WO2014122622A1 - Tyre body ply skim - Google Patents

Tyre body ply skim Download PDF

Info

Publication number
WO2014122622A1
WO2014122622A1 PCT/IB2014/058870 IB2014058870W WO2014122622A1 WO 2014122622 A1 WO2014122622 A1 WO 2014122622A1 IB 2014058870 W IB2014058870 W IB 2014058870W WO 2014122622 A1 WO2014122622 A1 WO 2014122622A1
Authority
WO
WIPO (PCT)
Prior art keywords
compound
phr
carbon black
body ply
lignin
Prior art date
Application number
PCT/IB2014/058870
Other languages
French (fr)
Inventor
Salvatore Cotugno
Ludovica CALIANO
Original Assignee
Bridgestone Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bridgestone Corporation filed Critical Bridgestone Corporation
Priority to JP2015556602A priority Critical patent/JP6342919B2/en
Priority to EP14710976.3A priority patent/EP2954000B1/en
Priority to CN201480008164.7A priority patent/CN104995244B/en
Priority to US14/766,476 priority patent/US9546264B2/en
Publication of WO2014122622A1 publication Critical patent/WO2014122622A1/en

Abstract

A compound for a tyre textile body ply skim. The compound has a cross- linkable, unsaturated-chain polymer base, a reinforcing filler composite, and a curing system having at least a curing agent and accelerants. The compound has 0.1 to 20 phr of a lignin derivative, 20 to 50 phr of a first carbon black with a surface area of 90 to 150 m2/g, and 5 to 20 phr of a second carbon black with a surface area of 10 to 40 m2/g.

Description

TYRE BODY PLY SKIM
TECHNICAL FIELD
The present invention relates to a tyre body ply skim.
In tyre manufacturing, reinforcing plies made of thermoplastic material (e.g. nylon, rayon, polyester, aramide) are used to ensure given resistance standards.
To improve cord-rubber adhesion, the plies are treated with adhesive before the rubber is applied. The resulting reinforced-rubber coat is normally about 1 mm thick. The rubber ply coating is commonly known as a ^body ply skim' and is referred to as such in the following description and accompanying Claims.
BACKGROUND ART
As anyone skilled in the art knows, reinforcing plies are commonly used to reinforce the carcass, and the belts located between the carcass and tread.
The carcass defines the shape of the tyre, supports the load and transmits vehicle stress groundwards, and ensures fatigue resistance of the stressed areas. The belts serve to further increase tyre resistance by stabilizing the tread and safeguarding against shock and damage to the inner layers .
As will be obvious to anyone skilled in the art, the body ply skim must adhere firmly to the plies. In fact, poor adhesion of the body ply skim to the ply invariably results in a short working life of the tyre. DISCLOSURE OF INVENTION
It is an object of the present invention to provide a body ply skim compound, which provides for firm adhesion to textile plies, while at the same time improving rolling resistance without compromising other characteristics .
The Applicant has devised a textile body ply skim compound designed to improve rubber- textile adhesion, while at the same time also achieving advantages in terms of rolling resistance.
Hereinafter, the term Nhigh-surface-area reinforcing filler' refers to one with a surface area of 90-150 m2/g, and v low-surface-area reinforcing filler' to one with a surface area of 10-40 m2/g.
According to the present invention, there is provided a compound comprising a cross-linkable, unsaturated-chain polymer base, a reinforcing filler composite, and a curing system comprising at least a curing agent and accelerants; said compound being characterized by comprising 0.1 to 20 phr of lignin and/or a lignin derivative; and in that said reinforcing filler composite comprises 20 to 50 phr of a first carbon black with a surface area of 90 to 150 m2/g, and 5 to 20 phr of a second carbon black with a surface area of 10 to 40 m2/g.
The surface areas were measured by nitrogen absorption as per ASTM Standard D6556.
Preferably, the body ply skim compound comprises 5 to 15 phr of the lignin derivative.
Preferably, the lignin derivative is sulphonated lignin.
Preferably, said reinforcing filler composite comprises 30 to 40 phr of said first carbon black, and 10 to 15 phr of said second carbon black.
Preferably, said lignin derivative is the only adhesion promoter in the compound.
Another object of the present invention is a tyre comprising a body ply skim; said skim being made from a compound in accordance with the present invention.
BEST MODE FOR CARRYING OUT THE INVENTION
The following are non^ limiting examples for a clearer understanding of the invention.
EXAMPLES
Two compounds according to the present invention
(Compounds A and B) were produced, and which differ from each other as regards exclusive use of lignin as an adhesion promoter.
Four control compounds (Compounds C-F) were produced. Compound C is a commonly used body ply skim compound containing an adhesion promoter of hexamethoxymethylmelamine . Compounds D and E are compounds containing the lignin derivative, but without conforming to the reinforcing filler content conditions of the present invention. And Compound F contains the reinforcing filler in accordance with the present invention, but no lignin derivative.
Compound preparation
(First mixing stage)
The compounds were produced using the standard procedure below, which is not pertinent to the present invention .
A 230-270-litre, tangential-rotor mixer was loaded, prior to mixing, with the cross- linkable polymer base and the reinforcing filler composite to a fill factor of 66-72%.
The mixer was operated at a speed of 40-60 rpm, and the resulting mixture unloaded on reaching a temperature of 140-160°C.
(Second mixing stage)
The curing system and zinc oxide were added to the mixture from the first stage to a fill factor of 63-67%.
The mixer was operated at a speed of 20-40 rpm, and the resulting mixture unloaded on reaching a temperature of 100-110°C.
Compound compositions
Table I shows the compositions in phr of the above six compounds A-F.
TABLE I
Figure imgf000006_0001
NR is a polymer base of natural 1,4-cis polyisoprene , the characteristics of which are well known to anyone skilled in the art;
SBR is a polymer base obtained by polymerization in emulsion or solution, with a 20 to 45% styrene content, and 0 to 30% oil content;
HMMM stands for hexamethoxymethylmelamine , and is a cross -linking agent normally used in body ply skims to improve adhesion to the ply;
N660 and N326 are carbon black classifications as per ASTM Standard D1765;
The term 'accelerant' is used to indicate a generic curing-assist agent.
Laboratory test results
The compounds described above were tested to determine adhesion to textile body plies, and rheometric, mechanical and dynamic mechanical properties . It should be pointed out that the compounds according to the present invention preferably apply to body plies made of thermoplastic material.
More specifically, rheometric properties were measured as per ASTM Standard D6204; mechanical properties were measured as per ASTM Standard D412C; and dynamic mechanical properties were measured as per ISO Standard 4664. As anyone skilled in the art knows, the rolling resistance parameter is closely related to 60°C tan5 values : the lower the 60°C tan5 value, the better the rolling resistance.
Adhesion of the compound to the textile ply was assessed as a percentage of the ply still covered with rubber after separating the two parts of the ply-rubber composite under load.
To show more clearly the advantages of the compounds according to the present invention, Table II shows the test results indexed to those of control Compound C representing, as stated, a commonly used body ply skim compound.
TABLE II
A B C D E F
ML 100 100 100 100 100 90
MH 92 90 100 100 100 90
T50 100 100 100 100 100 100
TB 97 90 100 90 97 97
M100 100 100 100 111 113 100
M300 77 77 100 100 100 77
EB 111 104 100 102 102 110 tan6 at 60°C 87 87 100 100 100 95
Coverage 129 120 100 100 129 95 As shown by the Table II results, only Compounds A and B according to the present invention provide for improving both adhesion to the thermoplastic ply and rolling resistance. As shown by the Compound D and E results, simply adding lignin, while improving adhesion, produces no improvement in rolling resistance. Whereas Compound F shows how simply reducing the reinforcing filler produces no improvement unless accompanied by the lignin derivative.
Compound B represents a preferred embodiment, and differs from Compound A by containing no HMMM compound, and so only comprising the lignin derivative as an adhesion promoter.
To fully appreciate the advantages of the present invention, it is important to bear in mind that lignin is a widely available natural substance, is cheap by being a waste product of various processes, is harmless to both health and environment, and can be used without a bonding agent to achieve firm rubber-ply adhesion.

Claims

1) A compound comprising a cross - linkable , unsaturated-chain polymer base, a reinforcing filler composite, and a curing system comprising at least a curing agent and accelerants; said compound being characterized by comprising 0.1 to 20 phr of lignin and/or a lignin derivative; and in that said reinforcing filler composite comprises 20 to 50 phr of a first carbon black with a surface area of 90 to 150 m2/g, and 5 to 20 phr of a second carbon black with a surface area of 10 to 40 m2/g-
2) A compound as claimed in Claim 1, characterized by comprising 5 to 15 phr of the lignin derivative.
3) A compound as claimed in Claim 1 or 2 , wherein the lignin derivative is sulphonated lignin.
4) A compound as claimed in one of the foregoing
Claims, wherein the lignin derivative is the only adhesion promoter in the compound.
5) A compound as claimed in one of the foregoing
Claims, wherein the reinforcing filler composite comprises 30 to 40 phr of said first carbon black, and
10 to 15 phr of said second carbon black.
6) A skim for tyre thermoplastic body plies, characterized by being made from a compound as claimed in one of the foregoing Claims . 7) A tyre comprising a body ply skim as claimed in Claim 6.
PCT/IB2014/058870 2013-02-08 2014-02-08 Tyre body ply skim WO2014122622A1 (en)