WO2013055075A2 - 다이캐스팅용 고열전도도 Ａｌ-Ｓｉ-Ｆｅ-Ｚｎ 합금 - Google Patents

다이캐스팅용 고열전도도 Ａｌ-Ｓｉ-Ｆｅ-Ｚｎ 합금 Download PDF

Info

Publication number
WO2013055075A2
WO2013055075A2 PCT/KR2012/008162 KR2012008162W WO2013055075A2 WO 2013055075 A2 WO2013055075 A2 WO 2013055075A2 KR 2012008162 W KR2012008162 W KR 2012008162W WO 2013055075 A2 WO2013055075 A2 WO 2013055075A2
Authority
WO
WIPO (PCT)
Prior art keywords
alloy
thermal conductivity
die casting
present
aluminum alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2012/008162
Other languages
English (en)
French (fr)
Other versions
WO2013055075A3 (ko
Inventor
김기태
신제식
고세현
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Korea Institute of Industrial Technology KITECH
Original Assignee
Korea Institute of Industrial Technology KITECH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Korea Institute of Industrial Technology KITECH filed Critical Korea Institute of Industrial Technology KITECH
Priority to US14/350,080 priority Critical patent/US20140234159A1/en
Publication of WO2013055075A2 publication Critical patent/WO2013055075A2/ko
Publication of WO2013055075A3 publication Critical patent/WO2013055075A3/ko
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

본 발명은 우수한 주조성과 양호한 기계적 특성을 가지면서 동시에 우수한 열전도도를 얻을 수 있어, 방열특성이 요구되는 각종 구조용 제품에 적용될 수 있는 다이캐스팅용 알루미늄 합금에 관한 것이다. 본 발명에 따른 다이캐스팅용 알루미늄 합금은, 실리콘(Si) 1.0 ~ 2.0중량%, 철(Fe) 0.8~1.6중량%, 및 아연(Zn) 0.6~ 1.3중량% 를 포함하고, 나머지는 알루미늄(Al)과 불가피한 불순물로 이루어진 것을 특징으로 한다.

Description

다이캐스팅용 고열전도도 Ａｌ-Ｓｉ-Ｆｅ-Ｚｎ 합금
본 발명은 다이캐스팅용 고열전도도 알루미늄 합금에 관한 것으로서 특히, 우수한 주조성을 가지면서 동시에 우수한 열전도도를 얻을 수 있는 알루미늄 합금에 관한 것이다.
다이캐스팅은 다이 주조라고도 한다. 필요한 주조형상에 완전히 일치하도록 정확하게 기계가공된 강제의 금형에 용융금속을 주입하여 금형과 똑같은 주물을 얻는 정밀주조법이며, 이 주조법을 통해 제조한 제품을 다이캐스트 주물이라고 한다.
다이캐스팅 주물은 치수가 정확하므로 다듬질할 필요가 거의 없는 장점 외에 기계적 성질이 우수하며, 대량생산이 가능하다는 특징이 있다. 한편, 다이캐스팅 주조에 이용되는 금속은 일반적으로 아연, 알루미늄, 주석, 구리, 마그네슘 등의 합금이며, 이들 합금은 용융되어 용탕으로 만들어진 후, 공기압, 수압, 유압 등의 가압장치를 통해 다이캐스트 장치의 금형에 주입되어 금속 냉각 응고된다.
이러한 과정을 통해 만들어진 다이캐스팅 주조품은 여러 분야에 사용되고 있으며, 특히 자동차부품에 많이 적용되고 있고, 전기기기, 광학기기, 차량, 방직기, 건축, 계측기 등의 부품 제작 등에도 널리 사용되고 있다.
한편, 다이캐스팅용 알루미늄 합금으로는 주조성이 우수한 Al-Si계 합금 및 Al-Mg계 합금 등이 주로 사용되고 있다. 그런데 Al-Si계 합금 또는 Al-Mg계 합금의 경우, 주조성은 우수하나 열전도도가 90~140W/mK로 낮기 때문에, 160W/mK 이상의 높은 열전도도를 필요로 하는 전기, 전자 및 자동차용 방열부품에는 사용이 제한되어 왔다.
이와 같은 높은 열전도도를 요구하는 방열부품에는, 종래 열전도도가 220W/mK 이상으로 매우 높은 순 알루미늄을 그대로 다이캐스팅한 제품이 전기, 전자제품용 로터 등에 일부 사용되고 있는데, 순 알루미늄은 열전도도는 매우 우수하지만 인장강도가 낮고 주조성이 좋지 않기 때문에, 열전도도와 함께 우수한 기계적 특성을 요구하는 구조용 부품에까지 적용하기에는 한계가 있다.
이에 따라, 전기, 전자 및 자동차용 방열부품 등에 사용하기 위하여 우수한 주조성을 가지면서 동시에 160W/mK 이상의 높은 열전도도를 갖는 다이캐스팅용 알루미늄 합금 개발에 대한 필요성이 절실히 요구되고 있지만, 현재까지는 우수한 주조성을 가지면서 동시에 160W/mK 이상의 열전도도를 갖는 다이캐스팅용 알루미늄 합금이 개발되지 못한 상태이므로, 열전도도가 90~140W/mK인 Al-Si계 합금 및 Al-Mg계 합금 등이 다이캐스팅용 알루미늄 합금으로 사용되고 있는 실정이다.
본 발명은 상기와 같은 종래기술의 문제점을 해결하기 위하여 안출한 것으로서, 우수한 주조성과 함께 순 알루미늄에 비해 높은 강도를 가지며, 동시에 160W/mK 이상의 열전도도를 나타내, 우수한 열전도도를 요하는 다양한 구조 부품에 적용할 수 있는 다이캐스팅용 알루미늄 합금을 제공하는 것을 과제로 한다.
상기의 과제의 해결수단으로 본 발명은, 실리콘(Si) 1.0~2.0중량%, 철(Fe) 0.5~1.6중량%, 및 아연(Zn) 0.6~1.6중량%를 포함하고, 나머지는 알루미늄(Al)과 불가피한 불순물로 이루어진 다이캐스팅용 알루미늄 합금을 제공한다.
또한, 본 발명에 따른 알루미늄 합금에 있어서, 열전도도는 160W/mK 이상이며, 바람직하게는 170W/mK 이상일 수 있다.
또한, 본 발명에 따른 알루미늄 합금에 있어서, 고액공존영역인 △T는 70℃ 이하이다.
또한, 본 발명에 따른 알루미늄 합금에 있어서, 인장강도는 110 MPa 이상이고, 바람직하게는 120MPa일 수 있다.
또한, 본 발명에 따른 알루미늄 합금에 있어서, 미세조직내에 분산된 Fe화합물을 포함할 수 있다.
본 발명에 따른 알루미늄 합금은, 실리콘(Si), 철(Fe) 및 아연(Zn)의 성분의 제어를 통해, 다이캐스팅 주조법에서 건전한 주물을 얻을 수 있는데 요구되는 주조성을 확보함과 동시에, 양호한 기계적 강도 및 우수한 열전도도를 가져, 160W/mK 이상의 열전도도를 요구하는 전기, 전자 및 자동차용 방열부품의 제조에 적합하게 사용될 수 있다.
도 1은 본 발명에 따른 알루미늄 합금의 주조성을 평가하기 위한 유동장 측정장치의 사진이다.
이하 본 발명의 바람직한 실시예에 따른 알루미늄 합금에 대하여 상세하게 설명하겠지만 본 발명이 하기의 실시예에 제한되는 것은 아니다. 따라서 해당 분야에서 통상의 지식을 가진 자라면 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 본 발명을 다양하게 변경할 수 있음은 자명하다.
또한, 본 발명의 실시예를 설명하기 위해 사용되는 단수 형태들은 문구들이 이와 명백히 반대의 의미를 나타내지 않는 한 복수 형태들도 포함하는 것을 의미한다.
본 발명은 실리콘(Si), 철(Fe) 및 아연(Zn)이 합금되어 구성된 다이캐스팅용 고열전도도 알루미늄 합금으로서, 실리콘(Si) 1.0~2.0중량%, 철(Fe) 0.5~1.6중량%, 아연(Zn) 0.6~1.6중량% 및 나머지는 알루미늄(Al)과 불순물로 구성된다.
본 발명은 상기 각각의 조성량에 따라서 알루미늄의 주조성을 향상시킬 수 있는 합금원소와 알루미늄 기지 금속에 고용되어 고용강화 효과를 얻을 수 있는 합금원소, 그리고 알루미늄 기지 금속에의 고용도가 매우 낮아서 열전도도 저하를 최소화할 수 있는 합금원소를 복합적으로 첨가함으로써, 우수한 주조성과 양호한 기계적 특성을 나타내면서 동시에 160W/mK 이상의 열전도도를 나타낼 수 있는 다이캐스팅용 고열전도도 알루미늄 합금을 얻는다.
상기 각 합금원소의 첨가 및 함량 한정 이유는 다음과 같다.
실리콘(Si)은 알루미늄에 합금원소로 첨가되어 주조성을 향상시키고 고용강화 효과에 따라서 인장강도를 증가시킬 수 있는 원소이다. 본 발명에 따른 합금에는 실리콘이 1.0~2.0중량% 첨가된다. 이는 상기 실리콘의 함량이 1.0중량% 미만이면 합금의 주조성이 저하되어 다이캐스팅에 의하여 제품을 성형할 때에 일부 미성형부가 발생되어 주조품의 건전성이 크게 훼손될 수 있고, 상기 실리콘의 함량이 2.0중량% 초과하면 열전도도가 저하되어, 본 발명에서 목적으로 하는 160W/mK 이상의 열전도도를 얻을 수 없기 때문이다.
철(Fe)은 상온에서 알루미늄에의 고용도가 0.052중량%로서 매우 낮아 주조 후에는 대부분 Al3Fe 등의 금속간화합물로 정출되기 때문에 알루미늄에 첨가되어 알루미늄의 열전도도 저하를 최소화하면서 강도를 증가시킬 수 있고, 동시에 다이캐스팅에 의하여 알루미늄 합금 제품을 성형할 때에 금형소착을 줄일 수 있도록 하는 합금원소이다. 본 발명에 의한 다이캐스팅용 합금에는 철이 0.5~1.6중량% 첨가된다. 이는, 상기 철의 함량이 0.5중량% 미만이면 금형소착 방지 효과가 낮아져 다이캐스팅에 의하여 제품을 성형할 때에 일부 금형부위에 제품의 소착현상이 발생하고 강도도 충분하지 못하게 되고, 상기 철의 함량이 1.6중량% 초과하면 합금내에서 Fe-부화상(Fe-rich상)이 과도하게 정출되어, 합금의 주조성을 저하시키기 때문이다. 바람직한 철(Fe) 함량은 0.8~1.2중량%이다.
아연(Zn)은 본 발명에 의한 알루미늄에 합금원소로 첨가되어 주조성을 향상시킬 뿐 아니라, 고용강화 효과를 통해 인장강도도 증가시킬 수 있는 합금원소이다. 본 발명에 의한 합금에는 아연이 0.6~1.6중량% 첨가되는데, 이는 상기 아연의 함량이 0.6중량% 미만이면 합금의 주조성이 저하되어 다이캐스팅에 의하여 제품을 성형할 때에 일부 미성형부가 발생되고, 아연의 함량이 1.6중량% 초과하면 합금의 열전도도가 저하되어 본 발명에서 목적으로 하는 160W/mK 이상의 양호한 열전도도를 얻을 수 없기 때문이다. 바람직한 아연(Zn)의 함량은 0.8~1.2중량%이다.
[실시예]
본 발명의 실시예에 따른 다이캐스팅용 고열전도도 Al-Si-Fe-Zn 합금에 대하여 하기 표 1 및 2를 참조하여, 상세하게 설명한다.
본 발명자들은 다이캐스팅용 고열전도도 Al-Si-Fe-Zn 합금을 제조하기 위해 하기 표 1에 나타낸 조성을 갖는 합금을, 다이캐스팅 제조시에 통상적으로 사용되는 용융 교반식 알루미늄 합금 제조 방법으로 시험편을 제조하였다.
표 1
합금(중량%) Si Fe Zn Al
실시예 1 1.03 0.89 1.00 bal.
2 1.21 1.08 0.97 bal.
3 1.67 0.84 1.00 bal.
4 1.21 0.59 1.42 bal.
5 1.51 0.57 1.44 bal.
비교예 1 10.20 1.17 0.92 bal.
2 0.56 0.79 1.02 bal.
3 4.5 0.8 0.60 bal.
4 1.12 1.83 0.75 bal.
5 1.33 1.14 0.46 bal.
6 1.58 0.97 1.45 bal.
구체적으로, 상기 표 1과 같은 조성이 되도록 알루미늄 합금의 원료를 준비한 후, 전기저항식 용해로에 장입하여 대기 중에서 원료를 용해하여 용탕을 제조한 후에, 금형을 이용하여 주조성 평가를 위한 유동성 시험편을 제조하였고 또한 열전도도, 액상 온도 및 고상온도 등을 측정하기 위한 특성평가용 시험편을 제조하였다.
본 발명의 실시예에 따른 합금의 주목적 중 하나인 열전도도에 대해서는, 먼저 도전율 측정기를 이용하여 제조한 시편의 상온에서 도전율을 측정한 후, 하기 [식 1]의 환산식으로 환산하는 방식을 통해 열전도도를 얻었다.
[식 1]
K 〓 5.02σT x 10-9 + 0.03
(여기서, K는 열전도도, σ는 도전율, T는 절대온도임)
또한, 다이캐스팅 주조에 필수적인 주조성 평가를 위해, 합금 용탕을 200℃의 온도로 유지된 폭 12㎜, 두께 5㎜, 최대길이 780㎜의 도 1과 같은 유동성 시험 금형에 주입하고 합금 용탕이 일정한 거리를 유동한 후에 응고된 길이를 측정하는 방법으로 유동장을 측정하였으며, 또한 열분석기를 이용하여 액상 온도 및 고상 온도의 차이를 측정하는 방식으로 고액공존영역의 크기(△T)를 측정하였다.
하기 표 2는 각 합금의 유동장, 열전도도, 액상 온도와 고상 온도 및 그 차이를 평가한 결과를 나타낸 것이다.
표 2
합금 유동장(mm) 열전도도(W/mK) 액상온도(℃) 고상온도(℃) △T(℃)
실시예 1 780 175 654 620 34
2 780 171 652 616 36
3 780 163 650 606 44
4 780 182 652 602 50
5 780 179 650 588 62
비교예 1 780 95 575 501 74
2 720 186 656 620 36
3 - 142 630 575 55
4 560 165 - - -
5 750 168 - - -
6 780 155 - - -
상기 표 2에서 확인되는 바와 같이, 본 발명의 실시예 1 내지 5에 따른 알루미늄 합금들은 모두 열전도도가 160W/mK 이상(나아가서는 170W/mK 이상)으로, 방열부품에 요구되는 수준의 우수한 열전도도를 나타내었다. 이 중에서 주조성을 해하지 않는 범위에서 실리콘(Si) 함량이 낮은 실시예 1과, 철(Fe) 함량이 상대적으로 많은 실시예 2, 실시예 4 및 5 합금의 열전도도가 모두 170W/mK 이상으로 매우 높음을 알 수 있다.
또한, 상기 표 2에서 나타낸 유동장과, 액상온도와 고상온도의 차이인 △T는 합금의 주조성을 평가할 수 있는 주요한 지표인데, 유동장은 클수록 합금의 유동성이 우수한 것을 나타내며 액상온도와 고상온도의 차이인 △T는 작을수록 주조성이 우수하다고 평가된다.
상기 표 2에서 확인되는 바와 같이, 본 발명의 실시예에 따른 알루미늄 합금들은 유동장의 길이가 780mm로, 다이캐스팅용 알루미늄 합금으로 널리 사용되고 있는 Al-Si 합금(ADC 12, 비교예 1)과 비교하여 동등한 수준임을 알 수 있다.
한편, △T의 경우, 본 발명의 실시예 1 내지 5에 따른 알루미늄 합금은 70℃ 미만인데, 다이캐스팅용 알루미늄 합금으로 널리 사용되고 있는 비교예 4의 74℃에 비해서도 낮다.
즉, 본 발명의 실시예 1 내지 5에 따른 합금은, 주조성을 나타내는 2가지 지표인 유동장과 △T에서 모두 다이캐스팅용 알루미늄 합금으로 널리 사용되는 비교예 1과 동등하거나 나은 수준이므로, 다이캐스팅에 요구되는 주조성을 구비하고 있다고 할 수 있다.
한편, 비교예 2는 본 발명의 실시예에 비해 실리콘(Si) 함량이 낮은 0.56중량%를 첨가한 Al-Si-Fe-Zn 합금인데, 실리콘(Si) 함량이 부족하여 유동장이 720mm로 본 발명의 실시예에 따른 알루미늄 합금에 비해 주조성이 떨어진다.
또한, 비교예 3은 본 발명의 실시예에 비해 실리콘(Si) 함량이 상당히 높은 4.5중량%를 첨가한 Al-Si-Fe-Zn 합금인데, 그 결과가 열전도도가 142W/mK로 방열제품에서 요구되는 수준을 맞추기 어렵다.
또한, 비교예 4는 본 발명의 실시예에 비해 철(Fe) 함량이 높은 1.83중량%를 첨가한 Al-Si-Fe-Zn 합금인데, 철(Fe) 함량이 높아 유동장이 560mm로, 본 발명의 실시예에 따른 알루미늄 합금에 비해 주조성이 현저하게 떨어진다.
또한, 비교예 5는 본 발명의 실시예에 비해 아연(Zn) 함량이 낮은 0.46중량%를 첨가한 Al-Si-Fe-Zn 합금인데, 유동장은 750mm로 본 발명의 실시예에 따른 합금에 비해 주조성이 떨어진다.
또한, 비교예 6은 본 발명의 실시예에 비해 아연(Zn) 함량이 높은 1.45중량%를 첨가한 Al-Si-Fe-Zn 합금인데, 주조성은 본 발명의 실시예와 동등한 수준이나, 열전도도가 155W/mK로 방열제품에서 요구하는 열전도도보다 낮다.

Claims (6)

  1. 실리콘(Si) 1.0~2.0중량%, 철(Fe) 0.5~1.6중량%, 및 아연(Zn) 0.6~1.6중량%를 포함하고, 나머지는 알루미늄(Al)과 불가피한 불순물로 이루어진 다이캐스팅용 알루미늄 합금.
  2. 제 1 항에 있어서,
    상기 철(Fe)의 함량은 0.8~1.2중량%인 것을 특징으로 하는 다이캐스팅용 알루미늄 합금.
  3. 제 1 항에 있어서,
    상기 아연(Zn)의 함량은 0.8~1.2중량%인 것을 특징으로 하는 다이캐스팅용 알루미늄 합금.
  4. 제 1 항에 있어서,
    상기 알루미늄 합금의 열전도도는 160W/mK 이상인 것을 특징으로 하는 다이캐스팅용 알루미늄 합금.
  5. 제 1 항에 있어서,
    상기 알루미늄 합금의 열전도도는 170W/mK 이상인 것을 특징으로 하는 다이캐스팅용 알루미늄 합금.
  6. 제 1 항에 있어서,
    상기 알루미늄 합금의 고액공존영역인 △T는 70℃ 이하인 다이캐스팅용 알루미늄 합금.
PCT/KR2012/008162 2011-10-10 2012-10-09 다이캐스팅용 고열전도도 Ａｌ-Ｓｉ-Ｆｅ-Ｚｎ 합금 Ceased WO2013055075A2 (ko)