WO2013171510A1 - Traitement de matériau polymère usagé - Google Patents
Traitement de matériau polymère usagé Download PDFInfo
- Publication number
- WO2013171510A1 WO2013171510A1 PCT/GB2013/051288 GB2013051288W WO2013171510A1 WO 2013171510 A1 WO2013171510 A1 WO 2013171510A1 GB 2013051288 W GB2013051288 W GB 2013051288W WO 2013171510 A1 WO2013171510 A1 WO 2013171510A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymeric material
- screw
- twin
- waste polymeric
- reactor
- Prior art date
Abstract
La présente invention concerne un procédé et un appareil de traitement de matériau polymère usagé pour produire un hydrocarbure liquide. Le matériau polymère usagé est introduit dans un réacteur à double vis, où le matériau polymère usagé est chauffé à une température à laquelle le matériau polymère usagé se décompose thermiquement. L'hydrocarbure liquide obtenu de la décomposition thermique du matériau polymère usagé est recueilli, de préférence par condensation.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB1208705.2A GB2502126A (en) | 2012-05-17 | 2012-05-17 | Thermal decomposition of waste plastic |
GB1208705.2 | 2012-05-17 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2013171510A1 true WO2013171510A1 (fr) | 2013-11-21 |
Family
ID=46546241
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/GB2013/051288 WO2013171510A1 (fr) | 2012-05-17 | 2013-05-17 | Traitement de matériau polymère usagé |
Country Status (2)
Country | Link |
---|---|
GB (1) | GB2502126A (fr) |
WO (1) | WO2013171510A1 (fr) |
Cited By (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN103773403A (zh) * | 2014-01-15 | 2014-05-07 | 东南大学 | 低热值粘性固体燃料的流化床分级差温热解装置及方法 |
CN106118707A (zh) * | 2016-07-28 | 2016-11-16 | 徐效奇 | 废塑料无害化处理设备及方法 |
US10551059B2 (en) | 2014-12-17 | 2020-02-04 | Pilkington Group Limited | Furnace |
CN112955525A (zh) * | 2018-10-25 | 2021-06-11 | 普罗伊尔有限责任公司 | 用于生产烃的塑料材料解聚方法及其设备 |
US20220219974A1 (en) * | 2021-01-11 | 2022-07-14 | The Boeing Company | Solid hydride flow reactor |
US11999920B2 (en) | 2020-09-14 | 2024-06-04 | Ecolab Usa Inc. | Cold flow additives for plastic-derived synthetic feedstock |
US12031097B2 (en) | 2021-10-14 | 2024-07-09 | Ecolab Usa Inc. | Antifouling agents for plastic-derived synthetic feedstocks |
Families Citing this family (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2503065B (en) * | 2013-02-20 | 2014-11-05 | Recycling Technologies Ltd | Process and apparatus for treating waste comprising mixed plastic waste |
US10377951B2 (en) | 2013-12-04 | 2019-08-13 | Ecomation Oy | Pyrolysis apparatus |
FI128105B (fi) | 2016-05-19 | 2019-09-30 | Ecomation Oy | Pyrolyysilaite |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH05245463A (ja) * | 1991-10-18 | 1993-09-24 | Agency Of Ind Science & Technol | 混合プラスチツク廃棄物の処理方法及び処理装置 |
US6165399A (en) * | 1996-09-26 | 2000-12-26 | Basf Aktiengesellschaft | Process for producing thermoplastics |
US7040797B1 (en) * | 1998-11-17 | 2006-05-09 | Sumitomo Chemical Company, Limited | Method of producing composition comprising thermoplastic resin and rubber |
US20080202983A1 (en) * | 2007-02-23 | 2008-08-28 | Smith David G | Apparatus and process for converting feed material into reusable hydrocarbons |
JP2010155944A (ja) * | 2008-12-29 | 2010-07-15 | Aasu Recycle Kk | 廃プラスチックの油化装置 |
Family Cites Families (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3984288A (en) * | 1974-10-04 | 1976-10-05 | Sumitomo Electric Industries, Ltd. | Method for treatment of rubber and plastic wastes |
JP2004204083A (ja) * | 2002-12-25 | 2004-07-22 | Japan Steel Works Ltd:The | 廃棄プラスチックの燃料化処理装置 |
EP1473137A1 (fr) * | 2003-04-30 | 2004-11-03 | Coperion Werner & Pfleiderer GmbH & Co. KG | Procédé de fusion et homogénéisation de polyoléfines bimodales ou multimodales |
US7846302B1 (en) * | 2006-06-12 | 2010-12-07 | Finley Dana J | Fractional destructive distillation array |
CN101469270B (zh) * | 2007-12-27 | 2012-08-22 | 牛斌 | 工业连续化塑料裂解器 |
US8328993B2 (en) * | 2009-05-18 | 2012-12-11 | Greenlight Energy Solutions, Llc | Pyrolysis reactor for processing municipal wastes |
WO2011007392A1 (fr) * | 2009-07-15 | 2011-01-20 | 株式会社環境創造 | Appareil pour la réduction d'un déchet de matière plastique en huile |
-
2012
- 2012-05-17 GB GB1208705.2A patent/GB2502126A/en not_active Withdrawn
-
2013
- 2013-05-17 WO PCT/GB2013/051288 patent/WO2013171510A1/fr active Application Filing
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH05245463A (ja) * | 1991-10-18 | 1993-09-24 | Agency Of Ind Science & Technol | 混合プラスチツク廃棄物の処理方法及び処理装置 |
US6165399A (en) * | 1996-09-26 | 2000-12-26 | Basf Aktiengesellschaft | Process for producing thermoplastics |
US7040797B1 (en) * | 1998-11-17 | 2006-05-09 | Sumitomo Chemical Company, Limited | Method of producing composition comprising thermoplastic resin and rubber |
US20080202983A1 (en) * | 2007-02-23 | 2008-08-28 | Smith David G | Apparatus and process for converting feed material into reusable hydrocarbons |
JP2010155944A (ja) * | 2008-12-29 | 2010-07-15 | Aasu Recycle Kk | 廃プラスチックの油化装置 |
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN103773403A (zh) * | 2014-01-15 | 2014-05-07 | 东南大学 | 低热值粘性固体燃料的流化床分级差温热解装置及方法 |
US10551059B2 (en) | 2014-12-17 | 2020-02-04 | Pilkington Group Limited | Furnace |
CN106118707A (zh) * | 2016-07-28 | 2016-11-16 | 徐效奇 | 废塑料无害化处理设备及方法 |
CN112955525A (zh) * | 2018-10-25 | 2021-06-11 | 普罗伊尔有限责任公司 | 用于生产烃的塑料材料解聚方法及其设备 |
US11999920B2 (en) | 2020-09-14 | 2024-06-04 | Ecolab Usa Inc. | Cold flow additives for plastic-derived synthetic feedstock |
US20220219974A1 (en) * | 2021-01-11 | 2022-07-14 | The Boeing Company | Solid hydride flow reactor |
US11827516B2 (en) * | 2021-01-11 | 2023-11-28 | The Boeing Company | Solid hydride flow reactor |
US12031097B2 (en) | 2021-10-14 | 2024-07-09 | Ecolab Usa Inc. | Antifouling agents for plastic-derived synthetic feedstocks |
Also Published As
Publication number | Publication date |
---|---|
GB201208705D0 (en) | 2012-07-04 |
GB2502126A (en) | 2013-11-20 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2013171510A1 (fr) | Traitement de matériau polymère usagé | |
EP2814909B1 (fr) | Appareil de pyrolyse à zone délimitée, à deux étages | |
RU2700030C1 (ru) | Способ и аппарат для производства нефтепродуктов | |
JPS6321544Y2 (fr) | ||
KR101298819B1 (ko) | 무수 무용매 중합체의 제조 방법 | |
US8674154B2 (en) | Apparatus and method for conducting thermolysis of plastic waste in continuous manner | |
CN102821929B (zh) | 不含水和溶剂的聚合物的生产方法 | |
EP2406348B1 (fr) | Appareil pour réaliser la thermolyse de déchets plastiques | |
EP2998383A1 (fr) | Appareil et procédé de pyrolyse à définition de zones destiné à la conversion de déchets de polymère | |
US20070131585A1 (en) | High-speed chamber mixer for catalytic oil suspensions as a reactor for the depolymerization and polymerization of hydrocarbon-containing residues in the oil circulation to obtain middle distillate | |
US20160040074A1 (en) | Method for the Degrading of Synthetic Polymers and Device for Carrying Out Said Method | |
GB2483851A (en) | Waste processing apparatus and methods with screw compaction and heating | |
CA2501262A1 (fr) | Dispositif et procede permettant le traitement d'un materiau dans des conditions pyrolytiques et utilisation de ceux-ci | |
JP2010500170A (ja) | 長鎖有機物の分子構造を分解するための装置 | |
CN105924552B (zh) | 一种外旋转自搅拌式反应釜热裂解法连续生产聚乙烯蜡方法 | |
JP5175721B2 (ja) | 固体材料の有機分子の炭素鎖の切断方法及び関連装置 | |
US20240059974A1 (en) | Char handling section and depolymerization process associated therewith | |
EP3347436B1 (fr) | Réacteur de pyrolyse flash | |
EP2368918A1 (fr) | Processus pour la fabrication de polymères sans eau et sans solvant | |
US4332932A (en) | Method for producing a rubber melt in a temperature-controlled screw extruder | |
US9657990B2 (en) | Apparatus for thermal degradation of feedstock | |
EP4182405B1 (fr) | Procédé de pyrolyse de déchets dans un procédé industriel | |
EP0763412B1 (fr) | Réacteur pyrolytique pour déchet en matière plastique | |
JP2023540691A (ja) | プラスチック変換供給システム | |
JPH06256769A (ja) | ゴム・プラスチック廃棄物の連続油化装置 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 13730045 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 13730045 Country of ref document: EP Kind code of ref document: A1 |