WO2014068082A2 - Thermal spraying of ceramic materials - Google Patents
Thermal spraying of ceramic materials Download PDFInfo
- Publication number
- WO2014068082A2 WO2014068082A2 PCT/EP2013/072861 EP2013072861W WO2014068082A2 WO 2014068082 A2 WO2014068082 A2 WO 2014068082A2 EP 2013072861 W EP2013072861 W EP 2013072861W WO 2014068082 A2 WO2014068082 A2 WO 2014068082A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- particles
- metal
- coating
- metal salt
- metal oxide
- Prior art date
Abstract
Description
Claims