WO2014165934A1 - Steel product and method of producing the product - Google Patents
Steel product and method of producing the product Download PDFInfo
- Publication number
- WO2014165934A1 WO2014165934A1 PCT/AU2014/000416 AU2014000416W WO2014165934A1 WO 2014165934 A1 WO2014165934 A1 WO 2014165934A1 AU 2014000416 W AU2014000416 W AU 2014000416W WO 2014165934 A1 WO2014165934 A1 WO 2014165934A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- steel
- heat treatment
- samples
- product
- yield stress
- Prior art date
Abstract
Description
Claims