WO2014177754A1 - Film pour étiquette, stratifié pour étiquette et procédé de fabrication d'un stratifié pour étiquette - Google Patents
Film pour étiquette, stratifié pour étiquette et procédé de fabrication d'un stratifié pour étiquette Download PDFInfo
- Publication number
- WO2014177754A1 WO2014177754A1 PCT/FI2013/050481 FI2013050481W WO2014177754A1 WO 2014177754 A1 WO2014177754 A1 WO 2014177754A1 FI 2013050481 W FI2013050481 W FI 2013050481W WO 2014177754 A1 WO2014177754 A1 WO 2014177754A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- plastic film
- release liner
- film
- label
- layer
- Prior art date
Abstract
La présente invention concerne un film en plastique d'un stratifié pour étiquette. Selon un mode de réalisation, le film en plastique peut comprendre au moins du polyéthylène, du polypropylène ou un copolymère de propylène, ainsi qu'au moins 0,01 % en poids de particules de silicone. Le film en plastique peut être orienté au moins dans une direction avec un rapport d'étirage d'au moins 4. Selon un mode de réalisation, le film en plastique peut être un revêtement anti-adhésif d'un stratifié pour étiquette. En outre, l'invention concerne une fabrication du film en plastique.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/FI2013/050481 WO2014177754A1 (fr) | 2013-04-30 | 2013-04-30 | Film pour étiquette, stratifié pour étiquette et procédé de fabrication d'un stratifié pour étiquette |
DE112013007014.6T DE112013007014T5 (de) | 2013-04-30 | 2013-04-30 | Folie für ein Etikett, Etikettenlaminat und Verfahren zur Herstellung eines Etikettenlaminats |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/FI2013/050481 WO2014177754A1 (fr) | 2013-04-30 | 2013-04-30 | Film pour étiquette, stratifié pour étiquette et procédé de fabrication d'un stratifié pour étiquette |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2014177754A1 true WO2014177754A1 (fr) | 2014-11-06 |
Family
ID=48483103
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/FI2013/050481 WO2014177754A1 (fr) | 2013-04-30 | 2013-04-30 | Film pour étiquette, stratifié pour étiquette et procédé de fabrication d'un stratifié pour étiquette |
Country Status (2)
Country | Link |
---|---|
DE (1) | DE112013007014T5 (fr) |
WO (1) | WO2014177754A1 (fr) |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0242055A2 (fr) * | 1986-03-17 | 1987-10-21 | Mitsubishi Petrochemical Co., Ltd. | Pellicule de polypropylène crystallin |
US5981047A (en) * | 1996-06-25 | 1999-11-09 | Applied Extrusion Technologies, Inc. | Matte finish biaxially oriented polypropylene film for cold seal release applications |
EP2599628A1 (fr) * | 2011-12-02 | 2013-06-05 | Irplast S.p.A. | Films en plastique |
EP2599627A1 (fr) * | 2011-12-02 | 2013-06-05 | Irplast S.p.A. | Films en plastique |
-
2013
- 2013-04-30 WO PCT/FI2013/050481 patent/WO2014177754A1/fr active Application Filing
- 2013-04-30 DE DE112013007014.6T patent/DE112013007014T5/de not_active Withdrawn
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0242055A2 (fr) * | 1986-03-17 | 1987-10-21 | Mitsubishi Petrochemical Co., Ltd. | Pellicule de polypropylène crystallin |
US5981047A (en) * | 1996-06-25 | 1999-11-09 | Applied Extrusion Technologies, Inc. | Matte finish biaxially oriented polypropylene film for cold seal release applications |
EP2599628A1 (fr) * | 2011-12-02 | 2013-06-05 | Irplast S.p.A. | Films en plastique |
EP2599627A1 (fr) * | 2011-12-02 | 2013-06-05 | Irplast S.p.A. | Films en plastique |
Also Published As
Publication number | Publication date |
---|---|
DE112013007014T5 (de) | 2016-01-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20140134430A1 (en) | Label facestock | |
US20180357936A1 (en) | Removable Adhesive Label Containing Inherently Shrinkable Polymeric Film | |
US11230089B2 (en) | Face film and an adhesive label comprising the face film | |
EP3221146B1 (fr) | Pellicule frontale d'étiquette | |
JP6050123B2 (ja) | 多層フィルム | |
WO2015118215A1 (fr) | Étiquette sans film protecteur, lavable, appareil et procédé de préparation d'une étiquette | |
KR20120087841A (ko) | 이형 필름 접합 양면 점착 시트 및 그의 제조 방법 | |
WO2011161324A1 (fr) | Doublure de polypropylène orientée dans le sens machine | |
US10293587B2 (en) | Substrate for a label laminate, a label laminate and a method for manufacturing a label laminate | |
WO2013140035A1 (fr) | Film pour frontal d'étiquette | |
WO2012123633A1 (fr) | Film stratifié | |
WO2012127121A2 (fr) | Film frontal pour étiquette | |
WO2017077184A1 (fr) | Film protecteur et étiquette adhésive comprenant le film protecteur | |
WO2014177754A1 (fr) | Film pour étiquette, stratifié pour étiquette et procédé de fabrication d'un stratifié pour étiquette | |
US10532533B2 (en) | Adhesive label, facestock for an adhesive label and adhesive label laminate | |
WO2015118214A1 (fr) | Étiquette lavable et son procédé de préparation | |
WO2016079368A1 (fr) | Pellicule frontale d'étiquette | |
WO2016079370A1 (fr) | Pellicule frontale d'étiquette | |
WO2016079369A1 (fr) | Pellicule frontale d'étiquette | |
WO2015092116A1 (fr) | Substrat antiadhésif protecteur, stratifié d'étiquette comprenant un substrat antiadhésif protecteur, et procédé pour produire un stratifié d'étiquette | |
US20130089685A1 (en) | Squeezable and Conformable Oriented Polypropylene Label | |
WO2015118209A1 (fr) | Étiquettes sans doublure | |
WO2015092117A1 (fr) | Couche de face, étiquette et stratifié d'étiquette comprenant une couche de face et procédé de conception d'un stratifié d'étiquette |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 13724613 Country of ref document: EP Kind code of ref document: A1 |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1120130070146 Country of ref document: DE Ref document number: 112013007014 Country of ref document: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 13724613 Country of ref document: EP Kind code of ref document: A1 |