WO2012051477A1 - Voc or compressed gas containment device made from a polyoxymethylene polymer - Google Patents

Abstract

VOC or compressed gas containment devices, such as polymer fuel tanks, are made from a polyoxymethylene polymer composition. The polymer composition contains a polyoxymethylene polymer that is directly or indirectly chemically attached to an impact modifier. In one embodiment, for instance, a coupling agent bonds the impact modifier to the polyoxymethylene polymer. In order to preserve the permeability of the polymer material when combined with the impact modifier, a polyoxymethylene polymer is used that contains a low level of low molecular weight constituents.

Description

VOC OR COMPRESSED GAS CONTAINMENT DEVICE MADE FROM A POLYOXYMETHYLENE POLYMER

RELATED APPLICATIONS

The present application is a continuation-in-part application of U.S. Patent Application Serial No. 12/904,575, filed on October 14, 2010, which is incorporated herein by reference.

BACKGROUND

Fuel tanks for use in vehicles or other mobile devices should generally possess various characteristics and properties. For instance, the fuel tanks should be capable of holding a fuel without significant amounts of fuel vapor escaping. The tanks should also be chemically resistant to the fuel that is contained in the tanks. The fuel tanks should also have good impact resistance properties. In the past, conventional fuel tanks were generally made from a metal.

In the relatively recent past, those skilled in the art have attempted to design fuel tanks made from polymers. For instance, many small fuel tanks, such as those used by small off-road vehicles and devices, are currently made from high density polyethylene. High density polyethylene has good impact strength resistance properties. The above polymer, however, has a tendency to release fuel vapors over time. Consequently, fuel tanks made from high density

polyethylene are typically fluorinated which not only adds significant cost to the product but is also shown to produce inconsistent results. Thus, those skilled in the art have been seeking to produce polymer fuel tanks from other types of polymers.

In this regard, those skilled in the art have proposed using polyester polymers to produce fuel tanks, particularly small fuel tanks. For instance, in U.S. Patent Application Publication No. 2006/0175325, which is incorporated herein by reference, an impact modified polyester is disclosed which comprises a polyester combined with an olefin-vinyl alcohol component and an impact modifier component.

Another type of polymer that has good permeability resistance properties are polyoxymethylene polymers. Although standard polyoxymethylene polymers have good permeability resistance, the polymers tend to have insufficient impact strength for fuel tank applications due to the high crystallintty of the material. The impact strength of polyoxymethylene polymers can be improved by incorporating an impact modifier into the material. It is known, however, that incorporating an impact modifier into a polyoxymethylene polymer can significantly increase the permeability properties of the polymer. Thus, problems have been encountered in being able to develop a polymer material containing a polyoxymethylene polymer for use in producing fuel tanks.

In U.S. Patent Application Publication No. 2009/0220719, which is incorporated herein by reference, a low fuel-permeable thermoplastic vessel is described made from a polyoxymethylene polymer in combination with an impact modifier. The 719 application teaches using an "uncompatibilized" blend of a polyoxymethylene, a thermoplastic polyurethane, and a copolyester, The term "uncompatibilized" as used in the 719 application means that the compositions do not contain polymer compatibilizers.

Although the teachings of the 719 application have provided great advancements in the art, further improvements are still needed.

SUMMARY

The present disclosure is generally directed to volatile organic compound ("VOC") and compressed gas containment devices made from a composition containing a polyoxymethylene polymer. The polyoxymethylene polymer composition is formulated to have a unique combination of properties making it well suited for use in constructing various hollow vessels, especially fuel tanks. For instance, the polymer composition not only has very good impact strength resistance properties, but is also well suited to preventing fuel vapors and gases from escaping the containment device over time. In particular, the polymer composition can be formulated so as to reduce or prevent VOC vapor emissions while still providing a fuel tank that is capable of not rupturing, even when subjected to relatively high impact forces at colder temperatures.

In this regard, in one embodiment, the present disclosure is directed to a containment device, such as a container, comprising an opening configured to receive a VOC or a compressed gas, such as a fuel. The containment device may also include a discharge for feeding the fuel to a combustion engine or other similar device. The containment device includes a volume surrounded by a wall. In accordance with the present disclosure, the wall is made from a polymer composition comprising a polyoxymethylene polymer. More particularly, the polyoxymethylene polymer for use in the composition comprises a

polyoxymethylene in which at least 50% of the terminal groups are hydroxyl groups. For instance, at least about 70% of the terminal groups can be hydroxyl groups, such as at least about 80% of the terminal groups can be hydroxyl groups, such as even greater than about 85% of the terminal groups can be hydroxyl groups. In addition, the polyoxymethylene polymer may contain little or no low molecular weight constituents having a molecular weight below 10,000 dalton. For instance, the polyoxymethylene polymer can contain low molecular weight constituents in an amount less than about 10% by weight, such as in an amount less than about 5% by weight, such as in an amount less than about 3% by weight, based on the total mass of polyoxymethylene.

In general, the molecular weight of the polyoxymethylene polymer may vary depending upon the particular application. For instance, the polyoxymethylene polymer may have a melt index of from about 1 cm³/10 min to about 50 cm³/ 0 min. As used herein, the melt index of the polymer is measured at 90°C at an applied weight of 2.16 kg according to ISO Test 1133. As will be described in greater detail below, in one embodiment, a polyoxymethylene polymer is used that has a relatively low molecular weight (higher melt index) to create molded articles, particularly blow molded articles, that have excellent multi axial impact strength at low temperatures, such as at -40°C.

In addition to a polyoxymethylene polymer, the composition further includes an impact modifier that is attached to the polyoxymethylene polymer. The impact modifier may comprise, for instance, a thermoplastic elastomer, such as a thermoplastic polyurethane elastomer. A coupling agent may be used to couple the impact modifier to the polyoxymethylene polymer. The coupling agent, for instance, may comprise an isocyanate. For example, in one embodiment, the coupling agent may comprise methylenediphenyl 4,4'-diisocyanate.

In one embodiment, the amount of low molecular weight constituents contained in the polyoxymethylene polymer, the amount of impact modifier, and the amount of the coupling agent are carefully controlled so that the resulting composition produces a polymer having good impact strength resistance in combination with low permeability properties. For instance, in one embodiment, the polymer composition can have a multi axial impact strength resistance at -30°C of greater than about 4 ftlb-f, such as greater than about 10 ftlb-f, such as greater than about 15 ftlb-f, when tested according to ASTM Test D3763.

In an alternative embodiment, the molecular weight of the polyoxymethylene polymer is relatively low and is used in combination with greater amounts of a coupling agent so as to produce a polymer composition not only amenable to blow molding, but also has excellent multi axial impact strength when measured at very low temperatures and according to stringent tests. For instance, in one

embodiment, the polyoxymethylene polymer not only has a significant number of hydroxyl terminal groups, but also has a melt index of from about 5 cm³/10 min to about 20 cm³/ 0 min. The polyoxymethylene polymer is combined with an impact modifier and a coupling agent in an amount greater than about 1.5% by weight, such as in an amount from about 1.5% to about 10% by weight. It has been discovered that the low molecular weight polyoxymethylene polymer in

combination with greater amounts of coupling agent produces a polymer composition having a multi axial impact strength at -40°C of greater than about 15 ftlb-f, such as greater than about 8 ftlb-f, such as greater than about 20 ftlb-f when tested according to ASTM Test D3763.

The permeation of polymer compositions made according to the present disclosure can be less than about 5 g mm/m² day at 40°C when tested according to SAE Test J2665. For instance, the permeation can be less than about 4 g mm/m² day, such as less than about 3 g mm/m² day, such as even less than about 2.5 g mm/m² day. When tested with a 2 mm wall thickness, for instance, the permeation can be less than about 2.5 g/m² day, such as less than 2 g/m² day, such as even less than .5 g/m² day.

As described above, in one embodiment, the polyoxymethylene polymer may contain relatively low amounts of low molecular weight constituents. In one embodiment, the polyoxymethylene polymer can be produced with relatively low amounts of low molecular weight constituents by using a heteropoly acid catalyst. The amount of polyoxymethylene polymer contained in the composition can generally be from about 50% to about 95% by weight, such as greater than about 65% by weight, such as greater than about 70% by weight. The impact modifier, on the other hand, can generally be present in an amount from about 5% by weight to about 30% by weight, such as from about 10% by weight to about 25% by weight. The coupling agent, on the other hand, can generally be present in an amount less than about 5% by weight, such as in an amount from about 0.2% to about 3% by weight.

Another aspect of the present disclosure is directed to a method for blow molding hollow articles. The method includes the steps of combining a

polyoxymethylene polymer with an impact modifier to produce a polymer composition. The polyoxymethylene polymer includes terminal groups wherein at least about 50% of the terminal groups are hydroxyl groups. The

polyoxymethylene polymer has a melt index of from about 5 cm³/10 min to about 20 cm³/10 min. The impact modifier comprises a thermoplastic elastomer and is present in the polymer composition in an amount of at least 5% by weight.

According to the present disclosure, a coupling agent is added to the polymer composition in an amount sufficient for the polymer composition to have a shear viscosity of at least about 8000 Pa~s at a shear rate of 0.1 rad/sec and at a temperature of 190°C. The coupling agent may comprise, for instance, an isocyanate that couples the impact modifier to the polyoxymethylene polymer. The method further includes the step of blow molding a hollow article from the polymer composition.

Although the polymer composition is suitable for producing all types of containment devices for VOC's and compressed gases, in one embodiment, a fuel tank is constructed having a fuel capacity of generally less than about five gallons. Of particular advantage, the fuel tank can be comprised of only a monolayer of the polymer composition. The container wall can generally have a thickness of from about 0.5 mm to about 0 mm, such as from about 1.5 mm to about 5 mm.

Any suitable molding process may be used to produce the containment device. For instance, in one embodiment, the containment device is blow molded. In an alternative embodiment, however, the containment device is injection molded. For instance, two different portions of the containment device may be injection molded and then later welded together.

Other features and aspects of the present disclosure are discussed in greater detail below. BRIEF DESCRIPTION OF THE DRAWINGS

A full and enabling disclosure of the present invention, including the best mode thereof to one skilled in the art, is set forth more particularly in the remainder of the specification, including reference to the accompanying figures, in which:

Figure 1 is a perspective view of one embodiment of a fuel tank made in accordance with the present disclosure;

Figure 2 is a cross sectional view of the fuel tank illustrated in Figure 1 ; and Figures 3 through 7 are graphical representations of the results obtained in the example below.

Repeat use of reference characters in the present specification and drawings is intended to represent the same or analogous features or elements of the present invention.

DETAILED DESCRIPTION

It is to be understood by one of ordinary skill in the art that the present discussion is a description of exemplary embodiments only, and is not intended as limiting the broader aspects of the present disclosure.

In general, the present disclosure is directed to polymer compositions containing a polyoxymethylene polymer that are particularly well suited to molding articles, such as VOC and compressed gas containment devices. As will be described in greater detail below, the polyoxymethylene polymer composition is formulated in a manner that produces molded articles with very good impact resistance properties in combination with very good permeability properties. In particular, the polymer compositions are capable of producing molded articles that are relatively impermeable to gas vapors, such as fuel vapors and other volatile organic compounds, and impermeable to compressed gases, such as natural gas, propane, and other hydrocarbon gases.

In the past, various problems were encountered in producing fuel tanks from polyoxymethylene polymers. Although polyoxymethylene polymers have good natural permeability properties, the materials tend not to have acceptable impact strength when used in fuel tank applications due to the high crystallinity of the material. Increasing the impact strength with compatibilized impact modifiers was found to adversely affect the permeability properties of the material. It was unexpectedly discovered, however, that by using a polyoxymethylene polymer with a high concentration of hydroxyl end groups and optionally with a low

concentration of low molecular weight fractions in combination with an impact modifier that can be chemically reacted with or otherwise attached to the

polyoxymethylene polymer, a polymeric material can be produced that has the desired balance of properties with respect to impact strength and permeability.

Although the polymer composition of the present disclosure can be used to produce any suitable type of VOC or compressed gas containment device, the polymer composition is particularly well suited to producing fuel tanks for a category of engines referred to as small off-road engines. Such engines typically have a power rating of up to 25 horsepower and are used in various vehicles and mobile devices. For instance, small off-road engines are typically used in small utility equipment, lawn mowers, weed trimmers, chain saws, motorcycles, lawn tractors, blowers, and the like. Such fuel tanks typically have a fuel capacity of less than 20 gallons, and particularly less than 5 gallons.

It should be understood, however, that other products and articles in addition to fuel tanks may be made in accordance with the present disclosure. In particular, any type of VOC or compressed gas containment device may be made in accordance with the present disclosure. As used herein, a "containment device" refers to any hollow article that is designed to contain or in any way come in contact with VOCs and/or compressed gases. In addition to tanks, for instance, a containment device may comprise a tube, a hose, or any other similar device. The containment device, for instance, may be designed to contact or contain

hydrocarbon fluids, pesticides, herbacides, brake fluid, paint thinners, and various compressed hydrocarbon gases, such as natural gas, propane, and the like.

When used as a fuel tank, the containment device may contact or contain any suitable hydrocarbon fluid, whether liquid or gas.

Referring to Figs. 1 and 2, for instance, one embodiment of a fuel tank 10 that may be made in accordance with the present disclosure is shown. The fuel tank 10 includes an opening or inlet 12 for receiving a fuel. The opening 12 can be defined by a threaded fixture 14. The threaded fixture 14 is adapted for receiving a fuel and for receiving a cap (not shown). A cap can be placed over the threaded fixture 14, for instance, in order to prevent fuel and vapors from leaving the fuel tank 10.

The fuel tank 0 further includes at least one outlet 6 for feeding a fuel to a combustion device, such as an engine.

The fuel tank 10 defines a container volume 18 for receiving a fuel. The container volume 18 is surrounded by a container wall 20. The container wall 20 can include multiple sides. For instance, the container wall can include a top panel, a bottom panel, and four side panels. Alternatively, the fuel tank 0 can have a spherical shape, a cylindrical shape, or any other suitable shape.

In accordance with the present disclosure, the fuel tank 0 is made from a polymer composition containing a polyoxymethylene polymer. Of particular advantage, the polymer composition is capable of forming a monolayer tank without having to apply any further coatings or layers to the container wall for increasing either impact resistance or permeability resistance.

For instance, polyoxymethylene polymer compositions made in accordance with the present disclosure can have a permeation of less than 5 g mm/m² per day at 40°C when tested according to SAE Test J2665. SAE Test J2665 tests the permeability of the material with a test fuel comprising 10% ethanol, 45% toluene, and 45% iso-octane. Determination of the steady-state flux reported in gmm/m² per day is carried out per SAE Test J2665, Section 10. In certain embodiments, the polymer composition is capable of producing a polymer material having a permeation of less than 4 g mm/m² per day, such as less than 3 g mm/m² per day, such as even less than 2.5 g mm/m² per day.

When tested according to a 2 mm wall thickness, such as according to SAE Test J2665, Section 1 , the polymer composition of the present disclosure may have a permeation of less than about 2.5 g/m² per day, such as less than 2 g/m² per day, such as even less than 1.5 g/m² per day.

In addition to having excellent permeability properties, as described above, the polymer composition formulated according to the present disclosure also displays excellent impact strength resistance. For instance, the polymer composition may have a multi axial impact strength at -30°C according to ASTM Test D3763 of greater than 4 ftlb-f, such as greater than 10 ftlb-f, such as greater than 15 ftlb-f. The multi axial impact strength is generally less than 60 ftlb-f, such as from about 5 ftlb-f to about 25 ftlb-f.

Since the polyoxymethylene polymer is a thermoplastic polymer, the fuel tank 10 as shown in Figs. 1 and 2 can be made according to different processes. For instance, in one embodiment, the fuel tank 10 can be formed through a blow molding process. Alternatively, rotational molding or injection molding may be used to produce the tank.

In one particular embodiment, different portions of the fuel tank 10 can be made using injection molding. For instance, as shown in Figs. 1 and 2, the fuel tank 10 may be formed from a first portion or half 22 and a second portion or half

24. The first portion 22 can then be attached to the second portion 24 using any suitable welding process. Such welding processes include hot-plate welding, vibration welding, laser welding, or ultrasonic welding.

The polymer composition of the present disclosure generally contains a polyoxymethylene polymer that is chemically reacted with or attached to an impact modifier. For example, in one embodiment, a coupling agent may be present in the composition that couples the impact modifier to the polyoxymethylene polymer.

More particularly, the coupling agent may react with first reactive groups on the polyoxymethylene polymer and with second reactive groups present on the impact modifier. In one embodiment, for instance, the coupling agent may comprise an isocyanate that chemically attaches the impact modifier to the polyoxymethylene polymer.

The polyoxymethylene polymer used in the polymer composition may comprise a homopolymer or a copolymer. The polyoxymethylene polymer, however, generally contains a relatively high amount of reactive groups, such as hydroxy! groups in the terminal positions. More particularly, the polyoxymethylene polymer can have terminal hydroxyl groups, for example hydroxyethylene groups and/or hydroxyl side groups, in at least more than about 50% of all the terminal sites on the polymer. For instance, the polyoxymethylene polymer may have at least about 70%, such as at least about 80%, such as at least about 85% of its terminal groups be hydroxyl groups, based on the total number of terminal groups present. It should be understood that the total number of terminal groups present includes all side terminal groups. In one embodiment, the polyoxymethylene polymer has a content of terminal hydroxyl groups of at least 5 mmol/kg, such as at least 10 mmol/kg, such as at least 15 mmol/kg. In one embodiment, the terminal hydroxyl group content ranges from 18 to 500 mmol/kg, such as from about 50 mmol/kg to about 400 mmol/kg. In one particular embodiment, for instance, the terminal hydroxyl group content may be from about 100 mmol/kg to about 400 mmol/kg.

In addition to the terminal hydroxyl groups, the polyoxymethylene polymer may also have other terminal groups usual for these polymers. Examples of these are alkoxy groups, formate groups, acetate groups or aldehyde groups. According to one embodiment, the polyoxymethylene is a homo- or copolymer which comprises at least 50 mol-%, such as at least 75 mol-%, such as at least 90 mol-% and such as even at least 95 mol-% of -CHaO-repeat units.

In addition to having a relatively high terminal hydroxyl group content, the polyoxymethylene polymer according to the present disclosure can also have a relatively low amount of low molecular weight constituents. As used herein, low molecular weight constituents (or fractions) refer to constituents having molecular weights below 10,000 dalton. In order to produce a polymer having the desired permeability requirements, the present inventors unexpectedly discovered that reducing the proportion of low molecular weight constituents can dramatically improve the permeability properties of the resulting material, when attached to an impact modifier. In this regard, the polyoxymethylene polymer contains low molecular weight constituents in an amount less than about 10% by weight, based on the total weight of the polyoxymethylene. In certain embodiments, for instance, the polyoxymethylene polymer may contain low molecular weight constituents in an amount less than about 5% by weight, such as in an amount less than about 3% by weight, such as even in an amount less than about 2% by weight.

The preparation of the polyoxymethylene can be carried out by

polymerization of polyoxymethylene-forming monomers, such as trioxane or a mixture of trioxane and dioxolane, in the presence of ethylene glycol as a molecular weight regulator. The polymerization can be effected as precipitation polymerization or in the melt. By a suitable choice of the polymerization

parameters, such as duration of polymerization or amount of molecular weight regulator, the molecular weight and hence the MVR value of the resulting polymer can be adjusted. The above-described procedure for the polymerization can lead to polymers having comparatively small proportions of low molecular weight constituents. If a further reduction in the content of low molecular weight constituents were to be desired, this can be effected by separating off the low molecular weight fractions of the polymer after the deactivation and the

degradation of the unstable fractions after treatment with a basic protic solvent. This may be a fractional precipitation from a solution of the stabilized polymer; polymer fractions of different molecular weight distribution being obtained.

In one embodiment, a polyoxymethy!ene polymer with hydroxyl terminal groups can be produced using a cationic polymerization process followed by solution hydrolysis to remove any unstable end groups. During cationic

polymerization, a glycol, such as ethylene glycol can be used as a chain terminating agent. The cationic polymerization results in a bimodal molecular weight distribution containing low molecular weight constituents. In one particular embodiment, the low molecular weight constituents can be significantly reduced by conducting the polymerization using a heteropoly acid such as phosphotungstic acid as the catalyst. When using a heteropoly acid as the catalyst, for instance, the amount of low molecular weight constituents can be less than about 2% by weight.

A heteropoly acid refers to polyacids formed by the condensation of different kinds of oxo acids through dehydration and contains a mono- or poly- nuclear complex ion wherein a hetero element is present in the center and the oxo acid residues are condensed through oxygen atoms. Such a heteropoly acid is represented by the formula:

H_x[M_m '_nO_z]yH₂0

wherein

represents an element selected from the group consisting of P, Si, Ge, Sn, As, Sb, U, Mn, Re, Cu, Ni, Ti, Co, Fe, Cr, Th or Ce,

M' represents an element selected from the group consisting of W, Mo, V or

Nb,

m is 1 to 10,

n is 6 to 40, z is 10 to 100,

x is an integer of 1 or above, and

y is 0 to 50.

The central element (M) in the formula described above may be composed of one or more kinds of elements selected from P and Si and the coordinate element (Μ') is composed of at least one element selected from W, Mo and V, particularly W or Mo.

Specific examples of heteropoly acids are phosphomolybdic acid, phosphotungstic acid, phosphomolybdotungstic acid, phosphomolybdovanadic acid, phosphomolybdotungstovanadic acid, phosphotungstovanadic acid, silicotungstic acid, silicomolybdic acid, silicomolybdotungstic acid,

silicomolybdotungstovanadic acid and acid salts thereof.

Excellent results have been achieved with heteropoly acids selected from 12-molybdophosphoric acid (H₃PMo-i₂0₄o) and 12-tungstophosphoric acid

(H₃PWi2O₄₀) and mixtures thereof.

The heteropoly acid may be dissolved in an alkyl ester of a polybasic carboxylic acid. It has been found that alkyl esters of polybasic carboxylic acid are effective to dissolve the heteropoly acids or salts thereof at room temperature (25°C).

The alkyl ester of the polybasic carboxylic acid can easily be separated from the production stream since no azeotropic mixtures are formed. Additionally, the alkyl ester of the polybasic carboxylic acid used to dissolve the heteropoly acid or an acid salt thereof fulfils the safety aspects and environmental aspects and, moreover, is inert under the conditions for the manufacturing of oxymethylene polymers.

Preferably the alkyl ester of a polybasic carboxylic acid is an alkyl ester of an aliphatic dicarboxylic acid of the formula:

(ROOCMCH₂)„.(COOR') wherein

n is an integer from 2 to 12, preferably 3 to 6 and R and R' represent independently from each other an alkyl group having 1 to 4 carbon atoms, preferably selected from the group consisting of methyl, ethyl, n- propyl, iso-propyl, n-butyl, iso-butyl and tert.-butyl.

In one embodiment, the polybasic carboxylic acid comprises the dimethyl or diethyl ester of the above-mentioned formula, such as a dimethyl adipate (DMA).

The alkyl ester of the polybasic carboxylic acid may also be represented by the following formula:

(ROOC)₂-CH-(CH₂)_m-CH-(COOR^,)₂ wherein

m is an integer from 0 to 10, preferably from 2 to 4 and

R and R' are independently from each other alkyl groups having 1 to 4 carbon atoms, preferably selected from the group consisting of methyl, ethyl, n-propyl, iso- propyl, n-butyl, iso-butyl and tert.-butyl.

Particularly preferred components which can be used to dissolve the heteropoly acid according to the above formula are butantetracarboxylic acid tetratethyl ester or butantetracarboxylic acid tetramethyf ester.

Specific examples of the alkyl ester of a polybasic carboxylic acid are dimethyl glutaric acid, dimethyl adipic acid, dimethyl pimelic acid, dimethyl suberic acid, diethyl glutaric acid, diethyl adipic acid, diethyl pimelic acid, diethyl suberic acid, diemethyl phthalic acid, dimethyl isophthalic acid, dimethyl terephthalic acid, diethyl phthalic acid, diethyl isophthalic acid, diethyl terephthalic acid,

butantetracarboxylic acid tetramethylester and butantetracarboxylic acid

tetraethylester as well as mixtures thereof. Other examples include

dimethylisophthalate, diethylisophthalate, dimethyiterephthalate or

diethylterephthalate.

Preferably, the heteropoly acid is dissolved in the alkyl ester of the polybasic carboxylic acid in an amount lower than 5 weight percent, preferably in an amount ranging from 0.01 to 5 weight percent, wherein the weight is based on the entire solution.

In some embodiments, the polymer composition of the present disclosure may contain other polyoxymethylene homopolymers and/or polyoxymethylene copolymers. Such polymers, for instance, are generally unbranched linear polymers which contain as a rule at least 80%, such as at least 90%,

oxymethylene units. Such conventional polyoxymethylenes may be present in the composition as long as the resulting mixture maintains the above amounts of hydroxyl terminated groups and the above amounts of low molecular weight constituents.

The polyoxymethylene polymer present in the composition can generally have a melt volume rate (MVR) or melt index of less than 50 cm³/10 min, such as from about 1 to about 40 cm³/10 min, determined according to ISO 1133 at 190°C and 2.16 kg. In general, the molecular weight of the polyoxymethylene polymer is related to the melt index. In particular, a higher melt index refers to a lower molecular weight. In one embodiment of the present disclosure, a

polyoxymethylene polymer is incorporated into the polymer composition having a relatively low molecular weight. The amount of coupling agent, however, is increased based upon the molecular weight and the number of terminal hydroxyl groups. It has been discovered that lowering the molecular weight of the polymer while increasing the amount of coupling agent produces a polymer composition capable of being blow molded and that has significantly improved multi axial impact properties, especially when measured at extremely low temperatures.

For example, in one embodiment, the present disclosure is directed to a polyoxymethylene polymer having an increased number of hydroxyl terminal groups and that has a melt index of from about 5 cm³/ 0 min to about 20 cm³/ 0 min, such as from about 7 cm³/ 0 min to about 12 cm³/10 min, such as from about 8 cm³/10 min to about 10 cm³/10 min. In this embodiment, the polyoxymethylene polymer may optionally have lower amounts of low molecular weight constituents. In the past, polyoxymethylene polymers having a melt index within the above range have been found unsuitable for use in some blow molding applications since the polymers do not have sufficient shear viscosity. The present inventors discovered, however, that using lower molecular weight polymers as described above in combination with greater amounts of coupling agent produces polymer compositions that not only have increased shear viscosity, but also have excellent multi axial impact properties. The amount of polyoxymethylene polymer present in the polymer

composition of the present disclosure can vary depending upon the particular application. In one embodiment, for instance, the composition contains

polyoxymethylene polymer in an amount of at least 50% by weight, such as in an amount greater than about 60% by weight, such as in an amount greater than about 65% by weight, such as in an amount greater than about 70% by weight. In general, the polyoxymethylene polymer is present in an amount less than about 95% by weight, such as in an amount less than about 90% by weight, such as in an amount less than about 85% by weight.

As described above, in addition to a polyoxymethylene polymer, the composition also contains an impact modifier and a coupling agent if needed for an attachment to occur. The impact modifier may comprise a thermoplastic elastomer. In general, any suitable thermoplastic elastomer may be used according to the present disclosure as long as the thermoplastic elastomer can attach to the polyoxymethylene polymer whether through the use of a coupling agent or otherwise. In one embodiment, for instance, the thermoplastic elastomer may include reactive groups that directly or indirectly attach to reactive groups contained on the polyoxymethylene polymer. For instance, in one particular embodiment, the thermoplastic elastomer has active hydrogen atoms which allow for covalent bonds to form with the hydroxyl groups on the polyoxymethylene using the coupling agent.

Thermoplastic elastomers are materials with both thermoplastic and elastomeric properties. Thermoplastic elastomers include styrenic block copolymers, polyolefin blends referred to as thermoplastic olefin elastomers, elastomeric alloys, thermoplastic polyurethanes, thermoplastic copolyesters, and thermoplastic polyamides.

Thermoplastic elastomers well suited for use in the present disclosure are polyester elastomers (TPE-E), thermoplastic polyamide elastomers (TPE-A) and in particular thermoplastic polyurethane elastomers (TPE-U). The above

thermoplastic elastomers have active hydrogen atoms which can be reacted with the coupling reagents and/or the polyoxymethylene polymer. Examples of such groups are urethane groups, amido groups, amino groups or hydroxyl groups. For instance, terminal polyester diol flexible segments of thermoplastic polyurethane elastomers have hydrogen atoms which can react, for example, with isocyanate groups.

In one particular embodiment, a thermoplastic polyurethane elastomer is used as the impact modifier either alone or in combination with other impact modifiers. The thermoplastic polyurethane elastomer, for instance, may have a soft segment of a long-chain diol and a hard segment derived from a diisocyanate and a chain extender. In one embodiment, the polyurethane elastomer is a polyester type prepared by reacting a long-chain diol with a diisocyanate to produce a polyurethane prepolymer having isocyanate end groups, followed by chain extension of the prepolymer with a diol chain extender. Representative long- chain diols are polyester diols such as poly(butylene adipate)diol, poly(ethylene adipate)diol and poly(e-caprolactone)diol; and polyether diols such as

poly(tetramethylene ether)glycol, polypropylene oxide)glycol and poly(ethylene oxide)glycol. Suitable diisocyanates include 4_r4'-methylenebis(phenyl isocyanate), 2,4-toluene diisocyanate, 1 ,6-hexamethylene diisocyanate and 4,4'-methylenebis- (cycloxylisocyanate). Suitable chain extenders are C₂-C₆ aliphatic diols such as ethylene glycol, 1 ,4-butanediol, 1 ,6-hexanediol and neopentyl glycol. One example of a thermoplastic polyurethane is characterized as essentially poly(adipic acid-co- butylene glycol-co-diphenylmethane diisocyanate).

The amount of impact modifier contained in the polymer composition used to form the containment device can vary depending on many factors. The amount of impact modifier present in the composition may depend, for instance, on the desired permeability of the resulting material and/or on the amount of coupling agent present and the amount of terminal hydroxyl groups present on the polyoxymethylene polymer. In general, one or more impact modifiers may be present in the composition in an amount greater than about 5% by weight, such as in an amount greater than about 10% by weight. The impact modifier is generally present in an amount less than 30% by weight, such as in an amount less than about 25% by weight, such as in an amount up to about 18% by weight in order to provide sufficient impact strength resistance while preserving the permeability properties of the material.

The coupling agent present in the polymer composition comprises a coupling agent capable of coupling the impact modifier to the polyoxymethylene polymer. In order to form bridging groups between the polyoxymethylene polymer and the impact modifier, a wide range of polyfunctional, such as trifunctional or bifunctional coupling agents, may be used. The coupling agent may be capable of forming covalent bonds with the terminal hydroxyl groups on the polyoxymethylene polymer and with active hydrogen atoms on the impact modifier. In this manner, the impact modifier becomes coupled to the polyoxymethylene through covalent bonds.

In one embodiment, the coupling agent comprises a diisocyanate, such as an aliphatic, cycloaliphatic and/or aromatic diisocyanate. The coupling agent may be in the form of an oligomer, such as a trimer or a dimer.

In one embodiment, the coupling agent comprises a diisocyanate or a triisocyanate which is selected from 2,2'-, 2,4'-, and 4,4'-diphenylmethane diisocyanate ( DI); 3,3'-dimethyl-4,4'-biphenylene diisocyanate (TODI); toluene diisocyanate (TDI); polymeric MDI; carbodiimide-modified liquid 4,4'- diphenylmethane diisocyanate; para-phenylene diisocyanate (PPDI); meta- phenylene diisocyanate (MPDI); triphenyl methane-4,4'- and triphenyl methane- 4,4"-triisocyanate; naphthylene-1 ,5-diisocyanate; 2,4'-, 4,4'-, and 2,2-biphenyl diisocyanate; polyphenylene polymethylene polyisocyanate (PMDI) (also known as polymeric PMDI); mixtures of MDI and PMDI; mixtures of PMDI and TDI; ethylene diisocyanate; propylene-1 ,2-diisocyanate; trimethylene diisocyanate; butylenes diisocyanate; bitolylene diisocyanate; tolidine diisocyanate; tetramethylene- ,2- diisocyanate; tetramethylene-1 ,3-diisocyanate; tetramethylene-1 ,4-diisocyanate; pentamethylene diisocyanate; 1 ,6-hexamethylene diisocyanate (HDI);

octamethylene diisocyanate; decamethylene diisocyanate; 2,2,4- trimethylhexamethylene diisocyanate; 2,4,4-trimethyIhexamethylene diisocyanate; dodecane-1 ,12-diisocyanate; dicyclohexylmethane diisocyanate; cyclobutane-1 ,3- diisocyanate; cyclohexane- ,2-diisocyanate; cyclohexane-1 , 3-diisocyanate;

cyclohexane-1 ,4-diisocyanate; diethylidene diisocyanate; methylcyclohexylene diisocyanate (HTDI); 2,4-methylcyc!ohexane diisocyanate; 2,6-methylcyclohexane diisocyanate; 4,4'-dicyclohexyl diisocyanate; 2,4'-dicyclohexyl diisocyanate; 1 ,3,5- cyclohexane triisocyanate; isocyanatomethylcyclohexane isocyanate; 1- isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane;

isocyanatoethylcyclohexane isocyanate; bis(isocyanatomethyl)-cyctohexane diisocyanate; 4,4'-bis(isocyanatomethyl) dicyclohexane; 2,4'-bis(isocyanatomethyl) dicyclohexane; isophorone diisocyanate (IPDI); dimeryl diisocyanate, dodecane- 1 ,12-diisocyanate, 1 ,10-decamethylene diisocyanate, cyclohexylene-1 ,2- diisocyanate, 1 ,10-decamethylene diisocyanate, 1-chlorobenzene-2,4- diisocyanate, furfurylidene diisocyanate, 2,4,4-trimethyl hexamethylene

diisocyanate, 2,2,4-trimethyl hexamethylene diisocyanate, dodecamethylene diisocyanate, 1,3-cyclopentane diisocyanate, 1 ,3-cyclohexane diisocyanate, 1 ,3- cyclobutane diisocyanate, 1 ,4-cyclohexane diisocyanate, 4,4'- methylenebis(cyclohexyl isocyanate), 4,4'-methylenebis(phenyl isocyanate), 1- methy[-2,4-cyclo exane diisocyanate, 1-methyl-2,6-cyclohexane diisocyanate, 1 ,3- bis (isocyanato-methyl)cyclohexane, 1 ,6-diisocyanato-2,2,4,4-tetra-methylhexane, 1 ,6-diisocyanato-2,4,4-tetra-trimethylhexane, trans-cyclohexane-1 ,4-diisocyanate, 3-isocyanato-methyl-3,5,5-trimethylcyclo-hexyl isocyanate, 1-isocyanato-3,3,5- trimethyl~5-isocyanatomethylcyclohexane, cyclo-hexyl isocyanate,

dicyclohexylmethane 4,4'-diisocyanate, 1 ,4-bis(isocyanatomethyl)cyclohexane, m- phenylene diisocyanate, m-xylylene diisocyanate, m-tetramethylxylylene

diisocyanate, p-phenylene diisocyanate, ρ,ρ'-biphenyl diisocyanate, 3,3'-dimethyl- 4,4'-biphenylene diisocyanate, 3,3'-dimethoxy-4,4'-biphenylene diisocyanate, 3,3'- diphenyl-4,4'-biphenylene diisocyanate, 4,4'-biphenylene diisocyanate, 3,3'- dichloro-4,4'-biphenylene diisocyanate, 1 ,5-naphthalene diisocyanate, 4-chloro-

1.3- phenylene diisocyanate, 1 ,5-tetrahydronaphthalene diisocyanate, metaxylene diisocyanate, 2,4-toluene diisocyanate, 2,4'-diphenylmethane diisocyanate, 2,4- chlorophenylene diisocyanate, 4,4'-diphenylmethane diisocyanate, ρ,ρ'- diphenylmethane diisocyanate, 2,4-tolyiene diisocyanate, 2,6-tolylene

diisocyanate, 2,2-diphenylpropane-4,4'-diisocyanate, 4,4'-toluidine diisocyanate, dianidine diisocyanate, 4,4 -diphenyl ether diisocyanate, 1 ,3-xylylene diisocyanate,

1.4- naphthylene diisocyanate, azobenzene-4,4'-diisocyanate, diphenyl sulfone- 4,4'-diisocyanate, or mixtures thereof.

In one embodiment, an aromatic polyisocyanate is used, such as 4,4'- diphenylmethane diisocyanate (MDI).

The polymer composition generally contains the coupling agent in an amount from about 0.1% to about 10% by weight. In one embodiment, for instance, the coupling agent is present in an amount greater than about 1% by weight, such as in an amount greater than 2% by weight. In one particular embodiment, the coupling agent is present in an amount from about 0.2% to about 5% by weight. To ensure that the impact modifier has been completely coupled to the polyoxymethylene polymer, in one embodiment, the coupling agent can be added to the polymer composition in molar excess amounts when comparing the reactive groups on the coupling agent with the amount of terminal hydroxyl groups on the polyoxymethylene polymer.

As described above, in one embodiment, greater amounts of the coupling agent are combined with the polyoxymethylene polymer when the

polyoxymethylene polymer has a relatively low molecular weight. For instance, in one embodiment, the polyoxymethylene polymer can have a melt index of greater than about 5 cm³/10 min, such as greater than about 7 cm³/10 min. For instance, the polyoxymethylene polymer can have a melt index of from about 5 cm³/10 min to about 20 cm³/10 min, such as from about 7 cm³/10 min to about 2 cm³/10 min, such as from about 8 cm³/10 min to about 10 cm³/10 min. In this embodiment, the coupling agent may be added in an amount such that there is from about 0.8 to about 2 mol of the coupling agent per mol of hydroxyl groups on the

polyoxymethylene polymer. For instance, in one embodiment, the coupling agent can be added in an amount greater than 1.5% by weight, such as in an amount greater than about 3% by weight, such as from about 1.5% by weight to about 10% by weight, such as from about 1.5% by weight to about 5% by weight.

Combining a relatively low molecular weight polyoxymethylene polymer with greater amounts of coupling agent may produce hollow articles having increased multi axial impact strengths, especially at relatively low temperatures. For instance, the polymer composition may have a multi axial impact strength when tested according to AST D3763 and when measured at -40°C of greater than about 15 ftlb-f, such as greater than about 18 ftlb-f, such as greater than about 20 ftlb-f. In general, the impact strength will be less than about 50 ftlb-f. Articles produced from the composition can thus pass SAE Test J288.

In one embodiment, a relatively low molecular weight polyoxymethylene polymer may be used and sufficient amounts of coupling agent may be combined with the polymer in conjunction with an impact modifier so as to produce a polymer composition that not only has excellent multi axial impact strength characteristics, but also is capable of being used in a blow molding process. In this regard, in one embodiment, the coupling agent can be added to the polymer composition in an amount sufficient for the polymer composition to have a shear viscosity of at least about 8000 Pa-s at a shear rate of 0.1 rad/sec and at a temperature of 190°C. For instance, the coupling agent may be added such that the polymer composition has a shear viscosity of from about 8000 Pa-s at the above conditions to about 30,000 Pa-s, such as from about 8000 Pa-s to about 15,000 Pa-s, such as from about 8000 Pa-s to about 12,000 Pa-s.

The above polymer composition is particularly well suited to producing small off-road engine fuel tanks that may require very high impact strength at cold temperatures, such as temperatures even as low as -40°C. The above results can be obtained using a polyoxymethylene polymer having a relatively high number of terminal hydroxyl groups that may also optionally have a relatively low amount of low molecular weight constituents.

In one embodiment, a formaldehyde scavenger may also be included in the composition. The formaldehyde scavenger, for instance, may be amine-based and may be present in an amount less than about 1 % by weight.

The polymer composition of the present disclosure can optionally contain a stabilizer and/or various other known additives. Such additives can include, for example, antioxidants, acid scavengers, UV stabilizers or heat stabilizers. In addition, the molding material or the molding may contain processing auxiliaries, for example adhesion promoters, lubricants, nucleating agents, demolding agents, fillers, reinforcing materials or antistatic agents and additives which impart a desired property to the molding material or to the molding, such as dyes and/or pigments.

In general, other additives can be present in the polymer composition in an amount up to about 10% by weight, such as from about 0.1% to about 5% by weight, such as from about 0.1 to about 2% by weight.

When forming containment devices in accordance with the present disclosure, the above described components can be melt blended together, which automatically causes the reaction to occur between the coupling agent, the polyoxymethylene polymer, and the impact modifier. As described above, the coupling agent reacts with the reactive end groups on the polyoxymethylene polymer and the reactive groups on the impact modifier. The reaction between the components can occur simultaneously or in sequential steps. In one particular embodiment, the components in the composition are mixed together and then melt blended in an extruder.

The reaction of the components is typically effected at temperatures of from

100 to 240°C, such as from 150 to 220°C, and the duration of mixing is typically from 0.5 to 60 minutes.

The proportion of coupling agent in relation to the other components can be chosen within wide limits. For instance, the coupling agent may be used in an amount such that there are from 0.2 to 5 mol, preferably from 0.5 to 4 mol, of the coupling agent per mole of active hydrogen atoms, for example in the form of hydroxyl groups, of the polyoxymethylene containing active hydrogen atoms.

When using a polyoxymethylene polymer having a relatively low molecular weight, for instance, the coupling agent may be present in the composition such that there is at least 0.6 mol of coupling agent, such as from about 0.6 mol of coupling agent to about 4 mol, such as from about 0.6 mol of coupling agent to about 2 mol of coupling agent per mol of hydroxyl groups on the polyoxymethylene polymer.

In one embodiment, the molding composition of the present disclosure is reacted together and compounded prior to being used in a molding process. For instance, in one embodiment, the different components can be melted and mixed together in a conventional single or twin screw extruder at a temperature described above. Extruded strands may be produced by the extruder which are then pelletized. Prior to compounding, the polymer components may be dried to a moisture content of about 0.05 weight percent or less. If desired, the pelletized compound can be ground to any suitable particle size, such as in the range of from about 100 microns to about 500 microns.

As described above, the formation of VOC and compressed gas

containment devices in accordance with the present disclosure can be done using any suitable molding process, such as blow molding, rotational molding, or injection molding. In one particular embodiment, injection molding is used to form the containment devices. For instance, a plurality of portions of the containment devices can be first produced and then welded together.

When injection molding, the pre-compounded composition or the individual components can be fed to a heated barrel, mixed and forced into a moid cavity.

The heated barrel may comprise a single screw extruder or a twin screw extruder. While in the barrel, the composition is heated to a temperature sufficient to form a molten mixture that flows. Once forced into a mold cavity, the polymer

composition cools and hardens producing the desired part. In one embodiment, injection molding can be gas assisted. For instance, non-reactive gases, such as nitrogen or supercritical gases can be used to place pressure on the molten

material for forcing the material against the walls of the mold. In other

embodiments, however, no such gas is needed to obtain the pressures necessary during injection into the mold.

After the portions or parts of the containment device are molded, the

different portions are then attached together. In one embodiment, for instance, any suitable welding process may be used to attach the portions together. For example, the portions may be attached together using laser welding, ultrasonic welding, linear vibration, orbital vibration, hot plate welding, or spin welding.

During laser welding, the components are subjected to electromagnetic radiation at wavelengths that causes absorption. The absorption of the electromagnetic radiation results in heating and melting at the interface of the components causing the different parts to join together.

During linear vibration, heat is generated by moving one part against another under pressure through a linear displacement in the plane of the joint.

When a molten state is reached at the joint interface, vibration is stopped and clamping pressure is maintained until a bond is formed between the parts. Orbital vibration is similar to linear vibration only an electromagnetic drive is used to create relative motion between the two thermoplastic portions. This constant velocity motion generates heat and causes the two parts to bond together.

During hot plate welding, a heated platen assembly is introduced between the two portions to be joined together. Once the interface polymer on each part is melted or softened, the heated platen is withdrawn and the parts are clamped together.

Spin welding is a process that joins circular thermoplastic parts by bringing the part interfaces together under pressure with a circular spinning motion. One of · the portions is typically held stationary in a fixture while the other is rotated against it under pressure. The frictional heat that is generated causes the part interfaces to melt and fuse together.

In one particular embodiment, the different parts or portions of the containment device are bonded together using ultrasonic welding. During ultrasonic welding, an ultrasonic tool called a horn transfers vibratory energy through one or both parts at the interface. The vibratory energy is converted into heat through friction which causes the parts to bond together when pressure is applied. More particularly, during ultrasonic welding, one or more of the parts can be held between an anvil and the horn, which is connected to a transducer.

Typically, a low-amplitude acoustic vibration is emitted. The frequency used during ultrasonic welding can generally be from about 10 kHz to about 100 kHz.

The present disclosure may be better understood with reference to the following example.

EXAMPLE NO. 1

The following experiments were conducted in order to show some of the benefits and advantages of compositions made according to the present disclosure.

First, polyoxymethylene polymers were prepared using cationic

polymerization with ethylene glycol as the chain terminating agent, followed by solution hydrolysis. One of the polyoxymethylene polymers (Sample No. 1) was made using a conventional catalyst, namely boron trifluoride (BF₃). For purposes of comparison, a polyoxymethylene polymer (Sample No. 2) was produced using a heteropoly acid (HPA) as a catalyst.

The polymer feed composition for Sample Nos. 1 and 2 are included in the following table.

Table 1

The molecular weight distribution of the polyoxymethylene samples was determined by GPC. Each sample was dissolved (-30 minutes at 40°C, under 2 (g)) in distilled hexafluoroisopropanol (HFIP) buffered with potassium trifluroacetate. The samples were closely monitored and removed from heating as soon as the material was dissolved. The solution was filtered through a 0.45uM PTFE filter.

The analysis was performed at 40°C using HFIP w/ TEAN as the mobile phase on a Waters 2695 separations unit coupled with a Waters 2410 refractive index (Rl) detector. Two PL-HFIP gel columns fitted with an HFIP-gel guard column were used for the separation. The data was acquired and processed with EMPOWER PRO software. The sampling conditions were as follows: Conditions

1. Flow rate: 1.0ml/min

2. 100uL injection volume

3. Collection time 30mins

4. Multiple injections

5. Calibrated vs. well known PMMA standards

The end group analysis for the polyoxymethylene samples was determined by NMR. The samples were prepared by silylation prior to being tested. A solution of 0.84ml_ BSTFA and 63μ!_ pyridine (anhydrous) was added under nitrogen to a 10mL vial fitted with TEFLON septum.

The solution was heated to 45°C in a sample preparation unit with agitation. A second solution containing 30mg acetal and 0.6ml_ 60%CHCI₃/40%HFIP was prepared at 45°C. The acetal solution was transferred to the BSTFA solution via a glass syringe with metal tip that was preheated in an oven to 50°C. The mixture was agitated at 45°C for 1 hour after which time the solvent was evaporated under a stream of dry nitrogen. The white residue was re-dissolved and evaporated with dry HFIP an additional 3 times in the same manner.

The residue was dissolved at 45°C in a HFIP-d2 solution (w/ 0.1% pyridine). The H NMR spectrum for each sample was collected on a Bruker DMX300 spectrometer (Dual 5mm probe, 30° pulse, D1=6s, 256 transients, 40°C). Peak deconvolution was performed with the Bruker TopSpin v.1.3 software.

The following results were obtained: Table 2

LMWF - "low molecular weight fractions"

The molecular weight distribution for the polyoxymethylene polymers are also shown in Figs. 3 and 4. A comparison of the GPC curve in Figs. 3 and 4 demonstrates the reduction in the low molecular weight constituents that is achieved through the use of the heteropoly acid catalysts.

As shown above, the polyoxymethylene polymer made with the heteropoly acid contained less than 2% by weight low molecular weight constituents. Both polymers contained significant amounts of hydroxyl terminal groups.

The above polyoxymethylene polymers were then melt blended with an impact modifier, a coupling agent, and a stabilizer package including an antioxidant and a lubricant. The lubricant used contained a combination of ethylene bis stearamide and ethylene bis palmitamide. The antioxidant used was tetrakis-(methylene-(3,5-di-(tert)-butyl-4-hydrocinnamate))methane. The formulated compositions were melt blended using a 92 mm twin screw extruder. The extrusion conditions were as follows:

Table 3

The polymers were blended with a thermoplastic polyurethane elastomer impact modifier. In particular, the impact modifier was obtained from BASF under the trade name ELASTOLLAN. The coupling agent used was 4,4'- diphenylmethane diisocyanate. As described above, the compositions also contained a stabilizer package including an antioxidant and a lubricant. The samples were molded for multi axial impact testing using a Roboshot 165 SiB molding machine. The test specimen was a 4" diameter disc 1/8" of an inch thick. The molding conditions are included in the following table.

Table 4

The molded discs were tested for multi axial impact at -30 °C using ASTM method D3763. The instrument was a Dynatup 8250. The test speed was 1 1 ft/sec. The samples were conditioned for 24 hours at 23 °C and 50% RH prior to testing.

The permeation testing was conducted using molded discs. The discs were molded using the same molding machine (Roboshot 165 SiB) and molding conditions as the multi axial samples.

Material sample plaques were made by injection molding four inch diameter discs with an average thickness between 1/32 and 1/8 of an inch. The plaques were die cut into three inch circles in order to fit the permeation cup. The thickness of the material was measured at a minimum of five points, and the average thickness was determined from these measurements. Permeation cup test fixtures were assembled with the desired material plaque per SAE J2665, Sections 8.3 through 8.1 1 .

Permeation values of the material were determined gravimetrically using a modified version of SAE J2665 "Cup Weight Loss Method" (Issued Oct. 2006).

Vapometer Model 68 permeation cups, commercially available from Thwing-Albert, were used as the test fixture. The cups were modified per SAE J2665 in the following manner: 1) Neoprene gaskets were replaced with FK gaskets and 2) the six supplied knurled head screws were replaced to allow for torque wrench tightening.

Fuel CE10 was used as the test fuel (10% ethanol, 45% toluene, and 45% iso-octane). The cups were placed right-side up into a controlled thermal environment (T = 40 °C + 2 °C) so that the test material was in contact with only the vapor phase of the fuel. The weight of the test fixtures were measured twice a week. Weight-loss versus time was plotted using the method described in SAE J2665, Section 9. Determination of the steady-state flux, reported as [grams/(m²- day)], was carried out per SAE J2665, Section 10. Determination of the vapor transmission rate (VTR), or "permeation constant," reported as [grams-mm/(m²- day)], was carried out per SAE J2665, Section 1.

In the first set of experiments using the above procedures, permeation was tested on compositions where the impact modifier levels were varied. More particularly, a first set of compositions were formulated that are indicated below as "Sample No. 3". The Sample No. 3 compositions contained the polyoxymethylene polymer described above that contained low molecular weight constituents in an amount of greater than 0% by weight. Identical compositions were also formulated and are indicated in the table below as "Sample No. 4". The Sample No. 4 compositions contained the polyoxymethylene polymer described above that contained low molecular weight constituents in an amount less than 2% by weight.

Each of the Sample No. 3 compositions and the Sample No. 4 compositions contained the stabilizer package in an amount of 0.4% by weight and the impact modifier in the amounts listed below in Table 6. For compositions containing 18% by weight impact modifier or less, the compositions contained the coupling agent in an amount of 0.5% by weight. For the compositions containing the impact modifier in an amount of 30% by weight or more, the compositions contained the coupling agent in an amount of 0.8% by weight. The remainder of each composition was made up of the appropriate polyoxymethylene polymer. The following results were obtained: Table 5

— Not analyzed.

Compositions indicated as "Sample 3" above contained polyoxymethylene polymer that included low molecular weight constituents in an amount greater than 10% by weight.

Compositions indicated as "Sample 4" above contained polyoxymethylene polymer that included low molecular weight constituents in an amount less than 2% by weight.

The above results are also graphically shown in Fig. 5.

The data above illustrates the dramatic and unexpected reduction in permeability for the Sample 4 compositions containing the polyoxymethylene polymer having low levels of low molecular weight constituents. For instance, permeation decreased by greater than 30% on average when using the polyoxymethylene polymer containing low amounts of low molecular weight constituents.

It is believed that the lower permeability of the polyoxymethylene polymer containing low amounts of low molecular weight constituents allows the impact modifier concentration to be increased, while still maintaining the permeability performance of the material. The permeation data at a 2 mm wall thickness for compositions made according to Sample No. 3 and compositions made according to Sample No. 4 are shown below.

Table 6

-— Not analyzed Currently, most fuel tanks require that the material used to form the tank have a permeation of no greater than 2.5 g/m² day. The above results are also graphically illustrated in Fig. 7.

The following experiments were conducted to show how multi axial impact strength changes based on the amount of coupling agent present in the

composition. Multi axial impact strength is measured at -30°C.

The following compositions were formulated:

Table 7

As shown above, all of the "Sample No. 5" compositions and all of the "Sample No. 6" compositions were formulated using the polyoxymethylene polymer that contained the low molecular weight constituents in an amount greater than 10% by weight. The compositions made according to Sample No. 5 contained an impact modifier in an amount of 9% by weight, while the

compositions formulated according to Sample No. 6 contained the impact modifier in an amount of 18% by weight.

The following results were obtained:

Table 8

— Not analyzed As shown above, the cold temperature multi axial impact strength increases significantly as the coupling agent concentration increases and as the impact modifier amount increases. The above shows that the impact strength of the material can be increased by increasing the concentration of the coupling agent.

EXAMPLE NO. 2

The following experiments were conducted in order to demonstrate the advantages to using a lower molecular weight polyoxymethylene polymer in combination with higher amounts of a coupling agent. It is believed that the lower molecular weight polyoxymethylene polymer may contribute to better multi axial impact strength characteristics, while the higher amounts of coupling agent may increase the shear viscosity of the composition sufficient so the composition can be used in blow molding processes.

Impact modified polyoxymethylene polymer samples were prepared by melt blending a polyoxymethylene polymer with an impact modifier, a coupling agent, and a stabilizer package. The stabilizer package included an antioxidant and a lubricant. The extrusion conditions that were used to produce Sample Nos. 1-8 are provided in the following table.

TABLE 9

Sample Nos. 1-3 above were prepared using a higher molecular weight polyoxymethylene polymer having a melt index of 2.5 cm³/10 min. Samples 4-8, on the other hand, were prepared using a lower molecular weight

polyoxymethylene polymer having a melt index of about 9 cm³/10 min. The polyoxymethylene polymers used in Samples 4-8 also contained less than 10% by weight low molecular weight constituents. The polyoxymethylene polymer used in Samples 1-3, however, contained greater amounts of the low molecular weight constituents than Samples 4-8. The coupling agent used was 4,4'- diphenylmethane diisocyanate. The amount of each component (weight percent) is included in the following table.

TABLE 10

The above polymer compositions were molded into discs. The discs were molded using a Roboshot 165 SiB molding machine. Each test specimen had a 4" diameter and each disc was 1/8" thick. The molding conditions were as follows:

TABLE 11

The sample discs were tested for multi axial impact strength at 23°C, at -30°C, and at -40°C according to ASTM Method D3763. The testing speed was 11 ft sec.

Various physical properties of the polymer compositions were also tested using ISO tensile bars. The tensile bars were molded on a Roboshot 110 SiB 5 molding machine. The tensile properties were measured according to ISO Test Method 527. Charpy impact properties were also measured according to ISO Method 179. The following results were obtained:

TABLE 12

10 As shown above, polymer compositions made from the lower molecular weight polyoxymethylene polymers had better multi, axial impact strength, especially at lower temperatures. Sample Nos. 4 and 7 also demonstrated a shear viscosity of greater than 8000 Pa-s, indicating that the low molecular weight polyoxymethylene polymer compositions were also amenable to blow molding

15 processes.

These and other modifications and variations to the present invention may be practiced by those of ordinary skill in the art, without departing from the spirit and scope of the present invention, which is more particularly set forth in the appended claims. In addition, it should be understood that aspects of the various 20 embodiments may be interchanged both in whole or in part. Furthermore, those of ordinary skill in the art will appreciate that the foregoing description is by way of example only, and is not intended to limit the invention so further described in such appended claims.

Claims

What Is Claimed:

1. A VOC or compressed gas containment device comprising:

an opening configured to receive a volatile organic compound or a compressed gas, the VOC or compressed gas containment device including a volume surrounded by a wall;

and wherein the wall is made from a polymer composition comprising:

a) a polyoxymethylene polymer in which at least 50% of the terminal groups are hydroxyl groups, the polyoxymethylene polymer also

containing low molecular weight constituents having molecular weights beiow 10,000 dalton in an amount less than about 0% by weight, based on the total mass of polyoxymethylene polymer;

b) an impact modifier comprising a thermoplastic elastomer, the impact modifier being present in an amount of at least about 5% by weight, the impact modifier being chemically attached to the polyoxymethylene polymer;

and wherein the polymer composition has a permeation of less than

5 g mm/m² per day at 40°C according to SAE Test J2665 and has a multi axial impact strength at -30°C of greater than about 4 ftib-f according to ASTM Test D3763.

2. A VOC or compressed gas containment device as defined in claim , wherein the polymer composition further comprises a coupling agent, the coupling agent coupling the polyoxymethylene polymer and the thermoplastic elastomer together.

3. A VOC or compressed gas containment device as defined in claim 2, wherein the coupling agent comprises an isocyanate.

4. A VOC or compressed gas containment device as defined in claim , wherein the polymer composition has a permeation of less than about 2.5 g/m² day when tested at a thickness of 2 mm at 40°C.

5. A VOC or compressed gas containment device as defined in claim 1 , wherein the polymer composition has a permeation of less than about 3 g mm/m² per day at 40°C.

6. A VOC or compressed gas containment device as defined in claim 5, wherein the polymer composition has a multi axial impact of greater than about 10 ftlb-f at -30°C.

7. A VOC or compressed gas containment device as defined in claim 1 , wherein the VOC or compressed gas containment device comprises a fuel tank that has a volumetric capacity of up to 5 gallons.

8. A VOC or compressed gas containment device as defined in claim 1 , wherein the wall of the VOC or compressed gas containment device comprises only a monolayer of the polymer composition.

9. A VOC or compressed gas containment device as defined in claim 1 , wherein the wall has a thickness of from about 0.5 mm to about 10 mm.

10. A VOC or compressed gas containment device as defined in claim 1 , wherein the VOC or compressed gas containment device includes a first portion welded to a second portion, the first and second portions being formed by injection molding the polymer composition.

11. A VOC or compressed gas containment device as defined in claim 1 , wherein the polymer composition further comprises a heteropoly acid.

12. A VOC or compressed gas containment device as defined in claim 1 , wherein the thermoplastic elastomer comprises a thermoplastic polyurethane elastomer, the thermoplastic polyurethane elastomer being present in the polymer composition in an amount from about 10% to about 30% by weight.

13. A VOC or compressed gas containment device as defined in claim 2, wherein the coupling agent comprises methylenediphenyl 4,4 -diisocyanate, the methylenediphenyl 4,4'-diisocyanate being present in the polymer composition in an amount from about 0.5% to about 3% by weight.

14. A VOC or compressed gas containment device as defined in claim 3, wherein the thermoplastic elastomer comprises a thermoplastic polyurethane elastomer, the thermoplastic polyurethane elastomer being present in the polymer composition in an amount from about 10% to about 25% by weight, and wherein at least 70% of the terminal groups of the polyoxymethylene polymer are hydroxyl groups, the polyoxymethylene polymer being present in the polymer composition in an amount of at least about 70% by weight, the polyoxymethylene polymer containing the low molecular weight constitutents in an amount less than about 5% by weight based upon the total mass of the polyoxymethylene polymer, the wall of the VOC or compressed gas containment device comprising only a monolayer of the polymer composition, the wall having a thickness of from about 1.5 mm to about 4 mm,

15. A VOC or compressed gas containment device as defined in claim 14, wherein the containment device comprises a fuel tank.

16. A VOC or compressed gas containment device as defined in claim 14, wherein the polymer composition further comprises a heteropoly acid.

17. A VOC or compressed gas containment device as defined in claim 14, wherein the polymer composition has a multi axial impact of greater than about 10 ftlb-f at -30°C.

18. An engine incorporating a fuel tank, the fuel tank comprising a VOC or compressed gas containment device as defined in claim 1.

19. A VOC or compressed gas containment device as defined in claim 2, wherein the polyoxymethylene polymer includes first reactive groups and the impact modifier includes second reactive groups, the coupling agent causing covalent bonding to occur between the first reactive groups on the

polyoxymethylene polymer and between the second reactive groups on the impact modifier.

20. A process for producing the VOC or compressed gas containment device defined in claim 1 , the process comprising:

injection molding the polymer composition into a first mold to form a first portion of the containment device;

injection molding the polymer composition into a second mold to form a second portion of the containment device; and

welding the first portion to the second portion to form the VOC or compressed gas containment device.

21. A containment device having a hollow volume surrounded by a wall, the wall being made from a polymer composition comprising:

a) a polyoxymethylene polymer having terminal groups and wherein at least 50% of the terminal groups are hydroxyl groups, the

polyoxymethylene polymer having a melt index of from about 5 cm³/10 min to about 20 cm³/10 min measured at 190°C and at an applied weight of 2.16 kg; b) an impact modifier comprising a thermoplastic elastomer, the impact modifier being present in an amount of at least about 5% by weight, the impact modifier being chemically attached to the polyoxymethylene polymer;

c) a coupling agent present in an amount of from about 1.5% by weight to about 0% by weight, the coupling agent comprising an isocyanate;

and wherein the polymer composition has a permeation of less than 5 g mm/m² per day at 40°C according to SAE Test J2665 and has a multi axial impact strength at -40°C of greater than about 15 ftlb-f according to ASTM Test D3763.

22. A containment device as defined in claim 21 , wherein at least about 70% of the terminal groups on the polyoxymethylene poiymer are hydroxyl groups and wherein the polyoxymethylene polymer has a melt index of from about

7 cm³/10 min to about 12 cm³/10 min measured at 190°C and at an applied weight of 2.16 kg.

23. A containment device as defined in claim 21 , wherein the polymer composition has a multi axial impact strength at -40°C of greater than about

18 ftlb-f according to ASTM Test D3763.

24. A containment device as defined in claim 21 , wherein the polymer composition has a multi axial impact strength at -40°C of greater than about

20 ftlb-f according to ASTM Test D3763.

25. A containment device as defined in claim 21 , wherein the

containment device has been blow molded.

26. A containment device as defined in claim 25, wherein the

containment device comprises a fuel tank that has a volumetric capacity of up to 5 gallons.

27. A containment device as defined in claim 25, wherein the polymer composition has a shear viscosity of from about 8000 Pa-s to about 30,000 Pa-s at a shear rate of 0.1 rad/sec and at a temperature of 190°C.

28. A containment device as defined in claim 21 , wherein the wall comprises only a monolayer of the polymer composition.

29. A containment device as defined in claim 21 , wherein the coupling agent comprises methylenediphenyl 4,4'-diisocyanate.

30. A method for blow molding hollow articles comprising: combining a polyoxymethylene polymer with an impact modifier to produce a polymer composition, the polyoxymethylene polymer including terminal groups wherein at least about 50% of the terminal groups are hydroxyl groups, the polyoxymethylene polymer having a melt index of from about 5 cm³/ 0 min to about 20 cm³/10 min measured at 190°C and at an applied weight of 2.16 kg, the impact modifier comprising a thermoplastic elastomer, the impact modifier being present in the polymer composition in an amount of at least about 5% by weight;

adding a coupling agent to the polymer composition, the coupling agent comprising an isocyanate that couples the impact modifier to the

polyoxymethylene polymer, the coupling agent being added to the polymer composition in an amount sufficient for the polymer composition to have a shear viscosity of at least about 8000 Pa-s at a shear rate of 0.1 rad/sec and at a temperature of 190°C, and wherein greater amounts of the coupling agent are added to the polymer composition as the melt index of the polyoxymethylene polymer increases; and

blow molding a hollow article from the polymer composition.

31. A method as defined in claim 30, wherein at least about 70% of the terminal groups on the polyoxymethylene polymer are hydroxyl groups and wherein the polyoxymethylene polymer has a melt index of from about 7 cm³/10 min to about 12 cm³/10 min measured at 190°C and at an applied weight of 2.16 kg.

32. A method as defined in claim 30, wherein the polyoxymethylene polymer has a melt index of from about 10 cm³/10 min to about 11 cm³/10 min measured at 190°C and at an applied weight of 2.16 kg.

33. A method as defined in claim 30, wherein the coupling agent is added to the polymer composition in an amount from about 1.5% to about 10% by weight.

34. A method as defined in claim 30, wherein the coupling agent is added to the polymer composition in an amount from about 1.5% to about 5% by weight.

35. A method as defined in claim 30, wherein the polymer composition has a multi-axial impact strength at -40°C of greater than about 15 ftlb-f according to ASTM Test D3763.

36. A method as defined in claim 30, wherein the polymer composition has a multi-axial impact strength at -40°C of greater than about 8 ftlb-f according to ASTM Test D3763.

37. A method as defined in claim 30, wherein the coupling agent is added to the polymer composition such that there is from about 0.5 to about 4 mol of the coupling agent per mol of hydroxyl groups on the polyoxymethylene polymer.