Classifications

• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
  • H01M4/134—Electrodes based on metals, Si or alloys
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
  • H01M4/139—Processes of manufacture
  • H01M4/1395—Processes of manufacture of electrodes based on metals, Si or alloys
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/64—Carriers or collectors
  • H01M4/66—Selection of materials
  • H01M4/661—Metal or alloys, e.g. alloy coatings
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/64—Carriers or collectors
  • H01M4/66—Selection of materials
  • H01M4/665—Composites
  • H01M4/667—Composites in the form of layers, e.g. coatings
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/64—Carriers or collectors
  • H01M4/70—Carriers or collectors characterised by shape or form
  • H01M4/80—Porous plates, e.g. sintered carriers
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M10/00—Secondary cells; Manufacture thereof
  • H01M10/05—Accumulators with non-aqueous electrolyte
  • H01M10/052—Li-accumulators
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
  • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
  • Y02E60/10—Energy storage using batteries

Definitions

• High capacity electrochemically active materials are very desirable for battery applications.
• these materials exhibit substantial volume changes during battery cycling, e.g., swelling during lithiation and contracting during delithiation.
• silicon swells as much as 400% during lithiation to its theoretical capacity of about 4200 mAh/g or Li 4 4 Si structure. Volume changes of this magnitude cause pulverization of active materials structures, losses of electrical connections, and capacity fading.
• Nanostructures have at least one nanoscale dimension, and swelling- contracting along this dimension tends to be less destructive than along larger sides and dimensions. As such, nanostructures can remain substantially intact during battery cycling.
• integrating multiple nanostructures into battery electrode layers that have adequate active material loadings is difficult. Such integration involves establishing and maintaining electrical interconnections between such nanostructures and current collectors and providing mechanical support to these nanostructures on the current collectors or some other substrates over many cycles.
• smaller nanostructures often do not provide adequate amounts of high capacity active materials in certain electrode designs. For example, depositing a nanofilm onto a conventional flat substrate does not provide adequate active material loading if the nanofilm is kept thinner than typical fracture limits of high capacity active materials.
• nanostructures are slow and often involve expensive materials. For example, etching silicon nanowires from bulk particles uses silver catalysts and expensive etching solution. Growing long crystalline silicon structures can also be a relative slow process and may involve expensive catalysts, such as gold.
• a battery electrode structure may include multiple template layers.
• An initial template layer may include nanostructures attached to a substrate and have a controlled density. This initial layer may be formed using a controlled thickness source material layer provided, for example, on a substantially inert substrate.
• Additional one or more template layers are then formed over the initial layer resulting in a multilayer template structure with specific characteristics, such as a surface area, thickness, and porosity.
• the multilayer template structure is then coated with a high capacity active material.
• an electrode material includes an electronically conductive layer, a layer of first nanostructures positioned on the electronically conductive layer, and a layer of second nanostructures positioned on the layer of the first nanostructures.
• the first nanostructures include one or more metal silicides.
• the electrode material also includes a coating of electrode active material that covers at least a portion of the first nanostructures and the second nanostructures. Examples of metal silicides that could be included in the first nanostructures include nickel silicides, cobalt silicides, copper silicides, silver silicides, chromium silicides, titanium silicides, aluminum silicides, zinc silicides, and iron silicides.
• metal silicides include Ni2Si, NiSi, NiSi 2 , and combinations thereof.
• the electronically conductive layer may include stainless steel.
• electrode active materials include crystalline silicon, amorphous silicon, silicon oxides, silicon oxy-nitrides, tin-containing materials, germanium -containing materials, and carbon- containing materials.
• the layer of the first nanostructures includes multiple nanowires rooted to the electromcally conductive layer.
• the electrode material may have porosity between about 30% and 50%.
• the coating of the electrode active material may include multiple layers. At least some of these multiple layers may have different porosities.
• multiple layers may include an inner layer and an outer layer.
• the inner layer may have a lower porosity than the outer layer.
• the multiple layers may include at least some layers that have different hydrogen concentrations or, more generally, different compositions. In certain embodiments, at least some of the multiple layers have different morphologies. In certain
• the coating of the electrode active material is positioned between at least a portion of the layer of the first nanostructures and the layer of the second nanostructures.
• a lay er of the second nanostructures may include carbon nanofibers and/or multidimensional metal silicide structures.
• Multidimensional metal silicide structures may include support structures to which plurality of metal silicide nanowires are attached.
• an electrode assembly including a conductive substrate for conducting electrical current between an electrode active material and batter ⁇ ' terminal and an electrode material.
• the electrode material in turn includes a layer of the first nanostructures attached to the conductive substrate.
• the first nanostructures include one or more metal silicides.
• the electrode material also includes a layer of second nanostructures positioned on the layer of the first nanostructures and a coating of the el ectrode active material that covers at least a portion of the first nanostructures and the second nanostructures.
• the first and second nanostructures may provide electronic communication between the electrode active material and conductive substrate.
• an electrochemical cell including a first electrode, a second electrode, and an electrolyte providing ionic communication between the first electrode and the second electrode.
• the first electrode may include an electronically conductive layer, a layer of first nanostructures positioned on the electronically conductive layer, a layer of second nanostructures positioned on the layer of the first nanostructures, and a coating of electrode active material that covers at least a portion of the first nanostructures and the second nanostructures.
• the first nanostructures may include one or more metal silicides.
• a method of fabricating an electrode may involve receiving a substrate having a base material and forming a source material layer having a controlled thickness.
• the source material layer may include a metal that is different from the base material.
• the method may proceed with forming multiple template nanostructures having a metal silicide attached to the base material by chemically reacted the metal with a silicon containing precursor.
• the method may then proceed with forming a coating of an electrochemically active material over the template nanostructures.
• the electrochemically active material is configured to take in and release lithium ions during cycling. Multiple template nanostructures facilitate conduction of electrical current to and from the electrochemically active material.
• forming the coating of the electrochemically active material involves forming a first portion of the coating using thermal chemical vapor deposition and forming a second portion of the coating using plasma enhanced chemical vapor deposition.
• the method may also involve controlling porosity of the coating of the electrochemically active material using one or more of the following techniques: doping, etching, ion implantation, and annealing.
• forming the coating of the electrochemically active material involves multistep thermal chemical vapor deposition.
• FIGS. 1A-C are schematic representations of an electrode substrate at different stages of template formation, in accordance with certain embodiments.
• FIG. ID is a Scanning Electron Microscope image of a nanostructured template containing nickel silicide nanowires.
• FIG. IE is a Scanning Electron Microscope image of a nanostructured template containing nickel silicide nanowires with carbon nanofibers (CNF) deposited over the nickel silicide nanowires.
• CNF carbon nanofibers
• FIG. IF is a Scanning Electron Microscope image of a nanostructured template containing nickel silicide nanowires with a layer of multidimensional nickel silicide structures deposited over the nickel silicide nanowires.
• FIGS. 2A-2C are Scanning Electron Microscope images of three electrode layers having different porosities.
• FIG. 3A is a schematic representation of an electrode layer containing a single- layer template coated with a high capacity active material, in accordance with certain embodiments.
• FIG. 3B is a Scanning Electron Microscope image of an electrode layer containing a single-layer nickel silicide template coated with amorphous silicon.
• FIG. 3C is a schematic representation of an electrode layer containing a multilayer template formed by a single-layered template and carbon nanofibers (CNF), in accordance with certain embodiments.
• CNF carbon nanofibers
• FIG. 3D is a Scanning Electron Microscope image of an electrode layer containing a multilayer template formed by a nickel silicide template and carbon nanofibers (CNF) and coated with amorphous silicon.
• CNF nickel silicide template and carbon nanofibers
• FIG. 3E is a schematic representation of an electrode layer containing a multilayer template formed by a single-layered template and multidimensional silicide structures ("fuzzy balls"), in accordance with certain embodiments.
• FIG. 3F is a Scanning Electron Microscope image of an electrode layer containing a multilayer template formed by a nickel silicide template and multidimensional nickel silicide structures and coated with amorphous silicon.
• FIG. 4A is a process flowchart corresponding to a method of fabricating a battery electrode layer, in accordance with certain embodiments.
• FIGS. 4B-4E illustrate Raman spectrums representing short range order (SRO) ratios of four amorphous silicon layers deposited using different process conditions.
• FIG. 4F is a schematic representation of a residual stress model for a multilayer electrode layer structure, in accordance with certain embodiments.
• FIGS. 5A-B are top and side schematic views of an illustrative electrode arrangement in accordance with certain embodiments.
• FIGS. 6A-B are top and perspective schematic views of an illustrative round wound cell in accordance with certain embodiments.
• FIG. 7 is a top schematic view of an illustrative prismatic wound cell in accordance with certain embodiments.
• FIGS. 8A-B are top and perspective schematic views of an illustrative stack of electrodes and separator sheets in accordance with certain embodiments.
• FIG. 9 is a schematic cross-section view of an example of a wound cell in accordance with embodiments.
• FIG. 10 is cycling data corresponding to a cell fabricated using electrode material described herein.
• Nanostructures are less likely to deteriorate than larger structures during battery cycling. Specifically, they are less likely to pulverize and/or lose electrical contacts with one another because of lower mechanical stresses built up in the nanostructures during lithiation. Yet, integrating nanostructures into a battery electrode layer that has adequate active material loading may be challenging because of their small sizes and need to establish and maintain many electrical connections within the electrode. For example, it is difficult to mechanically arrange, support, and electrically interconnect many small
• Nanostructures as well as to preserve these arrangements and interconnections over a large number of swelling-contraction cycles. Further, nanoparticles that are only 50- 100 nanometers in diameter will have to rely on hundreds and even thousands of particle-to-particle connections and possibly intermediate conductive structures to pass an electrical current in a typical electrode design. Initial connections formed, for example, by direct contacts of the nanoparticle and/or conductive additives are often lost when the nanoparticles swell and then contract. While swelling, the nanoparticles push each other and other components apart. During delithiation, the same nanoparticles shrink, and the original contacts may be lost due to electrode elasticity constraints. This may result in unconnected active particles, which effectively become inactive. Nanofilms have been proposed as alternative nanostructures.
• nanofilms deposited on flat substrates contain only very small amounts of the active material over the surface area of an electrode and therefore are not practical for most battery applications.
• High surface area substrates help to increase active material loading while keeping active material structures relatively small. These substrates, when coated with active materials, can yield a higher capacity per unit area (based on the flat electrode surface area) than conventional flat substrates.
• High surface area substrates may be formed by roughening substrate surface or forming templates on a surface of the initial flat substrate.
• a flat metallic substrate may be processed to form silicide nanostructures extending from the substrate surface. The addition of the nanostructures substantially increases the overall surface area available for coating.
• These silicide nanostructures can serve as a high surface area template used for coating active materials.
• silicide nanostructures may be shaped as nanowires that have substrate rooted ends or middle portions. The rooted ends may form integral structures with the substrate surface. In some cases, the nanowires may not have a clearly defined morphological boundary at the interface with the substrate. As a result, nanowires may have superior mechanical attachment to the substrate and a low electronic contact resistance.
• Some template nanostructures can be difficult to grow above certain dimensions. For example, when forming metal silicide templates, the growth is believed to be limited by diffusion rates of silicon and metals through the respective silicide phases. Only relative short structures may be formed resulting in thin template layers, for example, less than 10-20 micrometers in thickness for nickel silicide nanowires. Such silicide structures do not provide an adequate surface area to support enough active material. If an active material is coated over this template such that the coating thickness does not exceed the fracture limit of the active material, the total amount of active materials per unit area may be not sufficient for a commercially viable electrode. [0039] Furthermore, forming silicide nanostructures on metal surfaces with an excess of source metals, such as forming nickel silicide nanowires on a thick nickel foil, may cause undesirable deposits formed near the bases of the silicide
• Novel template layer structures and fabrication techniques are provided and described herein. These structures allow having higher mass loading of high capacity active materials per electrode unit area without exceeding fracture limits of these active materials. Higher mass loading corresponds to a higher capacity per electrode unit area and, in certain embodiments, to a higher capacity of electrochemical cells. Controlling thickness of the active material coating and keeping it under the fracture limit may result in more robust cycling performance characteristics.
• An initial template layer may be formed on a substrate that is relatively inert during template formation.
• a substrate for forming a template may include a base layer and a source layer. Only a source layer is consumed during template fabrication, while the base layer stays substantially intact.
• the source layer may have a controlled thickness to control a density and length of the formed template structures.
• the source layer may be fully consumed during formation of the nanostructure template layer.
• a layer of nickel metal having a controlled thickness may be used as the template source material. The layer is exposed to a silicon precursor, such as silane, until the layer is fully consumed. In the course of the process, nickel silicide nanostructures are formed. These nickel silicide
• nanostructures serve as the template layer.
• an initial template layer is enhanced by forming additional one or more template layers over that initial layer.
• the resulting structure is referred to herein as a multilayer template structure.
• Additional layers may be formed using prefabricated structures, such as carbon nanofibers (CNF) and/or multidimensional silicide structures, which are sometimes referred to as “fuzzy balls” or “urchin” structures.
• CNF carbon nanofibers
• multidimensional silicide structures typically may have a central support structure and multiple metal silicide nanowires attached to the support structure and extending into different directions away from the support structure. This arrangement gives a "fuzzy ball" look to such structures.
• template structures of additional template layers may be formed directly over an initial template layer, which is further described in US Patent
• cell performance and active material loading can be substantially improved by using various novel active material coating structures.
• a multi-layered active material coating may be formed on template structures.
• Various deposition and post-deposition treatment techniques are described below to achieve desired compositions as well as morphological and dimensional structures within these active material coatings.
• a typical electrode material or electrode structure may include different layers, which should be distinguished from each other. Specifically, an "active material layer” should be distinguished from a “template layer” and an “electrode layer”.
• a “template layer” is a layer formed by one or more template structures, such as nickel silicide nanowires. An initial template layer is formed over a substrate surface. In embodiments involving silicide nanowires, this initial layer may be about 10-20 micrometers thick. Additional template layers may be formed over the initial template layer to form a multilayer template structure. A thickness of the multilayer template structure equals a sum of thicknesses of individual template layers.
• An "active material layer” is a thin layer of an active electrode material, such as amorphous silicon, that is formed over the template layer structures.
• the active material layer is often referred to as an active material coating because it is often formed by coating template structured with an active material.
• the thickness of the active material layer / coating is typically chosen to be less than material's fracture limits for given lithiation levels. The fracture limit may be further adjusted by varying porosity and other parameters of the active material coating.
• Multiple template layers may be stacked one on top of the other and these layers are generally parallel to the substrate surface. On the other hand, the active material coating follows contours of template structures.
• an active material coating layers may be considered a shell surrounding template nanostructures within the template layer.
• an active material coating may have has multiple layers forming a multilayer active material coating or structure.
• Electrode layer is commonly used in the art to describe a collective structure formed on one or both side of a conductive substrate. This structure includes an active material and various other components that may be added to provide mechanical support and electrical conductivity within the electrode layer. In certain embodiments, the electrode layer includes a combination of a template layer and an active material coating.
• FIGS. 1 A-B are schematic representations of a template at different stages of its formation, in accordance with certain embodiments.
• FIG. 1 A illustrates an initial stage where substrate 100 has base layer 102 and source layer 104.
• a template formation process may start with depositing a source layer on a base layer.
• base layer 102 contains little or no source material that could be used to form template structures.
• base layer 102 may include an inert material, at least on its top surface.
• base layer 102 needs be inert only at process conditions used during template formation. For example, a stainless steel foil may remain
• a substrate does not have distinctive base and source layers and the same material is used both as a base and a source, for example, of metal during silicides formation.
• Base layer 102 may be made from various conductive materials and serve as a current collector for active materials.
• Some example of base layer materials include copper, copper coated with metal oxides, stainless steel, titanium, aluminum, nickel, chromium, tungsten, metal nitrides, metal carbides, carbon, carbon fiber, graphite, graphene, carbon mesh, conductive polymers, or combinations of above including multi-layer structures.
• the base layer material may be formed as a foil, film, mesh, foam, laminate, wires, tubes, particles, multi-layer structure, or any other suitable configuration.
• a base material is a metallic foil with a thickness of between about 1 micrometer and 50 micrometers or, more specifically between about 5 micrometers and 30 micrometers.
• Examples of materials for source layer 104 include any of a number of materials that form silicide nanostructures. Such materials include nickel, cobalt, copper, silver, chromium, titanium, iron, zinc, aluminum, tin, and their combinations. Examples of some alloys include nickel/phosphorus, nickel/tungsten,
• Source layer 104 may be at least about 10 nanometers thick or, more specifically, at least about 100 nanometers thick. In more specific embodiments, a nickel source layer is between about 100 nanometers and 300 nanometers thick. In another specific embodiment, a nickel phosphate source layer is between 300 nanometers and 10 micrometers. In some exemplary embodiments, the nickel phosphate layer is about 500 nanometers thick, or about 1.5 micrometers thick, or about 8 micrometers thick.
• a source layer may also be made from NiFe, NiW, and NiMo alloys with a thickness of between about 0.5 micrometers and 10 micrometers.
• a specific thickness of source layer 104 may cause specific characteristics of the resulting template layer. For example, it has been found that thicker source layers may lead to formation of denser and/or longer silicide structures. For example, two nickel layers having different thicknesses were exposed to silane at typical nickel silicide formation conditions and then tested for weight gain. A sample with a 100 nanometers layer showed 0.04 milligrams per centimeter square weight gain, while the one with a 300 nanometers layer showed 0.1 milligrams per centimeter square weight gain.
• a substrate may have an intermediate protective layer formed between the base and source layers (not shown).
• This protective layer may be made from inert materials and can protect the base layer from being exposed to reactive species, e.g., silane. When a protective layer is used, it is possible to use material that can react with silane if they were in direct contact for the base.
• reactive species e.g., silane.
• intermediate layers may be used to enhance adhesion between the template structures and the base layer.
• Other intermediate layers that offer other desirable characteristic can also be used.
• a source material is provided in a form of particles or other discrete structures. These structures are still described as source layer 104 formed on a surface of the base layer. These discrete structures may be provided as a layer having a thickness of at least about 10 nanometers or, more specifically, between about 10 nanometers and 500 nanometers. In certain embodiments, precursor particles are used to control the porosity of the resulting electrode layer and have diameters of between about 1 and 3 micrometers.
• FIG. IB illustrates an intermediate stage of template formation with an intermediate template structure 108 formed over a residual source layer 106.
• Some of the initial source material has been consumed to form intermediate template structures 108. Therefore, residual source layer 106 shown in FIG. IB is typically thinner than initial source layer 104 shown in FIG. 1 A. At this stage, there may be still some remaining source material to support further growth of intermediate template structures 108.
• residual layer 106 may include reaction products of source materials forming an alloy, which cause some swelling. Therefore, in these embodiments, residual layer 106 may sometimes be thicker than initial source layer 104.
• a specific example would be the formation of a very metal rich silicide phase, such as nickel silicide or copper silicide, where the residual layer may expand as it alloys with the silicon.
• a very metal rich silicide phase such as nickel silicide or copper silicide
• the residual layer may expand as it alloys with the silicon.
• FIG. 1C illustrates a final stage of the template formation operation where template structures 110 are finally formed.
• template structures 110 have their ends rooted to base layer 102.
• Template structures 110 may be between about 5 nanometers and 100 nanometers in diameter (i.e., prior to depositing active material) or, more specifically, between about 10 nanometers and 50 nanometers. Further, template structures 110 may be between about 1 micrometer and 100 micrometers long or, more specifically, between about 2 micrometers and 25 micrometers long. In the depicted embodiment where template structures 1 10 extend substantially perpendicular to the flat surface of the base layer, this length corresponds to a thickness of a template layer 112.
• Template layer 112 may have a porosity of at least about 50% or, more particularly, at least about 75%, or even at least about 90%>.
• the porosity of template layer 112 that does not include any active material should be distinguished from a porosity of the active layer (i.e., a thin layer of active material formed on a surface of template structures 110) or a porosity of the electrode layer.
• residual source layer 106 has been substantially consumed.
• the thickness of initial source layer 104 may be specifically selected such that most or all of the source material is eventually consumed during template formation. This approach may eliminate formation of undesirable materials, such as metal silicides, at the interface with the base layer.
• a brittle silicide phase is formed on the surface, then various stresses generated before, during, or even after active material deposition may lead to fracture of that silicide phase. Some phases may also have poor adhesion to the substrate below or the active material on top.
• Another example demonstrates some drawback of having a thick (e.g., at least about 500 nanometers) nickel film. Nickel is known to diffuse relatively fast in silicon structures. If some residual nickel is left at the interface, it may react with silicon at high temperatures during silicon deposition, and "consume" a portion of silicon that is meant to be active material. This may in turn cause an unbalanced electrochemical cell (i.e., inadequate amounts of the negative active material) and possibly overcharge. Furthermore, this initial thickness may be selected to achieve certain density and length of template structures as described above.
• the template material is highly electronically conductive and mechanically stable in the face of stresses experienced from expansion and
• template materials include metal silicides (e.g., copper silicides, nickel silicides, aluminum silicides), carbon, certain metal or semiconductor oxides (e.g. zinc oxide, tin oxide, indium oxide, cadmium oxide, aluminum oxide, titania / titanium dioxide, silicon oxides), and certain metals (copper, nickel, aluminum).
• metal silicides e.g., copper silicides, nickel silicides, aluminum silicides
• carbon certain metal or semiconductor oxides (e.g. zinc oxide, tin oxide, indium oxide, cadmium oxide, aluminum oxide, titania / titanium dioxide, silicon oxides), and certain metals (copper, nickel, aluminum).
• metal or semiconductor oxides e.g. zinc oxide, tin oxide, indium oxide, cadmium oxide, aluminum oxide, titania / titanium dioxide, silicon oxides
• certain metals copper, nickel, aluminum
• template structures are formed into nanowires and include silicides.
• nickel silicide nanowires may include one, two, or all three phases of nickel silicide, i.e., Ni 2 Si, NiSi, and NiSi 2 . It is believed that higher nickel content phases form stronger bonds with nickel metal. Therefore, this variability may provide relatively strong adhesion of nickel silicide nanowires to the base layer and reduce the contact resistance. The conductivity and lithium irreversibility of these different nickel silicide phases also varies.
• Cone shaped nanowires may also result from greater availability of the metal near the substrate/support rooted ends of the nanowires.
• an average diameter near the substrate/support rooted ends is at least about twice that near the free end.
• nanowires' bases may be large enough even to touch one another at the proximal ends on the surface of the substrate, but the distal tips are free and unconnected because of a decrease in diameter along the structure form the base to the tip.
• a ratio of diameters between the proximal and distal nanowire ends is at least about 4 or, more particularly, at least about 10. Wider bases may help to maintain adhesion to the substrare.
• FIG. ID is a Scanning Electron Microscope image of a nanostructured template containing nickel silicide nanowires. These nanowires were deposited directly on a hard rolled nickel foil available from Carl Schlenk AG Company in Roth, Germany. The foil was first oxidized for one minute at 300°C in a process chamber containing air at a pressure of 50 Torr. The foil was then heated to 450°C and a process gas containing 1% silane by volume was introduced into the chamber for ten minutes. Resulting silicide nanowires were about 10-50 nanometers in diameters and about 1-30 micrometers in length. A density of nanowires was between about 10-70%. As it can be seen from the SEM image in FIG. ID, the nanowires form a template with a relatively large surface area. The substrate carrying this template was punched into discs that were approximately 15 millimeters in diameter to construct coin cells.
• an initial nanostructure template layer formed on a substrate does not provide a sufficient surface area and/or thickness for deposition of the active material desired.
• a certain minimal surface area of a template may be needed per planar electrode surface area to achieve adequate active material loading.
• one or more additional template layers may be provided over the initial template layer to form a multilayer template structure.
• an initial silicide template may be coated with a layer of carbon nanofibers (CNF).
• FIG. IE is a Scanning Electron Microscope image of a nanostructured template containing nickel silicide nanowires with carbon nanofibers (CNF) deposited over the nickel silicide nanowires.
• an available surface area of the initial silicide template is increased by providing a second layer of structures that form a second template layer.
• These structures of the second template layer may have characteristics similar to structures in the initial layer, e.g., both may be electronically conductive and form porous template layers available for active material coating.
• the second template layer includes fibers or linear nanostructures. Examples of such structures include carbon fibers, carbon nanotubes, and silicide nanowires.
• multidimensional nanostructures may be provided in one or more additional template layers.
• One example of such structures has a central core to which multiple metal silicide nanowires are attached forming "fuzzy balls" or "snowballs" like structures.
• FIG. IF is a Scanning Electron Microscope image of a nanostructured template containing nickel silicide nanowires and a layer of nickel silicide fuzzy ball structures over the nickel silicide nanowires.
• Structures of additional template layers may be made of the same materials as the initial layer, e.g., silicides, or made be made from different materials, e.g., carbon containing materials, different silicides.
• a multilayer template structure may be at least about 10 nanometers thick or, more particularly, at least 50 nanometers thick or even at least 100 nanometers thick. Additional template layers may be deposited after the initial layer is coated with an active material. In another arrangement, the additional template layers are deposited before the initial layer is coated with an active material, and subsequently the two-layer template is coated with the active material.
• Various operation sequences are further described below with reference to FIG. 4A.
• Template structures can provide mechanical support and/or electrical connection to an active material coating. Having a much higher surface area in comparison to a flat substrate, a nanostructure template allows forming a thin active material coating while still providing a sufficient amount of active material per electrode unit area (the planar surface of the electrode).
• An active material coating generally has a thickness below the fracture limit of the active material used and morphological structure of the active material. For example, a thickness of an amorphous silicon coating may be less than about 300 nanometers or, more specifically, less than about 100 nanometers.
• various new structures as well as deposition and treatment techniques described herein that change morphological characteristics of the active material coating allow increasing the coating thickness above typical fracture limit values.
• a multilayer active material coating may be formed where each layer has a different composition, physical and/or morphological structure.
• a multilayer active material coating includes inner and outer amorphous silicon layers. The inner layer has a lower porosity than an outer layer.
• negative electrochemically active materials that can be deposited over a template include, but are not limited to, various silicon containing materials
• negative electrochemically active materials include tin-containing materials (e.g., tin, tin oxide), germanium, carbon- containing materials, a variety of metal hydrides (e.g., MgH 2 ), silicides, phosphides, and nitrides.
• Still other examples include carbon-silicon combinations (e.g., carbon- coated silicon, silicon-coated carbon, carbon doped with silicon, silicon doped with carbon, and alloys including carbon and silicon), carbon-germanium combinations (e.g., carbon-coated germanium, germanium-coated carbon, carbon doped with germanium, and germanium doped with carbon), and carbon-tin combinations (e.g., carbon-coated tin, tin-coated carbon, carbon doped with tin, and tin doped with carbon).
• High capacity active materials are generally defined as active materials with theoretical lithiation capacities of at least about 700 mAh/g.
• positive electrochemically active materials that can serve as coatings include various lithium metal oxides (e.g., LiCo0 2 , LiFeP0 4 , LiMn0 2 , LiNi0 2 , LiMn 2 0 4 , LiCoP0 4 ,
• dopant includes elements from the groups III and V of the periodic table (e.g., boron, aluminum, gallium, indium, thallium, phosphorous, arsenic, antimony, and bismuth) as well as other appropriate dopants (e.g., sulfur and selenium).
• Coating an active material over template structures forms an electrode or, more specifically, an electrode layer.
• an electrode layer typically has a thickness comparable to that of the over template layer, which may itself include multiple template layers.
• the porosity of the electrode layer is generally lower than the porosity of the corresponding overall template layer because the active material occupies some void space in between template structures.
• the electrode layer porosity generally depends on the composition and thickness of the active material coating as well as cycling characteristics of the cell, e.g., its depths of charge and discharge. It has been found that a suitable porosity of the electrode layer having an amorphous silicon coating is between about 20% and 80% or, more specifically, between about 30%> and 60%>.
• FIGS. 2A- 2C are Scanning Electron Microscope (SEM) images of three different electrode layers having different porosities in the 30% and 50% range.
• An active material coating may be itself a porous structure, typically having internal voids of much smaller dimension than those associated with the porosity of the overall, two-layer template nanostructures.
• the electrode layer porosity values recited above do not take into account the porosity of the active material coating.
• the experimental data suggests that higher active material porosity, i.e., an internal porosity of the active material coating, as well other associated factors result in cells with better cycling performance.
• the porosity within the active material coating is controlled to achieve a desired cell performance.
• FIG. 3 A is a schematic representation of an electrode layer containing a number of nanostructures 315 that make up a single-layer template 320.
• Template 320 is coated with a high capacity active material 340.
• high capacity active material 340 provides an adequate surface and/or thickness for deposition of high capacity active material 340.
• high rate battery applications generally use thinner electrodes for their high electronic and ionic conductivities needed to generate and draw high electrical currents.
• areal mass density of high capacity active material is between about 1.5 and 4.5 milligram per centimeter square. Such densities translate into an overall thickness of the active material coated template to between about 10 micrometers and 40 micrometers.
• FIG. 3B is a Scanning Electron Microscope image of an electrode layer containing a single- layer nickel silicide template coated with amorphous silicon.
• an initial template layer formed on a substrate does not provide a sufficient surface area for deposition of a desired amount of active material and additional template layers are formed over the initial template layer.
• materials that may be employed to produce these additional layers include carbon nanofibers (CNF) and multidimensional silicide structures.
• FIG. 3C is a schematic representation of an electrode layer containing a multilayer template formed by a first layer 340 of nanostructured silicide template and a second template layer 360 of carbon nanofibers (CNF). Both template layers are coated with a high capacity active. For clarity, an active material coating is not shown in FIG. 3C. The active material coating may be performed sequentially, after each template layer is formed or in one step after all template layers are formed.
• FIG. 3D is a Scanning Electron Microscope image of an electrode layer containing a multilayer template formed by a nickel silicide template and carbon nanofibers (CNF) and coated with amorphous silicon.
• FIG. 3E is a schematic representation of an electrode layer containing a multilayer template formed from a initial template layer 370 of silicide nanowires and an additional template layer 380 of multidimensional silicide structures. Both template layers are coated with a high capacity active material. For clarity and simplicity, an active material coating is not shown in FIG. 3E.
• the multidimensional silicide structures may be used to form an electrode with any thickness, for example, continuously deposited over initial template layer 370 until the desirable
• Additional template layer 380 helps to thicken the overall template beyond the lengths of original template structures. There are generally no upper thickness limits for electrode layers fabricated from multiple template layers. This feature allows one to form battery electrode layers with large active material masses per unit area and, therefore, very high capacities per unit area. Multilayer template structures may be stacked up to any thickness as desired for capacity and other battery performance parameters (e.g., cycling rate). For example, it is useful to use thicker electrode layers for high capacity applications, while it is also useful to use thinner more conductive battery electrode layers for high cycling rates (high charge and/or discharge currents).
• template layers may be employed, where the individual layers are made from various different materials and/or nanostructure morphologies.
• suitable materials for the template include silicides, carbon (fullerene or otherwise), nitrides, carbides, etc. Almost any material that can be formed into an appropriate nanostructure and does not aggressively consume silicon (or other corresponding active material coatings) at temperatures up to about 500°C or 600°C can be used as a template material.
• the template material is electronically conductive.
• suitable template nanostructures include nanowires, fuzzy balls, nanofibers, nanotubes, spheres, cones, rods, wires, arcs, saddles, flakes, ellipsoids, spikes, caterpillar structures, etc.
• Second layer template structures can be bound to the substrate or lower layer template structures using a polymeric binder and/or active material coating. For example, if an active material coating is deposited after the second layer template has been added, the active material itself can join the template layers together.
• FIG. 4A is a process flowchart corresponding to method 400 for fabricating an electrode layer, in accordance with certain embodiments.
• Method 400 may start with receiving a substrate having a base layer during operation 402. Various substrate examples are described above. Method 400 may proceed with operation 404 during which a source layer having a controlled thickness is formed on the substrate.
• PVD physical vapor deposition
• CVD chemical vapor deposition
• a layer of nickel having a thickness of between about 100 nanometers and 500 nanometers is deposited on one or both sides of a stainless steel or tungsten foil.
• the foil may be between about 5 micrometers and 50 micrometers thick.
• Operation 404 may also involve treating a source layer surface, for example, to increase its surface roughness and/or to change its surface compositions.
• treatment techniques include introducing silicide precursors into the surfaces (e.g., silicon, metal, and/or catalyst containing materials), chemically modifying the surfaces (e.g., forming oxides, nitrides, carbides, initial silicide structures, and treatments with various oxidizing and reducing agents), and physically modifying the surfaces (e.g., increasing surface roughness with laser ablation and/or plasma treatment).
• Other examples include changing grain orientation, annealing, sonication, doping, and ion implantation.
• a modified surface of the source layer may enhance formation of the template structures during operation 406.
• a source layer is oxidized at a temperature of between about 150°C and 500°C (more specifically around 250°C) for a period of between about 0.1 minutes and 10 minutes or, more specifically, around one minute, in a gas stream containing oxygen or other suitable oxidant. It has been found that some oxidation helps roughening the surface and helps initial formation of nickel silicide structures. Without being restricted to any particular theory, it is believed that rough oxide edges may serve as nucleation sites during silicide formation. Further, the oxide may act as a mask to allow nucleation only at the pores. Another function of an oxide may be to regulate the diffusion rate of the metal to the reaction site. It has been also found that excessive oxidation may be detrimental to silicide formation. As such, oxidation conditions may be optimized for each metal containing material and structures containing these materials.
• Method 400 may proceed with formation of template structures during operation 406, e.g., using CVD.
• a process gas that includes a silicon containing precursor e.g., silane
• the volumetric concentration of silane in the process gas is less than about 10%, or more specifically less than about 5%, or even less than about 1%. In particular embodiments, the concentration of silane is about 1%.
• a process gas may also include one or more carrier gases, such as argon, nitrogen, helium, hydrogen, oxygen (although typically not with silane), carbon dioxide, and methane.
• the gas and/or substrate may be maintained at a temperature of between about 350°C and 500°C or, more specifically, between about 425°C and 475°C.
• the duration of deposition may be between about 1 minute and 30 minutes or, more specifically between about 5 minutes and 15 minutes.
• appropriate adjustments to the gas phase precursor and other process conditions may be employed.
• process conditions are varied during operation 406. For example, during formation of silicide structures, silane may be introduced initially at a relatively high concentration in order to promote nucleation and then reduced when, e.g., further silicide formation is limited by source metal diffusion from the rooted ends of the structures towards the growing tips.
• process temperature may be kept low initially and then increased in order to promote such metal diffusion.
• process conditions may be varied to control physical (e.g., length, diameter, shape, orientation, areal density) and morphological (e.g., stoichiometric phases to ensure high conductivity of the silicide, for example, distribution along the length, crystalline / amorphous) properties of the formed template structures.
• Other process conditions that could be varied during operation 406 include composition of the gas mixture (in addition to variable silane
• PECVD plasma-enhanced chemical vapor deposition
• Method 400 may proceed with forming of an additional template layer during operation 408.
• a single-layer template is transformed into a multilayer template structure.
• an initial silicide template may be coated with a layer of carbon nanofibers (CNF).
• CNF or multidimensional silicide structures may be suspended in a liquid to form slurry and then coated over the initial layer using a "doctor blade" technique or a spraying technique followed by drying.
• additional template layers may be formed either before or after the initial template layer is coated with an active material as further described in the context of decision block 414.
• Method 400 then proceeds with forming an active material coating over a single-layered or multi-layered template structure during operation 410.
• Deposition of the active material coating may involve CVD, PVD, electroplating, electroless plating, or solution deposition.
• An example of a PECVD technique will now be described in more detail.
• a template layer provided into the chamber and/or the process gas are heated to between about 200°C and 400°C or, more specifically, between about 250°C and 350°C.
• the gas delivered into the chamber can include a silicon containing precursor (e.g., silane) and one or more carrier gases (e.g., argon, nitrogen, helium, hydrogen, carbon dioxide, and methane).
• a concentration of silane in helium is between about 5% and 20%, or more specifically between about 8% and 15%.
• the gas may also include a dopant containing material, such as phosphine.
• the RF power may be delivered at between about 10W and 1000W, which generally depends on the size of the chamber and other factors.
• Method 400 may then proceed with an optional post-deposition treatment during operation 412.
• post-deposition treatment techniques include chemical etching, annealing, and coating.
• a coating of carbon-containing materials is deposited over a high capacity active material.
• a coating of amorphous silicon deposited in 410 is chemically etched to introduce pores into the active material coating.
• a solid reaction phase technique or a liquid phase deposition technique is used.
• a liquid-containing active material species may deposited onto the template and then physically or chemically converted into a solid active material.
• a liquid-containing tetraethyl orthosilicate (TEOS) sol-gel (Si0 2 ) can be deposited onto a template followed by chemical reduction to silicon.
• TEOS tetraethyl orthosilicate
• operations 408-412 are repeated (decision block 414) to form multi- layered active material coatings that demonstrate superior cell performance characteristics in comparison with single-layered active material coatings.
• a first layer/coating of amorphous silicon is deposited using a PECVD technique followed by a second layer/coating of amorphous silicon deposited by a thermal CVD technique, or vice versa.
• Each of these two active material coatings has a different crystallinity, porosity, density, impurities' concentrations (e.g., hydrogen), vacancies, and residual stress levels.
• a series of tests was performed to determine effects of process conditions on an atomic density of silicon.
• silicon was deposited using a thermal CVD technique at 520°C resulting in a structure having of 95% of silicon and 5% of hydrogen and having a density of 5.40E22 atoms per cubic centimeter.
• silicon was deposited using a thermal CVD technique but at a higher temperature of 550°C, which resulted in a structure having of 98% of silicon and 1% of hydrogen and having a density of only 5.16E22 atoms per cubic centimeter.
• silicon was deposited using a PECVD technique at 520°C resulting in a structure having of 89% of silicon and 11% of hydrogen and having a density of 5.88E22 atoms per cubic centimeter.
• a first layer/coating of amorphous silicon is deposited using a thermal CVD technique using one set of process conditions (e.g., a substrate temperature, chamber pressure, precursors' compositions), while a second set of process conditions (e.g., a substrate temperature, chamber pressure, precursors' compositions), while a second
• a layer/coating is also deposited using a thermal CVD technique but another set of conditions.
• a first layer/coating of amorphous silicon is deposited and then etched to form a porous amorphous silicon layer.
• a second layer/coating of amorphous silicon is the deposited over this porous layer.
• the second layer/coating may or may not undergo similar etching.
• a higher porosity of at least the first inner layer helps to overcome large volume changes of this silicon multilayer structure during cycling.
• FIG. 4B-4E illustrates short range order ratios of four amorphous silicon coatings deposited using different process conditions.
• FIG. 4B corresponds to an un-doped amorphous silicon coating deposited using a PECVD process.
• FIG. 4C corresponds to a silicon layer deposited using a thermal CVD technique at 520°C. A curve fitting was used to determine that an ordered (crystalline) silicon phase is predominantly at 520 cm "1 position. Another peak at about 480cm " Corresponds to amorphous silicon.
• FIG. 4D corresponds to a doped silicon material deposited using a PECVD technique performed at about 550°C. From the curve fitting, it can be observed that a PECVD leads to almost all silicon deposited in an amorphous state.
• An SRO ration for silicon deposited using a thermal CVD at 520°C was 4%, while for silicon deposited at 550°C, it was about 14%.
• 4F is a schematic representation of a residual stress model for a multilayer electrode structure in accordance with certain embodiments.
• This model has been developed from linear elastic fracture mechanics (LEFM) for multi-layered coatings to estimate the stress level.
• LFM linear elastic fracture mechanics
• CTE coefficient of thermal expansion
• This in turn may help to prevent cracking and separating of the coating at least during processing, where these materials are subjected to severe thermal fluctuations. It has been found that specifically tailoring these characteristics of active material coatings help to overcome some of the stress induced fracture described above. In other words, more active material can be deposited on the same template structure without sacrificing cycling performance of the cell, while improving its overall capacity.
• FIG. 5A is a plan view of a partially-assembled electrochemical cell that uses electrodes described herein, according to an embodiment of the invention.
• the cell has a positive electrode active layer 502 that is show covering a major portion of a positive current collector 503.
• the cell also has a negative electrode active layer 504 that is show covering a major portion of a negative current collector 505.
• a separator 506 Between the positive electrode active layer 502 and the negative electrode active layer 504 is a separator 506.
• the negative electrode active layer 504 is slightly larger than the positive electrode active layer 502 to ensure trapping of the lithium ions released from the positive electrode active layer 502 by the active material of the negative active layer 504.
• the negative active layer 504 extends at least between about 0.25 and 5 mm beyond the positive active layer 502 in one or more directions. In a more specific embodiment, the negative layer extends beyond the positive layer by between about 1 and 2 mm in one or more directions. In certain embodiments, the edges of the separator 506 extend beyond the outer edges of at least the negative active layer 504 to provide complete electronic insulation of the negative electrode from the other battery components.
• FIG. 5B is a cross-section view of a partially-assembled electrochemical cell 500 that uses electrodes described herein, according to an embodiment of the invention.
• Cell 500 includes a positive current collector 503 that has a positive electrode active layer 502a on one side and a positive electrode active layer 502b on the opposite side.
• Cell 500 also includes a negative current collector 505 that has a negative electrode active layer 504a on one side and a negative electrode active layer 504b on the opposite side.
• the separator 506 serves to maintain mechanical separation between the positive electrode active layer 502a and the negative electrode active layer 504a and acts as a sponge to soak up liquid electrolyte (not shown) that will be added later.
• the ends of the current collectors 503, 505 on which there is no active material can be used for connecting to the appropriate terminal of a cell (not shown).
• the electrode layers 502a, 504a, the current collectors 503, 505, and the separator 506a together can be said to form one electrochemical cell unit.
• the complete stack 500 shown in FIG. 5B includes the electrode layers 502b, 504b and the additional separator 506b.
• the current collectors 503, 505 can be shared between adjacent cells. When such stacks are repeated, the result is a cell or battery with larger capacity than that of a single cell unit.
• Another way to make a battery or cell with large capacity is to make one very large cell unit and wind it in upon itself to make multiple stacks.
• FIG. 6A shows how long and narrow electrodes can be wound together with two sheets of separator to form a battery or cell, sometimes referred to as a jellyroll 600.
• the jellyroll is shaped and sized to fit the internal dimensions of a curved, often cylindrical, case 602.
• the jellyroll 600 has a positive electrode 606 and a negative electrode 604.
• the white spaces between the electrodes are the separator sheets.
• the jelly roll can be inserted into the case 602.
• the jellyroll 600 may have a mandrel 608 in the center that establishes an initial winding diameter and prevents the inner winds from occupying the center axial region.
• the mandrel 608 may be made of conductive material, and, in some embodiments, it may be a part of a cell terminal.
• FIG. 6B shows a perspective view of the jelly roll 600 with a positive tab 612 and a negative tab 614 extending from the positive current collector (not shown) and the negative current collector (not shown), respectively.
• the tabs
• the length and width of the electrodes depend on the overall dimensions of the cell and thicknesses of the active layers and the current collectors. For example, a conventional 18650 cell with 18 mm diameter and 65 mm length may have electrodes that are between about 300 and 1000 mm long. Shorter electrodes corresponding to lower rate / higher capacity applications are thicker and have fewer winds.
• a cylindrical design may be desirable for some lithium ion cells because the electrodes can swell during cycling and thus exert pressure on the casing. It is useful to use a cylindrical casing that is as thin as possible while still able to maintain sufficient pressure on the cell (with a good safety margin).
• Prismatic (flat) cells may be similarly wound, but their case may be flexible so that they can bend along the longer sides to accommodate the internal pressure. Moreover, the pressure may not be the same within different parts of the cell, and the corners of the prismatic cell may be left empty. Empty pockets are not desirable within lithium ions cells because electrodes tend to be unevenly pushed into these pockets during electrode swelling.
• FIG. 7 illustrates a top view of a wound prismatic jellyroll 700.
• the jellyroll 700 includes a positive electrode 704 and a negative electrode 706.
• the white space between the electrodes is the separator sheet.
• the jelly roll 700 is enclosed in a rectangular prismatic case 702. Unlike cylindrical jellyrolls shown in FIGS.
• the winding of the prismatic jellyroll starts with a flat extended section in the middle of the jelly roll.
• the jelly roll may include a mandrel (not shown) in the middle of the jellyroll onto which the electrodes and separator are wound.
• FIG. 8A illustrates a cross-section of a stacked cell that includes a plurality of cells (801a, 801b, 801c, 80 Id, and 80 le), each having a positive electrode (e.g., 803a, 803b), a positive current collector (e.g., 802), a negative electrode (e.g., 805a, 805b), a negative current collector (e.g., 804), and a separator (e.g., 806a, 806b) between the electrodes.
• Each current collector is shared by adjacent cells.
• One advantage of stacking cells is that the stack can be made in almost any shape, which is particularly suitable for prismatic batteries.
• the current collector tabs typically extend from the stack and lead to a battery terminal.
• FIG. 8B shows a perspective view of a stacked cell that includes a plurality of cells.
• the battery is filled with electrolyte.
• the electrolyte in lithium ions cells may be liquid, solid, or gel. Lithium ion cells with the solid electrolyte are also referred to as a lithium polymer cells.
• a typical liquid electrolyte includes one or more solvents and one or more salts, at least one of which includes lithium.
• the organic solvent in the electrolyte can partially decompose on the negative electrode surface to form a solid electrolyte interphase layer (SEI layer).
• SEI layer solid electrolyte interphase layer
• the interphase is generally electrically insulating but ionically conductive, allowing lithium ions to pass through. The interphase also prevents decomposition of the electrolyte in the later charging sub-cycles.
• non-aqueous solvents suitable for some lithium ion cells include the following: cyclic carbonates (e.g., ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC) and vinylethylene carbonate (VEC)), lactones (e.g., gamma-butyrolactone (GBL), gamma-valerolactone (GVL) and alpha- angelica lactone (AGL)), linear carbonates (e.g., dimethyl carbonate (DMC), methyl ethyl carbonate (MEC), diethyl carbonate (DEC), methyl propyl carbonate (MPC), dipropyl carbonate (DPC), methyl butyl carbonate (NBC) and dibutyl carbonate (DBC)), ethers (e.g., tetrahydrofuran (THF), 2-methyltetrahydrofuran, 1,4-dioxane, 1 ,2-dimethoxyethane
• Non-aqueous liquid solvents can be employed in combination.
• the combinations include combinations of cyclic carbonate-linear carbonate, cyclic carbonate-lactone, cyclic carbonate-lactone-linear carbonate, cyclic carbonate-linear carbonate-lactone, cyclic carbonate-linear carbonate-ether, and cyclic carbonate-linear carbonate-linear ester.
• a cyclic carbonate may be combined with a linear ester.
• a cyclic carbonate may be combined with a lactone and a linear ester.
• the ratio of a cyclic carbonate to a linear ester is between about 1 :9 to 10:0, preferably 2:8 to 7:3, by volume.
• a salt for liquid electrolytes may include one or more of the following: LiPF 6 , LiBF 4 , L1CIO 4 LiAsFg, LiN(CF 3 S0 2 ) 2 , LiN(C 2 F 5 S0 2 ) 2 , LiCF 3 S0 3 , LiC(CF 3 S0 2 ) 3 , LiPF 4 (CF 3 ) 2 , LiPF 3 (C 2 F 5 ) 3 , LiPF 3 (CF 3 ) 3 , LiPF 3 (iso-C 3 F 7 ) 3 , LiPF 5 (iso-C 3 F 7 ), lithium salts having cyclic alkyl groups (e.g., (CF 2 ) 2 (S0 2 ) 2x Li and (CF 2 ) 3 (S0 2 ) 2x Li), and combination of thereof.
• LiPF 6 LiBF 4 , L1CIO 4 LiAsFg
• LiN(CF 3 S0 2 ) 2 LiN(C 2 F 5 S0 2 ) 2 , LiCF
• the total concentration of salt in a liquid nonaqueous solvent is at least about 0.3 M; in a more specific embodiment, the salt concentration is at least about 0.7M.
• the upper concentration limit may be driven by a solubility limit or may be no greater than about 2.5 M; in a more specific embodiment, no more than about 1.5 M.
• a solid electrolyte is typically used without the separator because it serves as the separator itself. It is electrically insulating, ionically conductive, and electrochemically stable.
• solid electrolyte configuration a lithium containing salt, which could be the same as for the liquid electrolyte cells described above, is employed but rather than being dissolved in an organic solvent, it is held in a solid polymer composite.
• solid polymer electrolytes may be ionically conductive polymers prepared from monomers containing atoms having lone pairs of electrons available for the lithium ions of electrolyte salts to attach to and move between during conduction, such as Polyvinylidene fluoride (PVDF) or chloride or copolymer of their derivatives, Poly(chlorotrifluoroethylene), poly(ethylene- chlorotrifluoro-ethylene), or poly(fluorinated ethylene-propylene), Polyethylene oxide (PEO) and oxymethylene linked PEO, PEO-PPO-PEO crosslinked with trifunctional urethane, Poly(bis(methoxy-ethoxy-ethoxide))-phosphazene (MEEP), Triol-type PEO crosslinked with difunctional
• polyester polypropylene
• PEN polyethylene napthalate
• PVDF polyvinylidene fluoride
• PC polycarbonate
• PPS polyphenylene sulfide
• PTFE polytetrafluoroethylene
• FIG. 9 illustrates a cross-section view of the wound cylindrical cell in accordance with one embodiment.
• a jelly roll includes a spirally wound positive electrode 902, a negative electrode 904, and two sheets of the separator 906.
• the jelly roll is inserted into a cell case 916, and a cap 918 and gasket 920 are used to seal the cell.
• cap 912 or case 916 includes a safety device.
• a safety vent or burst valve may be employed to break open if excessive pressure builds up in the battery.
• a positive thermal coefficient (PTC) device may be incorporated into the conductive pathway of cap 918 to reduce the damage that might result if the cell suffered a short circuit.
• PTC positive thermal coefficient
• the external surface of the cap 918 may be used as the positive terminal, while the external surface of the cell case 916 may serve as the negative terminal.
• the polarity of the battery is reversed and the external surface of the cap 918 is used as the negative terminal, while the external surface of the cell case 916 serves as the positive terminal.
• Tabs 908 and 910 may be used to establish a connection between the positive and negative electrodes and the corresponding terminals.
• Appropriate insulating gaskets 914 may be inserted to prevent the possibility of internal shorting. For example, a KaptonTM film may be used for internal insulation.
• the cap 918 may be crimped to the case 916 in order to seal the cell. However prior to this operation, electrolyte (not shown) is added to fill the porous spaces of the jelly roll.
• a rigid case is typically required for lithium ion cells, while lithium polymer cells may be packed into a flexible, foil-type (polymer laminate) case.
• a variety of materials can be chosen for the case.
• Ti-6-4, other Ti alloys, Al, Al alloys, and 300 series stainless steels may be suitable for the positive conductive case portions and end caps, and commercially pure Ti, Ti alloys, Cu, Al, Al alloys, Ni, Pb, and stainless steels may be suitable for the negative conductive case portions and end caps.
• a lithium ion battery which may form or be part of a cell pack or a battery pack, includes one or more lithium ion electrochemical cells of this invention, each containing electrochemically active materials.
• a lithium ion battery may also include a power management circuit to control balance power among multiple cells, control charge and discharge parameters, ensure safety (thermal and electrical runaways), and other purposes.
• Individual cells may be connected in series and/or in parallel with each other to form a battery with appropriate voltage, power, and other characteristics.
• metal silicides may be used in fuel cells (e.g., for negative electrodes, positive electrodes, and electrolytes), hetero-junction solar cell active materials, various forms of current collectors, and/or absorption coatings. Some of these applications can benefit from a high surface area provided by metal silicide structures, high conductivity of silicide materials, and fast inexpensive deposition techniques.
• FIG. 10 illustrates cycling data corresponding to one such cell. Specifically, FIG. 10 illustrates columbic efficiency 1002 and delithiation capacity 1004 over 160 cycles. The cell maintained a stable capacity of over 1000 mAh/g over this number of cycles. The columbic efficiency was at about 99.1% in each cycle.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Electrochemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Materials Engineering (AREA)
• Manufacturing & Machinery (AREA)
• Composite Materials (AREA)
• Battery Electrode And Active Subsutance (AREA)
• Cell Electrode Carriers And Collectors (AREA)

Applications Claiming Priority (2)

Publications (2)

Family

ID=45975896

Family Applications (1)

Country Status (2)

Cited By (40)

Families Citing this family (10)

Citations (3)

Family Cites Families (2)

• 2011
  • 2011-10-20 WO PCT/US2011/057159 patent/WO2012054767A2/en active Application Filing
  • 2011-10-21 TW TW105142724A patent/TWI642225B/zh active
  • 2011-10-21 TW TW100138369A patent/TWI575800B/zh active