로써, 글라스 프릿의 소결 온도를 제어할 수 있다. 즉, 글라스 프릿에 V2O5, MgO, 및 TeO2 중 적어도 하나를 더 포함시켜 글라스 프릿의 소결 온도가 550℃ 이하가 되도록 제어할 수 있다. 이에 의해, 형광체와 혼합된 글라스 프릿의 소성 시 형광체의 품질 변화를 방지할 수 있다.
또한, 본 발명에 따른 글라스 프릿은 PbO와 Na2O를 실질적으로 포함하지 않는 것이 바람직하다. 여기서, '실질적으로 포함하지 않는다' 등의 표현은 해당 성분을 의도적으로 첨가하지는 않으나 원재료 중 불순물로 혼입되는 것을 배제할 수 없다는 의미로 사용된다.
글라스 프릿이 환경 오염 물질인 PbO를 포함하지 않음으로써, 본 발명에 따른 글라스 프릿을 친환경적으로 제조할 수 있다. 그리고, Na2O를 포함하지 않음으로써, 소성 시 글라스 프릿의 착색과 결정화를 억제하여 소성 후 광투과율을 향상시킬 수 있다.
또한, 본 발명에 따른 글라스 프릿은 100㎛ 이하의 입경을 갖는 것이 바람직하다.
입경이 100㎛ 이상일 경우 소성 중 미 연화된 분말들이 발생할 수 있고, 분말간 공극이 크므로 소성 후 발생되는 기포의 크기도 커져 이에 따른 산란으로 투과도의 저하를 일으킬 수 있기 때문이다.

도 1은 본 발명에 따른 발광 다이오드의 개략적인 단면도이다.
도 1에 도시된 바와 같이, 본 발명에 따른 발광 다이오드는 본체, 발광 다이오드 칩, 및 커버 플레이트를 포함하여 이루어진다.
본체(100)는 소정 형상의 개구부가 형성된 구조체로서 발광 다이오드 칩이 실장되는 구조적 공간을 제공한다.
본체(100)에는 발광다이오드 칩(200)을 외부 전원과 전기적으로 접속시키는 와이어와 리드 프레임이 설치될 수 있다.
발광 다이오드 칩(200)은 본체(100)에 실장되며, 외부에서 인가되는 전류에 의해 광을 방출하는 광원으로서, 전자(electron)를 제공하는 n형 반도체층과 정공(hole)을 제공하는 p형 반도체층의 순방향 접합으로 이루어진다.
바람직하게, 본 발명의 발광 다이오드 칩(200)은 청색 광을 방출할 것이며, 복수 개의 발광 다이오드 칩이 본체(100)에 실장될 수 있다.
커버 플레이트(300)는 발광 다이오드 칩(200)의 상부에 배치되어 발광 다이오드 칩(200)을 밀봉한다.
커버 플레이트(300)는 기판(310)과 발광 다이오드 칩(200)을 향하는 기판(310)의 일면에 형성되되, 형광체(322)와 글라스 프릿이 혼합되어 이루어진 형광체층(320)을 포함하여 이루어진다.
여기서, 글라스 프릿은 전술한 바와 동일하므로 이에 대한 구체적인 설명은 생략한다.
형광체(322)는 글라스 프릿에 혼합되어, 발광 다이오드 칩(200)에 의해 방출된 광의 일부를 색변환시킨다. 이에 의해, 발광 다이오드는 형광체(322)에 의해 색변환된 광과 발광 다이오드 칩(200)에 의해 방출된 광이 혼합되어 구현된 색을 발광하게 된다. 일례로, 백색 발광 다이오드는 청색을 방출하는 발광 다이오드 칩 상에 황색 형광체를 분포시킴으로써 제조할 수 있다. 여기서, 황색 형광체로는 YAG:Ce3+ 가 사용될 수 있다.
커버 플레이트(300)는 글라스 프릿과 형광체가 혼합된 페이스트(paste)를 기판(310)에 도포한 후 소성시킴으로써 제조될 수 있다. 여기서, 페이스트는 글라스 프릿과 형광체의 혼합물에 에스테르 알코올과 에틸셀룰로오스 바인더가 혼합된 비히클(vehicle)을 혼합시킴으로써 제조할 수 있다. 또한, 페이스트에는 분산제, 안정제, 계면활성제 등이 추가적으로 혼합될 수 있다.
이와 같이 구성된 본 발명에 따른 발광 다이오드는 우수한 광 추출 효율을 가진다.
[표 2]는 본 발명에 따른 발광 다이오드의 광량을 나타낸 표이고, 도 2는 이의 파장별 광량을 나타낸 그래프이다.
여기서, 비교예는 소다 라임 유리만으로 이루어진 커버 플레이트를 구비한 발광 다이오드이다. 실시예 1은 전술한 [표 1]에서의 No.2 조성에 추진제(필러)가 1wt% 더 포함된 글라스 프릿을 이용한 형광층을 구비한 발광 다이오드이고, 실시예 2는 전술한 [표 1]에서의 No.7 조성에 TiO2가 10wt% 더 포함된 글라스 프릿을 이용한 형광층을 구비한 발광 다이오드이다. 또한 실시예 3은 전술한 [표 1]에서의 No.6 조성에 Quartz가 10wt% 더 포함된 글라스 프릿을 이용한 형광층을 구비한 발광 다이오드이고, 실시예 4는 전술한 [표 1]에서의 No.7 조성에 SiO2가 10wt% 더 포함된 글라스 프릿을 이용한 형광층을 구비한 발광 다이오드이다.
비교예 실시예 1 실시예 2 실시예 3 실시예 4
최대 5260.0 6731.0 6018.0 6415.0 6566.0
% 100.0 128.0 114.4 122.0 124.8
[표 2] 및 도 2에 나타난 바와 같이, 본 발명에 따른 커버 플레이트를 구비한 발광 다이오드는 그렇지 않은 발광 다이오드에 비해 월등히 향상된 광 추출 효율을 가짐을 알 수 있다.
한편, 기판은 소다 라임(soda-lime) 유리로 이루어질 수 있다.
이 경우, 본 발명에 따른 7.49 ~ 39.11 mol%의 Bi2O3 및 20 ~ 70 mol%의 B2O3를 포함하여 이루어진 글라스 프릿은 소다 라임 유리와 유사한 열팽창 계수를 가지므로, 형광층의 열팽창 계수를 조절하기 위한 별도의 필러(filler)를 추가적으로 투입할 필요가 없을 것이다.

이상과 같이 본 발명은 비록 한정된 실시 예와 도면에 의해 설명되었으나, 본 발명은 상기의 실시 예에 한정되는 것은 아니며, 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다.
그러므로 본 발명의 범위는 설명된 실시 예에 국한되어 정해져서는 아니 되며, 후술하는 특허청구범위뿐만 아니라 특허청구범위와 균등한 것들에 의해 정해져야 한다.
[부호의 설명]
100: 본체
200: 발광 다이오드 칩
300: 커버 플레이트
310: 기판
320: 형광체층
322: 형광체

Claims (9)

  1. 7.49 ~ 39.11 mol%의 Bi2O3 및 20 ~ 70 mol%의 B2O3를 포함하는 것을 특징으로 하는 글라스 프릿.
  2. 제1항에 있어서,
    10 ~ 60 mol%의 ZnO를 더 포함하는 것을 특징으로 하는 글라스 프릿.
  3. 제1항에 있어서,
    V2O5, MgO, 및 TeO2 중 적어도 하나를 더 포함하는 것을 특징으로 하는 글라스 프릿.
  4. 제3항에 있어서,
    상기 글라스 프릿의 소결 온도는 550℃ 이하인 것을 특징으로 하는 글라스 프릿.
  5. 제1항에 있어서,
    상기 글라스 프릿은 PbO와 Na2O를 실질적으로 포함하지 않는 것을 특징으로 하는 글라스 프릿.
  6. 제1항에 있어서,
    상기 글라스 프릿의 입경은 100㎛ 이하인 것을 특징으로 하는 글라스 프릿.
  7. 본체;
    상기 본체에 실장되는 발광 다이오드 칩; 및
    상기 발광 다이오드 칩의 상부에 배치되며, 본체를 밀봉하는 커버 플레이트를 포함하되,
    상기 커버 플레이트는,
    기판; 및
    상기 본체의 내부를 향하는 상기 기판의 일면에 형성되되, 형광체와 상기 청구항 제1항 내지 제6항 중 어느 한 항의 글라스 프릿이 혼합되어 이루어진 형광체층을 포함하여 이루어지는 발광 다이오드.
  8. 제7항에 있어서,
    상기 기판은 소다 라임(soda-lime) 유리로 이루어지는 것을 특징으로 하는 발광 다이오드.
  9. 제7항에 있어서,
    상기 발광 다이오드 칩은 청색 발광 다이오드 칩이고,
    상기 형광체는 황색 형광체인 것을 특징으로 하는 발광 다이오드.
PCT/KR2014/012187 2013-12-16 2014-12-11 글라스 프릿 및 이를 이용한 발광 다이오드 WO2015093783A1 (ko)