WO2012037214A1 - Fibre de verre à faible densité et haute résistance pour applications balistiques - Google Patents

Fibre de verre à faible densité et haute résistance pour applications balistiques Download PDF

Info

Publication number
WO2012037214A1
WO2012037214A1 PCT/US2011/051544 US2011051544W WO2012037214A1 WO 2012037214 A1 WO2012037214 A1 WO 2012037214A1 US 2011051544 W US2011051544 W US 2011051544W WO 2012037214 A1 WO2012037214 A1 WO 2012037214A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight percent
glass
composite
fabric
glass fibers
Prior art date
Application number
PCT/US2011/051544
Other languages
English (en)
Inventor
James Carl Peters
Juan Camilo Serrano
Hong Li
Cheryl A. Richards
Original Assignee
Ppg Industries Ohio, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US12/940,764 external-priority patent/US8697590B2/en
Priority claimed from US13/229,012 external-priority patent/US8697591B2/en
Application filed by Ppg Industries Ohio, Inc. filed Critical Ppg Industries Ohio, Inc.
Publication of WO2012037214A1 publication Critical patent/WO2012037214A1/fr

Abstract

L'invention concerne des tissus, des composites, des pré-imprégnés, des stratifiés et d'autres produits incorporant des fibres de verre formées à partir de compositions de verre. Les fibres de verre, dans certaines formes de réalisation, sont incorporées dans des composites pouvant être utilisés dans des applications pour impacts de grande énergie, telles que des applications balistiques ou de résistance à l'explosion. Les fibres de verre formées à partir de certaines formes de réalisation des compositions de verre peuvent présenter certaines propriétés voulues, y compris, par exemple, des propriétés électriques voulues (p. ex. faible valeur Dk) ou des propriétés mécaniques voulues (p. ex. résistance spécifique).
PCT/US2011/051544 2010-09-14 2011-09-14 Fibre de verre à faible densité et haute résistance pour applications balistiques WO2012037214A1 (fr)

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US38279410P 2010-09-14 2010-09-14
US61/382,794 2010-09-14
US12/940,764 2010-11-05
US12/940,764 US8697590B2 (en) 2006-12-14 2010-11-05 Low dielectric glass and fiber glass for electronic applications
US13/229,012 2011-09-09
US13/229,012 US8697591B2 (en) 2006-12-14 2011-09-09 Low dielectric glass and fiber glass

Publications (1)

Publication Number Publication Date
WO2012037214A1 true WO2012037214A1 (fr) 2012-03-22

Family

ID=45831950

Family Applications (2)

Application Number Title Priority Date Filing Date
PCT/US2011/051532 WO2012037205A1 (fr) 2010-09-14 2011-09-14 Fibre de verre à faible densité et haute résistance pour applications balistiques
PCT/US2011/051544 WO2012037214A1 (fr) 2010-09-14 2011-09-14 Fibre de verre à faible densité et haute résistance pour applications balistiques

Family Applications Before (1)

Application Number Title Priority Date Filing Date
PCT/US2011/051532 WO2012037205A1 (fr) 2010-09-14 2011-09-14 Fibre de verre à faible densité et haute résistance pour applications balistiques

Country Status (8)

Country Link
EP (1) EP2616399A1 (fr)
KR (1) KR20130100312A (fr)
CN (1) CN103153895A (fr)
CA (1) CA2811273A1 (fr)
MX (1) MX2013002775A (fr)
RU (1) RU2013116989A (fr)
TW (2) TW201223904A (fr)
WO (2) WO2012037205A1 (fr)

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9278883B2 (en) * 2013-07-15 2016-03-08 Ppg Industries Ohio, Inc. Glass compositions, fiberizable glass compositions, and glass fibers made therefrom
EP3439796A4 (fr) * 2016-04-04 2020-02-12 PPG Industries Ohio, Inc. Composites contenant de la fibre de verre ayant une longueur de fibre de verre retenue, une résistance aux chocs et des propriétés de traction améliorées
CN106587729A (zh) * 2016-12-07 2017-04-26 巢湖市伟业玻璃有限公司 一种用于冰柜上的安全玻璃
EP4286346A1 (fr) 2018-03-07 2023-12-06 Electric Glass Fiber America, LLC Compositions de verre, compositions de verre pouvant former des fibres, et fibres de verre constituées à partir de ces dernières
WO2020237360A1 (fr) * 2019-05-28 2020-12-03 Global Metallix Canada Inc. Coussinet de gilet pare-balles souple et procédé de fabrication associé
WO2020237365A1 (fr) * 2019-05-28 2020-12-03 Global Metallix Canada Inc. Plaque de blindage composite et procédé de fabrication d'une plaque de blindage composite
CN115818966A (zh) 2019-09-25 2023-03-21 巨石集团有限公司 一种电子级玻璃纤维组合物及其玻璃纤维和电子布

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3008841A (en) * 1959-06-19 1961-11-14 Owens Corning Fiberglass Corp Glass composition
GB1006524A (en) * 1963-11-05 1965-10-06 Goodrich Co B F High tensile strength magnesium aluminium silicate glass compositions
DE1496520A1 (de) * 1963-10-30 1969-08-21 Goodrich Co B F Glasmasse
EP0344693A2 (fr) * 1988-06-01 1989-12-06 Hercules Incorporated Amélioration des propriétés physiques d'un matériau composite de polydicyclopentadifne renforcé par du verre au moyen d'un traitement à la chaleur
JP2002137937A (ja) * 2000-10-24 2002-05-14 Nippon Electric Glass Co Ltd 低誘電率低誘電正接ガラス繊維
US6890050B2 (en) 2002-08-20 2005-05-10 Palo Alto Research Center Incorporated Method for the printing of homogeneous electronic material with a multi-ejector print head

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4147555A (en) * 1977-04-21 1979-04-03 Owens-Corning Fiberglas Corporation Size compositions for glass fiber reinforced cementitious products
US9187361B2 (en) * 2005-11-04 2015-11-17 Ocv Intellectual Capital, Llc Method of manufacturing S-glass fibers in a direct melt operation and products formed there from

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3008841A (en) * 1959-06-19 1961-11-14 Owens Corning Fiberglass Corp Glass composition
DE1496520A1 (de) * 1963-10-30 1969-08-21 Goodrich Co B F Glasmasse
GB1006524A (en) * 1963-11-05 1965-10-06 Goodrich Co B F High tensile strength magnesium aluminium silicate glass compositions
EP0344693A2 (fr) * 1988-06-01 1989-12-06 Hercules Incorporated Amélioration des propriétés physiques d'un matériau composite de polydicyclopentadifne renforcé par du verre au moyen d'un traitement à la chaleur
JP2002137937A (ja) * 2000-10-24 2002-05-14 Nippon Electric Glass Co Ltd 低誘電率低誘電正接ガラス繊維
US6890050B2 (en) 2002-08-20 2005-05-10 Palo Alto Research Center Incorporated Method for the printing of homogeneous electronic material with a multi-ejector print head

Also Published As

Publication number Publication date
MX2013002775A (es) 2013-10-28
CN103153895A (zh) 2013-06-12
TW201223904A (en) 2012-06-16
EP2616399A1 (fr) 2013-07-24
KR20130100312A (ko) 2013-09-10
TW201224018A (en) 2012-06-16
RU2013116989A (ru) 2014-10-20
CA2811273A1 (fr) 2012-03-22
WO2012037205A1 (fr) 2012-03-22

Similar Documents

Publication Publication Date Title
US9056786B2 (en) Low density and high strength fiber glass for ballistic applications
US9156728B2 (en) Low density and high strength fiber glass for ballistic applications
US11905199B2 (en) Glass compositions, fiberizable glass compositions, and glass fibers made therefrom
US10906835B2 (en) Glass compositions, fiberizable glass compositions, and glass fibers made therefrom
EP3022163B1 (fr) Compositions de verre, compositions de verre pour former des fibres et fibres de verre obtenues à partir de celles-ci
US10647610B2 (en) Low density and high strength fiber glass for reinforcement applications
WO2012037214A1 (fr) Fibre de verre à faible densité et haute résistance pour applications balistiques
EP2616400A1 (fr) Fibre de verre à faible densité et haute résistance pour applications de renfort
Navias US 9,056,786 Β2

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11760936

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 11760936

Country of ref document: EP

Kind code of ref document: A1