WO2014200112A1 - Reactive silicone composition, reactive thermoplastic, cured product and photosemiconductor device - Google Patents
Reactive silicone composition, reactive thermoplastic, cured product and photosemiconductor device Download PDFInfo
- Publication number
- WO2014200112A1 WO2014200112A1 PCT/JP2014/065833 JP2014065833W WO2014200112A1 WO 2014200112 A1 WO2014200112 A1 WO 2014200112A1 JP 2014065833 W JP2014065833 W JP 2014065833W WO 2014200112 A1 WO2014200112 A1 WO 2014200112A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- mass
- parts
- cured product
- sio
- Prior art date
Abstract
Provided are: a reactive silicone composition which comprises at least (A) an organo polysiloxane having an alkenyl group represented by an average unit formula, (B) an organo polysiloxane having an alkenyl group represented by a general formula, (C) an organo polysiloxane having a silicon-bonded hydrogen atom, (D) a hydrosilylation reaction catalyst, (E) a white pigment other than titanium oxide, and (F) spherical silica, nonspherical silica, or glass fiber; a reactive thermoplastic thereof, a cured product thereof and a photosemiconductor device having the cured product. The present invention provides: a reactive silicone composition which is capable of forming a reactive thermoplastic; a reactive thermoplastic which temporarily fluidizes when heated, then provides a cured product; a cured product which has small reduction in mechanical strength and less discoloration due to heat and light, a high optical reflectivity, in particular, in a range of 350 to 400 nm, and excellent adhesion to metal; and a photosemiconductor device which has a high luminous efficiency, less thermal degradation and photodegradation of a light reflection material, and excellent reliability.
Description
本発明は、反応性シリコーン組成物、反応性熱可塑体、硬化物、および光半導体装置に関する。
The present invention relates to a reactive silicone composition, a reactive thermoplastic, a cured product, and an optical semiconductor device.
ヒドロシリル化反応により硬化する硬化性シリコーン組成物は、フォトカプラー、発光ダイオード、固体撮像素子等の光半導体装置における光半導体素子の保護剤やコーティング剤；その他、レンズ成形材料、光反射材料等として使用されている。その中で、光反射材料として使用される組成物としては、例えば、ビニル基およびアリル基のいずれか一方と、水素原子が、直接ケイ素原子に結合してなる構造を有する熱硬化型付加反応性シリコーン樹脂、硬化触媒としての白金系触媒、および酸化チタン等の白色顔料からなる光半導体素子収納用実装パッケージ用樹脂組成物（特許文献１参照）、重量平均分子量（Ｍｗ）が３０，０００以上であるビニル基含有オルガノポリシロキサン、一分子中にケイ素結合水素原子を少なくとも２個有するオルガノハイドロジェンポリシロキサン、酸化チタン等の白色顔料、白色顔料以外の無機充填剤、白金金属系触媒、および反応制御剤からなる、硬化後の可視光平均反射率が８０％以上である付加硬化型シリコーン樹脂組成物（特許文献２参照）が挙げられる。
これらの組成物は、トランスファー成形、射出成形、あるいは圧縮成形において、金型充填性が低かったり、ボイドやバリが発生しやすかったり、金型離型性が悪いという課題があり、特に、硬化速度が遅く、成形操作の作業性が悪いという課題もある。また、これらの組成物を硬化して得られる硬化物は、熱や光による変色が少ないという利点があるものの、線膨張率が大きかったり、高温での機械的強度が低くいという課題や、光反射率が不十分で、熱や光による機械的強度の低下が大きく、金属に対する接着性が不十分であるという課題がある。さらに、これらの組成物では、一般に、反射率を高める目的で、白色顔料として酸化チタンが用いられるが、酸化チタンは紫外線領域の光を強く吸収するため、３５０~４００ｎｍの領域の反射率が低いという課題がある。 A curable silicone composition that cures by hydrosilylation reaction is used as a protective agent or coating agent for optical semiconductor elements in optical semiconductor devices such as photocouplers, light-emitting diodes, and solid-state imaging elements; Has been. Among them, as a composition used as a light reflecting material, for example, either a vinyl group or an allyl group and a thermosetting addition reactivity having a structure in which a hydrogen atom is directly bonded to a silicon atom A resin composition for mounting packages for housing an optical semiconductor element comprising a silicone resin, a platinum-based catalyst as a curing catalyst, and a white pigment such as titanium oxide (see Patent Document 1), with a weight average molecular weight (Mw) of 30,000 or more Certain vinyl group-containing organopolysiloxanes, organohydrogenpolysiloxanes having at least two silicon-bonded hydrogen atoms in one molecule, white pigments such as titanium oxide, inorganic fillers other than white pigments, platinum metal catalysts, and reaction control Addition-curing silicone resin composition comprising an agent and having an average visible light reflectance after curing of 80% or more (see Patent Document 2) And the like.
These compositions have problems such as transfer molding, injection molding, or compression molding that have low mold filling properties, are prone to voids and burrs, and have poor mold releasability. However, there is also a problem that the workability of the molding operation is poor. In addition, cured products obtained by curing these compositions have the advantage of less discoloration due to heat and light, but have problems such as high coefficient of linear expansion and low mechanical strength at high temperatures, There is a problem that the reflectivity is insufficient, the mechanical strength is greatly reduced by heat and light, and the adhesion to metal is insufficient. Further, in these compositions, titanium oxide is generally used as a white pigment for the purpose of increasing the reflectivity. However, since titanium oxide absorbs light in the ultraviolet region strongly, the reflectivity in the region of 350 to 400 nm is low. There is a problem.
これらの組成物は、トランスファー成形、射出成形、あるいは圧縮成形において、金型充填性が低かったり、ボイドやバリが発生しやすかったり、金型離型性が悪いという課題があり、特に、硬化速度が遅く、成形操作の作業性が悪いという課題もある。また、これらの組成物を硬化して得られる硬化物は、熱や光による変色が少ないという利点があるものの、線膨張率が大きかったり、高温での機械的強度が低くいという課題や、光反射率が不十分で、熱や光による機械的強度の低下が大きく、金属に対する接着性が不十分であるという課題がある。さらに、これらの組成物では、一般に、反射率を高める目的で、白色顔料として酸化チタンが用いられるが、酸化チタンは紫外線領域の光を強く吸収するため、３５０~４００ｎｍの領域の反射率が低いという課題がある。 A curable silicone composition that cures by hydrosilylation reaction is used as a protective agent or coating agent for optical semiconductor elements in optical semiconductor devices such as photocouplers, light-emitting diodes, and solid-state imaging elements; Has been. Among them, as a composition used as a light reflecting material, for example, either a vinyl group or an allyl group and a thermosetting addition reactivity having a structure in which a hydrogen atom is directly bonded to a silicon atom A resin composition for mounting packages for housing an optical semiconductor element comprising a silicone resin, a platinum-based catalyst as a curing catalyst, and a white pigment such as titanium oxide (see Patent Document 1), with a weight average molecular weight (Mw) of 30,000 or more Certain vinyl group-containing organopolysiloxanes, organohydrogenpolysiloxanes having at least two silicon-bonded hydrogen atoms in one molecule, white pigments such as titanium oxide, inorganic fillers other than white pigments, platinum metal catalysts, and reaction control Addition-curing silicone resin composition comprising an agent and having an average visible light reflectance after curing of 80% or more (see Patent Document 2) And the like.
These compositions have problems such as transfer molding, injection molding, or compression molding that have low mold filling properties, are prone to voids and burrs, and have poor mold releasability. However, there is also a problem that the workability of the molding operation is poor. In addition, cured products obtained by curing these compositions have the advantage of less discoloration due to heat and light, but have problems such as high coefficient of linear expansion and low mechanical strength at high temperatures, There is a problem that the reflectivity is insufficient, the mechanical strength is greatly reduced by heat and light, and the adhesion to metal is insufficient. Further, in these compositions, titanium oxide is generally used as a white pigment for the purpose of increasing the reflectivity. However, since titanium oxide absorbs light in the ultraviolet region strongly, the reflectivity in the region of 350 to 400 nm is low. There is a problem.
本発明は、反応性熱可塑体を形成し得る反応性シリコーン組成物、加熱すると一旦流動化し、その後、硬化物を与える反応性熱可塑体、熱や光による機械的強度の低下や変色が少なく、光反射率、特に３５０~４００ｎｍの領域の光反射率が高く、金属に対して優れた接着力を有する硬化物、および発光効率が高く、光反射材の熱劣化や光劣化が少なく、信頼性が優れる光半導体装置を提供することを目的とする。
The present invention relates to a reactive silicone composition capable of forming a reactive thermoplastic, a reactive thermoplastic that once fluidizes when heated, and then gives a cured product, a decrease in mechanical strength and discoloration due to heat and light. , High light reflectivity, especially in the 350-400 nm region, high cured product with excellent adhesion to metal, and high luminous efficiency, less light heat deterioration and light deterioration of the light reflecting material, reliable An object of the present invention is to provide an optical semiconductor device having excellent properties.
本発明の反応性シリコーン組成物は、
（Ａ）平均単位式：
（Ｒ１ ３ＳｉＯ１／２）ａ（Ｒ１ ２ＳｉＯ２／２）ｂ（Ｒ１ＳｉＯ３／２）ｃ（ＳｉＯ４／２）ｄ（Ｒ２Ｏ１／２）ｅ
（式中、Ｒ１は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、もしくは炭素原子数２~６のアルケニル基であり、ただし、全Ｒ１の３０~８０モル％はフェニル基であり、全Ｒ１の１０~２０モル％はアルケニル基であり、Ｒ２は水素原子または炭素原子数１~６のアルキル基であり、ａ、ｂ、ｃ、ｄ、およびｅはそれぞれ、０≦ａ≦０．３０、０≦ｂ≦０．７０、０．３≦ｃ≦０．９、０≦ｄ≦０．２０、０≦ｅ≦０．１０、かつａ＋ｂ＋ｃ＋ｄ＝１を満たす数である。）
で表されるオルガノポリシロキサン １００質量部、
（Ｂ）一般式：
Ｒ３ ３ＳｉＯ（Ｒ３ ２ＳｉＯ）ｍＳｉＲ３ ３
（式中、Ｒ３は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、もしくは炭素原子数２~６のアルケニル基であり、ただし、全Ｒ３の３０~７０モル％はフェニル基であり、全Ｒ３の少なくとも１個はアルケニル基であり、ｍは１０~１００の整数である。）
で表されるオルガノポリシロキサン ０~４０質量部、
（Ｃ）一分子中に少なくとも２個のケイ素原子結合水素原子を有し、ケイ素原子結合全有機基の２０~７０モル％がフェニル基であるオルガノポリシロキサン｛（Ａ）成分および（Ｂ）成分中のアルケニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．５~２モルとなる量｝、
（Ｄ）ヒドロシリル化反応用触媒｛（Ａ）成分および（Ｂ）成分中のアルケニル基と（Ｃ）成分中のケイ素原子結合水素原子とのヒドロシリル化反応を促進するに十分な量｝、
（Ｅ）酸化チタン以外の白色顔料｛（Ａ）成分~（Ｄ）成分の合計１００質量部に対して５０質量部以上｝、および
（Ｆ）非球状シリカ、球状シリカまたはガラスファイバー｛（Ａ）成分~（Ｄ）成分の合計１００質量部に対して１００質量部以上｝
から少なくともなり、（Ｅ）成分および（Ｆ）成分の合計の含有量が、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して４００質量部以下であることを特徴とする。
また、本発明の反応性熱可塑体は、上記の反応性シリコーン組成物のヒドロシリル化反応を７０~９５％転化率となるまで進行させてなることを特徴とする。
さらに、本発明の硬化物は、上記の反応性熱可塑体を１００℃以上に加熱することにより得られ、３００℃で固体もしくは粘度が１，０００，０００Ｐａ・ｓ以上であることを特徴とするか、または、上記の反応性シリコーン組成物を硬化してなることを特徴とする。
さらに、本発明の光半導体装置は、上記の硬化物により光反射材を形成してなることを特徴とする。 The reactive silicone composition of the present invention comprises:
(A) Average unit formula:
(R 1 3 SiO 1/2 ) a (R 1 2 SiO 2/2 ) b (R 1 SiO 3/2 ) c (SiO 4/2 ) d (R 2 O 1/2 ) e
(Wherein R 1 is the same or different and is a phenyl group, an alkyl group having 1 to 6 carbon atoms, or an alkenyl group having 2 to 6 carbon atoms, provided that 30 to 80 mol% of all R 1 s ) Is a phenyl group, 10 to 20 mol% of all R 1 is an alkenyl group, R 2 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, and a, b, c, d, and e are 0 ≦ a ≦ 0.30, 0 ≦ b ≦ 0.70, 0.3 ≦ c ≦ 0.9, 0 ≦ d ≦ 0.20, 0 ≦ e ≦ 0.10, and a + b + c + d = 1 are satisfied. Number.)
100 parts by mass of an organopolysiloxane represented by
(B) General formula:
R 3 3 SiO (R 3 2 SiO) m SiR 3 3
(Wherein R 3 is the same or different and is a phenyl group, an alkyl group having 1 to 6 carbon atoms, or an alkenyl group having 2 to 6 carbon atoms, provided that 30 to 70 mol% of all R 3 s ) Is a phenyl group, at least one of all R 3 is an alkenyl group, and m is an integer of 10 to 100.)
0 to 40 parts by mass of an organopolysiloxane represented by
(C) Organopolysiloxane having at least two silicon-bonded hydrogen atoms in one molecule and 20 to 70 mol% of all silicon-bonded organic groups being phenyl groups {component (A) and component (B) Amount of silicon atom-bonded hydrogen atoms in this component to be 0.5 to 2 moles relative to a total of 1 mole of alkenyl groups therein},
(D) Hydrosilylation catalyst {a sufficient amount to promote the hydrosilylation reaction between the alkenyl group in components (A) and (B) and the silicon atom-bonded hydrogen atom in component (C)},
(E) White pigment other than titanium oxide {50 parts by mass or more with respect to 100 parts by mass in total of components (A) to (D)}, and (F) non-spherical silica, spherical silica or glass fiber {(A) Component ~ (D) 100 parts by mass or more with respect to 100 parts by mass in total}
The total content of the component (E) and the component (F) is 400 parts by mass or less with respect to 100 parts by mass in total of the components (A) to (D).
The reactive thermoplastic of the present invention is characterized in that the hydrosilylation reaction of the above reactive silicone composition is allowed to proceed until a conversion of 70 to 95% is achieved.
Furthermore, the cured product of the present invention is obtained by heating the above-described reactive thermoplastic to 100 ° C. or higher, and is characterized by having a solid or a viscosity of 1,000,000 Pa · s or higher at 300 ° C. Or the above-mentioned reactive silicone composition is cured.
Furthermore, the optical semiconductor device of the present invention is characterized in that a light reflecting material is formed from the above cured product.
（Ａ）平均単位式：
（Ｒ１ ３ＳｉＯ１／２）ａ（Ｒ１ ２ＳｉＯ２／２）ｂ（Ｒ１ＳｉＯ３／２）ｃ（ＳｉＯ４／２）ｄ（Ｒ２Ｏ１／２）ｅ
（式中、Ｒ１は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、もしくは炭素原子数２~６のアルケニル基であり、ただし、全Ｒ１の３０~８０モル％はフェニル基であり、全Ｒ１の１０~２０モル％はアルケニル基であり、Ｒ２は水素原子または炭素原子数１~６のアルキル基であり、ａ、ｂ、ｃ、ｄ、およびｅはそれぞれ、０≦ａ≦０．３０、０≦ｂ≦０．７０、０．３≦ｃ≦０．９、０≦ｄ≦０．２０、０≦ｅ≦０．１０、かつａ＋ｂ＋ｃ＋ｄ＝１を満たす数である。）
で表されるオルガノポリシロキサン １００質量部、
（Ｂ）一般式：
Ｒ３ ３ＳｉＯ（Ｒ３ ２ＳｉＯ）ｍＳｉＲ３ ３
（式中、Ｒ３は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、もしくは炭素原子数２~６のアルケニル基であり、ただし、全Ｒ３の３０~７０モル％はフェニル基であり、全Ｒ３の少なくとも１個はアルケニル基であり、ｍは１０~１００の整数である。）
で表されるオルガノポリシロキサン ０~４０質量部、
（Ｃ）一分子中に少なくとも２個のケイ素原子結合水素原子を有し、ケイ素原子結合全有機基の２０~７０モル％がフェニル基であるオルガノポリシロキサン｛（Ａ）成分および（Ｂ）成分中のアルケニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．５~２モルとなる量｝、
（Ｄ）ヒドロシリル化反応用触媒｛（Ａ）成分および（Ｂ）成分中のアルケニル基と（Ｃ）成分中のケイ素原子結合水素原子とのヒドロシリル化反応を促進するに十分な量｝、
（Ｅ）酸化チタン以外の白色顔料｛（Ａ）成分~（Ｄ）成分の合計１００質量部に対して５０質量部以上｝、および
（Ｆ）非球状シリカ、球状シリカまたはガラスファイバー｛（Ａ）成分~（Ｄ）成分の合計１００質量部に対して１００質量部以上｝
から少なくともなり、（Ｅ）成分および（Ｆ）成分の合計の含有量が、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して４００質量部以下であることを特徴とする。
また、本発明の反応性熱可塑体は、上記の反応性シリコーン組成物のヒドロシリル化反応を７０~９５％転化率となるまで進行させてなることを特徴とする。
さらに、本発明の硬化物は、上記の反応性熱可塑体を１００℃以上に加熱することにより得られ、３００℃で固体もしくは粘度が１，０００，０００Ｐａ・ｓ以上であることを特徴とするか、または、上記の反応性シリコーン組成物を硬化してなることを特徴とする。
さらに、本発明の光半導体装置は、上記の硬化物により光反射材を形成してなることを特徴とする。 The reactive silicone composition of the present invention comprises:
(A) Average unit formula:
(R 1 3 SiO 1/2 ) a (R 1 2 SiO 2/2 ) b (R 1 SiO 3/2 ) c (SiO 4/2 ) d (R 2 O 1/2 ) e
(Wherein R 1 is the same or different and is a phenyl group, an alkyl group having 1 to 6 carbon atoms, or an alkenyl group having 2 to 6 carbon atoms, provided that 30 to 80 mol% of all R 1 s ) Is a phenyl group, 10 to 20 mol% of all R 1 is an alkenyl group, R 2 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, and a, b, c, d, and e are 0 ≦ a ≦ 0.30, 0 ≦ b ≦ 0.70, 0.3 ≦ c ≦ 0.9, 0 ≦ d ≦ 0.20, 0 ≦ e ≦ 0.10, and a + b + c + d = 1 are satisfied. Number.)
100 parts by mass of an organopolysiloxane represented by
(B) General formula:
R 3 3 SiO (R 3 2 SiO) m SiR 3 3
(Wherein R 3 is the same or different and is a phenyl group, an alkyl group having 1 to 6 carbon atoms, or an alkenyl group having 2 to 6 carbon atoms, provided that 30 to 70 mol% of all R 3 s ) Is a phenyl group, at least one of all R 3 is an alkenyl group, and m is an integer of 10 to 100.)
0 to 40 parts by mass of an organopolysiloxane represented by
(C) Organopolysiloxane having at least two silicon-bonded hydrogen atoms in one molecule and 20 to 70 mol% of all silicon-bonded organic groups being phenyl groups {component (A) and component (B) Amount of silicon atom-bonded hydrogen atoms in this component to be 0.5 to 2 moles relative to a total of 1 mole of alkenyl groups therein},
(D) Hydrosilylation catalyst {a sufficient amount to promote the hydrosilylation reaction between the alkenyl group in components (A) and (B) and the silicon atom-bonded hydrogen atom in component (C)},
(E) White pigment other than titanium oxide {50 parts by mass or more with respect to 100 parts by mass in total of components (A) to (D)}, and (F) non-spherical silica, spherical silica or glass fiber {(A) Component ~ (D) 100 parts by mass or more with respect to 100 parts by mass in total}
The total content of the component (E) and the component (F) is 400 parts by mass or less with respect to 100 parts by mass in total of the components (A) to (D).
The reactive thermoplastic of the present invention is characterized in that the hydrosilylation reaction of the above reactive silicone composition is allowed to proceed until a conversion of 70 to 95% is achieved.
Furthermore, the cured product of the present invention is obtained by heating the above-described reactive thermoplastic to 100 ° C. or higher, and is characterized by having a solid or a viscosity of 1,000,000 Pa · s or higher at 300 ° C. Or the above-mentioned reactive silicone composition is cured.
Furthermore, the optical semiconductor device of the present invention is characterized in that a light reflecting material is formed from the above cured product.
本発明の反応性シリコーン組成物は、反応性熱可塑体を形成することができるという特徴がある。また、本発明の反応性熱可塑体は、加熱すると一旦流動化し、その後、硬化物を与えるという特徴がある。また、本発明の硬化物は、熱や光による機械的強度の低下や変色が少なく、光反射率、特に３５０~４００ｎｍの領域の光反射率が高く、金属に対して優れた接着力を有するという特徴がある。さらに、本発明の光半導体装置は、発光効率が高く、光反射材の熱劣化や光劣化が少なく、信頼性が優れるという特徴がある。
The reactive silicone composition of the present invention is characterized in that it can form a reactive thermoplastic. In addition, the reactive thermoplastic of the present invention is characterized by being fluidized once heated and then giving a cured product. In addition, the cured product of the present invention has little decrease in mechanical strength or discoloration due to heat or light, high light reflectivity, particularly in the region of 350 to 400 nm, and excellent adhesion to metal. There is a feature. Furthermore, the optical semiconductor device of the present invention is characterized by high luminous efficiency, low thermal degradation and light degradation of the light reflecting material, and excellent reliability.
図１は、本発明の光半導体装置の一例であるＬＥＤの断面図である。
FIG. 1 is a cross-sectional view of an LED which is an example of an optical semiconductor device of the present invention.
はじめに、本発明の反応性シリコーン組成物を詳細に説明する。
（Ａ）成分は、本組成物の主成分であり、平均単位式：
（Ｒ１ ３ＳｉＯ１／２）ａ（Ｒ１ ２ＳｉＯ２／２）ｂ（Ｒ１ＳｉＯ３／２）ｃ（ＳｉＯ４／２）ｄ（Ｒ２Ｏ１／２）ｅ
で表されるオルガノポリシロキサンである。
式中、Ｒ１は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、もしくは炭素原子数２~６のアルケニル基である。Ｒ１のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、シクロペンチル基、シクロヘキシル基が例示される。Ｒ１のアルケニル基としては、ビニル基、アリル基、ブテニル基、ペンテニル基、ヘキセニル基が例示される。なお、フェニル基の含有量は全Ｒ１の３０~８０モル％の範囲内であり、反応性熱可塑体を形成する場合は、全Ｒ１の６０~７５モル％の範囲内であることが好ましい。これは、フェニル基の含有量が上記範囲の下限以上であると、得られる反応性熱可塑体の室温での硬さと高温での流動特性が良好であり、また得られる硬化物の機械的強度が良好であり、一方、上記範囲の上限以下であると、得られる硬化物の高温での硬さが良好であるからである。また、式中、全Ｒ１の内、アルケニル基の含有量は１０~２０モル％の範囲内である。これは、アルケニル基の含有量が上記範囲の下限以上であると、得られる硬化物の室温での硬さが良好であり、一方、上記範囲の上限以下であると、得られる硬化物の機械的強度が良好であるからである。
また、式中、Ｒ２は水素原子または炭素原子数１~６のアルキル基である。Ｒ２のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基が例示される。
さらに、式中、ａは、一般式：Ｒ１ ３ＳｉＯ１／２で表されるシロキサン単位の割合を示す数であり、０≦ａ≦０．３０、好ましくは、０≦ａ≦０．２５を満たす数である。これは、ａが上記範囲の上限以下であると、得られる硬化物の室温での硬さが良好であるからである。また、式中、ｂは、一般式：Ｒ１ ２ＳｉＯ２／２で表されるシロキサン単位の割合を示す数であり、０≦ｂ≦０．７０を満たす数であり、反応性熱可塑体を形成する場合には、０．１０≦ｂ≦０．７０を満たす数であることが好ましく、さらには、０．１５≦ｂ≦０．６０を満たす数であることが好ましい。これは、ｂが上記範囲の下限以上であると、得られる反応性熱可塑体の室温での硬さと高温での流動特性が良好であり、一方、上記範囲の上限以下であると、得られる硬化物の室温での硬さが良好であるからである。また、ｃは、一般式：Ｒ１ＳｉＯ３／２で表されるシロキサン単位の割合を示す数であり、０．３≦ｃ≦０．９を満たす数であり、好ましくは、０．３５≦ｃ≦０．８５を満たす数であり、より好ましくは、０．４０≦ｃ≦０．８０を満たす数である。これは、ｃが上記範囲の下限以上であると、得られる硬化物の室温での硬さが良好であり、一方、上記範囲の上限以下であると、得られる硬化物の機械的強度が良好であるからである。また、ｄは、一般式：ＳｉＯ４／２で表されるシロキサン単位の割合を示す数であり、０≦ｄ≦０．２０、好ましくは、０≦ｂ≦０．１０を満たす数である。これは、ｄが上記範囲の上限以下であると、得られる硬化物の機械的強度が良好であるからである。また、ｅは、一般式：Ｒ２Ｏ１／２で表される単位の割合を示す数であり、０≦ｅ≦０．１０を満たす数である。これは、ｅが上記範囲の上限以下であると、得られる硬化物の室温での硬さが良好であるからである。なお、式中、ａ、ｂ、ｃ、およびｄの合計は１である。
（Ａ）成分は、通常、分子量分布を有するものであり、複数のオルガノポリシロキサンの混合物である。また、（Ａ）成分は、別々に調製されたオルガノポリシロキサンを混合したものであってもよいが、各オルガノポリシロキサンは上記式において、０≦ａ≦０．３０、０≦ｂ≦０．７０、０．３≦ｃ≦０．９、０≦ｄ≦０．２０、０≦ｅ≦０．１０を満たす数でなければならない。
（Ｂ）成分は、本組成物の粘度を調整し、得られる硬化物の硬さと機械的強度を調整するための任意成分であり、一般式：
Ｒ３ ３ＳｉＯ（Ｒ３ ２ＳｉＯ）ｍＳｉＲ３ ３
で表されるオルガノポリシロキサンである。
式中、Ｒ３は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、もしくは炭素原子数２~６のアルケニル基である。Ｒ３のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、シクロペンチル基、シクロヘキシル基が例示される。Ｒ３のアルケニル基としては、ビニル基、アリル基、ブテニル基、ペンテニル基、ヘキセニル基が例示される。なお、式中、全Ｒ３の内、フェニル基の含有量は３０~７０モル％の範囲内であり、好ましくは、４０~６０モル％の範囲内である。これは、フェニル基の含有量が上記範囲の下限以上であると、得られる硬化物の機械的強度が良好であり、一方、上記範囲の上限以下であると、得られる硬化物の硬さが良好であるからである。また、式中、Ｒ３の少なくとも１個はアルケニル基である。これは、アルケニル基を有すると、本成分が硬化反応に取り込まれるからである。
また、式中、ｍは１０~１００の範囲内の整数であり、好ましくは、１０~５０の範囲内の整数である。これは、ｍが上記範囲の下限以上であると、得られる硬化物の機械的強度が良好であり、一方、上記範囲の上限以下であると、得られる組成物の取扱作業性が良好であるからである。
本組成物において、（Ｂ）成分の含有量は、（Ａ）成分１００質量部に対して０~４０質量部の範囲内となる量であり、好ましくは、０~２０質量部の範囲内となる量である。これは、（Ｂ）成分の含有量が上記範囲の上限以下であると、得られる硬化物の硬さが良好であるからである。
（Ｃ）成分は、本組成物の架橋剤であり、一分子中に少なくとも２個のケイ素原子結合水素原子を有し、ケイ素原子結合全有機基の２０~７０モル％がフェニル基であるオルガノポリシロキサンである。（Ｃ）成分中のケイ素原子結合水素原子は一分子中に少なくとも２個であるが、これは、硬化のための架橋が十分であり、得られる硬化物の硬さが良好であるからである。また、（Ｃ）成分中のケイ素原子結合有機基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、ヘプチル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基等のアルキル基；フェニル基、トリル基、キシリル基等のアリール基；ベンジル基、フェネチル基等のアラルキル基等の脂肪族不飽和結合を有さない一価炭化水素基が例示され、好ましくは、フェニル基、または炭素原子数１~６のアルキル基である。（Ｃ）成分は、ケイ素原子結合全有機基の２０~７０モル％がフェニル基である。これは、フェニル基の含有量が上記範囲の下限以上であると、得られる硬化物の高温での機械的強度が良好であり、一方、上記範囲の上限以下であると、得られる硬化物の機械的強度が良好であるからである。
このような（Ｃ）成分としては、一般式：
（ＨＲ４ ２ＳｉＯ）２ＳｉＲ４ ２
で表されるオルガノトリシロキサン、一般式：
Ｒ５ ３ＳｉＯ（Ｒ５ ２ＳｉＯ）ｎＳｉＲ５ ３
で表される直鎖状のオルガノポリシロキサン、平均単位式：
（Ｒ５ＳｉＯ３／２）ｐ（Ｒ５ ２ＳｉＯ２／２）ｑ（Ｒ５ ３ＳｉＯ１／２）ｒ（ＳｉＯ４／２）ｓ（Ｒ６Ｏ１／２）ｔ
で表される分岐鎖状のオルガノポリシロキサンが例示される。
式中、Ｒ４は、同じかまたは異なる、フェニル基、もしくは炭素原子数１~６のアルキル基である。Ｒ４のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、シクロペンチル基、シクロヘキシル基が例示される。なお、全Ｒ４の内、フェニル基の含有量は３０~７０モル％の範囲内である。
また、式中、Ｒ５は、同じかまたは異なる、水素原子、フェニル基、もしくは炭素原子数１~６のアルキル基であり、式中、少なくとも２個のＲ５は水素原子である。Ｒ５のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、シクロペンチル基、シクロヘキシル基が例示される。なお、水素原子を除く全Ｒ５の内、フェニル基の含有量は３０~７０モル％の範囲内である。
また、式中、Ｒ６は水素原子または炭素原子数１~６のアルキル基である。Ｒ６のアルキル基としては、メチル基、エチル基、ブチル基、ペンチル基、ヘキシル基が例示される。
また、式中、ｎは５~１，０００の範囲内の整数である。
また、式中、ｐは正数であり、ｑは０又は正数であり、ｒは０又は正数であり、ｓは０又は正数であり、ｔは０又は正数であり、かつ、ｑ／ｐは０~１０の範囲内の数であり、ｒ／ｐは０~５の範囲内の数であり、ｓ／（ｐ＋ｑ＋ｒ＋ｓ）は０~０．３の範囲内の数であり、ｔ／（ｐ＋ｑ＋ｒ＋ｓ）は０~０．４の範囲内の数である。
このような（Ｃ）成分において、そのすべてが、一般式：
（ＨＲ４ ２ＳｉＯ）２ＳｉＲ４ ２
で表されるオルガノトリシロキサンであることが好ましいが、反応性熱可塑体を経ずに硬化物を形成する場合には、（Ｃ）成分の少なくとも５０質量％は上記のオルガノトリシロキサンであることが好ましい。さらに、得られる硬化物の硬さを調整するために適時その他のオルガノシロキサンを加えてもよい。
本組成物において、（Ｃ）成分の含有量は、（Ａ）成分および（Ｂ）成分中のアルケニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．５~２モルの範囲内となる量であり、好ましくは、０．５~１．５モルの範囲内となる量である。これは、（Ｃ）成分の含有量が上記範囲内であると、得られる硬化物の硬さが良好であるからである。
（Ｄ）成分は、（Ａ）成分および（Ｂ）成分中のアルケニル基と（Ｃ）成分中のケイ素原子結合水素原子とのヒドロシリル化反応を促進するためのヒドロシリル化反応用触媒である。（Ｄ）成分としては、白金系触媒、ロジウム系触媒、パラジウム系触媒が例示され、本組成物の硬化を著しく促進できることから白金系触媒が好ましい。この白金系触媒としては、白金微粉末、塩化白金酸、塩化白金酸のアルコール溶液、白金−アルケニルシロキサン錯体、白金−オレフィン錯体、白金−カルボニル錯体が例示され、特に、白金−アルケニルシロキサン錯体であることが好ましい。このアルケニルシロキサンとしては、１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン、１，３，５，７−テトラメチル−１，３，５，７−テトラビニルシクロテトラシロキサン、これらのアルケニルシロキサンのメチル基の一部をエチル基、フェニル基等で置換したアルケニルシロキサン、これらのアルケニルシロキサンのビニル基をアリル基、ヘキセニル基等で置換したアルケニルシロキサンが例示される。特に、この白金−アルケニルシロキサン錯体の安定性が良好であることから、１，３−ジビニル−１，１，３，３−トテラメチルジシロキサンが好ましい。また、この白金−アルケニルシロキサン錯体の安定性を向上させることができることから、この錯体に１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン、１，３−ジアリル−１，１，３，３−テトラメチルジシロキサン、１，３−ジビニル−１，３−ジメチル−１，３−ジフェニルジシロキサン、１，３−ジビニル−１，１，３，３−テトラフェニルジシロキサン、１，３，５，７−テトラメチル−１，３，５，７−テトラビニルシクロテトラシロキサン等のアルケニルシロキサンやジメチルシロキサンオリゴマー等のオルガノシロキサンオリゴマーを添加することが好ましく、特に、アルケニルシロキサンを添加することが好ましい。
本組成物において、（Ｄ）成分の含有量は、（Ａ）成分および（Ｂ）成分中のアルケニル基と（Ｃ）成分中のケイ素原子結合水素原子とのヒドロシリル化反応を促進するのに十分な量であれば特に限定されないが、好ましくは、本組成物に対して、本成分中の金属原子が質量単位で０．０１~５００ｐｐｍの範囲内となる量であることが好ましく、さらには、０．０１~１００ｐｐｍの範囲内となる量であることが好ましく、特には、０．０１~５０ｐｐｍの範囲内となる量であることが好ましい。これは、（Ｄ）成分の含有量が上記範囲の下限以上であると、得られる組成物の硬化が良好であり、一方、上記範囲の上限以下であると、得られる硬化物に着色を生じ難いからである。
（Ｅ）成分は、本組成物およびその硬化物を白色に着色し、光反射率を高めるための酸化チタン以外の白色顔料である。（Ｅ）成分としては、酸化亜鉛、チタン酸バリウム、アルミナ、酸化ジルコン、酸化マグネシウム、三酸化アンチモン等の金属酸化物；硫酸バリウム、硫化亜鉛、窒化ホウ素、窒化アルミニウム等の無機化合物が例示され、３５０~４００ｎｍの紫外線領域の光反射率と硬化物の金属に対する接着性の観点から、酸化亜鉛、チタン酸バリウム、および硫酸バリウムのいずれか、またはこれらの混合物であることが好ましく、特に、薄い厚みでの反射率（隠蔽性）が優れることから、チタン酸バリウムであることが好ましい。
（Ｅ）成分の平均粒径や形状は限定されないが、平均粒径は０．０５~１０．０μｍの範囲内であることが好ましく、特に、０．１~５．０μｍの範囲内であることが好ましい。白色顔料は、樹脂や無機充填剤との相溶性、分散性を高めるため、シランカップリング剤、シリカ、アルミナ等で表面処理したものを使用することができる。
本組成物において、（Ｅ）成分の含有量は、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して５０質量部以上であり、好ましくは、６０質量部以上である。これは、（Ｅ）成分の含有量が上記下限以上であると、得られる硬化物の光反射率が良好であるからである。
（Ｆ）成分は、本組成物の粘度の上昇による作業性の低下を改善し、硬化物の線膨張率を小さくし、寸法安定性を改善するための球状シリカ、非球状シリカもしくはガラスファイバーである。（Ｆ）成分の球状シリカとしては、乾式シリカ、湿式シリカ、溶融シリカ、爆燃シリカが例示されるが、本組成物への充填性が良好であることから、溶融シリカが好ましい。（Ｆ）成分の非球状シリカとしては、石英粉末、ガラスビーズが例示され、好ましくは、石英粉末である。（Ｆ）成分のガラスファイバーとしては、チョップドガラスファイバー、ミルドガラスファイバーが例示され、好ましくは、ミルドガラスファイバーである。
（Ｆ）成分の球状シリカの粒径は限定されないが、平均粒径は０．１~５０μｍの範囲内であることが好ましく、特に、０．５~２０μｍの範囲内であることが好ましい。（Ｆ）成分の非球状シリカの平均粒径は限定されないが、０．１~２０μｍの範囲内であることが好ましく、特に、０．５~１０μｍの範囲内であることが好ましい。（Ｆ）成分のガラスファイバーの形状は限定されないが、ファイバー径が１~５０μｍの範囲内であることが好ましく、特に、５~２０μｍの範囲内であることが好ましく、また、そのファイバー長が５~５００μｍの範囲内であることが好ましく、特に、１０~３００μｍの範囲内であることが好ましい。
本組成物において、（Ｆ）成分の含有量は、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して１００質量部以上であり、好ましくは、１２０質量部以上である。（Ｆ）成分の含有量が上記下限以上であると、得られる硬化物の線膨張率が低く、寸法安定性が良好であるからである。
本組成物において、（Ｅ）成分および（Ｆ）成分の合計の含有量は、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して４００質量部以下であり、好ましくは、３５０質量部以下である。（Ｅ）成分および（Ｆ）成分の合計の含有量が上記上限以下であると、得られる組成物の粘度が良好であるからである。
本組成物には、硬化途上で接触している基材への接着性を高めるための接着促進剤として、（Ｇ）平均単位式：
（Ｒ７ ３ＳｉＯ１／２）ｆ（Ｒ７ ２ＳｉＯ２／２）ｇ（Ｒ７ＳｉＯ３／２）ｈ（ＳｉＯ４／２）ｉ（Ｒ８Ｏ１／２）ｊ
で表されるオルガノポリシロキサンを含有することが好ましい。
式中、Ｒ７は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、炭素原子数２~６のアルケニル基もしくはエポキシ基含有有機基である。Ｒ７のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘプチル基、シクロペンチル基、シクロヘプチル基が例示される。Ｒ７のアルケニル基としては、ビニル基、アリル基、ブテニル基、ペンテニル基、ヘキセニル基が例示される。Ｒ７のエポキシ基含有有機基としては、３−グリシドキシプロピル基、４−グリシドキシブチル基、２−（３，４−エポキシシクロヘキシル）エチル基、３−（３，４−エポキシシクロヘキシル）プロピル基が例示される。なお、式中、全Ｒ７の内、フェニル基の含有量は１５~６０モル％の範囲内であり、好ましくは、２０~５０モル％の範囲内である。これは、フェニル基の含有量が上記範囲の下限以上であると、得られる硬化物の接着性と反射率が良好であるからであり、上記範囲の上限以下であると、得られる硬化物の接着性と耐熱性が良好であるからである。式中、全Ｒ７の内、アルケニル基の含有量は３~３０モル％の範囲内であり、好ましくは、５~２０モル％の範囲内である。これは、アルケニル基の含有量が上記範囲内であると、得られる硬化物の接着性が良好であるからである。また、全Ｒ７の内、エポキシ基含有有機基の含有量は５~３０モル％の範囲内であり、好ましくは、１０~２０モル％の範囲内である。これは、エポキシ基含有有機基の含有量が上記範囲の下限以上であると、得られる硬化物の接着性が良好であり、一方、上記範囲の上限以下であると、良好な耐熱性が得られるからである。
また、式中、Ｒ８は水素原子または炭素原子数１~６のアルキル基である。Ｒ６のアルキル基としては、メチル基、エチル基、ブチル基、ペンチル基、ヘキシル基が例示される。
また、式中、ｆは、一般式：Ｒ７ ３ＳｉＯ１／２で表されるシロキサン単位の割合を示す数であり、０≦ｆ≦０．５、好ましくは、０≦ｆ≦０．４を満たす数である。これは、ｆが上記範囲の上限以下であると、得られる硬化物の接着性が良好であるからである。また、式中、ｇは、一般式：Ｒ７ ２ＳｉＯ２／２で表されるシロキサン単位の割合を示す数であり、０≦ｇ≦０．９、好ましくは、０≦ｇ≦０．８を満たす数である。これは、ｇが上記範囲の上限以下であると、得られる硬化物の接着性が良好であるからである。また、ｈは、一般式：Ｒ７ＳｉＯ３／２で表されるシロキサン単位の割合を示す数であり、０≦ｈ≦０．７、好ましくは、０≦ｈ≦０．６を満たす数である。これは、ｈが上記範囲の上限以下であると、得られる硬化物の接着性が良好であるからである。また、ｉは、一般式：ＳｉＯ４／２で表されるシロキサン単位の割合を示す数であり、０≦ｉ≦０．３、好ましくは、０≦ｉ≦０．２を満たす数である。これは、ｉが上記範囲の上限以下であると、得られる硬化物の接着性が良好であるからである。また、ｊは、一般式：Ｒ６Ｏ１／２で表される単位の割合を示す数であり、０≦ｊ≦０．０２を満たす数である。これは、ｊが上記範囲の上限以下であると、本組成物の可使時間ならびに保存安定性が良好であるからである。なお、式中、ｆ、ｇ、ｈ、およびｉの合計は１である。
本組成物において、（Ｇ）成分の含有量は、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して０．５~１０．０質量部の範囲内となる量であることが好ましく、特に、１．０~８．０質量部の範囲内となる量であることが好ましい。これは、（Ｇ）成分の含有量が上記範囲の上限以下であると、得られる硬化物の耐熱性が良好であり、一方、上記範囲の下限以上であると、得られる硬化物の接着性が良好であるからである。
本組成物には、本組成物の硬化性を損なわずに、常温での可使時間を延長する目的、および本組成物の硬化物に対する光半導体装置用の封止材の接着性を高める目的で、第２の架橋剤である（Ｈ）一分子中に２個以上のケイ素原子結合水素原子を有し、ケイ素原子結合全有機基に対するフェニル基の含有量が２０モル％未満であるオルガノポリシロキサンを含有することが好ましい。
（Ｈ）成分中のケイ素原子結合水素原子は一分子中に２個以上であるが、これは、硬化のための架橋が十分であり、得られる硬化物の硬さが良好であるからである。また、（Ｈ）成分中のケイ素原子結合有機基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、ヘプチル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基等のアルキル基；フェニル基、トリル基、キシリル基等のアリール基；ベンジル基、フェネチル基等のアラルキル基等の脂肪族不飽和結合を有さない一価炭化水素基が例示され、好ましくは、フェニル基、または炭素原子数１~６のアルキル基である。（Ｈ）成分中のケイ素原子結合全有機基に対するフェニル基の含有量は２０モル％未満であり、好ましくは、１０モル％以下である。また、（Ｈ）成分中のケイ素原子結合全有機基の９０モル％以上がメチル基であることが好ましい。これは、フェニル基の含有量が上記上限未満であり、メチル基の含有量が上記範囲の下限以上であると、得られる硬化物の各種基材への接着性が良好であり、また硬化物に対する光半導体装置用の封止材の接着性が良好であるからである。
このような（Ｈ）成分としては、式：
（ＭｅＨＳｉＯ）ｋ
（式中、Ｍｅはメチル基を表わし、ｋは４~８の整数である）
で表されるオルガノポリシロキサン、一般式：
Ｍｅ３ＳｉＯ（ＭｅＨＳｉＯ）ｘＳｉＭｅ３
Ｍｅ３ＳｉＯ（ＭｅＨＳｉＯ）ｙ（Ｍｅ２ＳｉＯ）ｚＳｉＭｅ３
（式中、Ｍｅはメチル基を表わし、ｘは５以上の整数、ｙ、ｚはそれぞれ５以上の整数であるが、ｙはｚと同じかそれ以上である）
で表されるオルガノポリシロキサンが例示される。
本組成物において、（Ｈ）成分の含有量は、（Ａ）成分および（Ｂ）成分中のアルケニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．００１~０．２０モルの範囲内となる量であり、好ましくは、０．００２~０．１０モルの範囲内となる量である。これは、（Ｈ）成分の含有量が上記範囲内であると、組成物の常温での可使時間が延長され、得られる硬化物に対する光半導体装置用の封止材の接着性が良好となり、さらに本組成物をヒドロシリル化反応して得られる反応性熱可塑体の高温での流動性が良好となるからである。
本組成物を用いてトランスファー成形、射出成型、または圧縮成形により光半導体装置を作製する際、金型からの硬化物の離型性を高めるため、本組成物に、離型剤として、炭素原子数が１０以上のカルボン酸またはその金属塩を含有してもよい。このようなカルボン酸としては、ミリスチン酸、パルミチン酸、ステアリン酸、オレイン酸、リノール酸、リノレン酸が例示されるが、特に、オレイン酸、リノール酸、リノレン酸等の分子中に少なくとも１個の炭素−炭素二重結合を有するものが好ましい。具体的には、オレイン酸、リノール酸、リノレン酸、オレイン酸亜鉛、オレイン酸アルミニウム、オレイン酸カルシウムが例示される。酸化による経年劣化が少ないという観点から、一分子中に少なくとも１個の炭素−炭素二重結合を有する、オレイン酸およびその金属塩が好ましい。
上記のカルボン酸またはその金属塩の含有量は、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して、０．０１~８質量部の範囲内であることが好ましく、特に、０．０５~５質量部の範囲内であることが好ましい。これは、カルボン酸またはその金属塩の含有量が上記範囲の上限以下であると、得られる硬化物が柔らかくなりすぎないからであり、一方、上記範囲の下限以上であると、得られる硬化物の離型性が良好であるからである。
また、本組成物には、カルボン酸またはその金属塩以外の離型剤を含有してもよい。このような離型剤としては、カルナバワックス、メチルシリコーンオイル、フルオロシリコーンオイルが例示される。
本組成物は、上記（Ａ）成分~（Ｆ）成分から少なくともなるが、その他任意の成分として、１−エチニル−１−シクロヘキサノール、２−メチル−３−ブチン−２−オール、３，５−ジメチル−１−ヘキシン−３−オール、２−フェニル−３−ブチン−２−オール等のアルキンアルコール；３−メチル−３−ペンテン−１−イン、３，５−ジメチル−３−ヘキセン−１−イン等のエンイン化合物；１，３，５，７−テトラメチル−１，３，５，７−テトラビニルシクロテトラシロキサン、１，３，５，７−テトラメチル−１，３，５，７−テトラヘキセニルシクロテトラシロキサン、ベンゾトリアゾール等の反応抑制剤を含有してもよい。この反応抑制剤の含有量は限定されないが、本組成物に対して、質量単位で１~５，０００ｐｐｍの範囲内であることが好ましい。
本組成物には、上記（Ｇ）成分以外の接着促進剤を含有してもよい。このような接着促進剤としては、トリアルコキシシロキシ基（例えば、トリメトキシシロキシ基、トリエトキシシロキシ基）もしくはトリアルコキシシリルアルキル基（例えば、トリメトキシシリルエチル基、トリエトキシシリルエチル基）と、ヒドロシリル基もしくはアルケニル基（例えば、ビニル基、アリル基）を有するオルガノシラン、またはケイ素原子数４~２０程度の直鎖状構造、分岐状構造又は環状構造のオルガノシロキサンオリゴマー；トリアルコキシシロキシ基もしくはトリアルコキシシリルアルキル基とメタクリロキシアルキル基（例えば、３−メタクリロキシプロピル基）を有するオルガノシラン、またはケイ素原子数４~２０程度の直鎖状構造、分岐状構造又は環状構造のオルガノシロキサンオリゴマー；トリアルコキシシロキシ基もしくはトリアルコキシシリルアルキル基とエポキシ基結合アルキル基（例えば、３−グリシドキシプロピル基、４−グリシドキシブチル基、２−（３，４−エポキシシクロヘキシル）エチル基、３−（３，４−エポキシシクロヘキシル）プロピル基）を有するオルガノシランまたはケイ素原子数４~２０程度の直鎖状構造、分岐状構造又は環状構造のオルガノシロキサンオリゴマー；アミノアルキルトリアルコキシシランとエポキシ基結合アルキルトリアルコキシシランの反応物、エポキシ基含有エチルポリシリケートが挙げられ、具体的には、ビニルトリメトキシシラン、アリルトリメトキシシラン、アリルトリエトキシシラン、ハイドロジェントリエトキシシラン、３−グリシドキシプロピルトリメトキシシラン、３−グリシドキシプロピルトリエトキシシラン、２−（３，４−エポキシシクロヘキシル）エチルトリメトキシシラン、３−メタクリロキシプロピルトリメトキシシラン、３−メタクリロキシプロピルトリエトキシシラン、３−グリシドキシプロピルトリエトキシシランと３−アミノプロピルトリエトキシシランの反応物、シラノール基封鎖メチルビニルシロキサンオリゴマーと３−グリシドキシプロピルトリメトキシシランの縮合反応物、シラノール基封鎖メチルビニルシロキサンオリゴマーと３−メタクリロキシプロピルトリエトキシシランの縮合反応物、トリス（３−トリメトキシシリルプロピル）イソシアヌレート、酸無水物が挙げられる。
さらに、本組成物を反応性熱可塑体を経ずに硬化物を形成する場合には、本組成物の取扱作業性を向上させ、得られる硬化物の硬さを調整するため、ケイ素原子結合全有機基の３０~６０モル％が炭素原子数２~６のアルケニル基である、ケイ素原子数が１０以下のオルガノポリシロキサンを含有してもよい。このオルガノポリシロキサン中のアルケニル基としては、ビニル基、アリル基、ブテニル基、ペンテニル基、ヘキセニル基が例示される。また、このオルガノポリシロキサン中のアルケニル基以外のケイ素原子結合有機基は特に限定されないが、メチル基、フェニル基が例示され、好ましくは、メチル基である。また、ケイ素原子結合全有機基の３０~６０モル％が炭素原子数２~６のアルケニル基である。これは、アルケニル基の含有量が上記範囲の下限以上であると、得られる硬化物の硬さが良好であり、一方、上記範囲の上限以下であると、得られる硬化物の機械的強度が良好であるからである。さらに、ケイ素原子数が１０以下であるが、これは、ケイ素原子数が１０以下であると、組成物の粘度が良好であるからである。
このようなオルガノポリシロキサンとしては、１，３，５，７−テトラメチル−１，３，５，７−テトラビニルシクロテトラシロキサン、テトラキス（ジメチルビニルシロキシ）シラン、メチルトリス（ジメチルビニルシロキシ）シラン、およびフェニルトリス（ジメチルビニルシロキシ）シランが例示される。
このオルガノポリシロキサンの含有量は、（Ａ）成分１００質量部に対して、０~５０質量部の範囲内となる量であることが好ましく、特に、本組成物を液状の反応性シリコーン組成物として使用するときは、５~４０質量部の範囲内となる量であることが好ましい。これは、このオルガノポリシロキサンの含有量が上記範囲の下限以上であると、組成物の粘度が良好であり、一方、上記範囲の上限以下であると、得られる硬化物の機械的強度が良好であるからである。
さらに、本組成物には、本発明の目的を損なわない限り、その他任意の成分として、球状シリカ、非球状シリカ、ガラスファイバー以外の無機充填剤、ポリメタクリレート樹脂やシリコーン樹脂等の有機樹脂微粉末；ベンゾトリアゾール、カルボキシベンゾトリアゾールなどの腐食防止剤、耐熱剤、難燃性付与剤、溶剤等を含有してもよい。
本組成物の２５℃における粘度は特に限定されないが、反応性熱可塑体を得る場合には、好ましくは、１０，０００Ｐａ・ｓ以下であり、特に好ましくは、１０~５，０００Ｐａ・ｓの範囲内である。これは、粘度が上記範囲の下限以上であると、所望の形状の反応性熱可塑体を形成することが容易であり、一方、上記範囲の上限以下であると、得られる組成物の取扱作業性が良好であるからである。
また、本組成物を液状の反応性シリコーン組成物として使用する場合、その２５℃における粘度は、好ましくは５~２００Ｐａ・ｓの範囲内であり、さらに好ましくは５~１２０Ｐａ・ｓの範囲内であり、特に好ましくは１０~８０Ｐａ・ｓの範囲内である。これは、粘度が上記範囲の下限以上であると、成形時にバリの発生が抑制され、一方、上記範囲の上限以下であると、得られる組成物の取扱作業性が良好であるからである。
次に、本発明の反応性熱可塑体について詳細に説明する。
本発明の反応性熱可塑体は、上記の反応性シリコーン硬化物のヒドロシリル化反応の転化率が７０％~９５％となるまで反応させてなるものである。ヒドロシリル化の転化率とは、ヒドロシリル化反応する全官能基量のうち、実際に反応が起きたものの割合をパーセントで表わしたものであり、その確認法は特に限定されないが、例えば、示差走査熱量計（ＤＳＣ）を用いて、反応性シリコーン組成物と得られた反応性熱可塑体の反応発熱量を測定し、その差から転化率を簡便に算出することができる。反応は室温もしくは加熱により反応が進行するが、反応性熱可塑体を効率よく得るためには加熱することが好ましい。この加熱温度としては、５０~１５０℃の範囲内であることが好ましく、８０~１３０℃の範囲内であることがさらに好ましい。
本発明の反応性熱可塑体は、２５℃で固体もしくは粘度が１，０００，０００Ｐａ・ｓ以上であり、１００℃で粘度が１００，０００Ｐａ・ｓ以下の液状であるものが好ましい。
また、本発明の反応性熱可塑体は、ＪＩＳ Ｋ ７２１５—１９８６「プラスチックのデュロメータ硬さ試験方法」に規定のタイプＤデュロメータ硬さが２５℃で３０以上であることが好ましい。
このような本発明の反応性熱可塑体は、１００℃以上に加熱すると一旦流動化し、その後、ヒドロシリル化反応が進行し、硬化物を与える。
次に、本発明の硬化物について詳細に説明する。
本発明の硬化物は、上記の反応性熱可塑体を加熱して、残りのヒドロシリル化反応を行って得られるもの、または、反応性可塑体を経ずに、上記液状の反応性シリコーン組成物を加熱してヒドロシリル化反応を行って得られるものであり、３００℃で固体もしくは粘度が１，０００，０００Ｐａ・ｓ以上である。硬化物の硬さは特に限定されないが、ＪＩＳ Ｋ ７２１５—１９８６「プラスチックのデュロメータ硬さ試験方法」に規定のタイプＤデュロメータ硬さが６０以上であることが好ましく、さらには、６５以上であることが好ましく、特には、７０以上であることが好ましい。これは、硬度が上記下限以上であると、硬化物の寸法安定性が向上し、硬化物の変形が起こり難くなるためである。
また、本硬化物の反射率は特に限定されないが、ＪＩＳ Ｋ ７３７５：２００８「プラスチック−全光線透過率及び全光線反射率の求め方」に規定の方法により測定した全光線反射率が７５％以上であることが好ましく、特には、８０％以上であることが好ましい。
また、本硬化物の線膨張率は特に限定されないが、ＪＩＳ Ｋ ７１９７—１９９１「プラスチックの熱機械分析による線膨張率の試験方法」に規定の方法により測定した線膨張率が２５~２００℃の温度範囲での平均値として、２００ｐｐｍ／℃以下であることが好ましく、特に、１５０ｐｐｍ／℃以下であることが好ましい。
また、本発明の硬化物は、上記反応性熱可塑体または上記反応性シリコーン組成物を１００℃以上に加熱した金属金型中で硬化してなることが好ましい。光半導体装置の反射材として本硬化物を形成する場合の硬化方法としては、例えば、圧縮成形、トランスファー成形、射出成形が挙げられる。
次に、本発明の光半導体装置について詳細に説明する。
本発明の光半導体装置は、光反射材が上記硬化物により形成されていること特徴とする。このような光半導体装置としては、発光ダイオード（ＬＥＤ）が例示される。この光半導体装置において、光反射材は、光半導体装置の枠材（パッケージング材）としても機能している。
本半導体装置の一例である表面実装型ＬＥＤの断面図を図１に示した。図１で示されるＬＥＤは、光半導体素子１がリードフレーム２上にダイボンド材によりダイボンディングされ、この光半導体素子１とリードフレーム２、３とがボンディングワイヤ４、４’によりワイヤボンディングされている。この光半導体素子１の上部を除く周囲には、上記の硬化物からなる光反射材５を有し、この光反射材５の内側の光半導体素子１は封止材６により封止されている。
図１で示される表面実装型ＬＥＤを製造する方法としては、（１）本発明の反応性熱可塑体をトランスファー成形または圧縮成形により、リードフレーム２、３と一体化した光反射材５を形成する工程、（２）リードフレーム２上にダイボンド材により光半導体素子１をダイボンディングする工程、（３）光半導体素子１とリードフレーム２、３をボンディングワイヤ４、４’によりワイヤボンディングする工程、（４）光半導体素子１を封止材６に封止する工程からなる方法が例示される。 First, the reactive silicone composition of the present invention will be described in detail.
Component (A) is the main component of the present composition, and average unit formula:
(R 1 3 SiO 1/2 ) a (R 1 2 SiO 2/2 ) b (R 1 SiO 3/2 ) c (SiO 4/2 ) d (R 2 O 1/2 ) e
It is organopolysiloxane represented by these.
In the formula, R 1 is the same or different and is a phenyl group, an alkyl group having 1 to 6 carbon atoms, or an alkenyl group having 2 to 6 carbon atoms. Examples of the alkyl group for R 1 include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a cyclopentyl group, and a cyclohexyl group. Examples of the alkenyl group for R 1 include a vinyl group, an allyl group, a butenyl group, a pentenyl group, and a hexenyl group. The content of the phenyl groups is in the range of 30 to 80 mol% of all R 1, it the case of forming the reactive thermoplastic material is in the range of 60 to 75 mol% of all R 1 preferable. This is because when the phenyl group content is at least the lower limit of the above range, the resulting reactive thermoplastic has good room temperature hardness and high temperature flow characteristics, and the resulting cured product has mechanical strength. On the other hand, the hardness at high temperature of the obtained cured product is good when it is not more than the upper limit of the above range. In the formula, the content of the alkenyl group in the total R 1 is in the range of 10 to 20 mol%. This is because when the content of the alkenyl group is not less than the lower limit of the above range, the resulting cured product has good hardness at room temperature. This is because the mechanical strength is good.
In the formula, R 2 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms. Examples of the alkyl group for R 2 include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, and a hexyl group.
Further, in the formula, a is a number indicating the ratio of siloxane units represented by the general formula: R 1 3 SiO 1/2 , and 0 ≦ a ≦ 0.30, preferably 0 ≦ a ≦ 0.25. It is a number that satisfies This is because the hardness at room temperature of the obtained cured product is good when a is not more than the upper limit of the above range. In the formula, b is a number indicating the ratio of the siloxane unit represented by the general formula: R 1 2 SiO 2/2 and is a number satisfying 0 ≦ b ≦ 0.70, and is a reactive thermoplastic. Is preferably a number satisfying 0.10 ≦ b ≦ 0.70, and more preferably satisfying 0.15 ≦ b ≦ 0.60. This is obtained when b is equal to or higher than the lower limit of the above range, and the resulting thermoplastic thermoplastic resin has good room temperature hardness and high temperature flow characteristics, while being equal to or lower than the upper limit of the above range. This is because the hardness of the cured product at room temperature is good. C is a number indicating the ratio of siloxane units represented by the general formula: R 1 SiO 3/2 , and is a number satisfying 0.3 ≦ c ≦ 0.9, preferably 0.35 ≦ The number satisfies c ≦ 0.85, and more preferably the number satisfies 0.40 ≦ c ≦ 0.80. When c is equal to or higher than the lower limit of the above range, the cured product obtained has good hardness at room temperature. On the other hand, when c is equal to or lower than the upper limit of the above range, the obtained cured product has good mechanical strength. Because. D is a number indicating the ratio of the siloxane unit represented by the general formula: SiO 4/2 , and is a number satisfying 0 ≦ d ≦ 0.20, preferably 0 ≦ b ≦ 0.10. This is because the mechanical strength of the obtained cured product is good when d is not more than the upper limit of the above range. E is a number indicating the proportion of units represented by the general formula: R 2 O 1/2 and is a number satisfying 0 ≦ e ≦ 0.10. This is because the hardness of the obtained cured product at room temperature is good when e is not more than the upper limit of the above range. In the formula, the sum of a, b, c, and d is 1.
The component (A) usually has a molecular weight distribution and is a mixture of a plurality of organopolysiloxanes. In addition, the component (A) may be a mixture of separately prepared organopolysiloxanes, but each organopolysiloxane is 0 ≦ a ≦ 0.30, 0 ≦ b ≦ 0. 70, 0.3 ≦ c ≦ 0.9, 0 ≦ d ≦ 0.20, and 0 ≦ e ≦ 0.10.
Component (B) is an optional component for adjusting the viscosity of the present composition and adjusting the hardness and mechanical strength of the resulting cured product.
R 3 3 SiO (R 3 2 SiO) m SiR 3 3
It is organopolysiloxane represented by these.
In the formula, R 3 is the same or different, a phenyl group, an alkyl group having 1 to 6 carbon atoms, or an alkenyl group having 2 to 6 carbon atoms. Examples of the alkyl group for R 3 include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a cyclopentyl group, and a cyclohexyl group. Examples of the alkenyl group for R 3 include a vinyl group, an allyl group, a butenyl group, a pentenyl group, and a hexenyl group. In the formula, the content of phenyl group in the total R 3 is in the range of 30 to 70 mol%, preferably in the range of 40 to 60 mol%. If the phenyl group content is not less than the lower limit of the above range, the resulting cured product has good mechanical strength, whereas if it is not more than the upper limit of the above range, the hardness of the obtained cured product is It is because it is good. In the formula, at least one R 3 is an alkenyl group. This is because this component is taken into the curing reaction when it has an alkenyl group.
In the formula, m is an integer in the range of 10 to 100, preferably an integer in the range of 10 to 50. When m is not less than the lower limit of the above range, the resulting cured product has good mechanical strength, and when it is not more than the upper limit of the above range, the resulting composition has good handling workability. Because.
In the present composition, the content of the component (B) is an amount in the range of 0 to 40 parts by mass, preferably in the range of 0 to 20 parts by mass with respect to 100 parts by mass of the component (A). Is the amount. This is because the hardness of the obtained cured product is good when the content of the component (B) is not more than the upper limit of the above range.
Component (C) is a crosslinking agent of the present composition, and has at least two silicon atom-bonded hydrogen atoms in one molecule, and 20 to 70 mol% of all silicon atom-bonded organic groups are phenyl groups. Polysiloxane. (C) The number of silicon-bonded hydrogen atoms in the component is at least two in one molecule, because this is sufficient for crosslinking and the resulting cured product has good hardness. . In addition, as the silicon atom-bonded organic group in the component (C), alkyl groups such as a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, a cyclopentyl group, a cyclohexyl group, and a cycloheptyl group Aryl groups such as phenyl group, tolyl group and xylyl group; monovalent hydrocarbon groups having no aliphatic unsaturated bond such as aralkyl groups such as benzyl group and phenethyl group, and the like, preferably phenyl group, or An alkyl group having 1 to 6 carbon atoms. In the component (C), 20 to 70 mol% of the silicon atom-bonded all organic groups are phenyl groups. If the phenyl group content is not less than the lower limit of the above range, the resulting cured product has good mechanical strength at high temperatures, and if it is not more than the upper limit of the above range, This is because the mechanical strength is good.
As such component (C), the general formula:
(HR 4 2 SiO) 2 SiR 4 2
Organotrisiloxane represented by the general formula:
R 5 3 SiO (R 5 2 SiO) n SiR 5 3
A linear organopolysiloxane represented by the formula:
(R 5 SiO 3/2 ) p (R 5 2 SiO 2/2 ) q (R 5 3 SiO 1/2 ) r (SiO 4/2 ) s (R 6 O 1/2 ) t
The branched-chain organopolysiloxane represented by these is illustrated.
In the formula, R 4 is the same or different, a phenyl group, or an alkyl group having 1 to 6 carbon atoms. Examples of the alkyl group for R 4 include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a cyclopentyl group, and a cyclohexyl group. Note that the content of phenyl groups in the total R 4 is in the range of 30 to 70 mol%.
In the formula, R 5 is the same or different, a hydrogen atom, a phenyl group, or an alkyl group having 1 to 6 carbon atoms. In the formula, at least two R 5 are hydrogen atoms. Examples of the alkyl group for R 5 include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a cyclopentyl group, and a cyclohexyl group. Of all R 5 excluding hydrogen atoms, the phenyl group content is in the range of 30 to 70 mol%.
In the formula, R 6 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms. Examples of the alkyl group for R 6 include a methyl group, an ethyl group, a butyl group, a pentyl group, and a hexyl group.
In the formula, n is an integer in the range of 5 to 1,000.
In the formula, p is a positive number, q is 0 or a positive number, r is 0 or a positive number, s is 0 or a positive number, t is 0 or a positive number, and q / p is a number in the range of 0 to 10, r / p is a number in the range of 0 to 5, s / (p + q + r + s) is a number in the range of 0 to 0.3, t / (P + q + r + s) is a number in the range of 0 to 0.4.
In such component (C), all of them have the general formula:
(HR 4 2 SiO) 2 SiR 4 2
In the case where a cured product is formed without passing through a reactive thermoplastic, at least 50% by mass of the component (C) is the above organotrisiloxane. Is preferred. Furthermore, other organosiloxanes may be added at appropriate times to adjust the hardness of the resulting cured product.
In this composition, the content of component (C) is such that the silicon-bonded hydrogen atoms in this component are 0.5 to 2 with respect to a total of 1 mol of alkenyl groups in components (A) and (B). The amount is in the range of moles, preferably the amount in the range of 0.5 to 1.5 moles. This is because the hardness of the hardened | cured material obtained that content of (C) component exists in the said range is favorable.
The component (D) is a hydrosilylation reaction catalyst for promoting the hydrosilylation reaction between the alkenyl group in the components (A) and (B) and the silicon atom-bonded hydrogen atom in the component (C). Examples of the component (D) include platinum-based catalysts, rhodium-based catalysts, and palladium-based catalysts, and platinum-based catalysts are preferred because they can significantly accelerate the curing of the composition. Examples of the platinum-based catalyst include platinum fine powder, chloroplatinic acid, an alcohol solution of chloroplatinic acid, a platinum-alkenylsiloxane complex, a platinum-olefin complex, and a platinum-carbonyl complex, and in particular, a platinum-alkenylsiloxane complex. It is preferable. Examples of the alkenyl siloxane include 1,3-divinyl-1,1,3,3-tetramethyldisiloxane, 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane, Examples thereof include alkenyl siloxanes in which part of the methyl groups of these alkenyl siloxanes are substituted with ethyl groups, phenyl groups, and the like, and alkenyl siloxanes in which the vinyl groups of these alkenyl siloxanes are substituted with allyl groups, hexenyl groups, and the like. In particular, since the stability of this platinum-alkenylsiloxane complex is good, 1,3-divinyl-1,1,3,3-toteramethyldisiloxane is preferable. Further, since the stability of this platinum-alkenylsiloxane complex can be improved, 1,3-divinyl-1,1,3,3-tetramethyldisiloxane, 1,3-diallyl-1,1 can be added to this complex. , 3,3-tetramethyldisiloxane, 1,3-divinyl-1,3-dimethyl-1,3-diphenyldisiloxane, 1,3-divinyl-1,1,3,3-tetraphenyldisiloxane, , 3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane is preferably added, and alkenylsiloxane such as dimethylsiloxane oligomer is preferably added. It is preferable.
In the present composition, the content of component (D) is sufficient to promote the hydrosilylation reaction between the alkenyl group in component (A) and component (B) and the silicon-bonded hydrogen atom in component (C). Although it is not particularly limited as long as it is an amount, it is preferably an amount such that the metal atom in the component is in the range of 0.01 to 500 ppm by mass unit with respect to the composition, The amount is preferably in the range of 0.01 to 100 ppm, and particularly preferably in the range of 0.01 to 50 ppm. When the content of the component (D) is not less than the lower limit of the above range, the resulting composition is cured well. On the other hand, when the content is not more than the upper limit of the above range, the resulting cured product is colored. It is difficult.
Component (E) is a white pigment other than titanium oxide for coloring the present composition and its cured product white and increasing the light reflectance. Examples of the component (E) include metal oxides such as zinc oxide, barium titanate, alumina, zircon oxide, magnesium oxide, and antimony trioxide; inorganic compounds such as barium sulfate, zinc sulfide, boron nitride, and aluminum nitride; From the viewpoint of the light reflectivity in the ultraviolet region of 350 to 400 nm and the adhesion of the cured product to the metal, it is preferably any one of zinc oxide, barium titanate, and barium sulfate, or a mixture thereof, and particularly a thin thickness. Barium titanate is preferable because of its excellent reflectance (concealment).
The average particle size and shape of the component (E) are not limited, but the average particle size is preferably in the range of 0.05 to 10.0 μm, and particularly in the range of 0.1 to 5.0 μm. Is preferred. As the white pigment, in order to improve the compatibility and dispersibility with the resin and the inorganic filler, those which have been surface-treated with a silane coupling agent, silica, alumina or the like can be used.
In the present composition, the content of the component (E) is 50 parts by mass or more, preferably 60 parts by mass or more with respect to 100 parts by mass in total of the components (A) to (D). This is because the light reflectance of the obtained cured product is good when the content of the component (E) is not less than the above lower limit.
Component (F) is spherical silica, non-spherical silica or glass fiber for improving the workability reduction due to the increase in viscosity of the composition, reducing the linear expansion coefficient of the cured product, and improving the dimensional stability. is there. Examples of the spherical silica as the component (F) include dry silica, wet silica, fused silica, and deflagration silica, but fused silica is preferable because the filling property of the present composition is good. Examples of the non-spherical silica of component (F) include quartz powder and glass beads, and quartz powder is preferable. (F) As a glass fiber of a component, a chopped glass fiber and a milled glass fiber are illustrated, Preferably it is a milled glass fiber.
The particle size of the spherical silica as component (F) is not limited, but the average particle size is preferably in the range of 0.1 to 50 μm, and more preferably in the range of 0.5 to 20 μm. The average particle size of the non-spherical silica of the component (F) is not limited, but is preferably in the range of 0.1 to 20 μm, and particularly preferably in the range of 0.5 to 10 μm. The shape of the component (F) glass fiber is not limited, but the fiber diameter is preferably in the range of 1 to 50 μm, particularly preferably in the range of 5 to 20 μm, and the fiber length is 5 It is preferably in the range of ~ 500 μm, particularly preferably in the range of 10 to 300 μm.
In the present composition, the content of the component (F) is 100 parts by mass or more, preferably 120 parts by mass or more, with respect to 100 parts by mass in total of the components (A) to (D). It is because the linear expansion coefficient of the obtained cured product is low and the dimensional stability is good when the content of the component (F) is not less than the above lower limit.
In the present composition, the total content of the component (E) and the component (F) is 400 parts by mass or less, preferably 350 parts by mass with respect to a total of 100 parts by mass of the components (A) to (D). Or less. This is because the viscosity of the resulting composition is good when the total content of the component (E) and the component (F) is not more than the above upper limit.
In the present composition, as an adhesion promoter for enhancing the adhesion to a substrate that is in the process of curing, (G) average unit formula:
(R 7 3 SiO 1/2 ) f (R 7 2 SiO 2/2 ) g (R 7 SiO 3/2 ) h (SiO 4/2 ) i (R 8 O 1/2 ) j
It is preferable to contain the organopolysiloxane represented by these.
In the formula, R 7 is the same or different, a phenyl group, an alkyl group having 1 to 6 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, or an organic group containing an epoxy group. Examples of the alkyl group for R 7 include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a heptyl group, a cyclopentyl group, and a cycloheptyl group. Examples of the alkenyl group for R 7 include a vinyl group, an allyl group, a butenyl group, a pentenyl group, and a hexenyl group. Examples of the epoxy group-containing organic group for R 7 include 3-glycidoxypropyl group, 4-glycidoxybutyl group, 2- (3,4-epoxycyclohexyl) ethyl group, and 3- (3,4-epoxycyclohexyl). A propyl group is exemplified. In the formula, among all R 7 , the phenyl group content is in the range of 15 to 60 mol%, and preferably in the range of 20 to 50 mol%. This is because the adhesiveness and reflectance of the resulting cured product are good when the phenyl group content is at least the lower limit of the above range, and when the content of the phenyl group is below the upper limit of the above range, This is because the adhesiveness and heat resistance are good. In the formula, the content of the alkenyl group in the total R 7 is in the range of 3 to 30 mol%, preferably in the range of 5 to 20 mol%. This is because when the content of the alkenyl group is within the above range, the obtained cured product has good adhesiveness. In addition, among all R 7, the content of the epoxy group-containing organic group is in the range of 5 to 30 mol%, preferably in the range of 10 to 20 mol%. When the content of the epoxy group-containing organic group is at least the lower limit of the above range, the resulting cured product has good adhesiveness. On the other hand, when the content is below the upper limit of the above range, good heat resistance is obtained. Because it is.
In the formula, R 8 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms. Examples of the alkyl group for R 6 include a methyl group, an ethyl group, a butyl group, a pentyl group, and a hexyl group.
In the formula, f is a number indicating the ratio of siloxane units represented by the general formula: R 7 3 SiO 1/2 , and 0 ≦ f ≦ 0.5, preferably 0 ≦ f ≦ 0.4. It is a number that satisfies This is because the adhesiveness of the obtained hardened | cured material is favorable as f is below the upper limit of the said range. In the formula, g is a number indicating the ratio of siloxane units represented by the general formula: R 7 2 SiO 2/2 , and 0 ≦ g ≦ 0.9, preferably 0 ≦ g ≦ 0.8. It is a number that satisfies This is because the adhesiveness of the obtained cured product is good when g is not more than the upper limit of the above range. H is a number indicating the ratio of the siloxane unit represented by the general formula: R 7 SiO 3/2 , and is a number satisfying 0 ≦ h ≦ 0.7, preferably 0 ≦ h ≦ 0.6. is there. This is because the adhesiveness of the hardened | cured material obtained is favorable as h is below the upper limit of the said range. Further, i is a number indicating the ratio of the siloxane unit represented by the general formula: SiO 4/2 , and is a number satisfying 0 ≦ i ≦ 0.3, preferably 0 ≦ i ≦ 0.2. This is because the adhesiveness of the obtained cured product is good when i is not more than the upper limit of the above range. J is a number indicating the proportion of units represented by the general formula: R 6 O 1/2 and is a number satisfying 0 ≦ j ≦ 0.02. This is because the pot life and storage stability of the composition are good when j is not more than the upper limit of the above range. In the formula, the sum of f, g, h, and i is 1.
In the present composition, the content of the component (G) is an amount that is in the range of 0.5 to 10.0 parts by mass with respect to 100 parts by mass in total of the components (A) to (D). In particular, the amount is preferably in the range of 1.0 to 8.0 parts by mass. When the content of the component (G) is not more than the upper limit of the above range, the resulting cured product has good heat resistance, and on the other hand, if it is not less than the lower limit of the above range, the resulting cured product has adhesiveness. This is because is good.
The present composition has the purpose of extending the pot life at room temperature without impairing the curability of the composition, and the purpose of increasing the adhesiveness of the sealing material for optical semiconductor devices to the cured product of the composition The second crosslinking agent (H) is an organopolysiloxane having 2 or more silicon-bonded hydrogen atoms in one molecule and a phenyl group content of less than 20 mol% with respect to all silicon-bonded organic groups. It is preferable to contain siloxane.
(H) The number of silicon-bonded hydrogen atoms in the component is two or more in one molecule, because this is sufficient for crosslinking for curing and the resulting cured product has good hardness. . In addition, as the silicon atom-bonded organic group in the component (H), alkyl groups such as a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, a cyclopentyl group, a cyclohexyl group, and a cycloheptyl group Aryl groups such as phenyl group, tolyl group and xylyl group; monovalent hydrocarbon groups having no aliphatic unsaturated bond such as aralkyl groups such as benzyl group and phenethyl group, and the like, preferably phenyl group, or An alkyl group having 1 to 6 carbon atoms. The content of the phenyl group relative to the silicon-bonded all organic groups in the component (H) is less than 20 mol%, preferably 10 mol% or less. Moreover, it is preferable that 90 mol% or more of the silicon atom bond total organic group in (H) component is a methyl group. When the phenyl group content is less than the above upper limit and the methyl group content is not less than the lower limit of the above range, the resulting cured product has good adhesion to various substrates, and the cured product This is because the adhesiveness of the sealing material for the optical semiconductor device is good.
As such (H) component, the formula:
(MeHSiO) k
(In the formula, Me represents a methyl group, and k is an integer of 4 to 8)
Organopolysiloxane represented by the general formula:
Me 3 SiO (MeHSiO) x SiMe 3
Me 3 SiO (MeHSiO) y (Me 2 SiO) z SiMe 3
(In the formula, Me represents a methyl group, x is an integer of 5 or more, y and z are each an integer of 5 or more, and y is the same as or more than z)
The organopolysiloxane represented by these is illustrated.
In this composition, the content of the component (H) is such that the silicon-bonded hydrogen atoms in this component are 0.001 to 0 with respect to 1 mol in total of the alkenyl groups in the components (A) and (B). The amount is in the range of 20 moles, preferably in the range of 0.002 to 0.10 moles. This is because when the content of the component (H) is within the above range, the pot life at room temperature of the composition is extended, and the adhesiveness of the sealing material for optical semiconductor devices to the obtained cured product becomes good. Furthermore, this is because the flowability of the reactive thermoplastic obtained by hydrosilylation reaction of the composition at a high temperature is improved.
When producing an optical semiconductor device by transfer molding, injection molding, or compression molding using this composition, in order to improve the mold releasability of the cured product from the mold, the composition contains carbon atoms as a mold release agent. A carboxylic acid having a number of 10 or more or a metal salt thereof may be contained. Examples of such carboxylic acids include myristic acid, palmitic acid, stearic acid, oleic acid, linoleic acid, and linolenic acid. In particular, at least one oleic acid, linoleic acid, linolenic acid, and the like are present in the molecule. Those having a carbon-carbon double bond are preferred. Specific examples include oleic acid, linoleic acid, linolenic acid, zinc oleate, aluminum oleate, and calcium oleate. Oleic acid and a metal salt thereof having at least one carbon-carbon double bond in one molecule are preferable from the viewpoint of little deterioration over time due to oxidation.
The content of the carboxylic acid or a metal salt thereof is preferably in the range of 0.01 to 8 parts by mass with respect to a total of 100 parts by mass of the components (A) to (D), particularly 0 It is preferably in the range of 05 to 5 parts by mass. This is because if the content of the carboxylic acid or its metal salt is not more than the upper limit of the above range, the resulting cured product will not be too soft, whereas if it is not less than the lower limit of the above range, the resulting cured product will be obtained. This is because the releasability of is good.
Moreover, you may contain mold release agents other than carboxylic acid or its metal salt in this composition. Examples of such release agents include carnauba wax, methyl silicone oil, and fluorosilicone oil.
This composition is composed of at least the components (A) to (F), but as other optional components, 1-ethynyl-1-cyclohexanol, 2-methyl-3-butyn-2-ol, 3, 5 Alkyne alcohols such as dimethyl-1-hexyn-3-ol and 2-phenyl-3-butyn-2-ol; 3-methyl-3-penten-1-yne, 3,5-dimethyl-3-hexene-1 An enyne compound such as yne; 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane, 1,3,5,7-tetramethyl-1,3,5,7 -Reaction inhibitors such as tetrahexenylcyclotetrasiloxane and benzotriazole may be contained. The content of the reaction inhibitor is not limited, but is preferably in the range of 1 to 5,000 ppm by mass with respect to the present composition.
The composition may contain an adhesion promoter other than the component (G). Such adhesion promoters include trialkoxysiloxy groups (for example, trimethoxysiloxy group, triethoxysiloxy group) or trialkoxysilylalkyl groups (for example, trimethoxysilylethyl group, triethoxysilylethyl group), hydrosilyl An organosilane having an alkyl group or an alkenyl group (for example, a vinyl group, an allyl group), or a linear, branched or cyclic organosiloxane oligomer having about 4 to 20 silicon atoms; trialkoxysiloxy group or trialkoxy Organosilane having a silylalkyl group and a methacryloxyalkyl group (for example, 3-methacryloxypropyl group), or an organosiloxane oligomer having a linear structure, a branched structure or a cyclic structure having about 4 to 20 silicon atoms; Siloxy group or trialkoxysilylalkyl group and epoxy group-bonded alkyl group (for example, 3-glycidoxypropyl group, 4-glycidoxybutyl group, 2- (3,4-epoxycyclohexyl) ethyl group, 3- (3 , 4-epoxycyclohexyl) propyl group) or an organosiloxane oligomer having a linear structure, branched structure or cyclic structure having about 4 to 20 silicon atoms; aminoalkyltrialkoxysilane and epoxy group-bonded alkyltrialkoxy Examples include silane reactants and epoxy group-containing ethyl polysilicates. Specific examples include vinyltrimethoxysilane, allyltrimethoxysilane, allyltriethoxysilane, hydrogentriethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-grid Doxypropyltriethoxysilane, 2- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-methacryloxypropyltriethoxysilane, 3-glycidoxypropyltriethoxysilane Reaction product of 3-aminopropyltriethoxysilane, condensation reaction product of silanol-blocked methylvinylsiloxane oligomer and 3-glycidoxypropyltrimethoxysilane, silanol-blocked methylvinylsiloxane oligomer and 3-methacryloxypropyltriethoxysilane Examples include condensation reaction products, tris (3-trimethoxysilylpropyl) isocyanurate, and acid anhydrides.
Furthermore, when forming the cured product without passing through the reactive thermoplastic, the composition is improved by improving the handling workability of the composition and adjusting the hardness of the resulting cured product. An organopolysiloxane having 10 or less silicon atoms in which 30 to 60 mol% of all organic groups are alkenyl groups having 2 to 6 carbon atoms may be contained. Examples of the alkenyl group in the organopolysiloxane include a vinyl group, an allyl group, a butenyl group, a pentenyl group, and a hexenyl group. Further, the silicon atom-bonded organic group other than the alkenyl group in the organopolysiloxane is not particularly limited, but examples thereof include a methyl group and a phenyl group, and a methyl group is preferable. Further, 30 to 60 mol% of all silicon atom-bonded organic groups are alkenyl groups having 2 to 6 carbon atoms. When the content of the alkenyl group is not less than the lower limit of the above range, the resulting cured product has good hardness. On the other hand, when the content of the alkenyl group is not more than the upper limit of the above range, the resulting cured product has a mechanical strength. It is because it is good. Furthermore, although the number of silicon atoms is 10 or less, this is because the viscosity of the composition is good when the number of silicon atoms is 10 or less.
Such organopolysiloxanes include 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane, tetrakis (dimethylvinylsiloxy) silane, methyltris (dimethylvinylsiloxy) silane, And phenyltris (dimethylvinylsiloxy) silane.
The content of the organopolysiloxane is preferably an amount within the range of 0 to 50 parts by mass with respect to 100 parts by mass of the component (A). In particular, the present composition is a liquid reactive silicone composition. When it is used, it is preferable that the amount be in the range of 5 to 40 parts by mass. When the content of the organopolysiloxane is at least the lower limit of the above range, the viscosity of the composition is good. On the other hand, when the content is below the upper limit of the above range, the resulting cured product has good mechanical strength. Because.
Furthermore, the present composition includes, as optional components, spherical silica, non-spherical silica, inorganic fillers other than glass fibers, fine organic resin powders such as polymethacrylate resins and silicone resins, as long as the object of the present invention is not impaired. A corrosion inhibitor such as benzotriazole or carboxybenzotriazole, a heat-resistant agent, a flame retardant, and a solvent.
The viscosity at 25 ° C. of the present composition is not particularly limited, but when obtaining a reactive thermoplastic, it is preferably 10,000 Pa · s or less, particularly preferably in the range of 10 to 5,000 Pa · s. Is within. When the viscosity is equal to or higher than the lower limit of the above range, it is easy to form a reactive thermoplastic having a desired shape. On the other hand, when the viscosity is equal to or lower than the upper limit of the above range, the resulting composition is handled. This is because the property is good.
Further, when the present composition is used as a liquid reactive silicone composition, the viscosity at 25 ° C. is preferably in the range of 5 to 200 Pa · s, more preferably in the range of 5 to 120 Pa · s. And particularly preferably within the range of 10 to 80 Pa · s. This is because, when the viscosity is at least the lower limit of the above range, the occurrence of burrs is suppressed during molding, and when the viscosity is below the upper limit of the above range, the workability of the resulting composition is good.
Next, the reactive thermoplastic of the present invention will be described in detail.
The reactive thermoplastic of the present invention is obtained by reacting until the conversion rate of the hydrosilylation reaction of the above reactive silicone cured product becomes 70% to 95%. The conversion rate of hydrosilylation is the percentage of the total functional group that undergoes hydrosilylation reaction, in which the reaction actually takes place, and its confirmation method is not particularly limited. For example, differential scanning calorimetry Using a meter (DSC), the reaction calorific value of the reactive silicone composition and the obtained reactive thermoplastic can be measured, and the conversion rate can be easily calculated from the difference. The reaction proceeds at room temperature or by heating, but heating is preferable in order to obtain a reactive thermoplastic efficiently. The heating temperature is preferably in the range of 50 to 150 ° C, and more preferably in the range of 80 to 130 ° C.
The reactive thermoplastic of the present invention is preferably a solid at 25 ° C. or a liquid having a viscosity of 1,000,000 Pa · s or more at 100 ° C. and a liquid having a viscosity of 100,000 Pa · s or less at 100 ° C.
The reactive thermoplastic of the present invention preferably has a type D durometer hardness of 30 or more at 25 ° C. as defined in JIS K 7215-1986 “Plastic Durometer Hardness Test Method”.
Such a reactive thermoplastic of the present invention fluidizes once when heated to 100 ° C. or higher, and then undergoes a hydrosilylation reaction to give a cured product.
Next, the cured product of the present invention will be described in detail.
The cured product of the present invention is obtained by heating the reactive thermoplastic and performing the remaining hydrosilylation reaction, or the liquid reactive silicone composition without passing through the reactive plastic. Is obtained by heating and hydrosilylation reaction, and at 300 ° C., the solid or viscosity is 1,000,000 Pa · s or more. The hardness of the cured product is not particularly limited, but the type D durometer hardness specified in JIS K 7215-1986 “Plastic Durometer Hardness Test Method” is preferably 60 or more, and more preferably 65 or more. It is preferable that it is 70 or more especially. This is because when the hardness is equal to or higher than the above lower limit, the dimensional stability of the cured product is improved, and the cured product is hardly deformed.
The reflectivity of the cured product is not particularly limited, but the total light reflectivity measured by the method specified in JIS K 7375: 2008 “Plastics—Determination of total light transmittance and total light reflectivity” is 75% or more. In particular, it is preferably 80% or more.
Further, the linear expansion coefficient of the cured product is not particularly limited, but the linear expansion coefficient measured by the method specified in JIS K 7197-1991 “Test method for linear expansion coefficient by thermomechanical analysis of plastic” is 25 to 200 ° C. The average value in the temperature range is preferably 200 ppm / ° C. or less, and particularly preferably 150 ppm / ° C. or less.
Moreover, it is preferable that the hardened | cured material of this invention hardens | cures the said reactive thermoplastic body or the said reactive silicone composition in the metal metal mold | die heated at 100 degreeC or more. Examples of the curing method for forming the main cured product as the reflecting material of the optical semiconductor device include compression molding, transfer molding, and injection molding.
Next, the optical semiconductor device of the present invention will be described in detail.
The optical semiconductor device of the present invention is characterized in that the light reflecting material is formed of the cured product. As such an optical semiconductor device, a light emitting diode (LED) is exemplified. In this optical semiconductor device, the light reflecting material also functions as a frame material (packaging material) of the optical semiconductor device.
A cross-sectional view of a surface-mounted LED, which is an example of the semiconductor device, is shown in FIG. In the LED shown in FIG. 1, anoptical semiconductor element 1 is die-bonded on a lead frame 2 by a die bonding material, and the optical semiconductor element 1 and the lead frames 2 and 3 are wire-bonded by bonding wires 4 and 4 ′. . A light reflecting material 5 made of the above-described cured product is provided around the optical semiconductor element 1 except for the upper portion thereof, and the optical semiconductor element 1 inside the light reflecting material 5 is sealed with a sealing material 6. .
As a method of manufacturing the surface mount type LED shown in FIG. 1, (1) thelight reflecting material 5 integrated with the lead frames 2 and 3 is formed by transfer molding or compression molding of the reactive thermoplastic of the present invention. (2) a step of die-bonding the optical semiconductor element 1 on the lead frame 2 with a die bonding material; (3) a step of wire-bonding the optical semiconductor element 1 and the lead frames 2 and 3 with bonding wires 4 and 4 ′; (4) A method comprising a step of sealing the optical semiconductor element 1 with the sealing material 6 is exemplified.
（Ａ）成分は、本組成物の主成分であり、平均単位式：
（Ｒ１ ３ＳｉＯ１／２）ａ（Ｒ１ ２ＳｉＯ２／２）ｂ（Ｒ１ＳｉＯ３／２）ｃ（ＳｉＯ４／２）ｄ（Ｒ２Ｏ１／２）ｅ
で表されるオルガノポリシロキサンである。
式中、Ｒ１は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、もしくは炭素原子数２~６のアルケニル基である。Ｒ１のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、シクロペンチル基、シクロヘキシル基が例示される。Ｒ１のアルケニル基としては、ビニル基、アリル基、ブテニル基、ペンテニル基、ヘキセニル基が例示される。なお、フェニル基の含有量は全Ｒ１の３０~８０モル％の範囲内であり、反応性熱可塑体を形成する場合は、全Ｒ１の６０~７５モル％の範囲内であることが好ましい。これは、フェニル基の含有量が上記範囲の下限以上であると、得られる反応性熱可塑体の室温での硬さと高温での流動特性が良好であり、また得られる硬化物の機械的強度が良好であり、一方、上記範囲の上限以下であると、得られる硬化物の高温での硬さが良好であるからである。また、式中、全Ｒ１の内、アルケニル基の含有量は１０~２０モル％の範囲内である。これは、アルケニル基の含有量が上記範囲の下限以上であると、得られる硬化物の室温での硬さが良好であり、一方、上記範囲の上限以下であると、得られる硬化物の機械的強度が良好であるからである。
また、式中、Ｒ２は水素原子または炭素原子数１~６のアルキル基である。Ｒ２のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基が例示される。
さらに、式中、ａは、一般式：Ｒ１ ３ＳｉＯ１／２で表されるシロキサン単位の割合を示す数であり、０≦ａ≦０．３０、好ましくは、０≦ａ≦０．２５を満たす数である。これは、ａが上記範囲の上限以下であると、得られる硬化物の室温での硬さが良好であるからである。また、式中、ｂは、一般式：Ｒ１ ２ＳｉＯ２／２で表されるシロキサン単位の割合を示す数であり、０≦ｂ≦０．７０を満たす数であり、反応性熱可塑体を形成する場合には、０．１０≦ｂ≦０．７０を満たす数であることが好ましく、さらには、０．１５≦ｂ≦０．６０を満たす数であることが好ましい。これは、ｂが上記範囲の下限以上であると、得られる反応性熱可塑体の室温での硬さと高温での流動特性が良好であり、一方、上記範囲の上限以下であると、得られる硬化物の室温での硬さが良好であるからである。また、ｃは、一般式：Ｒ１ＳｉＯ３／２で表されるシロキサン単位の割合を示す数であり、０．３≦ｃ≦０．９を満たす数であり、好ましくは、０．３５≦ｃ≦０．８５を満たす数であり、より好ましくは、０．４０≦ｃ≦０．８０を満たす数である。これは、ｃが上記範囲の下限以上であると、得られる硬化物の室温での硬さが良好であり、一方、上記範囲の上限以下であると、得られる硬化物の機械的強度が良好であるからである。また、ｄは、一般式：ＳｉＯ４／２で表されるシロキサン単位の割合を示す数であり、０≦ｄ≦０．２０、好ましくは、０≦ｂ≦０．１０を満たす数である。これは、ｄが上記範囲の上限以下であると、得られる硬化物の機械的強度が良好であるからである。また、ｅは、一般式：Ｒ２Ｏ１／２で表される単位の割合を示す数であり、０≦ｅ≦０．１０を満たす数である。これは、ｅが上記範囲の上限以下であると、得られる硬化物の室温での硬さが良好であるからである。なお、式中、ａ、ｂ、ｃ、およびｄの合計は１である。
（Ａ）成分は、通常、分子量分布を有するものであり、複数のオルガノポリシロキサンの混合物である。また、（Ａ）成分は、別々に調製されたオルガノポリシロキサンを混合したものであってもよいが、各オルガノポリシロキサンは上記式において、０≦ａ≦０．３０、０≦ｂ≦０．７０、０．３≦ｃ≦０．９、０≦ｄ≦０．２０、０≦ｅ≦０．１０を満たす数でなければならない。
（Ｂ）成分は、本組成物の粘度を調整し、得られる硬化物の硬さと機械的強度を調整するための任意成分であり、一般式：
Ｒ３ ３ＳｉＯ（Ｒ３ ２ＳｉＯ）ｍＳｉＲ３ ３
で表されるオルガノポリシロキサンである。
式中、Ｒ３は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、もしくは炭素原子数２~６のアルケニル基である。Ｒ３のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、シクロペンチル基、シクロヘキシル基が例示される。Ｒ３のアルケニル基としては、ビニル基、アリル基、ブテニル基、ペンテニル基、ヘキセニル基が例示される。なお、式中、全Ｒ３の内、フェニル基の含有量は３０~７０モル％の範囲内であり、好ましくは、４０~６０モル％の範囲内である。これは、フェニル基の含有量が上記範囲の下限以上であると、得られる硬化物の機械的強度が良好であり、一方、上記範囲の上限以下であると、得られる硬化物の硬さが良好であるからである。また、式中、Ｒ３の少なくとも１個はアルケニル基である。これは、アルケニル基を有すると、本成分が硬化反応に取り込まれるからである。
また、式中、ｍは１０~１００の範囲内の整数であり、好ましくは、１０~５０の範囲内の整数である。これは、ｍが上記範囲の下限以上であると、得られる硬化物の機械的強度が良好であり、一方、上記範囲の上限以下であると、得られる組成物の取扱作業性が良好であるからである。
本組成物において、（Ｂ）成分の含有量は、（Ａ）成分１００質量部に対して０~４０質量部の範囲内となる量であり、好ましくは、０~２０質量部の範囲内となる量である。これは、（Ｂ）成分の含有量が上記範囲の上限以下であると、得られる硬化物の硬さが良好であるからである。
（Ｃ）成分は、本組成物の架橋剤であり、一分子中に少なくとも２個のケイ素原子結合水素原子を有し、ケイ素原子結合全有機基の２０~７０モル％がフェニル基であるオルガノポリシロキサンである。（Ｃ）成分中のケイ素原子結合水素原子は一分子中に少なくとも２個であるが、これは、硬化のための架橋が十分であり、得られる硬化物の硬さが良好であるからである。また、（Ｃ）成分中のケイ素原子結合有機基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、ヘプチル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基等のアルキル基；フェニル基、トリル基、キシリル基等のアリール基；ベンジル基、フェネチル基等のアラルキル基等の脂肪族不飽和結合を有さない一価炭化水素基が例示され、好ましくは、フェニル基、または炭素原子数１~６のアルキル基である。（Ｃ）成分は、ケイ素原子結合全有機基の２０~７０モル％がフェニル基である。これは、フェニル基の含有量が上記範囲の下限以上であると、得られる硬化物の高温での機械的強度が良好であり、一方、上記範囲の上限以下であると、得られる硬化物の機械的強度が良好であるからである。
このような（Ｃ）成分としては、一般式：
（ＨＲ４ ２ＳｉＯ）２ＳｉＲ４ ２
で表されるオルガノトリシロキサン、一般式：
Ｒ５ ３ＳｉＯ（Ｒ５ ２ＳｉＯ）ｎＳｉＲ５ ３
で表される直鎖状のオルガノポリシロキサン、平均単位式：
（Ｒ５ＳｉＯ３／２）ｐ（Ｒ５ ２ＳｉＯ２／２）ｑ（Ｒ５ ３ＳｉＯ１／２）ｒ（ＳｉＯ４／２）ｓ（Ｒ６Ｏ１／２）ｔ
で表される分岐鎖状のオルガノポリシロキサンが例示される。
式中、Ｒ４は、同じかまたは異なる、フェニル基、もしくは炭素原子数１~６のアルキル基である。Ｒ４のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、シクロペンチル基、シクロヘキシル基が例示される。なお、全Ｒ４の内、フェニル基の含有量は３０~７０モル％の範囲内である。
また、式中、Ｒ５は、同じかまたは異なる、水素原子、フェニル基、もしくは炭素原子数１~６のアルキル基であり、式中、少なくとも２個のＲ５は水素原子である。Ｒ５のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、シクロペンチル基、シクロヘキシル基が例示される。なお、水素原子を除く全Ｒ５の内、フェニル基の含有量は３０~７０モル％の範囲内である。
また、式中、Ｒ６は水素原子または炭素原子数１~６のアルキル基である。Ｒ６のアルキル基としては、メチル基、エチル基、ブチル基、ペンチル基、ヘキシル基が例示される。
また、式中、ｎは５~１，０００の範囲内の整数である。
また、式中、ｐは正数であり、ｑは０又は正数であり、ｒは０又は正数であり、ｓは０又は正数であり、ｔは０又は正数であり、かつ、ｑ／ｐは０~１０の範囲内の数であり、ｒ／ｐは０~５の範囲内の数であり、ｓ／（ｐ＋ｑ＋ｒ＋ｓ）は０~０．３の範囲内の数であり、ｔ／（ｐ＋ｑ＋ｒ＋ｓ）は０~０．４の範囲内の数である。
このような（Ｃ）成分において、そのすべてが、一般式：
（ＨＲ４ ２ＳｉＯ）２ＳｉＲ４ ２
で表されるオルガノトリシロキサンであることが好ましいが、反応性熱可塑体を経ずに硬化物を形成する場合には、（Ｃ）成分の少なくとも５０質量％は上記のオルガノトリシロキサンであることが好ましい。さらに、得られる硬化物の硬さを調整するために適時その他のオルガノシロキサンを加えてもよい。
本組成物において、（Ｃ）成分の含有量は、（Ａ）成分および（Ｂ）成分中のアルケニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．５~２モルの範囲内となる量であり、好ましくは、０．５~１．５モルの範囲内となる量である。これは、（Ｃ）成分の含有量が上記範囲内であると、得られる硬化物の硬さが良好であるからである。
（Ｄ）成分は、（Ａ）成分および（Ｂ）成分中のアルケニル基と（Ｃ）成分中のケイ素原子結合水素原子とのヒドロシリル化反応を促進するためのヒドロシリル化反応用触媒である。（Ｄ）成分としては、白金系触媒、ロジウム系触媒、パラジウム系触媒が例示され、本組成物の硬化を著しく促進できることから白金系触媒が好ましい。この白金系触媒としては、白金微粉末、塩化白金酸、塩化白金酸のアルコール溶液、白金−アルケニルシロキサン錯体、白金−オレフィン錯体、白金−カルボニル錯体が例示され、特に、白金−アルケニルシロキサン錯体であることが好ましい。このアルケニルシロキサンとしては、１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン、１，３，５，７−テトラメチル−１，３，５，７−テトラビニルシクロテトラシロキサン、これらのアルケニルシロキサンのメチル基の一部をエチル基、フェニル基等で置換したアルケニルシロキサン、これらのアルケニルシロキサンのビニル基をアリル基、ヘキセニル基等で置換したアルケニルシロキサンが例示される。特に、この白金−アルケニルシロキサン錯体の安定性が良好であることから、１，３−ジビニル−１，１，３，３−トテラメチルジシロキサンが好ましい。また、この白金−アルケニルシロキサン錯体の安定性を向上させることができることから、この錯体に１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン、１，３−ジアリル−１，１，３，３−テトラメチルジシロキサン、１，３−ジビニル−１，３−ジメチル−１，３−ジフェニルジシロキサン、１，３−ジビニル−１，１，３，３−テトラフェニルジシロキサン、１，３，５，７−テトラメチル−１，３，５，７−テトラビニルシクロテトラシロキサン等のアルケニルシロキサンやジメチルシロキサンオリゴマー等のオルガノシロキサンオリゴマーを添加することが好ましく、特に、アルケニルシロキサンを添加することが好ましい。
本組成物において、（Ｄ）成分の含有量は、（Ａ）成分および（Ｂ）成分中のアルケニル基と（Ｃ）成分中のケイ素原子結合水素原子とのヒドロシリル化反応を促進するのに十分な量であれば特に限定されないが、好ましくは、本組成物に対して、本成分中の金属原子が質量単位で０．０１~５００ｐｐｍの範囲内となる量であることが好ましく、さらには、０．０１~１００ｐｐｍの範囲内となる量であることが好ましく、特には、０．０１~５０ｐｐｍの範囲内となる量であることが好ましい。これは、（Ｄ）成分の含有量が上記範囲の下限以上であると、得られる組成物の硬化が良好であり、一方、上記範囲の上限以下であると、得られる硬化物に着色を生じ難いからである。
（Ｅ）成分は、本組成物およびその硬化物を白色に着色し、光反射率を高めるための酸化チタン以外の白色顔料である。（Ｅ）成分としては、酸化亜鉛、チタン酸バリウム、アルミナ、酸化ジルコン、酸化マグネシウム、三酸化アンチモン等の金属酸化物；硫酸バリウム、硫化亜鉛、窒化ホウ素、窒化アルミニウム等の無機化合物が例示され、３５０~４００ｎｍの紫外線領域の光反射率と硬化物の金属に対する接着性の観点から、酸化亜鉛、チタン酸バリウム、および硫酸バリウムのいずれか、またはこれらの混合物であることが好ましく、特に、薄い厚みでの反射率（隠蔽性）が優れることから、チタン酸バリウムであることが好ましい。
（Ｅ）成分の平均粒径や形状は限定されないが、平均粒径は０．０５~１０．０μｍの範囲内であることが好ましく、特に、０．１~５．０μｍの範囲内であることが好ましい。白色顔料は、樹脂や無機充填剤との相溶性、分散性を高めるため、シランカップリング剤、シリカ、アルミナ等で表面処理したものを使用することができる。
本組成物において、（Ｅ）成分の含有量は、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して５０質量部以上であり、好ましくは、６０質量部以上である。これは、（Ｅ）成分の含有量が上記下限以上であると、得られる硬化物の光反射率が良好であるからである。
（Ｆ）成分は、本組成物の粘度の上昇による作業性の低下を改善し、硬化物の線膨張率を小さくし、寸法安定性を改善するための球状シリカ、非球状シリカもしくはガラスファイバーである。（Ｆ）成分の球状シリカとしては、乾式シリカ、湿式シリカ、溶融シリカ、爆燃シリカが例示されるが、本組成物への充填性が良好であることから、溶融シリカが好ましい。（Ｆ）成分の非球状シリカとしては、石英粉末、ガラスビーズが例示され、好ましくは、石英粉末である。（Ｆ）成分のガラスファイバーとしては、チョップドガラスファイバー、ミルドガラスファイバーが例示され、好ましくは、ミルドガラスファイバーである。
（Ｆ）成分の球状シリカの粒径は限定されないが、平均粒径は０．１~５０μｍの範囲内であることが好ましく、特に、０．５~２０μｍの範囲内であることが好ましい。（Ｆ）成分の非球状シリカの平均粒径は限定されないが、０．１~２０μｍの範囲内であることが好ましく、特に、０．５~１０μｍの範囲内であることが好ましい。（Ｆ）成分のガラスファイバーの形状は限定されないが、ファイバー径が１~５０μｍの範囲内であることが好ましく、特に、５~２０μｍの範囲内であることが好ましく、また、そのファイバー長が５~５００μｍの範囲内であることが好ましく、特に、１０~３００μｍの範囲内であることが好ましい。
本組成物において、（Ｆ）成分の含有量は、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して１００質量部以上であり、好ましくは、１２０質量部以上である。（Ｆ）成分の含有量が上記下限以上であると、得られる硬化物の線膨張率が低く、寸法安定性が良好であるからである。
本組成物において、（Ｅ）成分および（Ｆ）成分の合計の含有量は、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して４００質量部以下であり、好ましくは、３５０質量部以下である。（Ｅ）成分および（Ｆ）成分の合計の含有量が上記上限以下であると、得られる組成物の粘度が良好であるからである。
本組成物には、硬化途上で接触している基材への接着性を高めるための接着促進剤として、（Ｇ）平均単位式：
（Ｒ７ ３ＳｉＯ１／２）ｆ（Ｒ７ ２ＳｉＯ２／２）ｇ（Ｒ７ＳｉＯ３／２）ｈ（ＳｉＯ４／２）ｉ（Ｒ８Ｏ１／２）ｊ
で表されるオルガノポリシロキサンを含有することが好ましい。
式中、Ｒ７は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、炭素原子数２~６のアルケニル基もしくはエポキシ基含有有機基である。Ｒ７のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘプチル基、シクロペンチル基、シクロヘプチル基が例示される。Ｒ７のアルケニル基としては、ビニル基、アリル基、ブテニル基、ペンテニル基、ヘキセニル基が例示される。Ｒ７のエポキシ基含有有機基としては、３−グリシドキシプロピル基、４−グリシドキシブチル基、２−（３，４−エポキシシクロヘキシル）エチル基、３−（３，４−エポキシシクロヘキシル）プロピル基が例示される。なお、式中、全Ｒ７の内、フェニル基の含有量は１５~６０モル％の範囲内であり、好ましくは、２０~５０モル％の範囲内である。これは、フェニル基の含有量が上記範囲の下限以上であると、得られる硬化物の接着性と反射率が良好であるからであり、上記範囲の上限以下であると、得られる硬化物の接着性と耐熱性が良好であるからである。式中、全Ｒ７の内、アルケニル基の含有量は３~３０モル％の範囲内であり、好ましくは、５~２０モル％の範囲内である。これは、アルケニル基の含有量が上記範囲内であると、得られる硬化物の接着性が良好であるからである。また、全Ｒ７の内、エポキシ基含有有機基の含有量は５~３０モル％の範囲内であり、好ましくは、１０~２０モル％の範囲内である。これは、エポキシ基含有有機基の含有量が上記範囲の下限以上であると、得られる硬化物の接着性が良好であり、一方、上記範囲の上限以下であると、良好な耐熱性が得られるからである。
また、式中、Ｒ８は水素原子または炭素原子数１~６のアルキル基である。Ｒ６のアルキル基としては、メチル基、エチル基、ブチル基、ペンチル基、ヘキシル基が例示される。
また、式中、ｆは、一般式：Ｒ７ ３ＳｉＯ１／２で表されるシロキサン単位の割合を示す数であり、０≦ｆ≦０．５、好ましくは、０≦ｆ≦０．４を満たす数である。これは、ｆが上記範囲の上限以下であると、得られる硬化物の接着性が良好であるからである。また、式中、ｇは、一般式：Ｒ７ ２ＳｉＯ２／２で表されるシロキサン単位の割合を示す数であり、０≦ｇ≦０．９、好ましくは、０≦ｇ≦０．８を満たす数である。これは、ｇが上記範囲の上限以下であると、得られる硬化物の接着性が良好であるからである。また、ｈは、一般式：Ｒ７ＳｉＯ３／２で表されるシロキサン単位の割合を示す数であり、０≦ｈ≦０．７、好ましくは、０≦ｈ≦０．６を満たす数である。これは、ｈが上記範囲の上限以下であると、得られる硬化物の接着性が良好であるからである。また、ｉは、一般式：ＳｉＯ４／２で表されるシロキサン単位の割合を示す数であり、０≦ｉ≦０．３、好ましくは、０≦ｉ≦０．２を満たす数である。これは、ｉが上記範囲の上限以下であると、得られる硬化物の接着性が良好であるからである。また、ｊは、一般式：Ｒ６Ｏ１／２で表される単位の割合を示す数であり、０≦ｊ≦０．０２を満たす数である。これは、ｊが上記範囲の上限以下であると、本組成物の可使時間ならびに保存安定性が良好であるからである。なお、式中、ｆ、ｇ、ｈ、およびｉの合計は１である。
本組成物において、（Ｇ）成分の含有量は、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して０．５~１０．０質量部の範囲内となる量であることが好ましく、特に、１．０~８．０質量部の範囲内となる量であることが好ましい。これは、（Ｇ）成分の含有量が上記範囲の上限以下であると、得られる硬化物の耐熱性が良好であり、一方、上記範囲の下限以上であると、得られる硬化物の接着性が良好であるからである。
本組成物には、本組成物の硬化性を損なわずに、常温での可使時間を延長する目的、および本組成物の硬化物に対する光半導体装置用の封止材の接着性を高める目的で、第２の架橋剤である（Ｈ）一分子中に２個以上のケイ素原子結合水素原子を有し、ケイ素原子結合全有機基に対するフェニル基の含有量が２０モル％未満であるオルガノポリシロキサンを含有することが好ましい。
（Ｈ）成分中のケイ素原子結合水素原子は一分子中に２個以上であるが、これは、硬化のための架橋が十分であり、得られる硬化物の硬さが良好であるからである。また、（Ｈ）成分中のケイ素原子結合有機基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、ヘプチル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基等のアルキル基；フェニル基、トリル基、キシリル基等のアリール基；ベンジル基、フェネチル基等のアラルキル基等の脂肪族不飽和結合を有さない一価炭化水素基が例示され、好ましくは、フェニル基、または炭素原子数１~６のアルキル基である。（Ｈ）成分中のケイ素原子結合全有機基に対するフェニル基の含有量は２０モル％未満であり、好ましくは、１０モル％以下である。また、（Ｈ）成分中のケイ素原子結合全有機基の９０モル％以上がメチル基であることが好ましい。これは、フェニル基の含有量が上記上限未満であり、メチル基の含有量が上記範囲の下限以上であると、得られる硬化物の各種基材への接着性が良好であり、また硬化物に対する光半導体装置用の封止材の接着性が良好であるからである。
このような（Ｈ）成分としては、式：
（ＭｅＨＳｉＯ）ｋ
（式中、Ｍｅはメチル基を表わし、ｋは４~８の整数である）
で表されるオルガノポリシロキサン、一般式：
Ｍｅ３ＳｉＯ（ＭｅＨＳｉＯ）ｘＳｉＭｅ３
Ｍｅ３ＳｉＯ（ＭｅＨＳｉＯ）ｙ（Ｍｅ２ＳｉＯ）ｚＳｉＭｅ３
（式中、Ｍｅはメチル基を表わし、ｘは５以上の整数、ｙ、ｚはそれぞれ５以上の整数であるが、ｙはｚと同じかそれ以上である）
で表されるオルガノポリシロキサンが例示される。
本組成物において、（Ｈ）成分の含有量は、（Ａ）成分および（Ｂ）成分中のアルケニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．００１~０．２０モルの範囲内となる量であり、好ましくは、０．００２~０．１０モルの範囲内となる量である。これは、（Ｈ）成分の含有量が上記範囲内であると、組成物の常温での可使時間が延長され、得られる硬化物に対する光半導体装置用の封止材の接着性が良好となり、さらに本組成物をヒドロシリル化反応して得られる反応性熱可塑体の高温での流動性が良好となるからである。
本組成物を用いてトランスファー成形、射出成型、または圧縮成形により光半導体装置を作製する際、金型からの硬化物の離型性を高めるため、本組成物に、離型剤として、炭素原子数が１０以上のカルボン酸またはその金属塩を含有してもよい。このようなカルボン酸としては、ミリスチン酸、パルミチン酸、ステアリン酸、オレイン酸、リノール酸、リノレン酸が例示されるが、特に、オレイン酸、リノール酸、リノレン酸等の分子中に少なくとも１個の炭素−炭素二重結合を有するものが好ましい。具体的には、オレイン酸、リノール酸、リノレン酸、オレイン酸亜鉛、オレイン酸アルミニウム、オレイン酸カルシウムが例示される。酸化による経年劣化が少ないという観点から、一分子中に少なくとも１個の炭素−炭素二重結合を有する、オレイン酸およびその金属塩が好ましい。
上記のカルボン酸またはその金属塩の含有量は、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して、０．０１~８質量部の範囲内であることが好ましく、特に、０．０５~５質量部の範囲内であることが好ましい。これは、カルボン酸またはその金属塩の含有量が上記範囲の上限以下であると、得られる硬化物が柔らかくなりすぎないからであり、一方、上記範囲の下限以上であると、得られる硬化物の離型性が良好であるからである。
また、本組成物には、カルボン酸またはその金属塩以外の離型剤を含有してもよい。このような離型剤としては、カルナバワックス、メチルシリコーンオイル、フルオロシリコーンオイルが例示される。
本組成物は、上記（Ａ）成分~（Ｆ）成分から少なくともなるが、その他任意の成分として、１−エチニル−１−シクロヘキサノール、２−メチル−３−ブチン−２−オール、３，５−ジメチル−１−ヘキシン−３−オール、２−フェニル−３−ブチン−２−オール等のアルキンアルコール；３−メチル−３−ペンテン−１−イン、３，５−ジメチル−３−ヘキセン−１−イン等のエンイン化合物；１，３，５，７−テトラメチル−１，３，５，７−テトラビニルシクロテトラシロキサン、１，３，５，７−テトラメチル−１，３，５，７−テトラヘキセニルシクロテトラシロキサン、ベンゾトリアゾール等の反応抑制剤を含有してもよい。この反応抑制剤の含有量は限定されないが、本組成物に対して、質量単位で１~５，０００ｐｐｍの範囲内であることが好ましい。
本組成物には、上記（Ｇ）成分以外の接着促進剤を含有してもよい。このような接着促進剤としては、トリアルコキシシロキシ基（例えば、トリメトキシシロキシ基、トリエトキシシロキシ基）もしくはトリアルコキシシリルアルキル基（例えば、トリメトキシシリルエチル基、トリエトキシシリルエチル基）と、ヒドロシリル基もしくはアルケニル基（例えば、ビニル基、アリル基）を有するオルガノシラン、またはケイ素原子数４~２０程度の直鎖状構造、分岐状構造又は環状構造のオルガノシロキサンオリゴマー；トリアルコキシシロキシ基もしくはトリアルコキシシリルアルキル基とメタクリロキシアルキル基（例えば、３−メタクリロキシプロピル基）を有するオルガノシラン、またはケイ素原子数４~２０程度の直鎖状構造、分岐状構造又は環状構造のオルガノシロキサンオリゴマー；トリアルコキシシロキシ基もしくはトリアルコキシシリルアルキル基とエポキシ基結合アルキル基（例えば、３−グリシドキシプロピル基、４−グリシドキシブチル基、２−（３，４−エポキシシクロヘキシル）エチル基、３−（３，４−エポキシシクロヘキシル）プロピル基）を有するオルガノシランまたはケイ素原子数４~２０程度の直鎖状構造、分岐状構造又は環状構造のオルガノシロキサンオリゴマー；アミノアルキルトリアルコキシシランとエポキシ基結合アルキルトリアルコキシシランの反応物、エポキシ基含有エチルポリシリケートが挙げられ、具体的には、ビニルトリメトキシシラン、アリルトリメトキシシラン、アリルトリエトキシシラン、ハイドロジェントリエトキシシラン、３−グリシドキシプロピルトリメトキシシラン、３−グリシドキシプロピルトリエトキシシラン、２−（３，４−エポキシシクロヘキシル）エチルトリメトキシシラン、３−メタクリロキシプロピルトリメトキシシラン、３−メタクリロキシプロピルトリエトキシシラン、３−グリシドキシプロピルトリエトキシシランと３−アミノプロピルトリエトキシシランの反応物、シラノール基封鎖メチルビニルシロキサンオリゴマーと３−グリシドキシプロピルトリメトキシシランの縮合反応物、シラノール基封鎖メチルビニルシロキサンオリゴマーと３−メタクリロキシプロピルトリエトキシシランの縮合反応物、トリス（３−トリメトキシシリルプロピル）イソシアヌレート、酸無水物が挙げられる。
さらに、本組成物を反応性熱可塑体を経ずに硬化物を形成する場合には、本組成物の取扱作業性を向上させ、得られる硬化物の硬さを調整するため、ケイ素原子結合全有機基の３０~６０モル％が炭素原子数２~６のアルケニル基である、ケイ素原子数が１０以下のオルガノポリシロキサンを含有してもよい。このオルガノポリシロキサン中のアルケニル基としては、ビニル基、アリル基、ブテニル基、ペンテニル基、ヘキセニル基が例示される。また、このオルガノポリシロキサン中のアルケニル基以外のケイ素原子結合有機基は特に限定されないが、メチル基、フェニル基が例示され、好ましくは、メチル基である。また、ケイ素原子結合全有機基の３０~６０モル％が炭素原子数２~６のアルケニル基である。これは、アルケニル基の含有量が上記範囲の下限以上であると、得られる硬化物の硬さが良好であり、一方、上記範囲の上限以下であると、得られる硬化物の機械的強度が良好であるからである。さらに、ケイ素原子数が１０以下であるが、これは、ケイ素原子数が１０以下であると、組成物の粘度が良好であるからである。
このようなオルガノポリシロキサンとしては、１，３，５，７−テトラメチル−１，３，５，７−テトラビニルシクロテトラシロキサン、テトラキス（ジメチルビニルシロキシ）シラン、メチルトリス（ジメチルビニルシロキシ）シラン、およびフェニルトリス（ジメチルビニルシロキシ）シランが例示される。
このオルガノポリシロキサンの含有量は、（Ａ）成分１００質量部に対して、０~５０質量部の範囲内となる量であることが好ましく、特に、本組成物を液状の反応性シリコーン組成物として使用するときは、５~４０質量部の範囲内となる量であることが好ましい。これは、このオルガノポリシロキサンの含有量が上記範囲の下限以上であると、組成物の粘度が良好であり、一方、上記範囲の上限以下であると、得られる硬化物の機械的強度が良好であるからである。
さらに、本組成物には、本発明の目的を損なわない限り、その他任意の成分として、球状シリカ、非球状シリカ、ガラスファイバー以外の無機充填剤、ポリメタクリレート樹脂やシリコーン樹脂等の有機樹脂微粉末；ベンゾトリアゾール、カルボキシベンゾトリアゾールなどの腐食防止剤、耐熱剤、難燃性付与剤、溶剤等を含有してもよい。
本組成物の２５℃における粘度は特に限定されないが、反応性熱可塑体を得る場合には、好ましくは、１０，０００Ｐａ・ｓ以下であり、特に好ましくは、１０~５，０００Ｐａ・ｓの範囲内である。これは、粘度が上記範囲の下限以上であると、所望の形状の反応性熱可塑体を形成することが容易であり、一方、上記範囲の上限以下であると、得られる組成物の取扱作業性が良好であるからである。
また、本組成物を液状の反応性シリコーン組成物として使用する場合、その２５℃における粘度は、好ましくは５~２００Ｐａ・ｓの範囲内であり、さらに好ましくは５~１２０Ｐａ・ｓの範囲内であり、特に好ましくは１０~８０Ｐａ・ｓの範囲内である。これは、粘度が上記範囲の下限以上であると、成形時にバリの発生が抑制され、一方、上記範囲の上限以下であると、得られる組成物の取扱作業性が良好であるからである。
次に、本発明の反応性熱可塑体について詳細に説明する。
本発明の反応性熱可塑体は、上記の反応性シリコーン硬化物のヒドロシリル化反応の転化率が７０％~９５％となるまで反応させてなるものである。ヒドロシリル化の転化率とは、ヒドロシリル化反応する全官能基量のうち、実際に反応が起きたものの割合をパーセントで表わしたものであり、その確認法は特に限定されないが、例えば、示差走査熱量計（ＤＳＣ）を用いて、反応性シリコーン組成物と得られた反応性熱可塑体の反応発熱量を測定し、その差から転化率を簡便に算出することができる。反応は室温もしくは加熱により反応が進行するが、反応性熱可塑体を効率よく得るためには加熱することが好ましい。この加熱温度としては、５０~１５０℃の範囲内であることが好ましく、８０~１３０℃の範囲内であることがさらに好ましい。
本発明の反応性熱可塑体は、２５℃で固体もしくは粘度が１，０００，０００Ｐａ・ｓ以上であり、１００℃で粘度が１００，０００Ｐａ・ｓ以下の液状であるものが好ましい。
また、本発明の反応性熱可塑体は、ＪＩＳ Ｋ ７２１５—１９８６「プラスチックのデュロメータ硬さ試験方法」に規定のタイプＤデュロメータ硬さが２５℃で３０以上であることが好ましい。
このような本発明の反応性熱可塑体は、１００℃以上に加熱すると一旦流動化し、その後、ヒドロシリル化反応が進行し、硬化物を与える。
次に、本発明の硬化物について詳細に説明する。
本発明の硬化物は、上記の反応性熱可塑体を加熱して、残りのヒドロシリル化反応を行って得られるもの、または、反応性可塑体を経ずに、上記液状の反応性シリコーン組成物を加熱してヒドロシリル化反応を行って得られるものであり、３００℃で固体もしくは粘度が１，０００，０００Ｐａ・ｓ以上である。硬化物の硬さは特に限定されないが、ＪＩＳ Ｋ ７２１５—１９８６「プラスチックのデュロメータ硬さ試験方法」に規定のタイプＤデュロメータ硬さが６０以上であることが好ましく、さらには、６５以上であることが好ましく、特には、７０以上であることが好ましい。これは、硬度が上記下限以上であると、硬化物の寸法安定性が向上し、硬化物の変形が起こり難くなるためである。
また、本硬化物の反射率は特に限定されないが、ＪＩＳ Ｋ ７３７５：２００８「プラスチック−全光線透過率及び全光線反射率の求め方」に規定の方法により測定した全光線反射率が７５％以上であることが好ましく、特には、８０％以上であることが好ましい。
また、本硬化物の線膨張率は特に限定されないが、ＪＩＳ Ｋ ７１９７—１９９１「プラスチックの熱機械分析による線膨張率の試験方法」に規定の方法により測定した線膨張率が２５~２００℃の温度範囲での平均値として、２００ｐｐｍ／℃以下であることが好ましく、特に、１５０ｐｐｍ／℃以下であることが好ましい。
また、本発明の硬化物は、上記反応性熱可塑体または上記反応性シリコーン組成物を１００℃以上に加熱した金属金型中で硬化してなることが好ましい。光半導体装置の反射材として本硬化物を形成する場合の硬化方法としては、例えば、圧縮成形、トランスファー成形、射出成形が挙げられる。
次に、本発明の光半導体装置について詳細に説明する。
本発明の光半導体装置は、光反射材が上記硬化物により形成されていること特徴とする。このような光半導体装置としては、発光ダイオード（ＬＥＤ）が例示される。この光半導体装置において、光反射材は、光半導体装置の枠材（パッケージング材）としても機能している。
本半導体装置の一例である表面実装型ＬＥＤの断面図を図１に示した。図１で示されるＬＥＤは、光半導体素子１がリードフレーム２上にダイボンド材によりダイボンディングされ、この光半導体素子１とリードフレーム２、３とがボンディングワイヤ４、４’によりワイヤボンディングされている。この光半導体素子１の上部を除く周囲には、上記の硬化物からなる光反射材５を有し、この光反射材５の内側の光半導体素子１は封止材６により封止されている。
図１で示される表面実装型ＬＥＤを製造する方法としては、（１）本発明の反応性熱可塑体をトランスファー成形または圧縮成形により、リードフレーム２、３と一体化した光反射材５を形成する工程、（２）リードフレーム２上にダイボンド材により光半導体素子１をダイボンディングする工程、（３）光半導体素子１とリードフレーム２、３をボンディングワイヤ４、４’によりワイヤボンディングする工程、（４）光半導体素子１を封止材６に封止する工程からなる方法が例示される。 First, the reactive silicone composition of the present invention will be described in detail.
Component (A) is the main component of the present composition, and average unit formula:
(R 1 3 SiO 1/2 ) a (R 1 2 SiO 2/2 ) b (R 1 SiO 3/2 ) c (SiO 4/2 ) d (R 2 O 1/2 ) e
It is organopolysiloxane represented by these.
In the formula, R 1 is the same or different and is a phenyl group, an alkyl group having 1 to 6 carbon atoms, or an alkenyl group having 2 to 6 carbon atoms. Examples of the alkyl group for R 1 include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a cyclopentyl group, and a cyclohexyl group. Examples of the alkenyl group for R 1 include a vinyl group, an allyl group, a butenyl group, a pentenyl group, and a hexenyl group. The content of the phenyl groups is in the range of 30 to 80 mol% of all R 1, it the case of forming the reactive thermoplastic material is in the range of 60 to 75 mol% of all R 1 preferable. This is because when the phenyl group content is at least the lower limit of the above range, the resulting reactive thermoplastic has good room temperature hardness and high temperature flow characteristics, and the resulting cured product has mechanical strength. On the other hand, the hardness at high temperature of the obtained cured product is good when it is not more than the upper limit of the above range. In the formula, the content of the alkenyl group in the total R 1 is in the range of 10 to 20 mol%. This is because when the content of the alkenyl group is not less than the lower limit of the above range, the resulting cured product has good hardness at room temperature. This is because the mechanical strength is good.
In the formula, R 2 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms. Examples of the alkyl group for R 2 include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, and a hexyl group.
Further, in the formula, a is a number indicating the ratio of siloxane units represented by the general formula: R 1 3 SiO 1/2 , and 0 ≦ a ≦ 0.30, preferably 0 ≦ a ≦ 0.25. It is a number that satisfies This is because the hardness at room temperature of the obtained cured product is good when a is not more than the upper limit of the above range. In the formula, b is a number indicating the ratio of the siloxane unit represented by the general formula: R 1 2 SiO 2/2 and is a number satisfying 0 ≦ b ≦ 0.70, and is a reactive thermoplastic. Is preferably a number satisfying 0.10 ≦ b ≦ 0.70, and more preferably satisfying 0.15 ≦ b ≦ 0.60. This is obtained when b is equal to or higher than the lower limit of the above range, and the resulting thermoplastic thermoplastic resin has good room temperature hardness and high temperature flow characteristics, while being equal to or lower than the upper limit of the above range. This is because the hardness of the cured product at room temperature is good. C is a number indicating the ratio of siloxane units represented by the general formula: R 1 SiO 3/2 , and is a number satisfying 0.3 ≦ c ≦ 0.9, preferably 0.35 ≦ The number satisfies c ≦ 0.85, and more preferably the number satisfies 0.40 ≦ c ≦ 0.80. When c is equal to or higher than the lower limit of the above range, the cured product obtained has good hardness at room temperature. On the other hand, when c is equal to or lower than the upper limit of the above range, the obtained cured product has good mechanical strength. Because. D is a number indicating the ratio of the siloxane unit represented by the general formula: SiO 4/2 , and is a number satisfying 0 ≦ d ≦ 0.20, preferably 0 ≦ b ≦ 0.10. This is because the mechanical strength of the obtained cured product is good when d is not more than the upper limit of the above range. E is a number indicating the proportion of units represented by the general formula: R 2 O 1/2 and is a number satisfying 0 ≦ e ≦ 0.10. This is because the hardness of the obtained cured product at room temperature is good when e is not more than the upper limit of the above range. In the formula, the sum of a, b, c, and d is 1.
The component (A) usually has a molecular weight distribution and is a mixture of a plurality of organopolysiloxanes. In addition, the component (A) may be a mixture of separately prepared organopolysiloxanes, but each organopolysiloxane is 0 ≦ a ≦ 0.30, 0 ≦ b ≦ 0. 70, 0.3 ≦ c ≦ 0.9, 0 ≦ d ≦ 0.20, and 0 ≦ e ≦ 0.10.
Component (B) is an optional component for adjusting the viscosity of the present composition and adjusting the hardness and mechanical strength of the resulting cured product.
R 3 3 SiO (R 3 2 SiO) m SiR 3 3
It is organopolysiloxane represented by these.
In the formula, R 3 is the same or different, a phenyl group, an alkyl group having 1 to 6 carbon atoms, or an alkenyl group having 2 to 6 carbon atoms. Examples of the alkyl group for R 3 include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a cyclopentyl group, and a cyclohexyl group. Examples of the alkenyl group for R 3 include a vinyl group, an allyl group, a butenyl group, a pentenyl group, and a hexenyl group. In the formula, the content of phenyl group in the total R 3 is in the range of 30 to 70 mol%, preferably in the range of 40 to 60 mol%. If the phenyl group content is not less than the lower limit of the above range, the resulting cured product has good mechanical strength, whereas if it is not more than the upper limit of the above range, the hardness of the obtained cured product is It is because it is good. In the formula, at least one R 3 is an alkenyl group. This is because this component is taken into the curing reaction when it has an alkenyl group.
In the formula, m is an integer in the range of 10 to 100, preferably an integer in the range of 10 to 50. When m is not less than the lower limit of the above range, the resulting cured product has good mechanical strength, and when it is not more than the upper limit of the above range, the resulting composition has good handling workability. Because.
In the present composition, the content of the component (B) is an amount in the range of 0 to 40 parts by mass, preferably in the range of 0 to 20 parts by mass with respect to 100 parts by mass of the component (A). Is the amount. This is because the hardness of the obtained cured product is good when the content of the component (B) is not more than the upper limit of the above range.
Component (C) is a crosslinking agent of the present composition, and has at least two silicon atom-bonded hydrogen atoms in one molecule, and 20 to 70 mol% of all silicon atom-bonded organic groups are phenyl groups. Polysiloxane. (C) The number of silicon-bonded hydrogen atoms in the component is at least two in one molecule, because this is sufficient for crosslinking and the resulting cured product has good hardness. . In addition, as the silicon atom-bonded organic group in the component (C), alkyl groups such as a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, a cyclopentyl group, a cyclohexyl group, and a cycloheptyl group Aryl groups such as phenyl group, tolyl group and xylyl group; monovalent hydrocarbon groups having no aliphatic unsaturated bond such as aralkyl groups such as benzyl group and phenethyl group, and the like, preferably phenyl group, or An alkyl group having 1 to 6 carbon atoms. In the component (C), 20 to 70 mol% of the silicon atom-bonded all organic groups are phenyl groups. If the phenyl group content is not less than the lower limit of the above range, the resulting cured product has good mechanical strength at high temperatures, and if it is not more than the upper limit of the above range, This is because the mechanical strength is good.
As such component (C), the general formula:
(HR 4 2 SiO) 2 SiR 4 2
Organotrisiloxane represented by the general formula:
R 5 3 SiO (R 5 2 SiO) n SiR 5 3
A linear organopolysiloxane represented by the formula:
(R 5 SiO 3/2 ) p (R 5 2 SiO 2/2 ) q (R 5 3 SiO 1/2 ) r (SiO 4/2 ) s (R 6 O 1/2 ) t
The branched-chain organopolysiloxane represented by these is illustrated.
In the formula, R 4 is the same or different, a phenyl group, or an alkyl group having 1 to 6 carbon atoms. Examples of the alkyl group for R 4 include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a cyclopentyl group, and a cyclohexyl group. Note that the content of phenyl groups in the total R 4 is in the range of 30 to 70 mol%.
In the formula, R 5 is the same or different, a hydrogen atom, a phenyl group, or an alkyl group having 1 to 6 carbon atoms. In the formula, at least two R 5 are hydrogen atoms. Examples of the alkyl group for R 5 include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a cyclopentyl group, and a cyclohexyl group. Of all R 5 excluding hydrogen atoms, the phenyl group content is in the range of 30 to 70 mol%.
In the formula, R 6 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms. Examples of the alkyl group for R 6 include a methyl group, an ethyl group, a butyl group, a pentyl group, and a hexyl group.
In the formula, n is an integer in the range of 5 to 1,000.
In the formula, p is a positive number, q is 0 or a positive number, r is 0 or a positive number, s is 0 or a positive number, t is 0 or a positive number, and q / p is a number in the range of 0 to 10, r / p is a number in the range of 0 to 5, s / (p + q + r + s) is a number in the range of 0 to 0.3, t / (P + q + r + s) is a number in the range of 0 to 0.4.
In such component (C), all of them have the general formula:
(HR 4 2 SiO) 2 SiR 4 2
In the case where a cured product is formed without passing through a reactive thermoplastic, at least 50% by mass of the component (C) is the above organotrisiloxane. Is preferred. Furthermore, other organosiloxanes may be added at appropriate times to adjust the hardness of the resulting cured product.
In this composition, the content of component (C) is such that the silicon-bonded hydrogen atoms in this component are 0.5 to 2 with respect to a total of 1 mol of alkenyl groups in components (A) and (B). The amount is in the range of moles, preferably the amount in the range of 0.5 to 1.5 moles. This is because the hardness of the hardened | cured material obtained that content of (C) component exists in the said range is favorable.
The component (D) is a hydrosilylation reaction catalyst for promoting the hydrosilylation reaction between the alkenyl group in the components (A) and (B) and the silicon atom-bonded hydrogen atom in the component (C). Examples of the component (D) include platinum-based catalysts, rhodium-based catalysts, and palladium-based catalysts, and platinum-based catalysts are preferred because they can significantly accelerate the curing of the composition. Examples of the platinum-based catalyst include platinum fine powder, chloroplatinic acid, an alcohol solution of chloroplatinic acid, a platinum-alkenylsiloxane complex, a platinum-olefin complex, and a platinum-carbonyl complex, and in particular, a platinum-alkenylsiloxane complex. It is preferable. Examples of the alkenyl siloxane include 1,3-divinyl-1,1,3,3-tetramethyldisiloxane, 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane, Examples thereof include alkenyl siloxanes in which part of the methyl groups of these alkenyl siloxanes are substituted with ethyl groups, phenyl groups, and the like, and alkenyl siloxanes in which the vinyl groups of these alkenyl siloxanes are substituted with allyl groups, hexenyl groups, and the like. In particular, since the stability of this platinum-alkenylsiloxane complex is good, 1,3-divinyl-1,1,3,3-toteramethyldisiloxane is preferable. Further, since the stability of this platinum-alkenylsiloxane complex can be improved, 1,3-divinyl-1,1,3,3-tetramethyldisiloxane, 1,3-diallyl-1,1 can be added to this complex. , 3,3-tetramethyldisiloxane, 1,3-divinyl-1,3-dimethyl-1,3-diphenyldisiloxane, 1,3-divinyl-1,1,3,3-tetraphenyldisiloxane, , 3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane is preferably added, and alkenylsiloxane such as dimethylsiloxane oligomer is preferably added. It is preferable.
In the present composition, the content of component (D) is sufficient to promote the hydrosilylation reaction between the alkenyl group in component (A) and component (B) and the silicon-bonded hydrogen atom in component (C). Although it is not particularly limited as long as it is an amount, it is preferably an amount such that the metal atom in the component is in the range of 0.01 to 500 ppm by mass unit with respect to the composition, The amount is preferably in the range of 0.01 to 100 ppm, and particularly preferably in the range of 0.01 to 50 ppm. When the content of the component (D) is not less than the lower limit of the above range, the resulting composition is cured well. On the other hand, when the content is not more than the upper limit of the above range, the resulting cured product is colored. It is difficult.
Component (E) is a white pigment other than titanium oxide for coloring the present composition and its cured product white and increasing the light reflectance. Examples of the component (E) include metal oxides such as zinc oxide, barium titanate, alumina, zircon oxide, magnesium oxide, and antimony trioxide; inorganic compounds such as barium sulfate, zinc sulfide, boron nitride, and aluminum nitride; From the viewpoint of the light reflectivity in the ultraviolet region of 350 to 400 nm and the adhesion of the cured product to the metal, it is preferably any one of zinc oxide, barium titanate, and barium sulfate, or a mixture thereof, and particularly a thin thickness. Barium titanate is preferable because of its excellent reflectance (concealment).
The average particle size and shape of the component (E) are not limited, but the average particle size is preferably in the range of 0.05 to 10.0 μm, and particularly in the range of 0.1 to 5.0 μm. Is preferred. As the white pigment, in order to improve the compatibility and dispersibility with the resin and the inorganic filler, those which have been surface-treated with a silane coupling agent, silica, alumina or the like can be used.
In the present composition, the content of the component (E) is 50 parts by mass or more, preferably 60 parts by mass or more with respect to 100 parts by mass in total of the components (A) to (D). This is because the light reflectance of the obtained cured product is good when the content of the component (E) is not less than the above lower limit.
Component (F) is spherical silica, non-spherical silica or glass fiber for improving the workability reduction due to the increase in viscosity of the composition, reducing the linear expansion coefficient of the cured product, and improving the dimensional stability. is there. Examples of the spherical silica as the component (F) include dry silica, wet silica, fused silica, and deflagration silica, but fused silica is preferable because the filling property of the present composition is good. Examples of the non-spherical silica of component (F) include quartz powder and glass beads, and quartz powder is preferable. (F) As a glass fiber of a component, a chopped glass fiber and a milled glass fiber are illustrated, Preferably it is a milled glass fiber.
The particle size of the spherical silica as component (F) is not limited, but the average particle size is preferably in the range of 0.1 to 50 μm, and more preferably in the range of 0.5 to 20 μm. The average particle size of the non-spherical silica of the component (F) is not limited, but is preferably in the range of 0.1 to 20 μm, and particularly preferably in the range of 0.5 to 10 μm. The shape of the component (F) glass fiber is not limited, but the fiber diameter is preferably in the range of 1 to 50 μm, particularly preferably in the range of 5 to 20 μm, and the fiber length is 5 It is preferably in the range of ~ 500 μm, particularly preferably in the range of 10 to 300 μm.
In the present composition, the content of the component (F) is 100 parts by mass or more, preferably 120 parts by mass or more, with respect to 100 parts by mass in total of the components (A) to (D). It is because the linear expansion coefficient of the obtained cured product is low and the dimensional stability is good when the content of the component (F) is not less than the above lower limit.
In the present composition, the total content of the component (E) and the component (F) is 400 parts by mass or less, preferably 350 parts by mass with respect to a total of 100 parts by mass of the components (A) to (D). Or less. This is because the viscosity of the resulting composition is good when the total content of the component (E) and the component (F) is not more than the above upper limit.
In the present composition, as an adhesion promoter for enhancing the adhesion to a substrate that is in the process of curing, (G) average unit formula:
(R 7 3 SiO 1/2 ) f (R 7 2 SiO 2/2 ) g (R 7 SiO 3/2 ) h (SiO 4/2 ) i (R 8 O 1/2 ) j
It is preferable to contain the organopolysiloxane represented by these.
In the formula, R 7 is the same or different, a phenyl group, an alkyl group having 1 to 6 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, or an organic group containing an epoxy group. Examples of the alkyl group for R 7 include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a heptyl group, a cyclopentyl group, and a cycloheptyl group. Examples of the alkenyl group for R 7 include a vinyl group, an allyl group, a butenyl group, a pentenyl group, and a hexenyl group. Examples of the epoxy group-containing organic group for R 7 include 3-glycidoxypropyl group, 4-glycidoxybutyl group, 2- (3,4-epoxycyclohexyl) ethyl group, and 3- (3,4-epoxycyclohexyl). A propyl group is exemplified. In the formula, among all R 7 , the phenyl group content is in the range of 15 to 60 mol%, and preferably in the range of 20 to 50 mol%. This is because the adhesiveness and reflectance of the resulting cured product are good when the phenyl group content is at least the lower limit of the above range, and when the content of the phenyl group is below the upper limit of the above range, This is because the adhesiveness and heat resistance are good. In the formula, the content of the alkenyl group in the total R 7 is in the range of 3 to 30 mol%, preferably in the range of 5 to 20 mol%. This is because when the content of the alkenyl group is within the above range, the obtained cured product has good adhesiveness. In addition, among all R 7, the content of the epoxy group-containing organic group is in the range of 5 to 30 mol%, preferably in the range of 10 to 20 mol%. When the content of the epoxy group-containing organic group is at least the lower limit of the above range, the resulting cured product has good adhesiveness. On the other hand, when the content is below the upper limit of the above range, good heat resistance is obtained. Because it is.
In the formula, R 8 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms. Examples of the alkyl group for R 6 include a methyl group, an ethyl group, a butyl group, a pentyl group, and a hexyl group.
In the formula, f is a number indicating the ratio of siloxane units represented by the general formula: R 7 3 SiO 1/2 , and 0 ≦ f ≦ 0.5, preferably 0 ≦ f ≦ 0.4. It is a number that satisfies This is because the adhesiveness of the obtained hardened | cured material is favorable as f is below the upper limit of the said range. In the formula, g is a number indicating the ratio of siloxane units represented by the general formula: R 7 2 SiO 2/2 , and 0 ≦ g ≦ 0.9, preferably 0 ≦ g ≦ 0.8. It is a number that satisfies This is because the adhesiveness of the obtained cured product is good when g is not more than the upper limit of the above range. H is a number indicating the ratio of the siloxane unit represented by the general formula: R 7 SiO 3/2 , and is a number satisfying 0 ≦ h ≦ 0.7, preferably 0 ≦ h ≦ 0.6. is there. This is because the adhesiveness of the hardened | cured material obtained is favorable as h is below the upper limit of the said range. Further, i is a number indicating the ratio of the siloxane unit represented by the general formula: SiO 4/2 , and is a number satisfying 0 ≦ i ≦ 0.3, preferably 0 ≦ i ≦ 0.2. This is because the adhesiveness of the obtained cured product is good when i is not more than the upper limit of the above range. J is a number indicating the proportion of units represented by the general formula: R 6 O 1/2 and is a number satisfying 0 ≦ j ≦ 0.02. This is because the pot life and storage stability of the composition are good when j is not more than the upper limit of the above range. In the formula, the sum of f, g, h, and i is 1.
In the present composition, the content of the component (G) is an amount that is in the range of 0.5 to 10.0 parts by mass with respect to 100 parts by mass in total of the components (A) to (D). In particular, the amount is preferably in the range of 1.0 to 8.0 parts by mass. When the content of the component (G) is not more than the upper limit of the above range, the resulting cured product has good heat resistance, and on the other hand, if it is not less than the lower limit of the above range, the resulting cured product has adhesiveness. This is because is good.
The present composition has the purpose of extending the pot life at room temperature without impairing the curability of the composition, and the purpose of increasing the adhesiveness of the sealing material for optical semiconductor devices to the cured product of the composition The second crosslinking agent (H) is an organopolysiloxane having 2 or more silicon-bonded hydrogen atoms in one molecule and a phenyl group content of less than 20 mol% with respect to all silicon-bonded organic groups. It is preferable to contain siloxane.
(H) The number of silicon-bonded hydrogen atoms in the component is two or more in one molecule, because this is sufficient for crosslinking for curing and the resulting cured product has good hardness. . In addition, as the silicon atom-bonded organic group in the component (H), alkyl groups such as a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, a cyclopentyl group, a cyclohexyl group, and a cycloheptyl group Aryl groups such as phenyl group, tolyl group and xylyl group; monovalent hydrocarbon groups having no aliphatic unsaturated bond such as aralkyl groups such as benzyl group and phenethyl group, and the like, preferably phenyl group, or An alkyl group having 1 to 6 carbon atoms. The content of the phenyl group relative to the silicon-bonded all organic groups in the component (H) is less than 20 mol%, preferably 10 mol% or less. Moreover, it is preferable that 90 mol% or more of the silicon atom bond total organic group in (H) component is a methyl group. When the phenyl group content is less than the above upper limit and the methyl group content is not less than the lower limit of the above range, the resulting cured product has good adhesion to various substrates, and the cured product This is because the adhesiveness of the sealing material for the optical semiconductor device is good.
As such (H) component, the formula:
(MeHSiO) k
(In the formula, Me represents a methyl group, and k is an integer of 4 to 8)
Organopolysiloxane represented by the general formula:
Me 3 SiO (MeHSiO) x SiMe 3
Me 3 SiO (MeHSiO) y (Me 2 SiO) z SiMe 3
(In the formula, Me represents a methyl group, x is an integer of 5 or more, y and z are each an integer of 5 or more, and y is the same as or more than z)
The organopolysiloxane represented by these is illustrated.
In this composition, the content of the component (H) is such that the silicon-bonded hydrogen atoms in this component are 0.001 to 0 with respect to 1 mol in total of the alkenyl groups in the components (A) and (B). The amount is in the range of 20 moles, preferably in the range of 0.002 to 0.10 moles. This is because when the content of the component (H) is within the above range, the pot life at room temperature of the composition is extended, and the adhesiveness of the sealing material for optical semiconductor devices to the obtained cured product becomes good. Furthermore, this is because the flowability of the reactive thermoplastic obtained by hydrosilylation reaction of the composition at a high temperature is improved.
When producing an optical semiconductor device by transfer molding, injection molding, or compression molding using this composition, in order to improve the mold releasability of the cured product from the mold, the composition contains carbon atoms as a mold release agent. A carboxylic acid having a number of 10 or more or a metal salt thereof may be contained. Examples of such carboxylic acids include myristic acid, palmitic acid, stearic acid, oleic acid, linoleic acid, and linolenic acid. In particular, at least one oleic acid, linoleic acid, linolenic acid, and the like are present in the molecule. Those having a carbon-carbon double bond are preferred. Specific examples include oleic acid, linoleic acid, linolenic acid, zinc oleate, aluminum oleate, and calcium oleate. Oleic acid and a metal salt thereof having at least one carbon-carbon double bond in one molecule are preferable from the viewpoint of little deterioration over time due to oxidation.
The content of the carboxylic acid or a metal salt thereof is preferably in the range of 0.01 to 8 parts by mass with respect to a total of 100 parts by mass of the components (A) to (D), particularly 0 It is preferably in the range of 05 to 5 parts by mass. This is because if the content of the carboxylic acid or its metal salt is not more than the upper limit of the above range, the resulting cured product will not be too soft, whereas if it is not less than the lower limit of the above range, the resulting cured product will be obtained. This is because the releasability of is good.
Moreover, you may contain mold release agents other than carboxylic acid or its metal salt in this composition. Examples of such release agents include carnauba wax, methyl silicone oil, and fluorosilicone oil.
This composition is composed of at least the components (A) to (F), but as other optional components, 1-ethynyl-1-cyclohexanol, 2-methyl-3-butyn-2-ol, 3, 5 Alkyne alcohols such as dimethyl-1-hexyn-3-ol and 2-phenyl-3-butyn-2-ol; 3-methyl-3-penten-1-yne, 3,5-dimethyl-3-hexene-1 An enyne compound such as yne; 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane, 1,3,5,7-tetramethyl-1,3,5,7 -Reaction inhibitors such as tetrahexenylcyclotetrasiloxane and benzotriazole may be contained. The content of the reaction inhibitor is not limited, but is preferably in the range of 1 to 5,000 ppm by mass with respect to the present composition.
The composition may contain an adhesion promoter other than the component (G). Such adhesion promoters include trialkoxysiloxy groups (for example, trimethoxysiloxy group, triethoxysiloxy group) or trialkoxysilylalkyl groups (for example, trimethoxysilylethyl group, triethoxysilylethyl group), hydrosilyl An organosilane having an alkyl group or an alkenyl group (for example, a vinyl group, an allyl group), or a linear, branched or cyclic organosiloxane oligomer having about 4 to 20 silicon atoms; trialkoxysiloxy group or trialkoxy Organosilane having a silylalkyl group and a methacryloxyalkyl group (for example, 3-methacryloxypropyl group), or an organosiloxane oligomer having a linear structure, a branched structure or a cyclic structure having about 4 to 20 silicon atoms; Siloxy group or trialkoxysilylalkyl group and epoxy group-bonded alkyl group (for example, 3-glycidoxypropyl group, 4-glycidoxybutyl group, 2- (3,4-epoxycyclohexyl) ethyl group, 3- (3 , 4-epoxycyclohexyl) propyl group) or an organosiloxane oligomer having a linear structure, branched structure or cyclic structure having about 4 to 20 silicon atoms; aminoalkyltrialkoxysilane and epoxy group-bonded alkyltrialkoxy Examples include silane reactants and epoxy group-containing ethyl polysilicates. Specific examples include vinyltrimethoxysilane, allyltrimethoxysilane, allyltriethoxysilane, hydrogentriethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-grid Doxypropyltriethoxysilane, 2- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-methacryloxypropyltriethoxysilane, 3-glycidoxypropyltriethoxysilane Reaction product of 3-aminopropyltriethoxysilane, condensation reaction product of silanol-blocked methylvinylsiloxane oligomer and 3-glycidoxypropyltrimethoxysilane, silanol-blocked methylvinylsiloxane oligomer and 3-methacryloxypropyltriethoxysilane Examples include condensation reaction products, tris (3-trimethoxysilylpropyl) isocyanurate, and acid anhydrides.
Furthermore, when forming the cured product without passing through the reactive thermoplastic, the composition is improved by improving the handling workability of the composition and adjusting the hardness of the resulting cured product. An organopolysiloxane having 10 or less silicon atoms in which 30 to 60 mol% of all organic groups are alkenyl groups having 2 to 6 carbon atoms may be contained. Examples of the alkenyl group in the organopolysiloxane include a vinyl group, an allyl group, a butenyl group, a pentenyl group, and a hexenyl group. Further, the silicon atom-bonded organic group other than the alkenyl group in the organopolysiloxane is not particularly limited, but examples thereof include a methyl group and a phenyl group, and a methyl group is preferable. Further, 30 to 60 mol% of all silicon atom-bonded organic groups are alkenyl groups having 2 to 6 carbon atoms. When the content of the alkenyl group is not less than the lower limit of the above range, the resulting cured product has good hardness. On the other hand, when the content of the alkenyl group is not more than the upper limit of the above range, the resulting cured product has a mechanical strength. It is because it is good. Furthermore, although the number of silicon atoms is 10 or less, this is because the viscosity of the composition is good when the number of silicon atoms is 10 or less.
Such organopolysiloxanes include 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane, tetrakis (dimethylvinylsiloxy) silane, methyltris (dimethylvinylsiloxy) silane, And phenyltris (dimethylvinylsiloxy) silane.
The content of the organopolysiloxane is preferably an amount within the range of 0 to 50 parts by mass with respect to 100 parts by mass of the component (A). In particular, the present composition is a liquid reactive silicone composition. When it is used, it is preferable that the amount be in the range of 5 to 40 parts by mass. When the content of the organopolysiloxane is at least the lower limit of the above range, the viscosity of the composition is good. On the other hand, when the content is below the upper limit of the above range, the resulting cured product has good mechanical strength. Because.
Furthermore, the present composition includes, as optional components, spherical silica, non-spherical silica, inorganic fillers other than glass fibers, fine organic resin powders such as polymethacrylate resins and silicone resins, as long as the object of the present invention is not impaired. A corrosion inhibitor such as benzotriazole or carboxybenzotriazole, a heat-resistant agent, a flame retardant, and a solvent.
The viscosity at 25 ° C. of the present composition is not particularly limited, but when obtaining a reactive thermoplastic, it is preferably 10,000 Pa · s or less, particularly preferably in the range of 10 to 5,000 Pa · s. Is within. When the viscosity is equal to or higher than the lower limit of the above range, it is easy to form a reactive thermoplastic having a desired shape. On the other hand, when the viscosity is equal to or lower than the upper limit of the above range, the resulting composition is handled. This is because the property is good.
Further, when the present composition is used as a liquid reactive silicone composition, the viscosity at 25 ° C. is preferably in the range of 5 to 200 Pa · s, more preferably in the range of 5 to 120 Pa · s. And particularly preferably within the range of 10 to 80 Pa · s. This is because, when the viscosity is at least the lower limit of the above range, the occurrence of burrs is suppressed during molding, and when the viscosity is below the upper limit of the above range, the workability of the resulting composition is good.
Next, the reactive thermoplastic of the present invention will be described in detail.
The reactive thermoplastic of the present invention is obtained by reacting until the conversion rate of the hydrosilylation reaction of the above reactive silicone cured product becomes 70% to 95%. The conversion rate of hydrosilylation is the percentage of the total functional group that undergoes hydrosilylation reaction, in which the reaction actually takes place, and its confirmation method is not particularly limited. For example, differential scanning calorimetry Using a meter (DSC), the reaction calorific value of the reactive silicone composition and the obtained reactive thermoplastic can be measured, and the conversion rate can be easily calculated from the difference. The reaction proceeds at room temperature or by heating, but heating is preferable in order to obtain a reactive thermoplastic efficiently. The heating temperature is preferably in the range of 50 to 150 ° C, and more preferably in the range of 80 to 130 ° C.
The reactive thermoplastic of the present invention is preferably a solid at 25 ° C. or a liquid having a viscosity of 1,000,000 Pa · s or more at 100 ° C. and a liquid having a viscosity of 100,000 Pa · s or less at 100 ° C.
The reactive thermoplastic of the present invention preferably has a type D durometer hardness of 30 or more at 25 ° C. as defined in JIS K 7215-1986 “Plastic Durometer Hardness Test Method”.
Such a reactive thermoplastic of the present invention fluidizes once when heated to 100 ° C. or higher, and then undergoes a hydrosilylation reaction to give a cured product.
Next, the cured product of the present invention will be described in detail.
The cured product of the present invention is obtained by heating the reactive thermoplastic and performing the remaining hydrosilylation reaction, or the liquid reactive silicone composition without passing through the reactive plastic. Is obtained by heating and hydrosilylation reaction, and at 300 ° C., the solid or viscosity is 1,000,000 Pa · s or more. The hardness of the cured product is not particularly limited, but the type D durometer hardness specified in JIS K 7215-1986 “Plastic Durometer Hardness Test Method” is preferably 60 or more, and more preferably 65 or more. It is preferable that it is 70 or more especially. This is because when the hardness is equal to or higher than the above lower limit, the dimensional stability of the cured product is improved, and the cured product is hardly deformed.
The reflectivity of the cured product is not particularly limited, but the total light reflectivity measured by the method specified in JIS K 7375: 2008 “Plastics—Determination of total light transmittance and total light reflectivity” is 75% or more. In particular, it is preferably 80% or more.
Further, the linear expansion coefficient of the cured product is not particularly limited, but the linear expansion coefficient measured by the method specified in JIS K 7197-1991 “Test method for linear expansion coefficient by thermomechanical analysis of plastic” is 25 to 200 ° C. The average value in the temperature range is preferably 200 ppm / ° C. or less, and particularly preferably 150 ppm / ° C. or less.
Moreover, it is preferable that the hardened | cured material of this invention hardens | cures the said reactive thermoplastic body or the said reactive silicone composition in the metal metal mold | die heated at 100 degreeC or more. Examples of the curing method for forming the main cured product as the reflecting material of the optical semiconductor device include compression molding, transfer molding, and injection molding.
Next, the optical semiconductor device of the present invention will be described in detail.
The optical semiconductor device of the present invention is characterized in that the light reflecting material is formed of the cured product. As such an optical semiconductor device, a light emitting diode (LED) is exemplified. In this optical semiconductor device, the light reflecting material also functions as a frame material (packaging material) of the optical semiconductor device.
A cross-sectional view of a surface-mounted LED, which is an example of the semiconductor device, is shown in FIG. In the LED shown in FIG. 1, an
As a method of manufacturing the surface mount type LED shown in FIG. 1, (1) the
本発明の硬化性シリコーン組成物、反応性熱可塑体、硬化物、および光半導体装置を実施例により詳細に説明する。なお、式中のＭｅ、Ｐｈ、Ｖｉ、およびＥｐは、それぞれメチル基、フェニル基、ビニル基、および３−グリシドキシプロピル基を表す。
また、反応性熱可塑体および硬化物の硬さは、ＪＩＳ Ｋ ７２１５—１９８６「プラスチックのデュロメータ硬さ試験方法」に規定のタイプＤデュロメータにより測定した。
また、硬化物の曲げ強さは、ＪＩＳ Ｋ ６９１１—１９９５「熱硬化性プラスチック一般試験方法」に規定の方法により測定した。
また、硬化物の全光線反射率は、ＪＩＳ Ｋ ７３７５：２００８「プラスチック−全光線透過率及び全光線反射率の求め方」に規定の方法により測定した。試験片は２ｍｍ厚の物を使用した。
また、硬化物の隠蔽性は０．２ｍｍ厚の試験片を用いて上記全光線反射率測定により評価した。
また、硬化物の４００ｎｍの波長での光反射率は上記全光線反射率で作成した試験片を用いて、分光光度計（島津製作所製のＵＶ−３１００ＰＣ）により測定した。
また、硬化物の線膨張率は、２５~２００℃の範囲内での平均線膨張率を、ＪＩＳ Ｋ ７１９７—１９９１「プラスチックの熱機械分析による線膨張率の試験方法」に規定の方法により測定した。
また、２５ｍｍ×７５ｍｍのアルミニウム板上に、反応性シリコーン組成物をディスペンサーにより約１００ｍｇづつを５ヶ所に塗布し、該組成物に厚さ１ｍｍの６ｍｍ角のアルミニウム製チップを被せ、１ｋｇの板により圧着した。次いで、これを１５０℃で２時間加熱し、反応性シリコーン組成物を硬化した。室温に冷却した後、シェア強度測定装置（西進商事株式会社製のボンドテスターＳＳ−１００ＫＰ）によりダイシェア強度を測定した。また、上記と同様にして、銀メッキ鋼板に対する銀メッキ鋼板製チップのダイシェア強度についても測定した。
また、本組成物の金型離型性はトランスファー成型機を用いて成型温度１２０℃、成形時間５分の条件でリードフレームとの一体成型を１０回行い、成型後の光半導体装置にクラック及びリードフレームからの剥離等の成型不良が発生した回数の確認により評価した。
また、ヒドロシリル化反応の転化率は、示差走査熱量計によって各状態での反応熱量を求め、その差から算出した。
［実施例１］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン １００質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １３．３質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ３３．３質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が１．１５モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．５μｍのチタン酸バリウム（富士チタン工業製のＨＰＢＴ−１） １２２質量部、および平均粒子径５μｍの破砕石英粉末（龍森製のクリスタライトＶＸ−５２） ２２０質量部を混合して、２５℃での粘度が３８０Ｐａ・ｓである反応性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度が測定不能な固体であり、タイプＤデュロメータ硬さが６３であり、１００℃での粘度が６００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は８５％であった。
得られた熱可塑体を１５０℃で加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃で粘度測定不能な固体であり、２５℃でのタイプＤデュロメータ硬さが８２であり、曲げ強さが１５ＭＰａ、全光線反射率が９３．５％（２ｍｍ厚の試験片）と８８．１％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７３．２％、硬化物の線膨張率が１１５ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、７．９および６．９Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、１０回中４回成型不良が確認されたが、成型不良がなかった物はバリやボイドがなく良好な成型物が得られた。
［実施例２］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ４８．４質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ５１．６質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２（ＭｅＥｐＳｉＯ２／２）０．２５（ＰｈＳｉＯ３／２）０．５５（ＨＯ１／２）０．００５
で表されるエポキシ基含有ポリシロキサン １．５質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １２．９質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２９．０質量部（上記のメチルビニルフェニルポリシロキサン、ジメチルビニルシロキシ末端ポリメチルフェニルシロキサン、エポキシ基含有ポリシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．９４モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、オレイン酸（東京化成工業製） ０．２質量部、平均一次粒子径０．５μｍのチタン酸バリウム（富士チタン工業製のＨＰＢＴ−１） １１８質量部、および平均粒子径１５μｍの球状シリカ（新日鉄マテリアルズ マイクロン社製のＨＳ−２０２）２１３質量部を混合して、２５℃での粘度が１７０Ｐａ・ｓである硬化性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが６１であり、１００℃での粘度が５，９００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は７９％であった。
得られた熱可塑体を１５０℃に加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃で粘度測定不能な固体であり、２５℃でのタイプＤデュロメータ硬さが８６であり、曲げ強さが２４ＭＰａ、全光線反射率が９３．３％（２ｍｍ厚の試験片）と８７．７％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７４．１％、硬化物の線膨張率が１０１ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、１１．２および９．１Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、成型不良は確認されず、バリやボイドのない良好な成形物が得られた。
［実施例３］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ４８．４質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ５１．６質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １２．９質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２９．０質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．９６モルとなる量）、１，３，５，７−テトラメチルテトラシクロシロキサン ０．５質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．０４６７モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．５μｍのチタン酸バリウム（富士チタン工業製のＨＰＢＴ−１） １１８質量部、および平均カット長２０μｍ、平均ファイバー径３μｍのミルドガラスファイバー（旭ファイバーグラス製のＭＦ０３ＪＢ１−２０）２１３質量部を混合して、２５℃での粘度が１５０Ｐａ・ｓである反応性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが６９であり、１００℃での粘度が１９，５００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は８６％であった。
得られた熱可塑体を１５０℃に加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８３であり、曲げ強さが１８ＭＰａ、全光線反射率が９４．１％（２ｍｍ厚の試験片）と８８．２％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７３．６％、硬化物の線膨張率が１０３ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、９．２および７．６Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、１０回中５回成型不良が確認されたが、成型不良がなかった物はバリやボイドがなく良好な成型物が得られた。
［実施例４］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ３８．５質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ６１．５質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １９．４質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２８．２質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．９２モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、オレイン酸（東京化成工業製） ０．２質量部、平均一次粒子径０．５μｍの酸化亜鉛（堺化学工業製の酸化亜鉛１種）１１８質量部、および平均粒子径５μｍの破砕石英粉末（山森土本鉱業所製のシルシックＳＡＢ−５００） ２１３質量部を混合して、２５℃での粘度が４５０Ｐａ・ｓである反応性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが７０であり、１００℃での粘度が１６，０００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は８９％であった。
得られた熱可塑体を１５０℃で加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８４であり、曲げ強さが２１ＭＰａ、全光線反射率が９２．３％（２ｍｍ厚の試験片）と８２．４％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７１．５％、硬化物の線膨張率が１２１ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、８．８および７．５Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、成型不良は確認されず、バリやボイドのない良好な成形物が得られた。
［実施例５］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ３８．５質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ６１．５質量部、平均式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２（ＭｅＥｐＳｉＯ２／２）０．２５（ＰｈＳｉＯ３／２）０．５５（ＨＯ１／２）０．００５
で表されるエポキシ基含有ポリシロキサン １．５質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン ２５．６質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２８．２質量部（上記のメチルビニルフェニルポリシロキサン、ジメチルビニルシロキシ末端ポリメチルフェニルシロキサン、エポキシ基含有ポリシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．８９モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．５μｍの酸化亜鉛（堺化学工業製の酸化亜鉛１種） １２８質量部、および平均粒子径１５μｍの球状シリカ（新日鉄マテリアルズ マイクロン社製のＨＳ−２０２） ２５６質量部を混合して、２５℃での粘度が１６８Ｐａ・ｓである反応性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが７１であり、１００℃での粘度が８，４００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は７９％であった。
得られた熱可塑体を１５０℃に加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８４であり、曲げ強さが２３ＭＰａ、全光線反射率が９１．８％（２ｍｍ厚の試験片）と８１．６％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７１．３％、硬化物の線膨張率が９０ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、１０．９および９．７Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、１０回中４回成型不良が確認されたが、成型不良がなかった物はバリやボイドがなく良好な成型物が得られた。
［実施例６］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ３８．５質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ６１．５質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン ２５．６質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２８．２質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．９モルとなる量）、１，３，５，７−テトラメチルテトラシクロシロキサン ０．５質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．０４３９モルとなる量）白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、オレイン酸（東京化成工業製） ０．２質量部、平均一次粒子径０．５μｍの酸化亜鉛（堺化学工業製の酸化亜鉛１種） １４１質量部、および平均カット長２０μｍ、平均ファイバー径３μｍのミルドガラスファイバー（旭ファイバーグラス製のＭＦ０３ＪＢ１−２０） ２８２質量部を混合して、２５℃での粘度が３７５Ｐａ・ｓである硬化性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが７２であり、１００℃での粘度が１０，５００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は８６％であった。
得られた熱可塑体を１５０℃に加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８５であり、曲げ強さが２６ＭＰａ、全光線反射率が９２．３％（２ｍｍ厚の試験片）と８２．８％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７３．８％、硬化物の線膨張率が７２ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、８．９および７．９Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、成型不良は確認されず、バリやボイドのない良好な成形物が得られた。
［実施例７］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ４８．４質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ５１．６質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １２．９質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２９．０質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．９６モルとなる量）、１，３，５，７−テトラメチルテトラシクロシロキサン ０．５質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．０４６７モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．４５μｍの硫酸バリウム（堺化学工業製のＢＢ−１）１２８質量部、および平均カット長２０μｍ、平均ファイバー径３μｍのミルドガラスファイバー（旭ファイバーグラス製のＭＦ０３ＪＢ１−２０） ２１３質量部を混合して、２５℃での粘度が２３６Ｐａ・ｓである反応性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが６４であり、１００℃での粘度が２４，５００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は８２％であった。
得られた熱可塑体を１５０℃に加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが７９であり、曲げ強さが１４ＭＰａ、全光線反射率が８３．３％（２ｍｍ厚の試験片）と６６．８％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が８１．２％、硬化物の線膨張率が１０５ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、１０．４および９．７Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、１０回中４回成型不良が確認されたが、成型不良がなかった物はバリやボイドがなく良好な成型物が得られた。
［実施例８］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ３８．５質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ６１．５質量部、平均式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２（ＭｅＥｐＳｉＯ２／２）０．２５（ＰｈＳｉＯ３／２）０．５５（ＨＯ１／２）０．００５
で表されるエポキシ基含有ポリシロキサン １．５質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン ２５．６質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２８．２質量部（上記のメチルビニルフェニルポリシロキサン、ジメチルビニルシロキシ末端ポリメチルフェニルシロキサン、エポキシ基含有ポリシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．８９モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、オレイン酸（東京化成工業製） ０．２質量部、平均一次粒子径０．４５μｍの硫酸バリウム（堺化学工業製のＢＢ−１） １２０質量部、および平均粒子径１５μｍの球状シリカ（新日鉄マテリアルズ マイクロン社製のＨＳ−２０２） ２５６質量部を混合して、２５℃での粘度が１９７Ｐａ・ｓである反応性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが６７であり、１００℃での粘度が１２，４００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は７３％であった。
得られた熱可塑体を１５０℃に加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８１であり、曲げ強さが１８ＭＰａ、全光線反射率が８２．１％（２ｍｍ厚の試験片）と６７．１％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７９．４％、硬化物の線膨張率が９７ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、１２．１および１１．４Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、成型不良は確認されず、バリやボイドのない良好な成形物が得られた。
［比較例１］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ４８．４質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ５１．６質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １２．９質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン １４．５質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．４８モルとなる量）、平均単位式：
（Ｍｅ２ＨＳｉＯ１／２）０．６０（ＳｉＯ４／２）０．４０
で表されるケイ素原子結合水素原子含有メチルフェニルポリシロキサン １４．５質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．４８モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．２μｍの酸化チタン（堺化学工業製のＳＸ−３１０３） １１８質量部、および平均粒子径１５μｍの球状シリカ（新日鉄マテリアルズ マイクロン社製のＨＳ−２０２） ２１３質量部を混合して、２５℃での粘度が５９２Ｐａ・ｓである硬化性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが７５であるものの、１００℃でも粘度測定不能な固体状であり、熱可塑体でないことがわかった。ヒドロシリル化反応の転化率は８８％であった。
また、図１で示される光半導体装置を製造するため、得られた固体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったが、全てにおいて金型にほとんど充填されず、不均一な成形物が得られた。
また、この組成物を直接１５０℃で２時間加熱して硬化物を形成した。この硬化物は、タイプＤデュロメータ硬さが９１、曲げ強度が２８ＭＰａ、全光線反射率が９４．６％（２ｍｍ厚の試験片）と９０．８％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が３３．１％、線膨張率が８９ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、８．２および６．８Ｎ／ｍｍ２であった。
［比較例２］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２０（Ｍｅ２ＳｉＯ２／２）０．２０（Ｐｈ２ＳｉＯ２／２）０．１０（ＰｈＳｉＯ３／２）０．５０（ＨＯ１／２）０．０３
で表されるメチルビニルフェニルポリシロキサン １００質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １３．３質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ３３．３質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が１．１０モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．２４μｍの酸化チタン（石原産業製のタイペークＲ−６３０） １２７質量部、および平均カット長２０μｍ、平均ファイバー径３μｍのミルドガラスファイバー（旭ファイバーグラス製のＭＦ０３ＪＢ１−２０） ２２０質量部を混合して、２５℃での粘度が１９５Ｐａ・ｓである硬化性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃での粘度が２３，０００Ｐａ・ｓであり、タイプＤデュロメータ硬さが１１であり、熱可塑体でないことがわかった。ヒドロシリル化反応の転化率は７９％であった。
また、図１で示される光半導体装置を製造するため、得られた液体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったが、全てにおいて金型への付着が大きく、また、成形部分が容易に変形した。
また、この組成物を直接１５０℃で２時間加熱して硬化物を形成した。この硬化物は、タイプＤデュロメータ硬さが７６、曲げ強度が９．４ＭＰａ、全光線反射率が９４．３％（２ｍｍ厚の試験片）と９１．２％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が３１．５％、線膨張率が９１ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、５．４および４．７Ｎ／ｍｍ２であった。
［比較例３］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン １００質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １３．３質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ３３．３質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が１．１５モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．５μｍのチタン酸バリウム（富士チタン工業製のＨＰＢＴ−１） ６５質量部、および平均粒子径５μｍの破砕石英粉末（龍森製のクリスタライトＶＸ−５２） ２８５質量部を混合して、２５℃での粘度が３３０Ｐａ・ｓである硬化性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが６２であり、１００℃での粘度が３，９００Ｐａ・ｓであり、熱可塑体であることがわかった。ヒドロシリル化反応の転化率は８４％であった。
得られた熱可塑体を１５０℃で加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８５であり、曲げ強さが１９ＭＰａ、全光線反射率が５５．４％（２ｍｍ厚の試験片）と５１．７％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が３４．５％、硬化物の線膨張率が９３ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、７．０および６．１Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、１０回中５回成型不良が確認されたが、バリやボイドのない良好な成形物が得られた。
［比較例４］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン １００質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １３．３質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ３３．３質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が１．１５モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．２４μｍの酸化チタン（石原産業製のタイペークＲ−６３０） ２２４質量部、および平均粒子径５μｍの破砕石英粉末（龍森製のクリスタライトＶＸ−５２） １１７質量部を混合し、２５℃での粘度が１，１５０Ｐａ・ｓである硬化性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが６９であるものの、１００℃での粘度が２，０００，０００Ｐａ・ｓと高く、良好な可塑体でないことがわかった。ヒドロシリル化反応の転化率は８６％であった。
得られた固体を１５０℃で加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８７であり、曲げ強さが２０ＭＰａ、全光線反射率が９３．５％（２ｍｍ厚の試験片）と９２．８％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が３０．９％、硬化物の線膨張率が１１５ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、６．７および５．８Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、１０回中５回成型不良が確認され、成型不良がなかった物にも多数のボイドがあり良好な成形物は得られなかった。
［比較例５］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン １００質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １３．３質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ３３．３質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が１．１５モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．５μｍのチタン酸バリウム（富士チタン工業製のＨＰＢＴ−１） １０２質量部、および平均粒子径５μｍの破砕石英粉末（龍森製のクリスタライトＶＸ−５２） ５１０質量部を混合したところ、粉体状の混合物が得られた。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、不均一な固体であり、また１００℃でも粘度測定不能な固体状であり、熱可塑体でないことがわかった。ヒドロシリル化反応の転化率は８２％であった。
また、図１で示される光半導体装置を製造するため、得られた固体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、全てにおいて金型未充填部が認められ、また多数のボイドが生じ、良好な成形物は得られなかった。 The curable silicone composition, reactive thermoplastic, cured product, and optical semiconductor device of the present invention will be described in detail with reference to examples. In the formulae, Me, Ph, Vi, and Ep represent a methyl group, a phenyl group, a vinyl group, and a 3-glycidoxypropyl group, respectively.
The hardness of the reactive thermoplastic and the cured product was measured with a type D durometer specified in JIS K 7215-1986 “Plastic Durometer Hardness Test Method”.
Further, the bending strength of the cured product was measured by the method specified in JIS K 6911-1995 “General Test Method for Thermosetting Plastics”.
Further, the total light reflectance of the cured product was measured by a method specified in JIS K 7375: 2008 “Plastics—How to obtain total light transmittance and total light reflectance”. A test piece having a thickness of 2 mm was used.
Further, the concealability of the cured product was evaluated by measuring the total light reflectance using a test piece having a thickness of 0.2 mm.
Further, the light reflectance at a wavelength of 400 nm of the cured product was measured with a spectrophotometer (UV-3100PC manufactured by Shimadzu Corporation) using the test piece prepared with the above total light reflectance.
The linear expansion coefficient of the cured product is measured by measuring the average linear expansion coefficient in the range of 25 to 200 ° C. according to the method specified in JIS K 7197-1991 “Test method for linear expansion coefficient by thermomechanical analysis of plastics”. did.
In addition, about 100 mg of the reactive silicone composition was applied to 5 locations on a 25 mm × 75 mm aluminum plate with a dispenser, and the composition was covered with 6 mm square aluminum chips having a thickness of 1 mm. Crimped. This was then heated at 150 ° C. for 2 hours to cure the reactive silicone composition. After cooling to room temperature, the die shear strength was measured with a shear strength measuring device (Bond Tester SS-100KP manufactured by Seishin Shoji Co., Ltd.). Moreover, it measured similarly about the die shear strength of the chip | tip made from the silver plating steel plate with respect to a silver plating steel plate similarly to the above.
In addition, the mold releasability of this composition is 10 times integral molding with a lead frame using a transfer molding machine at a molding temperature of 120 ° C. and a molding time of 5 minutes. Evaluation was made by confirming the number of molding defects such as peeling from the lead frame.
Also, the conversion rate of the hydrosilylation reaction was calculated from the difference obtained by obtaining the reaction heat in each state with a differential scanning calorimeter.
[Example 1]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
100 parts by mass of methylvinylphenylpolysiloxane represented by the formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
13.3 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 33.3 parts by mass (total of 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminatedpolymethylphenylsiloxane 1 The amount of silicon atom-bonded hydrogen atoms in this component is 1.15 moles per mole), platinum 1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex 1,3- Divinyl-1,1,3,3-tetramethyldisiloxane solution (amount in which platinum metal is 5.0 ppm by mass with respect to the composition), 1-ethynyl-1-cyclohexanol (to the composition) In an amount of 300 ppm in terms of mass unit), 122 parts by mass of barium titanate (HPBT-1 manufactured by Fuji Titanium Industry) having an average primary particle size of 0.5 μm, and average particles Diameter 5μm crushed quartz powder (Tatsumori Ltd. crystallites VX-52) were mixed 220 parts by weight of a viscosity at 25 ° C. to prepare a reactive silicone composition is 380Pa · s.
When this composition was heated at 120 ° C. for 10 minutes, it was a solid whose viscosity could not be measured at 25 ° C., a type D durometer hardness of 63, and a viscosity of 100 Pa · s at 100 ° C. I found out. The conversion rate of the hydrosilylation reaction was 85%.
When the obtained thermoplastic was heated at 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour is a solid whose viscosity cannot be measured at 300 ° C., the type D durometer hardness at 25 ° C. is 82, the bending strength is 15 MPa, and the total light reflectance is 93.5% (2 mm thick specimen) and 88.1% (0.2 mm thick specimen), light reflectance at a wavelength of 400 nm is 73.2%, and the linear expansion coefficient of the cured product is 115 ppm / ° C. Met. The die shear strengths for aluminum plates and silver-plated steel plates are 7.9 and 6.9 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, 4 out of 10 molding defects were confirmed. Good moldings without burrs and voids were obtained with no molding defects.
[Example 2]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methyl vinyl phenyl polysiloxane 48.4 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methylvinylphenylpolysiloxane represented by the formula: 51.6 parts by mass, average unit formula:
(Me2ViSiO1/2)0.2(MeEpSiO2/2)0.25(PhSiO3/2)0.55(HO1/2)0.005
Epoxy group-containing polysiloxane represented by the formula: 1.5 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
12.9 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 29.0 parts by mass (the above methylvinylphenylpolysiloxane, dimethylvinylsiloxy-terminated polymethylphenylsiloxane, epoxy group-containing polysiloxane The amount of silicon atom-bonded hydrogen atoms in this component is 0.94 mol with respect to a total of 1 mol of vinyl groups), 1,3-divinyl-1,1,3,3-tetramethyldisiloxane ofplatinum 1,3-divinyl-1,1,3,3-tetramethyldisiloxane solution of complex (amount in which platinum metal is 5.0 ppm by mass with respect to the present composition), 1-ethynyl-1-cyclohexanol (Amount to be 300 ppm by mass with respect to the present composition), oleic acid (manufactured by Tokyo Chemical Industry Co., Ltd.), 0.2 parts by mass, titanic acid having an average primary particle size of 0.5 μm Mixing 118 parts by mass of Lithium (HPBT-1 manufactured by Fuji Titanium Industry Co., Ltd.) and 213 parts by mass of spherical silica having a mean particle size of 15 μm (HS-202 manufactured by Nippon Steel Materials Micron), the viscosity at 25 ° C. is 170 Pa. A curable silicone composition that is s was prepared.
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., its type D durometer hardness is 61, and its viscosity at 100 ° C. is 5,900 Pa · s. I found out that The conversion rate of the hydrosilylation reaction was 79%.
When the obtained thermoplastic was heated to 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour is a solid whose viscosity cannot be measured at 300 ° C., has a type D durometer hardness of 86 at 25 ° C., a bending strength of 24 MPa, and a total light reflectance. 93.3% (2 mm thickness test piece) and 87.7% (0.2 mm thickness test piece), light reflectance at a wavelength of 400 nm is 74.1%, and the linear expansion coefficient of the cured product is 101 ppm / ° C. Met. Also, the die shear strength for aluminum plate and silver plated steel plate is 11.2 and 9.1 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, molding defects were not confirmed and there were no burrs or voids. A good molded product was obtained.
[Example 3]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methyl vinyl phenyl polysiloxane 48.4 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methylvinylphenylpolysiloxane represented by the formula: 51.6 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
12.9 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 29.0 parts by mass (1 total of vinyl groups of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated polymethylphenylsiloxane) The amount of silicon atom-bonded hydrogen atoms in this component is 0.96 mol with respect to mol), 0.5 parts by mass of 1,3,5,7-tetramethyltetracyclosiloxane (the above methylvinylphenylpolysiloxane) In addition, the amount of silicon atom-bonded hydrogen atoms in this component is 0.0467 mol with respect to a total of 1 mol of vinyl groups of dimethylvinylsiloxy-terminated polymethylphenylsiloxane), platinum 1,3-divinyl-1,1 1,3-Divinyl-1,1,3,3-tetramethyldisiloxa of 1,3,3-tetramethyldisiloxane complex Solution (amount in which platinum metal is 5.0 ppm by mass with respect to the present composition), 1-ethynyl-1-cyclohexanol (amount in 300 ppm by mass with respect to the present composition), average primary particle size Mixing 118 parts by mass of 0.5 μm barium titanate (HPBT-1 manufactured by Fuji Titanium Industry Co., Ltd.) and 213 parts by mass of milled glass fiber (MF03JB1-20 manufactured by Asahi Fiber Glass Co., Ltd.) with an average cut length of 20 μm and an average fiber diameter of 3 μm Then, a reactive silicone composition having a viscosity at 25 ° C. of 150 Pa · s was prepared.
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., has a type D durometer hardness of 69, and has a viscosity of 19,500 Pa · s at 100 ° C. I found out that The conversion rate of the hydrosilylation reaction was 86%.
When the obtained thermoplastic was heated to 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a Type D durometer hardness of 83 at 25 ° C., a bending strength of 18 MPa, and a total light reflectance of 94. 1% (2 mm thick test piece) and 88.2% (0.2 mm thick test piece), the light reflectance at a wavelength of 400 nm was 73.6%, and the linear expansion coefficient of the cured product was 103 ppm / ° C. It was. The die shear strengths for aluminum plates and silver-plated steel plates are 9.2 and 7.6 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, molding failure was confirmed 5 times out of 10 times. Good moldings without burrs and voids were obtained with no molding defects.
[Example 4]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methylvinylphenylpolysiloxane represented by the formula: 38.5 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methyl vinyl phenyl polysiloxane represented by the formula: 61.5 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
19.4 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane represented by 28.2 parts by mass (total 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated polymethylphenylsiloxane) The amount of silicon-bonded hydrogen atoms in this component to 0.92 mol), 1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex of platinum, Divinyl-1,1,3,3-tetramethyldisiloxane solution (amount in which platinum metal is 5.0 ppm by mass with respect to the composition), 1-ethynyl-1-cyclohexanol (to the composition) Oleic acid (manufactured by Tokyo Chemical Industry Co., Ltd.) 0.2 parts by mass, zinc oxide having an average primary particle size of 0.5 μm (zinc oxide 1 manufactured by Sakai Chemical Industry) ) Reactive silicone composition in which 118 parts by mass and 213 parts by mass of crushed quartz powder having an average particle diameter of 5 μm (Silchic SAB-500 manufactured by Yamamori Tsuchimoto Mining Co., Ltd.) and having a viscosity of 450 Pa · s at 25 ° C. A product was prepared.
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., has a type D durometer hardness of 70, and has a viscosity of 16,000 Pa · s at 100 ° C. I found out that The conversion rate of the hydrosilylation reaction was 89%.
When the obtained thermoplastic was heated at 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a type D durometer hardness of 84 at 25 ° C., a bending strength of 21 MPa, and a total light reflectance of 92.degree. 3% (2 mm thick specimen) and 82.4% (0.2 mm thick specimen), the light reflectance at a wavelength of 400 nm was 71.5%, and the linear expansion coefficient of the cured product was 121 ppm / ° C. It was. The die shear strength for aluminum plate and silver plated steel plate is 8.8 and 7.5 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, molding defects were not confirmed and there were no burrs or voids. A good molded product was obtained.
[Example 5]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methylvinylphenylpolysiloxane represented by the formula: 38.5 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methyl vinyl phenyl polysiloxane represented by the formula: 61.5 parts by mass, average formula:
(Me2ViSiO1/2)0.2(MeEpSiO2/2)0.25(PhSiO3/2)0.55(HO1/2)0.005
Epoxy group-containing polysiloxane represented by the formula: 1.5 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
25.6 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane represented by 28.2 parts by mass (the above methylvinylphenylpolysiloxane, dimethylvinylsiloxy-terminated polymethylphenylsiloxane, epoxy group-containing polysiloxane The amount of silicon atom-bonded hydrogen atoms in this component is 0.89 mol with respect to a total of 1 mol of vinyl groups), 1,3-divinyl-1,1,3,3-tetramethyldisiloxane ofplatinum 1,3-divinyl-1,1,3,3-tetramethyldisiloxane solution of complex (amount in which platinum metal is 5.0 ppm by mass with respect to the present composition), 1-ethynyl-1-cyclohexanol (Amount to be 300 ppm in terms of mass unit with respect to the present composition), zinc oxide having an average primary particle size of 0.5 μm (1 type zinc oxide manufactured by Sakai Chemical Industry), 128 parts by mass And average spherical silica (Nippon Steel Materials Micron Co. HS-202) particle size 15μm by mixing 256 parts by weight, a viscosity at 25 ° C. to prepare a reactive silicone composition is 168Pa · s.
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., has a type D durometer hardness of 71, and has a viscosity of 8,400 Pa · s at 100 ° C. I found out that The conversion rate of the hydrosilylation reaction was 79%.
When the obtained thermoplastic was heated to 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a type D durometer hardness of 84 at 25 ° C., a bending strength of 23 MPa, and a total light reflectance of 91.degree. 8% (2 mm thick specimen) and 81.6% (0.2 mm thick specimen), light reflectance at a wavelength of 400 nm was 71.3%, and the linear expansion coefficient of the cured product was 90 ppm / ° C. It was. Also, die shear strength for aluminum plate and silver plated steel plate is 10.9 and 9.7 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, 4 out of 10 molding defects were confirmed. Good moldings without burrs and voids were obtained with no molding defects.
[Example 6]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methylvinylphenylpolysiloxane represented by the formula: 38.5 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methyl vinyl phenyl polysiloxane represented by the formula: 61.5 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
25.6 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane represented by 28.2 parts by mass (total 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated polymethylphenylsiloxane) The amount of silicon-bonded hydrogen atoms in this component is 0.9 moles per mole), 0.5 parts by weight of 1,3,5,7-tetramethyltetracyclosiloxane (the above methylvinylphenylpolysiloxane) The amount of silicon atom-bonded hydrogen atoms in this component is 0.0439 mol with respect to a total of 1 mol of vinyl groups of dimethylvinylsiloxy-terminated polymethylphenylsiloxane) 1,3-divinyl-1,1, platinum 1,3-divinyl-1,1,3,3-tetramethyldisiloxane solution of 3,3-tetramethyldisiloxane complex (Amount that platinum metal is 5.0 ppm in mass units with respect to the present composition), 1-ethynyl-1-cyclohexanol (amount that is 300 ppm in mass units with respect to the present composition), oleic acid (Tokyo Kasei) (Made by Kogyo) 0.2 parts by mass, zinc oxide with an average primary particle diameter of 0.5 μm (Zinc oxide manufactured by Sakai Chemical Industry) 141 parts by mass, milled glass fiber with an average cut length of 20 μm and an average fiber diameter of 3 μm (Asahi A curable silicone composition having a viscosity at 25 ° C. of 375 Pa · s was prepared by mixing 282 parts by mass of MF03JB1-20) made of fiberglass.
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., has a type D durometer hardness of 72, and has a viscosity of 10,500 Pa · s at 100 ° C. I found out that The conversion rate of the hydrosilylation reaction was 86%.
When the obtained thermoplastic was heated to 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a Type D durometer hardness of 85 at 25 ° C., a bending strength of 26 MPa, and a total light reflectance of 92.degree. 3% (2 mm thick specimen) and 82.8% (0.2 mm thick specimen), the light reflectance at a wavelength of 400 nm was 73.8%, and the linear expansion coefficient of the cured product was 72 ppm / ° C. It was. Also, the die shear strength for aluminum plate and silver plated steel plate is 8.9 and 7.9 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, molding defects were not confirmed and there were no burrs or voids. A good molded product was obtained.
[Example 7]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methyl vinyl phenyl polysiloxane 48.4 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methylvinylphenylpolysiloxane represented by the formula: 51.6 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
12.9 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 29.0 parts by mass (1 total of vinyl groups of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated polymethylphenylsiloxane) The amount of silicon atom-bonded hydrogen atoms in this component is 0.96 mol with respect to mol), 0.5 parts by mass of 1,3,5,7-tetramethyltetracyclosiloxane (the above methylvinylphenylpolysiloxane) In addition, the amount of silicon atom-bonded hydrogen atoms in this component is 0.0467 mol with respect to a total of 1 mol of vinyl groups of dimethylvinylsiloxy-terminated polymethylphenylsiloxane),platinum 1,3-divinyl-1,1 1,3-Divinyl-1,1,3,3-tetramethyldisiloxa of 1,3,3-tetramethyldisiloxane complex Solution (amount in which platinum metal is 5.0 ppm by mass with respect to the present composition), 1-ethynyl-1-cyclohexanol (amount in 300 ppm by mass with respect to the present composition), average primary particle size 128 parts by mass of 0.45 μm barium sulfate (BB-1 manufactured by Sakai Chemical Industry) and 213 parts by mass of milled glass fiber (MF03JB1-20 manufactured by Asahi Fiber Glass) with an average cut length of 20 μm and an average fiber diameter of 3 μm are mixed. A reactive silicone composition having a viscosity at 25 ° C. of 236 Pa · s was prepared.
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., has a type D durometer hardness of 64, and has a viscosity of 24,500 Pa · s at 100 ° C. I found out that The conversion rate of the hydrosilylation reaction was 82%.
When the obtained thermoplastic was heated to 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a Type D durometer hardness of 79 at 25 ° C., a bending strength of 14 MPa, and a total light reflectance of 83. 3% (2 mm thick specimen) and 66.8% (0.2 mm thick specimen), the light reflectance at a wavelength of 400 nm was 81.2%, and the linear expansion coefficient of the cured product was 105 ppm / ° C. It was. The die shear strength for aluminum plate and silver plated steel plate is 10.4 and 9.7 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, 4 out of 10 molding defects were confirmed. Good moldings without burrs and voids were obtained with no molding defects.
[Example 8]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methylvinylphenylpolysiloxane represented by the formula: 38.5 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methyl vinyl phenyl polysiloxane represented by the formula: 61.5 parts by mass, average formula:
(Me2ViSiO1/2)0.2(MeEpSiO2/2)0.25(PhSiO3/2)0.55(HO1/2)0.005
Epoxy group-containing polysiloxane represented by the formula: 1.5 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
25.6 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane represented by 28.2 parts by mass (the above methylvinylphenylpolysiloxane, dimethylvinylsiloxy-terminated polymethylphenylsiloxane, epoxy group-containing polysiloxane The amount of silicon atom-bonded hydrogen atoms in this component is 0.89 mol with respect to a total of 1 mol of vinyl groups), 1,3-divinyl-1,1,3,3-tetramethyldisiloxane ofplatinum 1,3-divinyl-1,1,3,3-tetramethyldisiloxane solution of complex (amount in which platinum metal is 5.0 ppm by mass with respect to the present composition), 1-ethynyl-1-cyclohexanol (Amount to be 300 ppm by mass with respect to the present composition), oleic acid (manufactured by Tokyo Chemical Industry Co., Ltd.), 0.2 parts by mass, an average primary particle diameter of 0.45 μm Um (BB-1 manufactured by Sakai Chemical Industry Co., Ltd.), 120 parts by mass, and 256 parts by mass of spherical silica (HS-202, manufactured by Nippon Steel Materials Micron Co., Ltd.) having an average particle size of 15 μm were mixed, and the viscosity at 25 ° C. was 197 Pa. A reactive silicone composition was prepared which was s.
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., its type D durometer hardness is 67, and its viscosity at 100 ° C. is 12,400 Pa · s. I found out that The conversion rate of the hydrosilylation reaction was 73%.
When the obtained thermoplastic was heated to 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a Type D durometer hardness of 81 at 25 ° C., a bending strength of 18 MPa, and a total light reflectance of 82. 1% (2 mm thick specimen) and 67.1% (0.2 mm thick specimen), the light reflectance at a wavelength of 400 nm was 79.4%, and the linear expansion coefficient of the cured product was 97 ppm / ° C. It was. The die shear strengths for aluminum plates and silver-plated steel plates are 12.1 and 11.4 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, molding defects were not confirmed and there were no burrs or voids. A good molded product was obtained.
[Comparative Example 1]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methyl vinyl phenyl polysiloxane 48.4 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methylvinylphenylpolysiloxane represented by the formula: 51.6 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
12.9 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
14.5 parts by mass of 1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane represented by the above formula (total 1 vinyl groups of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated polymethylphenylsiloxane The amount of silicon atom-bonded hydrogen atoms in this component is 0.48 moles per mole), average unit formula:
(Me2HSiO1/2)0.60(SiO4/2)0.40
14.5 parts by mass of silicon-bonded hydrogen atom-containing methylphenylpolysiloxane represented by the formula (in this component with respect to a total of 1 mol of the vinyl groups of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated polymethylphenylsiloxane) In an amount of 0.48 mol of silicon-bonded hydrogen atoms), 1,3-divinyl-1,1,3,3 of 1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex of platinum. 3-tetramethyldisiloxane solution (amount in which platinum metal is 5.0 ppm by mass relative to the present composition), 1-ethynyl-1-cyclohexanol (an amount in which 300 ppm by mass is present relative to the present composition) ), Titanium oxide with an average primary particle size of 0.2 μm (SX-3103 manufactured by Sakai Chemical Industry), 118 parts by mass, and spherical with an average particle size of 15 μm A curable silicone composition having a viscosity of 592 Pa · s at 25 ° C. was prepared by mixing 213 parts by mass of silica (HS-202 manufactured by Nippon Steel Materials, Micron).
When this composition was heated at 120 ° C. for 10 minutes, it was a solid whose viscosity could not be measured at 25 ° C. and had a type D durometer hardness of 75, but was a solid whose viscosity could not be measured even at 100 ° C. I understood that it was not. The conversion rate of the hydrosilylation reaction was 88%.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, the obtained solid was integrally molded with the lead frame 10 times using a transfer molding machine, but in all cases, the mold was hardly filled and was not uniform. A molded product was obtained.
The composition was directly heated at 150 ° C. for 2 hours to form a cured product. This cured product has a type D durometer hardness of 91, a bending strength of 28 MPa, a total light reflectance of 94.6% (2 mm thick test piece) and 90.8% (0.2 mm thick test piece), 400 nm. The light reflectance at a wavelength of 33.1% and the linear expansion coefficient were 89 ppm / ° C. The die shear strength for aluminum plate and silver plated steel plate is 8.2 and 6.8 N / mm, respectively.2Met.
[Comparative Example 2]
Average unit formula:
(MeViSiO2/2)0.20(Me2SiO2/2)0.20(Ph2SiO2/2)0.10(PhSiO3/2)0.50(HO1/2)0.03
100 parts by mass of methylvinylphenylpolysiloxane represented by the formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
13.3 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 33.3 parts by mass (total of 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminatedpolymethylphenylsiloxane 1 The amount of silicon-bonded hydrogen atoms in this component is 1.10 moles per mole), 1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex of platinum, 1,3- Divinyl-1,1,3,3-tetramethyldisiloxane solution (amount in which platinum metal is 5.0 ppm by mass with respect to the composition), 1-ethynyl-1-cyclohexanol (to the composition) In an amount of 300 ppm in mass unit), titanium oxide having an average primary particle size of 0.24 μm (Taipaque R-630 manufactured by Ishihara Sangyo), 127 parts by mass, Length 20 [mu] m, an average fiber diameter 3μm of milled glass fibers (MF03JB1-20 of Asahi Fiberglass) were mixed to 220 parts by mass, to prepare a curable silicone composition having a viscosity at 25 ° C. is 195Pa · s.
When this composition was heated at 120 ° C. for 10 minutes, it was found that the viscosity at 25 ° C. was 23,000 Pa · s, the type D durometer hardness was 11, and it was not a thermoplastic. The conversion rate of the hydrosilylation reaction was 79%.
Moreover, in order to manufacture the optical semiconductor device shown in FIG. 1, the liquid obtained was integrally molded with the lead frame 10 times using a transfer molding machine, but the adhesion to the mold was large in all cases, The molded part was easily deformed.
The composition was directly heated at 150 ° C. for 2 hours to form a cured product. This cured product has a type D durometer hardness of 76, a bending strength of 9.4 MPa, and a total light reflectance of 94.3% (2 mm thick test piece) and 91.2% (0.2 mm thick test piece). The light reflectance at a wavelength of 400 nm was 31.5%, and the linear expansion coefficient was 91 ppm / ° C. The die shear strength for aluminum plate and silver plated steel plate is 5.4 and 4.7 N / mm, respectively.2Met.
[Comparative Example 3]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
100 parts by mass of methylvinylphenylpolysiloxane represented by the formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
13.3 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 33.3 parts by mass (total of 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminatedpolymethylphenylsiloxane 1 The amount of silicon atom-bonded hydrogen atoms in this component is 1.15 moles per mole), platinum 1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex 1,3- Divinyl-1,1,3,3-tetramethyldisiloxane solution (amount in which platinum metal is 5.0 ppm by mass with respect to the composition), 1-ethynyl-1-cyclohexanol (to the composition) 65 parts by mass of barium titanate (HPBT-1 manufactured by Fuji Titanium Industry) with an average primary particle size of 0.5 μm, and average particles 5μm crushed quartz powder (Tatsumori Ltd. crystallites VX-52) were mixed 285 parts by mass of, to prepare a curable silicone composition having a viscosity at 25 ° C. is 330 Pa · s.
When this composition was heated at 120 ° C. for 10 minutes, it was a solid whose viscosity could not be measured at 25 ° C., had a type D durometer hardness of 62, a viscosity at 100 ° C. of 3,900 Pa · s, and was thermoplastic. It turned out to be a body. The conversion rate of the hydrosilylation reaction was 84%.
When the obtained thermoplastic was heated at 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a Type D durometer hardness of 85 at 25 ° C., a bending strength of 19 MPa, and a total light reflectance of 55. 4% (2 mm thick specimen) and 51.7% (0.2 mm thick specimen), the light reflectance at a wavelength of 400 nm was 34.5%, and the linear expansion coefficient of the cured product was 93 ppm / ° C. It was. Also, the die shear strength for aluminum plate and silver-plated steel plate is 7.0 and 6.1 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, molding failure was confirmed 5 times out of 10 times. Good moldings free from burrs and voids were obtained.
[Comparative Example 4]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
100 parts by mass of methylvinylphenylpolysiloxane represented by the formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
13.3 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 33.3 parts by mass (total of 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminatedpolymethylphenylsiloxane 1 The amount of silicon atom-bonded hydrogen atoms in this component is 1.15 moles per mole), platinum 1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex 1,3- Divinyl-1,1,3,3-tetramethyldisiloxane solution (amount in which platinum metal is 5.0 ppm by mass with respect to the composition), 1-ethynyl-1-cyclohexanol (to the composition) 224 parts by mass of titanium oxide with an average primary particle size of 0.24 μm (Taipaque R-630, manufactured by Ishihara Sangyo), and average particles Mixing the crushed quartz powder (Tatsumori Ltd. crystallites VX-52) 117 parts by weight of 5 [mu] m, to prepare a curable silicone composition having a viscosity at 25 ° C. is 1,150Pa · s.
When this composition was heated at 120 ° C. for 10 minutes, it was a solid whose viscosity could not be measured at 25 ° C., and although the type D durometer hardness was 69, the viscosity at 100 ° C. was as high as 2,000,000 Pa · s. It was found that it was not a good plastic. The conversion rate of the hydrosilylation reaction was 86%.
When the obtained solid was heated at 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a Type D durometer hardness of 87 at 25 ° C., a bending strength of 20 MPa, and a total light reflectance of 93.degree. 5% (2 mm thickness test piece) and 92.8% (0.2 mm thickness test piece), the light reflectance at a wavelength of 400 nm was 30.9%, and the linear expansion coefficient of the cured product was 115 ppm / ° C. It was. The die shear strengths for aluminum plates and silver-plated steel plates are 6.7 and 5.8 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the above thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, 5 out of 10 molding defects were confirmed. There were many voids even in the case where there was no defect, and a good molded product could not be obtained.
[Comparative Example 5]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
100 parts by mass of methylvinylphenylpolysiloxane represented by the formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
13.3 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 33.3 parts by mass (total of 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminatedpolymethylphenylsiloxane 1 The amount of silicon atom-bonded hydrogen atoms in this component is 1.15 moles per mole), platinum 1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex 1,3- Divinyl-1,1,3,3-tetramethyldisiloxane solution (amount in which platinum metal is 5.0 ppm by mass with respect to the composition), 1-ethynyl-1-cyclohexanol (to the composition) In an amount of 300 ppm in mass unit), 102 parts by mass of barium titanate (HPBT-1 manufactured by Fuji Titanium Industry) having an average primary particle size of 0.5 μm, and average particles Were mixed crushed quartz powder (Tatsumori Ltd. crystallites VX-52) 510 parts by weight of diameter 5 [mu] m, a mixture of powdered was obtained.
When this composition was heated at 120 ° C. for 10 minutes, it was a solid whose viscosity could not be measured at 25 ° C., a non-uniform solid, and a solid whose viscosity could not be measured even at 100 ° C. and was not a thermoplastic. all right. The conversion rate of the hydrosilylation reaction was 82%.
Moreover, in order to manufacture the optical semiconductor device shown in FIG. 1, when the obtained solid was integrally molded with the lead frame 10 times using a transfer molding machine, all of the mold unfilled portions were recognized, and Many voids were generated, and a good molded product could not be obtained.
また、反応性熱可塑体および硬化物の硬さは、ＪＩＳ Ｋ ７２１５—１９８６「プラスチックのデュロメータ硬さ試験方法」に規定のタイプＤデュロメータにより測定した。
また、硬化物の曲げ強さは、ＪＩＳ Ｋ ６９１１—１９９５「熱硬化性プラスチック一般試験方法」に規定の方法により測定した。
また、硬化物の全光線反射率は、ＪＩＳ Ｋ ７３７５：２００８「プラスチック−全光線透過率及び全光線反射率の求め方」に規定の方法により測定した。試験片は２ｍｍ厚の物を使用した。
また、硬化物の隠蔽性は０．２ｍｍ厚の試験片を用いて上記全光線反射率測定により評価した。
また、硬化物の４００ｎｍの波長での光反射率は上記全光線反射率で作成した試験片を用いて、分光光度計（島津製作所製のＵＶ−３１００ＰＣ）により測定した。
また、硬化物の線膨張率は、２５~２００℃の範囲内での平均線膨張率を、ＪＩＳ Ｋ ７１９７—１９９１「プラスチックの熱機械分析による線膨張率の試験方法」に規定の方法により測定した。
また、２５ｍｍ×７５ｍｍのアルミニウム板上に、反応性シリコーン組成物をディスペンサーにより約１００ｍｇづつを５ヶ所に塗布し、該組成物に厚さ１ｍｍの６ｍｍ角のアルミニウム製チップを被せ、１ｋｇの板により圧着した。次いで、これを１５０℃で２時間加熱し、反応性シリコーン組成物を硬化した。室温に冷却した後、シェア強度測定装置（西進商事株式会社製のボンドテスターＳＳ−１００ＫＰ）によりダイシェア強度を測定した。また、上記と同様にして、銀メッキ鋼板に対する銀メッキ鋼板製チップのダイシェア強度についても測定した。
また、本組成物の金型離型性はトランスファー成型機を用いて成型温度１２０℃、成形時間５分の条件でリードフレームとの一体成型を１０回行い、成型後の光半導体装置にクラック及びリードフレームからの剥離等の成型不良が発生した回数の確認により評価した。
また、ヒドロシリル化反応の転化率は、示差走査熱量計によって各状態での反応熱量を求め、その差から算出した。
［実施例１］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン １００質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １３．３質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ３３．３質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が１．１５モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．５μｍのチタン酸バリウム（富士チタン工業製のＨＰＢＴ−１） １２２質量部、および平均粒子径５μｍの破砕石英粉末（龍森製のクリスタライトＶＸ−５２） ２２０質量部を混合して、２５℃での粘度が３８０Ｐａ・ｓである反応性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度が測定不能な固体であり、タイプＤデュロメータ硬さが６３であり、１００℃での粘度が６００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は８５％であった。
得られた熱可塑体を１５０℃で加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃で粘度測定不能な固体であり、２５℃でのタイプＤデュロメータ硬さが８２であり、曲げ強さが１５ＭＰａ、全光線反射率が９３．５％（２ｍｍ厚の試験片）と８８．１％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７３．２％、硬化物の線膨張率が１１５ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、７．９および６．９Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、１０回中４回成型不良が確認されたが、成型不良がなかった物はバリやボイドがなく良好な成型物が得られた。
［実施例２］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ４８．４質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ５１．６質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２（ＭｅＥｐＳｉＯ２／２）０．２５（ＰｈＳｉＯ３／２）０．５５（ＨＯ１／２）０．００５
で表されるエポキシ基含有ポリシロキサン １．５質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １２．９質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２９．０質量部（上記のメチルビニルフェニルポリシロキサン、ジメチルビニルシロキシ末端ポリメチルフェニルシロキサン、エポキシ基含有ポリシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．９４モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、オレイン酸（東京化成工業製） ０．２質量部、平均一次粒子径０．５μｍのチタン酸バリウム（富士チタン工業製のＨＰＢＴ−１） １１８質量部、および平均粒子径１５μｍの球状シリカ（新日鉄マテリアルズ マイクロン社製のＨＳ−２０２）２１３質量部を混合して、２５℃での粘度が１７０Ｐａ・ｓである硬化性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが６１であり、１００℃での粘度が５，９００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は７９％であった。
得られた熱可塑体を１５０℃に加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃で粘度測定不能な固体であり、２５℃でのタイプＤデュロメータ硬さが８６であり、曲げ強さが２４ＭＰａ、全光線反射率が９３．３％（２ｍｍ厚の試験片）と８７．７％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７４．１％、硬化物の線膨張率が１０１ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、１１．２および９．１Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、成型不良は確認されず、バリやボイドのない良好な成形物が得られた。
［実施例３］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ４８．４質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ５１．６質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １２．９質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２９．０質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．９６モルとなる量）、１，３，５，７−テトラメチルテトラシクロシロキサン ０．５質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．０４６７モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．５μｍのチタン酸バリウム（富士チタン工業製のＨＰＢＴ−１） １１８質量部、および平均カット長２０μｍ、平均ファイバー径３μｍのミルドガラスファイバー（旭ファイバーグラス製のＭＦ０３ＪＢ１−２０）２１３質量部を混合して、２５℃での粘度が１５０Ｐａ・ｓである反応性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが６９であり、１００℃での粘度が１９，５００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は８６％であった。
得られた熱可塑体を１５０℃に加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８３であり、曲げ強さが１８ＭＰａ、全光線反射率が９４．１％（２ｍｍ厚の試験片）と８８．２％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７３．６％、硬化物の線膨張率が１０３ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、９．２および７．６Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、１０回中５回成型不良が確認されたが、成型不良がなかった物はバリやボイドがなく良好な成型物が得られた。
［実施例４］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ３８．５質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ６１．５質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １９．４質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２８．２質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．９２モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、オレイン酸（東京化成工業製） ０．２質量部、平均一次粒子径０．５μｍの酸化亜鉛（堺化学工業製の酸化亜鉛１種）１１８質量部、および平均粒子径５μｍの破砕石英粉末（山森土本鉱業所製のシルシックＳＡＢ−５００） ２１３質量部を混合して、２５℃での粘度が４５０Ｐａ・ｓである反応性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが７０であり、１００℃での粘度が１６，０００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は８９％であった。
得られた熱可塑体を１５０℃で加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８４であり、曲げ強さが２１ＭＰａ、全光線反射率が９２．３％（２ｍｍ厚の試験片）と８２．４％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７１．５％、硬化物の線膨張率が１２１ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、８．８および７．５Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、成型不良は確認されず、バリやボイドのない良好な成形物が得られた。
［実施例５］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ３８．５質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ６１．５質量部、平均式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２（ＭｅＥｐＳｉＯ２／２）０．２５（ＰｈＳｉＯ３／２）０．５５（ＨＯ１／２）０．００５
で表されるエポキシ基含有ポリシロキサン １．５質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン ２５．６質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２８．２質量部（上記のメチルビニルフェニルポリシロキサン、ジメチルビニルシロキシ末端ポリメチルフェニルシロキサン、エポキシ基含有ポリシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．８９モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．５μｍの酸化亜鉛（堺化学工業製の酸化亜鉛１種） １２８質量部、および平均粒子径１５μｍの球状シリカ（新日鉄マテリアルズ マイクロン社製のＨＳ−２０２） ２５６質量部を混合して、２５℃での粘度が１６８Ｐａ・ｓである反応性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが７１であり、１００℃での粘度が８，４００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は７９％であった。
得られた熱可塑体を１５０℃に加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８４であり、曲げ強さが２３ＭＰａ、全光線反射率が９１．８％（２ｍｍ厚の試験片）と８１．６％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７１．３％、硬化物の線膨張率が９０ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、１０．９および９．７Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、１０回中４回成型不良が確認されたが、成型不良がなかった物はバリやボイドがなく良好な成型物が得られた。
［実施例６］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ３８．５質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ６１．５質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン ２５．６質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２８．２質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．９モルとなる量）、１，３，５，７−テトラメチルテトラシクロシロキサン ０．５質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．０４３９モルとなる量）白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、オレイン酸（東京化成工業製） ０．２質量部、平均一次粒子径０．５μｍの酸化亜鉛（堺化学工業製の酸化亜鉛１種） １４１質量部、および平均カット長２０μｍ、平均ファイバー径３μｍのミルドガラスファイバー（旭ファイバーグラス製のＭＦ０３ＪＢ１−２０） ２８２質量部を混合して、２５℃での粘度が３７５Ｐａ・ｓである硬化性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが７２であり、１００℃での粘度が１０，５００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は８６％であった。
得られた熱可塑体を１５０℃に加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８５であり、曲げ強さが２６ＭＰａ、全光線反射率が９２．３％（２ｍｍ厚の試験片）と８２．８％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７３．８％、硬化物の線膨張率が７２ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、８．９および７．９Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、成型不良は確認されず、バリやボイドのない良好な成形物が得られた。
［実施例７］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ４８．４質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ５１．６質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １２．９質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２９．０質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．９６モルとなる量）、１，３，５，７−テトラメチルテトラシクロシロキサン ０．５質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．０４６７モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．４５μｍの硫酸バリウム（堺化学工業製のＢＢ−１）１２８質量部、および平均カット長２０μｍ、平均ファイバー径３μｍのミルドガラスファイバー（旭ファイバーグラス製のＭＦ０３ＪＢ１−２０） ２１３質量部を混合して、２５℃での粘度が２３６Ｐａ・ｓである反応性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが６４であり、１００℃での粘度が２４，５００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は８２％であった。
得られた熱可塑体を１５０℃に加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが７９であり、曲げ強さが１４ＭＰａ、全光線反射率が８３．３％（２ｍｍ厚の試験片）と６６．８％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が８１．２％、硬化物の線膨張率が１０５ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、１０．４および９．７Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、１０回中４回成型不良が確認されたが、成型不良がなかった物はバリやボイドがなく良好な成型物が得られた。
［実施例８］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ３８．５質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ６１．５質量部、平均式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２（ＭｅＥｐＳｉＯ２／２）０．２５（ＰｈＳｉＯ３／２）０．５５（ＨＯ１／２）０．００５
で表されるエポキシ基含有ポリシロキサン １．５質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン ２５．６質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ２８．２質量部（上記のメチルビニルフェニルポリシロキサン、ジメチルビニルシロキシ末端ポリメチルフェニルシロキサン、エポキシ基含有ポリシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．８９モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、オレイン酸（東京化成工業製） ０．２質量部、平均一次粒子径０．４５μｍの硫酸バリウム（堺化学工業製のＢＢ−１） １２０質量部、および平均粒子径１５μｍの球状シリカ（新日鉄マテリアルズ マイクロン社製のＨＳ−２０２） ２５６質量部を混合して、２５℃での粘度が１９７Ｐａ・ｓである反応性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが６７であり、１００℃での粘度が１２，４００Ｐａ・ｓである熱可塑体であることがわかった。ヒドロシリル化反応の転化率は７３％であった。
得られた熱可塑体を１５０℃に加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８１であり、曲げ強さが１８ＭＰａ、全光線反射率が８２．１％（２ｍｍ厚の試験片）と６７．１％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が７９．４％、硬化物の線膨張率が９７ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、１２．１および１１．４Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、成型不良は確認されず、バリやボイドのない良好な成形物が得られた。
［比較例１］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン ４８．４質量部、平均単位式：
（Ｍｅ２ＶｉＳｉＯ１／２）０．２０（ＰｈＳｉＯ３／２）０．８０（ＨＯ１／２）０．０１
で表されるメチルビニルフェニルポリシロキサン ５１．６質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １２．９質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン １４．５質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．４８モルとなる量）、平均単位式：
（Ｍｅ２ＨＳｉＯ１／２）０．６０（ＳｉＯ４／２）０．４０
で表されるケイ素原子結合水素原子含有メチルフェニルポリシロキサン １４．５質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．４８モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．２μｍの酸化チタン（堺化学工業製のＳＸ−３１０３） １１８質量部、および平均粒子径１５μｍの球状シリカ（新日鉄マテリアルズ マイクロン社製のＨＳ−２０２） ２１３質量部を混合して、２５℃での粘度が５９２Ｐａ・ｓである硬化性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが７５であるものの、１００℃でも粘度測定不能な固体状であり、熱可塑体でないことがわかった。ヒドロシリル化反応の転化率は８８％であった。
また、図１で示される光半導体装置を製造するため、得られた固体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったが、全てにおいて金型にほとんど充填されず、不均一な成形物が得られた。
また、この組成物を直接１５０℃で２時間加熱して硬化物を形成した。この硬化物は、タイプＤデュロメータ硬さが９１、曲げ強度が２８ＭＰａ、全光線反射率が９４．６％（２ｍｍ厚の試験片）と９０．８％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が３３．１％、線膨張率が８９ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、８．２および６．８Ｎ／ｍｍ２であった。
［比較例２］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２０（Ｍｅ２ＳｉＯ２／２）０．２０（Ｐｈ２ＳｉＯ２／２）０．１０（ＰｈＳｉＯ３／２）０．５０（ＨＯ１／２）０．０３
で表されるメチルビニルフェニルポリシロキサン １００質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １３．３質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ３３．３質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が１．１０モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．２４μｍの酸化チタン（石原産業製のタイペークＲ−６３０） １２７質量部、および平均カット長２０μｍ、平均ファイバー径３μｍのミルドガラスファイバー（旭ファイバーグラス製のＭＦ０３ＪＢ１−２０） ２２０質量部を混合して、２５℃での粘度が１９５Ｐａ・ｓである硬化性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃での粘度が２３，０００Ｐａ・ｓであり、タイプＤデュロメータ硬さが１１であり、熱可塑体でないことがわかった。ヒドロシリル化反応の転化率は７９％であった。
また、図１で示される光半導体装置を製造するため、得られた液体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったが、全てにおいて金型への付着が大きく、また、成形部分が容易に変形した。
また、この組成物を直接１５０℃で２時間加熱して硬化物を形成した。この硬化物は、タイプＤデュロメータ硬さが７６、曲げ強度が９．４ＭＰａ、全光線反射率が９４．３％（２ｍｍ厚の試験片）と９１．２％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が３１．５％、線膨張率が９１ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、５．４および４．７Ｎ／ｍｍ２であった。
［比較例３］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン １００質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １３．３質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ３３．３質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が１．１５モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．５μｍのチタン酸バリウム（富士チタン工業製のＨＰＢＴ−１） ６５質量部、および平均粒子径５μｍの破砕石英粉末（龍森製のクリスタライトＶＸ−５２） ２８５質量部を混合して、２５℃での粘度が３３０Ｐａ・ｓである硬化性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが６２であり、１００℃での粘度が３，９００Ｐａ・ｓであり、熱可塑体であることがわかった。ヒドロシリル化反応の転化率は８４％であった。
得られた熱可塑体を１５０℃で加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８５であり、曲げ強さが１９ＭＰａ、全光線反射率が５５．４％（２ｍｍ厚の試験片）と５１．７％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が３４．５％、硬化物の線膨張率が９３ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、７．０および６．１Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、１０回中５回成型不良が確認されたが、バリやボイドのない良好な成形物が得られた。
［比較例４］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン １００質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １３．３質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ３３．３質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が１．１５モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．２４μｍの酸化チタン（石原産業製のタイペークＲ−６３０） ２２４質量部、および平均粒子径５μｍの破砕石英粉末（龍森製のクリスタライトＶＸ−５２） １１７質量部を混合し、２５℃での粘度が１，１５０Ｐａ・ｓである硬化性シリコーン組成物を調製した。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、タイプＤデュロメータ硬さが６９であるものの、１００℃での粘度が２，０００，０００Ｐａ・ｓと高く、良好な可塑体でないことがわかった。ヒドロシリル化反応の転化率は８６％であった。
得られた固体を１５０℃で加熱すると、流動化した後、流動性が失われた。１５０℃で１時間加熱して得られた硬化物は３００℃以下で流動性がなく、２５℃でのタイプＤデュロメータ硬さが８７であり、曲げ強さが２０ＭＰａ、全光線反射率が９３．５％（２ｍｍ厚の試験片）と９２．８％（０．２ｍｍ厚の試験片）、４００ｎｍの波長での光反射率が３０．９％、硬化物の線膨張率が１１５ｐｐｍ／℃であった。また、アルミニウム板および銀メッキ鋼板に対するダイシェア強度は、それぞれ、６．７および５．８Ｎ／ｍｍ２であった。
また、図１で示される光半導体装置を製造するため、上記熱可塑体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、１０回中５回成型不良が確認され、成型不良がなかった物にも多数のボイドがあり良好な成形物は得られなかった。
［比較例５］
平均単位式：
（ＭｅＶｉＳｉＯ２／２）０．２５（Ｐｈ２ＳｉＯ２／２）０．３０（ＰｈＳｉＯ３／２）０．４５（ＨＯ１／２）０．０２
で表されるメチルビニルフェニルポリシロキサン １００質量部、平均式：
ＶｉＭｅ２ＳｉＯ（ＭｅＰｈＳｉＯ）１７．５ＳｉＶｉＭｅ２
で表されるジメチルビニルシロキシ末端ポリメチルフェニルシロキサン １３．３質量部、式：
（ＨＭｅ２ＳｉＯ）２ＳｉＰｈ２
で表される１，１，５，５−テトラメチル−３，３−ジフェニルトリシロキサン ３３．３質量部（上記のメチルビニルフェニルポリシロキサンおよびジメチルビニルシロキシ末端ポリメチルフェニルシロキサンのビニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が１．１５モルとなる量）、白金の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン錯体の１，３−ジビニル−１，１，３，３−テトラメチルジシロキサン溶液（本組成物に対して白金金属が質量単位で５．０ｐｐｍとなる量）、１−エチニル−１−シクロヘキサノール（本組成物に対して質量単位で３００ｐｐｍとなる量）、平均一次粒子径０．５μｍのチタン酸バリウム（富士チタン工業製のＨＰＢＴ−１） １０２質量部、および平均粒子径５μｍの破砕石英粉末（龍森製のクリスタライトＶＸ−５２） ５１０質量部を混合したところ、粉体状の混合物が得られた。
この組成物を１２０℃で１０分間加熱したところ、２５℃で粘度測定不能な固体であり、不均一な固体であり、また１００℃でも粘度測定不能な固体状であり、熱可塑体でないことがわかった。ヒドロシリル化反応の転化率は８２％であった。
また、図１で示される光半導体装置を製造するため、得られた固体をトランスファー成形機を用いてリードフレームと一体成型を１０回行ったところ、全てにおいて金型未充填部が認められ、また多数のボイドが生じ、良好な成形物は得られなかった。 The curable silicone composition, reactive thermoplastic, cured product, and optical semiconductor device of the present invention will be described in detail with reference to examples. In the formulae, Me, Ph, Vi, and Ep represent a methyl group, a phenyl group, a vinyl group, and a 3-glycidoxypropyl group, respectively.
The hardness of the reactive thermoplastic and the cured product was measured with a type D durometer specified in JIS K 7215-1986 “Plastic Durometer Hardness Test Method”.
Further, the bending strength of the cured product was measured by the method specified in JIS K 6911-1995 “General Test Method for Thermosetting Plastics”.
Further, the total light reflectance of the cured product was measured by a method specified in JIS K 7375: 2008 “Plastics—How to obtain total light transmittance and total light reflectance”. A test piece having a thickness of 2 mm was used.
Further, the concealability of the cured product was evaluated by measuring the total light reflectance using a test piece having a thickness of 0.2 mm.
Further, the light reflectance at a wavelength of 400 nm of the cured product was measured with a spectrophotometer (UV-3100PC manufactured by Shimadzu Corporation) using the test piece prepared with the above total light reflectance.
The linear expansion coefficient of the cured product is measured by measuring the average linear expansion coefficient in the range of 25 to 200 ° C. according to the method specified in JIS K 7197-1991 “Test method for linear expansion coefficient by thermomechanical analysis of plastics”. did.
In addition, about 100 mg of the reactive silicone composition was applied to 5 locations on a 25 mm × 75 mm aluminum plate with a dispenser, and the composition was covered with 6 mm square aluminum chips having a thickness of 1 mm. Crimped. This was then heated at 150 ° C. for 2 hours to cure the reactive silicone composition. After cooling to room temperature, the die shear strength was measured with a shear strength measuring device (Bond Tester SS-100KP manufactured by Seishin Shoji Co., Ltd.). Moreover, it measured similarly about the die shear strength of the chip | tip made from the silver plating steel plate with respect to a silver plating steel plate similarly to the above.
In addition, the mold releasability of this composition is 10 times integral molding with a lead frame using a transfer molding machine at a molding temperature of 120 ° C. and a molding time of 5 minutes. Evaluation was made by confirming the number of molding defects such as peeling from the lead frame.
Also, the conversion rate of the hydrosilylation reaction was calculated from the difference obtained by obtaining the reaction heat in each state with a differential scanning calorimeter.
[Example 1]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
100 parts by mass of methylvinylphenylpolysiloxane represented by the formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
13.3 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 33.3 parts by mass (total of 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated
When this composition was heated at 120 ° C. for 10 minutes, it was a solid whose viscosity could not be measured at 25 ° C., a type D durometer hardness of 63, and a viscosity of 100 Pa · s at 100 ° C. I found out. The conversion rate of the hydrosilylation reaction was 85%.
When the obtained thermoplastic was heated at 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour is a solid whose viscosity cannot be measured at 300 ° C., the type D durometer hardness at 25 ° C. is 82, the bending strength is 15 MPa, and the total light reflectance is 93.5% (2 mm thick specimen) and 88.1% (0.2 mm thick specimen), light reflectance at a wavelength of 400 nm is 73.2%, and the linear expansion coefficient of the cured product is 115 ppm / ° C. Met. The die shear strengths for aluminum plates and silver-plated steel plates are 7.9 and 6.9 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, 4 out of 10 molding defects were confirmed. Good moldings without burrs and voids were obtained with no molding defects.
[Example 2]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methyl vinyl phenyl polysiloxane 48.4 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methylvinylphenylpolysiloxane represented by the formula: 51.6 parts by mass, average unit formula:
(Me2ViSiO1/2)0.2(MeEpSiO2/2)0.25(PhSiO3/2)0.55(HO1/2)0.005
Epoxy group-containing polysiloxane represented by the formula: 1.5 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
12.9 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 29.0 parts by mass (the above methylvinylphenylpolysiloxane, dimethylvinylsiloxy-terminated polymethylphenylsiloxane, epoxy group-containing polysiloxane The amount of silicon atom-bonded hydrogen atoms in this component is 0.94 mol with respect to a total of 1 mol of vinyl groups), 1,3-divinyl-1,1,3,3-tetramethyldisiloxane of
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., its type D durometer hardness is 61, and its viscosity at 100 ° C. is 5,900 Pa · s. I found out that The conversion rate of the hydrosilylation reaction was 79%.
When the obtained thermoplastic was heated to 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour is a solid whose viscosity cannot be measured at 300 ° C., has a type D durometer hardness of 86 at 25 ° C., a bending strength of 24 MPa, and a total light reflectance. 93.3% (2 mm thickness test piece) and 87.7% (0.2 mm thickness test piece), light reflectance at a wavelength of 400 nm is 74.1%, and the linear expansion coefficient of the cured product is 101 ppm / ° C. Met. Also, the die shear strength for aluminum plate and silver plated steel plate is 11.2 and 9.1 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, molding defects were not confirmed and there were no burrs or voids. A good molded product was obtained.
[Example 3]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methyl vinyl phenyl polysiloxane 48.4 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methylvinylphenylpolysiloxane represented by the formula: 51.6 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
12.9 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 29.0 parts by mass (1 total of vinyl groups of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated polymethylphenylsiloxane) The amount of silicon atom-bonded hydrogen atoms in this component is 0.96 mol with respect to mol), 0.5 parts by mass of 1,3,5,7-tetramethyltetracyclosiloxane (the above methylvinylphenylpolysiloxane) In addition, the amount of silicon atom-bonded hydrogen atoms in this component is 0.0467 mol with respect to a total of 1 mol of vinyl groups of dimethylvinylsiloxy-terminated polymethylphenylsiloxane), platinum 1,3-divinyl-1,1 1,3-Divinyl-1,1,3,3-tetramethyldisiloxa of 1,3,3-tetramethyldisiloxane complex Solution (amount in which platinum metal is 5.0 ppm by mass with respect to the present composition), 1-ethynyl-1-cyclohexanol (amount in 300 ppm by mass with respect to the present composition), average primary particle size Mixing 118 parts by mass of 0.5 μm barium titanate (HPBT-1 manufactured by Fuji Titanium Industry Co., Ltd.) and 213 parts by mass of milled glass fiber (MF03JB1-20 manufactured by Asahi Fiber Glass Co., Ltd.) with an average cut length of 20 μm and an average fiber diameter of 3 μm Then, a reactive silicone composition having a viscosity at 25 ° C. of 150 Pa · s was prepared.
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., has a type D durometer hardness of 69, and has a viscosity of 19,500 Pa · s at 100 ° C. I found out that The conversion rate of the hydrosilylation reaction was 86%.
When the obtained thermoplastic was heated to 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a Type D durometer hardness of 83 at 25 ° C., a bending strength of 18 MPa, and a total light reflectance of 94. 1% (2 mm thick test piece) and 88.2% (0.2 mm thick test piece), the light reflectance at a wavelength of 400 nm was 73.6%, and the linear expansion coefficient of the cured product was 103 ppm / ° C. It was. The die shear strengths for aluminum plates and silver-plated steel plates are 9.2 and 7.6 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, molding failure was confirmed 5 times out of 10 times. Good moldings without burrs and voids were obtained with no molding defects.
[Example 4]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methylvinylphenylpolysiloxane represented by the formula: 38.5 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methyl vinyl phenyl polysiloxane represented by the formula: 61.5 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
19.4 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane represented by 28.2 parts by mass (total 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated polymethylphenylsiloxane) The amount of silicon-bonded hydrogen atoms in this component to 0.92 mol), 1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex of platinum, Divinyl-1,1,3,3-tetramethyldisiloxane solution (amount in which platinum metal is 5.0 ppm by mass with respect to the composition), 1-ethynyl-1-cyclohexanol (to the composition) Oleic acid (manufactured by Tokyo Chemical Industry Co., Ltd.) 0.2 parts by mass, zinc oxide having an average primary particle size of 0.5 μm (
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., has a type D durometer hardness of 70, and has a viscosity of 16,000 Pa · s at 100 ° C. I found out that The conversion rate of the hydrosilylation reaction was 89%.
When the obtained thermoplastic was heated at 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a type D durometer hardness of 84 at 25 ° C., a bending strength of 21 MPa, and a total light reflectance of 92.degree. 3% (2 mm thick specimen) and 82.4% (0.2 mm thick specimen), the light reflectance at a wavelength of 400 nm was 71.5%, and the linear expansion coefficient of the cured product was 121 ppm / ° C. It was. The die shear strength for aluminum plate and silver plated steel plate is 8.8 and 7.5 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, molding defects were not confirmed and there were no burrs or voids. A good molded product was obtained.
[Example 5]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methylvinylphenylpolysiloxane represented by the formula: 38.5 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methyl vinyl phenyl polysiloxane represented by the formula: 61.5 parts by mass, average formula:
(Me2ViSiO1/2)0.2(MeEpSiO2/2)0.25(PhSiO3/2)0.55(HO1/2)0.005
Epoxy group-containing polysiloxane represented by the formula: 1.5 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
25.6 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane represented by 28.2 parts by mass (the above methylvinylphenylpolysiloxane, dimethylvinylsiloxy-terminated polymethylphenylsiloxane, epoxy group-containing polysiloxane The amount of silicon atom-bonded hydrogen atoms in this component is 0.89 mol with respect to a total of 1 mol of vinyl groups), 1,3-divinyl-1,1,3,3-tetramethyldisiloxane of
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., has a type D durometer hardness of 71, and has a viscosity of 8,400 Pa · s at 100 ° C. I found out that The conversion rate of the hydrosilylation reaction was 79%.
When the obtained thermoplastic was heated to 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a type D durometer hardness of 84 at 25 ° C., a bending strength of 23 MPa, and a total light reflectance of 91.degree. 8% (2 mm thick specimen) and 81.6% (0.2 mm thick specimen), light reflectance at a wavelength of 400 nm was 71.3%, and the linear expansion coefficient of the cured product was 90 ppm / ° C. It was. Also, die shear strength for aluminum plate and silver plated steel plate is 10.9 and 9.7 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, 4 out of 10 molding defects were confirmed. Good moldings without burrs and voids were obtained with no molding defects.
[Example 6]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methylvinylphenylpolysiloxane represented by the formula: 38.5 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methyl vinyl phenyl polysiloxane represented by the formula: 61.5 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
25.6 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane represented by 28.2 parts by mass (total 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated polymethylphenylsiloxane) The amount of silicon-bonded hydrogen atoms in this component is 0.9 moles per mole), 0.5 parts by weight of 1,3,5,7-tetramethyltetracyclosiloxane (the above methylvinylphenylpolysiloxane) The amount of silicon atom-bonded hydrogen atoms in this component is 0.0439 mol with respect to a total of 1 mol of vinyl groups of dimethylvinylsiloxy-terminated polymethylphenylsiloxane) 1,3-divinyl-1,1, platinum 1,3-divinyl-1,1,3,3-tetramethyldisiloxane solution of 3,3-tetramethyldisiloxane complex (Amount that platinum metal is 5.0 ppm in mass units with respect to the present composition), 1-ethynyl-1-cyclohexanol (amount that is 300 ppm in mass units with respect to the present composition), oleic acid (Tokyo Kasei) (Made by Kogyo) 0.2 parts by mass, zinc oxide with an average primary particle diameter of 0.5 μm (Zinc oxide manufactured by Sakai Chemical Industry) 141 parts by mass, milled glass fiber with an average cut length of 20 μm and an average fiber diameter of 3 μm (Asahi A curable silicone composition having a viscosity at 25 ° C. of 375 Pa · s was prepared by mixing 282 parts by mass of MF03JB1-20) made of fiberglass.
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., has a type D durometer hardness of 72, and has a viscosity of 10,500 Pa · s at 100 ° C. I found out that The conversion rate of the hydrosilylation reaction was 86%.
When the obtained thermoplastic was heated to 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a Type D durometer hardness of 85 at 25 ° C., a bending strength of 26 MPa, and a total light reflectance of 92.degree. 3% (2 mm thick specimen) and 82.8% (0.2 mm thick specimen), the light reflectance at a wavelength of 400 nm was 73.8%, and the linear expansion coefficient of the cured product was 72 ppm / ° C. It was. Also, the die shear strength for aluminum plate and silver plated steel plate is 8.9 and 7.9 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, molding defects were not confirmed and there were no burrs or voids. A good molded product was obtained.
[Example 7]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methyl vinyl phenyl polysiloxane 48.4 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methylvinylphenylpolysiloxane represented by the formula: 51.6 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
12.9 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 29.0 parts by mass (1 total of vinyl groups of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated polymethylphenylsiloxane) The amount of silicon atom-bonded hydrogen atoms in this component is 0.96 mol with respect to mol), 0.5 parts by mass of 1,3,5,7-tetramethyltetracyclosiloxane (the above methylvinylphenylpolysiloxane) In addition, the amount of silicon atom-bonded hydrogen atoms in this component is 0.0467 mol with respect to a total of 1 mol of vinyl groups of dimethylvinylsiloxy-terminated polymethylphenylsiloxane),
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., has a type D durometer hardness of 64, and has a viscosity of 24,500 Pa · s at 100 ° C. I found out that The conversion rate of the hydrosilylation reaction was 82%.
When the obtained thermoplastic was heated to 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a Type D durometer hardness of 79 at 25 ° C., a bending strength of 14 MPa, and a total light reflectance of 83. 3% (2 mm thick specimen) and 66.8% (0.2 mm thick specimen), the light reflectance at a wavelength of 400 nm was 81.2%, and the linear expansion coefficient of the cured product was 105 ppm / ° C. It was. The die shear strength for aluminum plate and silver plated steel plate is 10.4 and 9.7 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, 4 out of 10 molding defects were confirmed. Good moldings without burrs and voids were obtained with no molding defects.
[Example 8]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methylvinylphenylpolysiloxane represented by the formula: 38.5 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methyl vinyl phenyl polysiloxane represented by the formula: 61.5 parts by mass, average formula:
(Me2ViSiO1/2)0.2(MeEpSiO2/2)0.25(PhSiO3/2)0.55(HO1/2)0.005
Epoxy group-containing polysiloxane represented by the formula: 1.5 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
25.6 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane represented by 28.2 parts by mass (the above methylvinylphenylpolysiloxane, dimethylvinylsiloxy-terminated polymethylphenylsiloxane, epoxy group-containing polysiloxane The amount of silicon atom-bonded hydrogen atoms in this component is 0.89 mol with respect to a total of 1 mol of vinyl groups), 1,3-divinyl-1,1,3,3-tetramethyldisiloxane of
When this composition is heated at 120 ° C. for 10 minutes, it is a solid whose viscosity cannot be measured at 25 ° C., its type D durometer hardness is 67, and its viscosity at 100 ° C. is 12,400 Pa · s. I found out that The conversion rate of the hydrosilylation reaction was 73%.
When the obtained thermoplastic was heated to 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a Type D durometer hardness of 81 at 25 ° C., a bending strength of 18 MPa, and a total light reflectance of 82. 1% (2 mm thick specimen) and 67.1% (0.2 mm thick specimen), the light reflectance at a wavelength of 400 nm was 79.4%, and the linear expansion coefficient of the cured product was 97 ppm / ° C. It was. The die shear strengths for aluminum plates and silver-plated steel plates are 12.1 and 11.4 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, molding defects were not confirmed and there were no burrs or voids. A good molded product was obtained.
[Comparative Example 1]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
Methyl vinyl phenyl polysiloxane 48.4 parts by mass, average unit formula:
(Me2ViSiO1/2)0.20(PhSiO3/2)0.80(HO1/2)0.01
Methylvinylphenylpolysiloxane represented by the formula: 51.6 parts by mass, average formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
12.9 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
14.5 parts by mass of 1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane represented by the above formula (total 1 vinyl groups of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated polymethylphenylsiloxane The amount of silicon atom-bonded hydrogen atoms in this component is 0.48 moles per mole), average unit formula:
(Me2HSiO1/2)0.60(SiO4/2)0.40
14.5 parts by mass of silicon-bonded hydrogen atom-containing methylphenylpolysiloxane represented by the formula (in this component with respect to a total of 1 mol of the vinyl groups of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated polymethylphenylsiloxane) In an amount of 0.48 mol of silicon-bonded hydrogen atoms), 1,3-divinyl-1,1,3,3 of 1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex of platinum. 3-tetramethyldisiloxane solution (amount in which platinum metal is 5.0 ppm by mass relative to the present composition), 1-ethynyl-1-cyclohexanol (an amount in which 300 ppm by mass is present relative to the present composition) ), Titanium oxide with an average primary particle size of 0.2 μm (SX-3103 manufactured by Sakai Chemical Industry), 118 parts by mass, and spherical with an average particle size of 15 μm A curable silicone composition having a viscosity of 592 Pa · s at 25 ° C. was prepared by mixing 213 parts by mass of silica (HS-202 manufactured by Nippon Steel Materials, Micron).
When this composition was heated at 120 ° C. for 10 minutes, it was a solid whose viscosity could not be measured at 25 ° C. and had a type D durometer hardness of 75, but was a solid whose viscosity could not be measured even at 100 ° C. I understood that it was not. The conversion rate of the hydrosilylation reaction was 88%.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, the obtained solid was integrally molded with the lead frame 10 times using a transfer molding machine, but in all cases, the mold was hardly filled and was not uniform. A molded product was obtained.
The composition was directly heated at 150 ° C. for 2 hours to form a cured product. This cured product has a type D durometer hardness of 91, a bending strength of 28 MPa, a total light reflectance of 94.6% (2 mm thick test piece) and 90.8% (0.2 mm thick test piece), 400 nm. The light reflectance at a wavelength of 33.1% and the linear expansion coefficient were 89 ppm / ° C. The die shear strength for aluminum plate and silver plated steel plate is 8.2 and 6.8 N / mm, respectively.2Met.
[Comparative Example 2]
Average unit formula:
(MeViSiO2/2)0.20(Me2SiO2/2)0.20(Ph2SiO2/2)0.10(PhSiO3/2)0.50(HO1/2)0.03
100 parts by mass of methylvinylphenylpolysiloxane represented by the formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
13.3 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 33.3 parts by mass (total of 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated
When this composition was heated at 120 ° C. for 10 minutes, it was found that the viscosity at 25 ° C. was 23,000 Pa · s, the type D durometer hardness was 11, and it was not a thermoplastic. The conversion rate of the hydrosilylation reaction was 79%.
Moreover, in order to manufacture the optical semiconductor device shown in FIG. 1, the liquid obtained was integrally molded with the lead frame 10 times using a transfer molding machine, but the adhesion to the mold was large in all cases, The molded part was easily deformed.
The composition was directly heated at 150 ° C. for 2 hours to form a cured product. This cured product has a type D durometer hardness of 76, a bending strength of 9.4 MPa, and a total light reflectance of 94.3% (2 mm thick test piece) and 91.2% (0.2 mm thick test piece). The light reflectance at a wavelength of 400 nm was 31.5%, and the linear expansion coefficient was 91 ppm / ° C. The die shear strength for aluminum plate and silver plated steel plate is 5.4 and 4.7 N / mm, respectively.2Met.
[Comparative Example 3]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
100 parts by mass of methylvinylphenylpolysiloxane represented by the formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
13.3 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 33.3 parts by mass (total of 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated
When this composition was heated at 120 ° C. for 10 minutes, it was a solid whose viscosity could not be measured at 25 ° C., had a type D durometer hardness of 62, a viscosity at 100 ° C. of 3,900 Pa · s, and was thermoplastic. It turned out to be a body. The conversion rate of the hydrosilylation reaction was 84%.
When the obtained thermoplastic was heated at 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a Type D durometer hardness of 85 at 25 ° C., a bending strength of 19 MPa, and a total light reflectance of 55. 4% (2 mm thick specimen) and 51.7% (0.2 mm thick specimen), the light reflectance at a wavelength of 400 nm was 34.5%, and the linear expansion coefficient of the cured product was 93 ppm / ° C. It was. Also, the die shear strength for aluminum plate and silver-plated steel plate is 7.0 and 6.1 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, molding failure was confirmed 5 times out of 10 times. Good moldings free from burrs and voids were obtained.
[Comparative Example 4]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
100 parts by mass of methylvinylphenylpolysiloxane represented by the formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
13.3 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 33.3 parts by mass (total of 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated
When this composition was heated at 120 ° C. for 10 minutes, it was a solid whose viscosity could not be measured at 25 ° C., and although the type D durometer hardness was 69, the viscosity at 100 ° C. was as high as 2,000,000 Pa · s. It was found that it was not a good plastic. The conversion rate of the hydrosilylation reaction was 86%.
When the obtained solid was heated at 150 ° C., the fluidity was lost after fluidization. The cured product obtained by heating at 150 ° C. for 1 hour has no fluidity at 300 ° C. or less, has a Type D durometer hardness of 87 at 25 ° C., a bending strength of 20 MPa, and a total light reflectance of 93.degree. 5% (2 mm thickness test piece) and 92.8% (0.2 mm thickness test piece), the light reflectance at a wavelength of 400 nm was 30.9%, and the linear expansion coefficient of the cured product was 115 ppm / ° C. It was. The die shear strengths for aluminum plates and silver-plated steel plates are 6.7 and 5.8 N / mm, respectively.2Met.
Further, in order to manufacture the optical semiconductor device shown in FIG. 1, when the above thermoplastic body was integrally molded with the lead frame 10 times using a transfer molding machine, 5 out of 10 molding defects were confirmed. There were many voids even in the case where there was no defect, and a good molded product could not be obtained.
[Comparative Example 5]
Average unit formula:
(MeViSiO2/2)0.25(Ph2SiO2/2)0.30(PhSiO3/2)0.45(HO1/2)0.02
100 parts by mass of methylvinylphenylpolysiloxane represented by the formula:
ViMe2SiO (MePhSiO)17.5SiViMe2
13.3 parts by mass of a dimethylvinylsiloxy-terminated polymethylphenylsiloxane represented by the formula:
(HMe2SiO)2SiPh2
1,1,5,5-tetramethyl-3,3-diphenyltrisiloxane 33.3 parts by mass (total of 1 vinyl group of the above methylvinylphenylpolysiloxane and dimethylvinylsiloxy-terminated
When this composition was heated at 120 ° C. for 10 minutes, it was a solid whose viscosity could not be measured at 25 ° C., a non-uniform solid, and a solid whose viscosity could not be measured even at 100 ° C. and was not a thermoplastic. all right. The conversion rate of the hydrosilylation reaction was 82%.
Moreover, in order to manufacture the optical semiconductor device shown in FIG. 1, when the obtained solid was integrally molded with the lead frame 10 times using a transfer molding machine, all of the mold unfilled portions were recognized, and Many voids were generated, and a good molded product could not be obtained.
本発明の反応性シリコーン組成物は、反応性熱可塑体を与えることができ、この反応性熱可塑体は、加熱した金型中での硬化物の成形に適し、得られる硬化物は、熱や光による機械的強度の低下や変色が少なく、光反射率、特に３５０~４００ｎｍの領域の光反射率が高く、金属に対する接着力が高いので、発光ダイオードの白色枠材の形成材料として好適である。
The reactive silicone composition of the present invention can provide a reactive thermoplastic, which is suitable for molding a cured product in a heated mold, and the resulting cured product is It is suitable as a material for forming white frame materials for light-emitting diodes, because it has little reduction in mechanical strength and discoloration due to light and light, has high light reflectivity, particularly high light reflectivity in the region of 350 to 400 nm, and high adhesion to metal. is there.
１ 光半導体素子
２ リードフレーム
３ リードフレーム
４、４’ ボンディングワイヤ
５ 光反射材
６ 封止材 DESCRIPTION OFSYMBOLS 1 Optical semiconductor element 2 Lead frame 3 Lead frame 4, 4 'Bonding wire 5 Light reflecting material 6 Sealing material
２ リードフレーム
３ リードフレーム
４、４’ ボンディングワイヤ
５ 光反射材
６ 封止材 DESCRIPTION OF
Claims (15)
- （Ａ）平均単位式：
（Ｒ１ ３ＳｉＯ１／２）ａ（Ｒ１ ２ＳｉＯ２／２）ｂ（Ｒ１ＳｉＯ３／２）ｃ（ＳｉＯ４／２）ｄ（Ｒ２Ｏ１／２）ｅ
（式中、Ｒ１は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、もしくは炭素原子数２~６のアルケニル基であり、ただし、全Ｒ１の３０~８０モル％はフェニル基であり、全Ｒ１の１０~２０モル％はアルケニル基であり、Ｒ２は水素原子または炭素原子数１~６のアルキル基であり、ａ、ｂ、ｃ、ｄ、およびｅはそれぞれ、０≦ａ≦０．３０、０≦ｂ≦０．７０、０．３≦ｃ≦０．９、０≦ｄ≦０．２０、０≦ｅ≦０．１０、かつａ＋ｂ＋ｃ＋ｄ＝１を満たす数である。）
で表されるオルガノポリシロキサン １００質量部、
（Ｂ）一般式：
Ｒ３ ３ＳｉＯ（Ｒ３ ２ＳｉＯ）ｍＳｉＲ３ ３
（式中、Ｒ３は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、もしくは炭素原子数２~６のアルケニル基であり、ただし、全Ｒ３の３０~７０モル％はフェニル基であり、全Ｒ３の少なくとも１個はアルケニル基であり、ｍは１０~１００の整数である。）
で表されるオルガノポリシロキサン ０~４０質量部、
（Ｃ）一分子中に少なくとも２個のケイ素原子結合水素原子を有し、ケイ素原子結合全有機基の２０~７０モル％がフェニル基であるオルガノポリシロキサン｛（Ａ）成分および（Ｂ）成分中のアルケニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．５~２モルとなる量｝、
（Ｄ）ヒドロシリル化反応用触媒｛（Ａ）成分および（Ｂ）成分中のアルケニル基と（Ｃ）成分中のケイ素原子結合水素原子とのヒドロシリル化反応を促進するに十分な量｝、
（Ｅ）酸化チタン以外の白色顔料｛（Ａ）成分~（Ｄ）成分の合計１００質量部に対して５０質量部以上｝、および
（Ｆ）非球状シリカ、球状シリカまたはガラスファイバー｛（Ａ）成分~（Ｄ）成分の合計１００質量部に対して１００質量部以上｝
から少なくともなり、（Ｅ）成分および（Ｆ）成分の合計の含有量が、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して４００質量部以下である反応性シリコーン組成物。 (A) Average unit formula:
(R 1 3 SiO 1/2 ) a (R 1 2 SiO 2/2 ) b (R 1 SiO 3/2 ) c (SiO 4/2 ) d (R 2 O 1/2 ) e
(Wherein R 1 is the same or different and is a phenyl group, an alkyl group having 1 to 6 carbon atoms, or an alkenyl group having 2 to 6 carbon atoms, provided that 30 to 80 mol% of all R 1 s ) Is a phenyl group, 10 to 20 mol% of all R 1 is an alkenyl group, R 2 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, and a, b, c, d, and e are 0 ≦ a ≦ 0.30, 0 ≦ b ≦ 0.70, 0.3 ≦ c ≦ 0.9, 0 ≦ d ≦ 0.20, 0 ≦ e ≦ 0.10, and a + b + c + d = 1 are satisfied. Number.)
100 parts by mass of an organopolysiloxane represented by
(B) General formula:
R 3 3 SiO (R 3 2 SiO) m SiR 3 3
(Wherein R 3 is the same or different and is a phenyl group, an alkyl group having 1 to 6 carbon atoms, or an alkenyl group having 2 to 6 carbon atoms, provided that 30 to 70 mol% of all R 3 s ) Is a phenyl group, at least one of all R 3 is an alkenyl group, and m is an integer of 10 to 100.)
0 to 40 parts by mass of an organopolysiloxane represented by
(C) Organopolysiloxane having at least two silicon-bonded hydrogen atoms in one molecule and 20 to 70 mol% of all silicon-bonded organic groups being phenyl groups {component (A) and component (B) Amount of silicon atom-bonded hydrogen atoms in this component to be 0.5 to 2 moles relative to a total of 1 mole of alkenyl groups therein},
(D) Hydrosilylation catalyst {a sufficient amount to promote the hydrosilylation reaction between the alkenyl group in components (A) and (B) and the silicon atom-bonded hydrogen atom in component (C)},
(E) White pigment other than titanium oxide {50 parts by mass or more with respect to 100 parts by mass in total of components (A) to (D)}, and (F) non-spherical silica, spherical silica or glass fiber {(A) Component ~ (D) 100 parts by mass or more with respect to 100 parts by mass in total}
And a total content of the component (E) and the component (F) is 400 parts by mass or less with respect to a total of 100 parts by mass of the components (A) to (D). - （Ｅ）成分が、酸化亜鉛、チタン酸バリウム、および硫酸バリウムからなる群より選ばれる少なくとも１種の白色顔料である、請求項１に記載の反応性シリコーン組成物。 The reactive silicone composition according to claim 1, wherein the component (E) is at least one white pigment selected from the group consisting of zinc oxide, barium titanate, and barium sulfate.
- さらに、（Ｇ）平均単位式：
（Ｒ７ ３ＳｉＯ１／２）ｆ（Ｒ７ ２ＳｉＯ２／２）ｇ（Ｒ７ＳｉＯ３／２）ｈ（ＳｉＯ４／２）ｉ（Ｒ８Ｏ１／２）ｊ
（式中、Ｒ７は、同じかまたは異なる、フェニル基、炭素原子数１~６のアルキル基、炭素原子数２~６のアルケニル基もしくはエポキシ基含有有機基であり、ただし、全Ｒ７の１５~６０モル％はフェニル基であり、全Ｒ７の３~３０モル％はアルケニル基であり、５~３０モル％はエポキシ基含有有機基であり、Ｒ８は水素原子または炭素原子数１~６のアルキル基であり、ｆ、ｇ、ｈ、ｉ、およびｊはそれぞれ、０≦ｆ≦０．５、０≦ｇ≦０．９、０≦ｈ≦０．７、０≦ｉ≦０．３、０≦ｊ≦０．０２、かつｆ＋ｇ＋ｈ＋ｉ＝１を満たす数である。）
で表されるオルガノポリシロキサンを、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して０．５~１０．０質量部含有する、請求項１または２に記載の反応性シリコーン組成物。 Further, (G) average unit formula:
(R 7 3 SiO 1/2 ) f (R 7 2 SiO 2/2 ) g (R 7 SiO 3/2 ) h (SiO 4/2 ) i (R 8 O 1/2 ) j
(Wherein R 7 is the same or different, a phenyl group, an alkyl group having 1 to 6 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, or an epoxy group-containing organic group, provided that all R 7 15 to 60 mol% is a phenyl group, 3 to 30 mol% of all R 7 is an alkenyl group, 5 to 30 mol% is an epoxy group-containing organic group, and R 8 is a hydrogen atom or 1 carbon atom. To 6 alkyl groups, and f, g, h, i, and j are 0 ≦ f ≦ 0.5, 0 ≦ g ≦ 0.9, 0 ≦ h ≦ 0.7, and 0 ≦ i ≦ 0, respectively. .3, 0 ≦ j ≦ 0.02, and f + g + h + i = 1.)
The reactive silicone composition according to claim 1 or 2, which contains 0.5 to 10.0 parts by mass of the organopolysiloxane represented by the formula (A) to (D) with respect to 100 parts by mass in total. object. - さらに、（Ｈ）一分子中に少なくとも２個のケイ素原子結合水素原子を有し、ケイ素原子結合全有機基に対するフェニル基の含有量が２０モル％未満であるオルガノポリシロキサンを、（Ａ）成分および（Ｂ）成分中のアルケニル基の合計１モルに対して、本成分中のケイ素原子結合水素原子が０．００１~０．２０モルとなる量含有する、請求項１乃至３のいずれか１項に記載の反応性シリコーン組成物。 Further, (H) an organopolysiloxane having at least two silicon-bonded hydrogen atoms in one molecule and having a phenyl group content of less than 20 mol% with respect to all silicon-bonded organic groups, And (B) the silicon-bonded hydrogen atom in this component is contained in an amount of 0.001 to 0.20 mol with respect to a total of 1 mol of alkenyl groups in component (B). The reactive silicone composition according to item.
- さらに、（Ｉ）一分子中に少なくとも１個の炭素−炭素二重結合を有する、炭素原子数が１０以上のカルボン酸またはその金属塩を、（Ａ）成分~（Ｄ）成分の合計１００質量部に対して０．０１~８質量部含有する、請求項１乃至４のいずれか１項に記載の反応性シリコーン組成物。 Furthermore, (I) a carboxylic acid having at least one carbon-carbon double bond in one molecule and having 10 or more carbon atoms or a metal salt thereof, a total of 100 masses of components (A) to (D) The reactive silicone composition according to any one of claims 1 to 4, which is contained in an amount of 0.01 to 8 parts by mass relative to parts.
- ２５℃における粘度が１０，０００Ｐａ・ｓ以下である、請求項１乃至５のいずれか１項記載の反応性シリコーン組成物。 The reactive silicone composition according to any one of claims 1 to 5, wherein the viscosity at 25 ° C is 10,000 Pa · s or less.
- 請求項１乃至６のいずれか１項に記載の反応性シリコーン組成物のヒドロシリル化反応を７０~９５％転化率となるまで進行させてなる反応性熱可塑体。 A reactive thermoplastic obtained by allowing the hydrosilylation reaction of the reactive silicone composition according to any one of claims 1 to 6 to proceed until a conversion of 70 to 95% is achieved.
- ２５℃で固体もしくは粘度が１，０００，０００Ｐａ・ｓ以上であり、１００℃での粘度が１００，０００Ｐａ・ｓ以下の液状である、請求項７に記載の反応性熱可塑体。 The reactive thermoplastic according to claim 7, which is a solid or a liquid having a viscosity of 1,000,000 Pa · s or more at 25 ° C and a viscosity of 100,000 Pa · s or less at 100 ° C.
- ２５℃におけるＪＩＳ Ｋ ７２１５に規定のタイプＤデュロメーター硬さが３０以上である、請求項７または８に記載の反応性熱可塑体。 The reactive thermoplastic according to claim 7 or 8, wherein the type D durometer hardness specified in JIS K 7215 at 25 ° C is 30 or more.
- １００℃以上に加熱して、３００℃以下で流動性を示さない硬化物を形成する、請求項７乃至９のいずれか１項に記載の反応性熱可塑体。 The reactive thermoplastic according to any one of claims 7 to 9, which is heated to 100 ° C or higher to form a cured product that does not exhibit fluidity at 300 ° C or lower.
- 請求項７乃至１０のいずれか１項記載の反応性熱可塑体を１００℃以上に加熱することにより得られ、３００℃で固体もしくは粘度が１，０００，０００Ｐａ・ｓ以上である硬化物。 A cured product obtained by heating the reactive thermoplastic according to any one of claims 7 to 10 to 100 ° C or higher and having a solid or a viscosity of 1,000,000 Pa · s or higher at 300 ° C.
- 請求項１乃至６のいずれか１項に記載の反応性シリコーン組成物を硬化してなる硬化物。 Hardened | cured material formed by hardening | curing the reactive silicone composition of any one of Claims 1 thru | or 6.
- 全光線反射率が８０％以上である、請求項１１または１２に記載の硬化物。 The cured product according to claim 11 or 12, wherein the total light reflectance is 80% or more.
- ２５~２００℃の範囲内での平均線膨張率が２００ｐｐｍ／℃以下である請求項１１乃至１３のいずれか１項に記載の硬化物。 The cured product according to any one of claims 11 to 13, wherein an average linear expansion coefficient in a range of 25 to 200 ° C is 200 ppm / ° C or less.
- 請求項１１乃至１４のいずれか１項に記載の硬化物により光反射材を形成してなることを特徴とする光半導体装置。 An optical semiconductor device comprising a light reflecting material formed of the cured product according to any one of claims 11 to 14.