WO2014068196A2 - Method for producing nanofibrillar cellulose

Info

Publication number: WO2014068196A2
Application number: PCT/FI2013/051039
Authority: WO
Inventors: Antti Laukkanen; Markus Nuopponen
Original assignee: Upm-Kymmene Corporation
Priority date: 2012-11-03
Filing date: 2013-11-01
Publication date: 2014-05-08
Also published as: JP6272339B2; UY35113A; EP2914772B1; EP2914772A2; FI20126148A; JP2016501926A; US20150299955A1; WO2014068196A3; DK2914772T3; FI127526B; US9797093B2

Abstract

In a method for preparing nanofibrillar cellulose, fibrous dispersion of ionically charged cellulose is repeatedly passed through a mechanical process of disrupting fibers into fibrils until the viscosity starts to decrease. The number average diameter of the nanofibrillar cellulose after the mechanical process is in the range of 2 – 10 nm, and the zero-shear viscosity is below 10 Pa•s, preferably below 1 Pa•s, when measured in the concentration of 0.5 wt-%. The nanofibrillated cellulose is low aspect ratio nanofibrillated cellulose (NFC-L).

Description

Method for producing nanofibrillar cellulose Field of the Invention The present invention relates to a method for preparing nanofibrillar cellulose. The invention also relates to nanofibrillar cellulose and applications using said nanofibrillar cellulose.

Background of the Invention

Nanofibrillar cellulose refers to isolated cellulose microfibrils or microfibril bundles derived from cellulose raw material. Nanofibrillar cellulose (NFC), which is also known as microfibrillar cellulose (MFC), and by other related names, is a natural polymer that is abundant in nature. Generally, nanofibrillar cellulose has high aspect ratio and the fibril length can be up to several microns.

Traditionally, nanofibrillar cellulose production techniques are based on grinding (or homogenization) of aqueous dispersion of pulp fibers. The concentration of nanofibrillar cellulose in dispersions is typically low, usually around 1 -5 %.

The production of nanofibrillar cellulose by fibrillating cellulose fibers into nano-scale elements requires intensive mechanical treatment. In order to produce purified cellulose or reduce energy demand, chemical treatment or enzymatic treatment may be applied prior or posterior to mechanical fibrillation.

Through the mechanical fibrillating process, the fibrillated cellulose achieves a "gel-point" after repeated passes. The gel-point is characterized by a critical point in the process at which the cellulosic suspension rapidly thickens to a more viscous consistency. In other words, the viscosity of the pulp fiber suspension increases dramatically during the process. Therefore, after the grinding or homogenization process, the obtained nanofibrillar cellulose material is a dilute viscoelastic hydrogel, However, for certain applications, a challenge associated with using NFC/MFC is the high viscosity in aqueous state, for example for pickering stabilization and coating processes, wherein low viscosity is desirable. Pickering stabilization means the utilization of nanometer scale solid particles in stabilization of heterogeneous systems, like emulsions and foams.

Japanese published patent application JP2009-298972 describes a method for producing cellulose fibers as a gas barrier film material, said method comprising the steps of oxidation, microparticulation, UV irradiation and enzymatic treatment. PCT publication WO 2012043103 describes cellulose nanofibers being able to form a film with excellent oxygen barrier properties, said nanofibers being produced by the steps of oxidation and enzymatic treatment followed by mechanical treatment. Both publications involve three or more steps.

Contrary to the typical high aspect ratio nanofibrillar cellulose, there is another type of nanocellulose with low aspect ratio, cellulose whiskers, which can be obtained by subjecting cellulose fibers to extensive acid hydrolysis, through which cellulose fibers undergo transverse cleavage along the amorphous region and turn into cellulose nanowhiskers with low aspect ratio, which leads to low viscosity. However, the production yield trough acid hydrolysis is typically only 50-60% due to solubilization of amorphous regions upon hydrolysis. Thus, the cellulose nanowhiskers are considered remarkably more expensive materials compared to NFC/MFC-like products.

Therefore, there is a need of easy-to-produce and cost-effective nanowhisker-like materials having low viscosity and still preserving desirable properties of fibril cellulose. Summary of the Invention

It is a purpose of the invention to provide a novel method for preparing nanofibrillar cellulose of low viscosity. The concept "low viscosity" means in this context the degree of viscosity close to what nanocrystalline cellulose/whiskers have. In the method of the present invention, nanofibrillar cellulose is prepared by repeatedly passing fibrous dispersion of oxidized cellulose through a mechanical process of disrupting fibers into fibrils using a sufficient amount of energy until the viscosity starts to decrease. Herein "viscosity starts to decrease" means, while the viscosity of the pulp fiber suspension increases during the repeating disruptive process, the first sign of negative growth of the viscosity value, which can be obtained by measuring the nanofibrillar cellulose sample taken after each pass with a standard viscosity measurement method. The zero-shear viscosity value of nanofibrillar cellulose may decrease to the point below 10 Pa-s, preferably below 1 Pa-s, when measured by a rotational rheometer in the concentration of 0.5%. The zero-shear viscosity value is the value in the region of constant viscosity at small shear stresses. After the viscosity has been decreasing, the number average length of the nanofibrillar cellulose may be below 1 micron, preferably below 500 nm, while the number average diameter of the nanofibrillar cellulose remains essentially unchanged, in the range of 2 to 10 nm. The average aspect ratio of the nanofibrillar cellulose may be in the range of 80-300, preferably 100-250. In another embodiment, the viscosity of the nanofibrillar cellulose measured with Brookfield viscometer at 10 rpm (Brookfield viscosity) is below 10 000 mPa.s, preferably below 5000 mPa.s, and preferably not lower than 1000 mPa.s in the concentration of 0.8 %. It is another purpose of the invention to provide a novel use of nanofibrillar cellulose prepared by the method of the invention for pickering stabilization, especially for foam stabilization in various paractical applications.

Description of the Drawings

The invention will be explained in the following with reference to the appended drawings, where

Fig. 1 shows AFM images of nanofibrillar cellulose,

Fig. 2 shows flow profiles of different nanofibrillar cellulose grades,

Fig. 3 shows the viscosity change of nanofibrillar cellulose along with the number of passes, Fig. 4 shows the pickering stabilization ability of nanofibrillar cellulose according to one embodiment,

Fig. 5 shows the pickering stabilization ability in numerical values,

Fig. 6 shows the structure of the foams in more detail, and

Fig. 7 shows the width distribution of oxidized low-aspect ratio NFC.

Detailed Description of the Invention

The term "nanofibrillar cellulose" refers to a collection of isolated cellulose microfibrils or microfibril bundles derived from cellulose raw material. Microfibrils have typically high aspect ratio: the length might exceed one micrometer while the number-average diameter is typically below 200 nm. The diameter of microfibril bundles can also be larger but generally less than 1 micrometer. The smallest microfibrils are similar to so called elementary fibrils, which are typically 2-12 nm in diameter. The dimensions of the fibrils or fibril bundles are dependent on raw material and disintegration method. The nanofibrillar cellulose may also contain some hemicelluloses; the amount is dependent on the plant source. Mechanical disintegration of microfibrillar cellulose from cellulose raw material, cellulose pulp, or refined pulp is normally carried out with suitable equipment such as a refiner, grinder, homogenizer, colloider, friction grinder, ultrasound sonicator, fluidizer such as microfluidizer, macrofluidizer or fluidizer-type homogenizer. In this case the nanofibrillar cellulose is obtained through disintegration of plant cellulose material and can also be called "nanofibrillated cellulose".

Thus, nanofibrillar cellulose has typically a high aspect ratio: the length might exceed one micrometer while the number-average diameter is typically below 200 nm. Now a unique combination of chemical modification and mechanical disruptive treatment to diminish length of the NFC was found. This new grade of nanofibrillar cellulose has lower aspect ratio and higher surface area than typical fibril cellulose. The lower aspect ratio leads to lower viscosity of the dispersion in water, which is beneficial in certain applications, such as pickering stabilization and coating processes. The surface of original, chemically unmodified cellulose in the fibrous starting material is charged ionically in a chemical pretreatment before the mechanical disruptive treatment. In this way the internal bonds in the cellulose between the microfibrils is weakened, and it is thus possible to enhance the separation of nanofibrils. Some methods for charging the cellulose can be given as example. Oxidation pretreatment of cellulose before the mechanical disruptive treatment is a promising method for surface modification of native cellulose, by which carboxylate and aldehyde functional groups can be introduced into solid native cellulose under aqueous and mild conditions. When native cellulose is used, the oxidation occurs at the surface of the microfibrils, which become negatively (anionically) charged and subsequently results in repulsion of the nanofibers, thus easing fibrillation. Cellulose obtained through N-oxyl mediated catalytic oxidation (e.g. through 2,2,6,6-tetramethyl-1 -piperidine N-oxide, known by abbreviation "TEMPO") or carboxymethylated cellulose are examples of anionically charged nanofibrillar cellulose where the anionic charge is due to a dissociated carboxylic acid moiety. Cellulose derivative where the cellulose contains quaternary ammonium groups is an example of cationically charged nanofibrillar cellulose.

According to one embodiment of the method, primary alcohols of cellulose are oxidized to aldehydes and carboxylic acids through N-oxyl mediated catalytic oxidation, for example through TEMPO, by using sodium hypochlorite as the main oxidant. Regarding the finding that low degree of oxidation does not allow efficient enough fibrillation and higher degree of oxidation inflicts degradation of cellulose after mechanical disruptive treatment, the carboxylate content of the oxidized cellulose may be at least 0.75 mmol COOH/ g pulp, preferably 0.8 - 1 .2 mmol COOH/g pulp, most preferably 0,9 - 1 .1 mmol COOH/g pulp.

The catalytic oxidation does not change the crystalline structure of the cellulose, but the crystalline structure remains "cellulose I" also in the oxidized cellulose.

Then, the oxidized cellulose is subjected to a mechanical process of fibrillating. According to one embodiment of the method, the mechanical process of fibrillating is conducted in a high pressure homogenizer, and according to another embodiment, a fluidizer is used. The energy taken by the fibrillating work is normally expressed in terms of energy per processed material quantity, in units of e.g. kWh/kg, MWh/ton, or units proportional to these. In order to reach sufficient fibrillation level as well as desired viscosity, at least 2 MWh / t (dry pulp) may be required. According to still another embodiment of the method, fibrillation is performed in low concentration (1 -4 %) aqueous dispersion. In this context, fibrillating means disintegrating the fibers to microfibrils, not to be confused with the method where fibrils are only made to protrude from the surface of the pulp fibers.

Fluidizers and homogenizers are known in fibrillating fibrous dispersions into microfibrils, and the process is based on the use of high pressure and shear forces at high speeds when the dispersion is forced through a small gap. Fluidizers of microfluidics and homogenizers of GEA can be mentioned as two examples.

The invention is not limited to catalytically oxidized nanofibrillar cellulose, but carboxymethylated and cationically charged nanofibrillar cellulose can be used as well, if the pretreatment is performed carefully enough so that the crystalline structure of the cellulose is not altered and it is "cellulose I" also in the chemically modified form. As shown in Fig. 1 , the left image is an AFM (atomic force microscopy) image of nanofibrillar cellulose with low aspect ratio (low aspect ratio nanofibrillar cellulose, "NFC-L") according to one embodiment of the method. The image area is 5 microns. The right image is an AFM image of oxidized cellulose with higher aspect ratio. The image area is 2 microns (μιτι).

The sample in Fig. 1 was obtained from catalytically oxidized cellulose having 1 ,02 mmol COOH/ g oxidized pulp, which was made to nanofibrillar cellulose by a fluidizer. Compared with the previously known cellulose whiskers, made by acid hydrolysis, the low aspect ratio nanofibrillar cellulose (NFC-L) is longer and has more bent shape, while it is shorter than the nanofibrillar cellulose that is conventionally made to achieve high viscosity. This is believed to be related to the presence of the amorphous regions of cellulose next to the crystalline regions of cellulose in the fibrils, which amorphous regions were conserved during the treatment. Thus, the method where chemical pretreatment is combined with mechanical treatment, which is allowed to proceed far enough beyond the highest value of viscosity, yields an aqueous dispersion of new grade of nanofibrillar cellulose which, in addition to novel rheological properties expressed as viscosity values, also shows novel morphology of the microfibrils.

Fig. 2 shows flow profiles (viscosity vs. shear stress) of 0.5 % aqueous dispersions of high aspect ratio nanofibrillar cellulose (NFC-H) and low aspect ratio nanofibrillar cellulose (NFC-L). SampleNFC-H is TEMPO- oxidized cellulose with high aspect ratio, leading to high viscosity. Sample NFC-L is the "whisker-like" nanofibrillar cellulose with low aspect ratio, leading to low viscosity.

Samples of the obtained low-aspect ratio nanofibrillar cellulose were also pre-ground, followed by fibrillation in Microfluidics Fluidizer M-7250, once trough ΑΡΜ+200μιη prechambers and 7 times through APM+100 μιτι chambers. The zero-shear viscosity measured by a rotational rheometer is the viscosity value of aqueous 0.5 wt-% nanofibrillar cellulose dispersion in a region of constant viscosity at small shear stresses when the shear stresses approach zero. It can be seen that in the curves, the zero shear viscosity is below 10 Pa*s and even below 1 Pa*s for a 0.5 wt-% aqueous dispersion of NFC-L.

The apparent viscosity of NFC is measured with a Brookfield viscometer (Brookfield viscosity) or another corresponding apparatus. Suitably a vane spindle (number 73) is used. There are several commercial Brookfield viscometers available for measuring apparent viscosity, which all are based on the same principle. Suitably RVDV spring (Brookfield RVDV-III) is used in the apparatus. As a result, a viscosity graph is obtained with varying shear rate. A low rotational speed 10 rpm is suitable. Fig. 3 shows the viscosity change of nanofibrillar cellulose along with the number of passes (cycles), and columns "Trend 1 " shows the measurements measured immediately after fluidization, the NFC sample being diluted in water with agitation to a concentration 0.8 wt-% for the measurement. As can be seen in the figure, the Brookfield viscosity at 10 rpm increased dramatically up to 18,000 mPa-s after the second pass, and after the third pass, the viscosity value is clearly inversely proportional to the number of passes. The mechanical treatment is preferably continued until the Brookfield viscosity is below 5000 mPa*s , which is attained after the 4^th pass in Fig. 3. The treatment is preferably discontinued before the Brookfield viscosity drops below 1000 mPa-s (measured at 0.8 wt-%).

Turbidity may be measured quantitatively using optical turbidity measuring instruments. There are several commercial turbidometers available for measuring quantitatively turbidity. In the present case the method based on nephelometry is used. The units of turbidity from a calibrated nephelometer are called Nephelometric Turbidity Units (NTU). The measuring apparatus (turbidometer) is calibrated and controlled with standard calibration samples, followed by measuring of the turbidity of the diluted NFC sample.

In the method, a nanofibrillar cellulose sample is diluted within a liquid, preferably in water, to a concentration below the gel point of said nanofibrillar cellulose, and turbidity of the diluted sample is measured. Said concentrationwhere the turbidity of the nanofibrillar cellulose sampples is measured is 0.1 %. The mean value and standard deviation are calculated from the obtained results, and the final result is given as NTU units. The novel low-aspect ratio grade has typically the turbidity below 10 NTU in the above-mentioned measuring conditions.

Fig. 4 shows the pickering stabilization ability of nanofibrillar cellulose according to one embodiment. 1 % SDS surfactant was used to create foam in both experimental group and control group, and in the experimental group 0.5% of nanofibrillar cellulose was also used. Materials were mixed with ultraturrax to create the foams. Both the high-aspect ratio nanofibrillar cellulose (NFC-H) and novel low-aspect ratio oxidized nanofibrillar cellulose (NFC-L) was used. Highest row represents the control foam made only from water and air with 1 % SDS, middle row describes the 0.5% NFC-H sample, and the lowest row represents the 0.5% NFC-L sample. As can be seen in the figure, the nanofibrillar cellulose made by the method (NFC-L) performed excellently in pickering stability of foam.

The results of the same sample foams are described in the curve of Fig. 5 as the amount of drained water vs. storage time. The drained liquid was measured from the top fraction of the foams placed in the vials with a Turbiscan device. From Figures 4 and 5 it is clear that the low aspect ratio oxidized nanofibrillar cellulose is extremely efficient stabilizer of foams against coalescence upon aging. As Fig. 4 visualizes the foam structures as a function of time for the three model foams, Fig. 5 shows the kinetics of the bubble coalescence and water bleeding. Foam stabilized with NFC-L is stabile several days, while the control foam collapses within minutes and in the foam stabilized with NFC-H the water bleedin starts gradually.

Fig. 6 shows photographs of three fresh model foam systems made in accordance with the description above. A in the upper left corner is the reference foam, scale bar 200 microns, B in the upper right corner is the foam with NFC-H, scale bar 100 microns, C in the lower left corner is foam with NFC-L, scale bar 100 microns, and D on the lower right corner is the same foam with NFC-L, scale bar 200 microns.

The foam structures are clearly different for the three model foams. In the reference SDS foam (1 % SDS, air, and water mixed with ultraturrax), the bubbles are closely packed and partially started to coalesce. The bubble diameters are between 100 to 200 microns. In the model foam with 1 % SDS and 0.5% high aspect ratio NFC (NFC-H), the bubbles are slightly smaller and not as tightly packed. In the model foam with 1 % SDS and 0.5% low aspect ratio NFC (NFC-L), the bubbles are clearly much smaller, typically 20 to 50 microns and well distributed over the whole volume. The bubbles are also well separated without coalescence.

Fig. 7 illustrates the width distribution of oxidized low-aspect ratio NFC, (NFC-L) measured from cryo-TEM image. The continued mechanical disruptive action beyound the peak viscosity values is found to make the fibrils shorter without essential effect on the diameter of the microfibrils, which is also exemplified by the diagram. The number average fibril width is between 2 and 6 nm, while the whole distribution is within the range of 1 to 10 nm.

The novel low-aspect ratio nanofibrillar cellulose has many potential uses, one of which is the pickering stability of heterogeneous systems comprising two immiscible phases which form a dispersion. The nanofibrillar cellulose can be used especially in foam stabilization in oil drilling, foam explosives, or in a so-called foam forming technology. In foam forming, air is mixed to water-based fiber furnish containing structural fibers (such as papermaking fibers) surfactant, and nanofibrillar cellulose as foam stabilisator. The obtained composition is used for forming fibrous sheet-like products, such as mainly porous, smooth and lightweight paper products. However, the applications of the low-aspect ratio nanofibrillar cellulose are not limited to the stabilization of the above-mentioned compositions and to the stabilization of the heteregeneous systems in general. The NFC can also be used in other fields where its morfology and/or rheological properties can be utilized.

Claims

Claims:

1 . Method for preparing nanofibrillar cellulose, comprising

- repeatedly passing fibrous dispersion of ionically charged cellulose through a mechanical process of disrupting fibers into fibrils until the viscosity starts to decrease, wherein the number average diameter of the nanofibrillar cellulose after the mechanical process is in the range of 2 - 10 nm, and the zero-shear viscosity is below 10 Pa-s, preferably below 1 Pa-s, when measured in the concentration of 0.5 wt-%.

2. The method according to claim 1 , wherein the nanofibrillar cellulose has crystalline structure being cellulose I.

3. The method according to claim 1 or 2, wherein the nanofibrillar cellulose has amorphous regions.

4. The method according to any of the preceding claims, wherein the number average length of the nanofibrillar cellulose is below 1 micron, preferably below 500 nm.

5. The method according to any of the preceding claims, wherein the average aspect ratio of the nanofibrillar cellulose is in the range of 80- 300, preferably 100-250.

6. The method according to any of the preceding claims, wherein the method further comprises oxidizing cellulose through N-oxyl mediated catalytic oxidation to obtain oxidized cellulose.

7. The method according to claim 6, wherein the oxidized cellulose has the carboxylate content of at least 0.75 mmol COOH/g pulp, preferably 0.8-1 .2 mmol COOH/g pulp, and most preferably 0.9-1 .1 mmol COOH/g pulp.

8. The method according to any of the preceding claims, wherein the mechanical process of disrupting fibers into fibrils is performed by passing fibrous dispersion through a high pressure homogenizer or fluidizer.

9. Nanofibrillar cellulose obtainable by the method for preparing nanofibrillar cellulose according to any one of claims 1 to 8, wherein the number average diameter of the nanofibrillar cellulose is in the range of 2 - 10 nm, and the zero-shear viscosity is below 10 Pa-s, preferably below 1 Pa-s, when measured in the concentration of 0.5%.

10. The nanofibrillar cellulose according to claim 9, wherein the nanofibrillar cellulose has crystalline structure being cellulose I.

1 1 . The nanofibrillar cellulose according to claim 9 or 10, wherein the nanofibrillar cellulose has amorphous regions.

12. Use of nanofibrillar cellulose prepared by a method according to any of claims 1 -8 or nanofibrillar cellulose according any of claims 9-1 1 for pickering stabilization.

13. Use according to claim 12 in foam stabilization.

14. Use according to claim 13 in foam forming for making fibrous sheet-like products.