WO2011142986A1 - Tampon abrasif fixe avec agent de surface à des fins de planarisation par polissage chimico-mécanique - Google Patents

Tampon abrasif fixe avec agent de surface à des fins de planarisation par polissage chimico-mécanique Download PDF

Info

Publication number
WO2011142986A1
WO2011142986A1 PCT/US2011/034439 US2011034439W WO2011142986A1 WO 2011142986 A1 WO2011142986 A1 WO 2011142986A1 US 2011034439 W US2011034439 W US 2011034439W WO 2011142986 A1 WO2011142986 A1 WO 2011142986A1
Authority
WO
WIPO (PCT)
Prior art keywords
structured
structured abrasive
abrasive article
abrasive
meth
Prior art date
Application number
PCT/US2011/034439
Other languages
English (en)
Inventor
Julie Y. Qian
Jimmie R. Baran, Jr.
Original Assignee
3M Innovative Properties Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Company filed Critical 3M Innovative Properties Company
Priority to US13/696,908 priority Critical patent/US20130059506A1/en
Priority to KR1020127031934A priority patent/KR20130081229A/ko
Priority to CN201180023624.XA priority patent/CN102892553B/zh
Priority to JP2013510126A priority patent/JP2013526777A/ja
Priority to SG2012083150A priority patent/SG185523A1/en
Publication of WO2011142986A1 publication Critical patent/WO2011142986A1/fr

Abstract

L'invention concerne un tampon abrasif fixe (100) présenté sous la forme d'un article abrasif structuré qui comporte une couche abrasive structurée (120) disposée sur un support (110). La couche abrasive structurée (120) comprend un liant polymère, des particules abrasives dispersées dans le liant et un agent de surface de polyéther non ionique dispersé dans le liant. Les particules abrasives ont une grosseur moyenne de particule de moins d'environ 250 nm et l'agent de surface est dans le liant en une quantité allant de 0,75 à 2,2 en pourcentage en poids en se basant sur le poids total de la couche abrasive structurée. L'invention concerne aussi un procédé permettant d'abraser une pièce en utilisant le tampon abrasif fixe fourni.
PCT/US2011/034439 2010-05-11 2011-04-29 Tampon abrasif fixe avec agent de surface à des fins de planarisation par polissage chimico-mécanique WO2011142986A1 (fr)

Priority Applications (5)

Application Number Priority Date Filing Date Title
US13/696,908 US20130059506A1 (en) 2010-05-11 2011-04-29 Fixed abrasive pad with surfactant for chemical mechanical planarization
KR1020127031934A KR20130081229A (ko) 2010-05-11 2011-04-29 화학 기계적 평탄화를 위한 계면활성제를 포함하는 고정 연마 패드
CN201180023624.XA CN102892553B (zh) 2010-05-11 2011-04-29 用于化学机械平面化的具有表面活性剂的固定磨料垫片
JP2013510126A JP2013526777A (ja) 2010-05-11 2011-04-29 化学機械平坦化用の界面活性剤を含む固定研磨パッド
SG2012083150A SG185523A1 (en) 2010-05-11 2011-04-29 Fixed abrasive pad with surfactant for chemical mechanical planarization

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US33335110P 2010-05-11 2010-05-11
US61/333,351 2010-05-11

Publications (1)

Publication Number Publication Date
WO2011142986A1 true WO2011142986A1 (fr) 2011-11-17

Family

ID=44383031

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2011/034439 WO2011142986A1 (fr) 2010-05-11 2011-04-29 Tampon abrasif fixe avec agent de surface à des fins de planarisation par polissage chimico-mécanique

Country Status (7)

Country Link
US (1) US20130059506A1 (fr)
JP (1) JP2013526777A (fr)
KR (1) KR20130081229A (fr)
CN (1) CN102892553B (fr)
SG (1) SG185523A1 (fr)
TW (1) TWI532597B (fr)
WO (1) WO2011142986A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014047014A1 (fr) * 2012-09-21 2014-03-27 3M Innovative Properties Company Incorporation d'additifs dans des bandes abrasives fixes pour de meilleures performances cmp
WO2014189086A1 (fr) * 2013-05-24 2014-11-27 Jsr株式会社 Tampon de polissage chimio-mécanique et procédé de polissage chimio-mécanique l'utilisant
US11926780B2 (en) 2014-12-23 2024-03-12 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and method of forming same

Families Citing this family (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20150104940A1 (en) * 2013-10-11 2015-04-16 Air Products And Chemicals Inc. Barrier chemical mechanical planarization composition and method thereof
US9873180B2 (en) * 2014-10-17 2018-01-23 Applied Materials, Inc. CMP pad construction with composite material properties using additive manufacturing processes
US10875145B2 (en) 2014-10-17 2020-12-29 Applied Materials, Inc. Polishing pads produced by an additive manufacturing process
US9776361B2 (en) 2014-10-17 2017-10-03 Applied Materials, Inc. Polishing articles and integrated system and methods for manufacturing chemical mechanical polishing articles
US11745302B2 (en) 2014-10-17 2023-09-05 Applied Materials, Inc. Methods and precursor formulations for forming advanced polishing pads by use of an additive manufacturing process
US10821573B2 (en) 2014-10-17 2020-11-03 Applied Materials, Inc. Polishing pads produced by an additive manufacturing process
CN113579992A (zh) 2014-10-17 2021-11-02 应用材料公司 使用加成制造工艺的具复合材料特性的cmp衬垫建构
US10875153B2 (en) 2014-10-17 2020-12-29 Applied Materials, Inc. Advanced polishing pad materials and formulations
US10399201B2 (en) 2014-10-17 2019-09-03 Applied Materials, Inc. Advanced polishing pads having compositional gradients by use of an additive manufacturing process
BR112017011164B1 (pt) 2014-11-26 2021-10-05 3M Innovative Properties Company Artigo abrasivo, conjunto abrasivo e método para sua utilização
EP3237147B1 (fr) * 2014-12-23 2020-02-19 Saint-Gobain Ceramics&Plastics, Inc. Particules abrasives façonnées et procédé de formation de celles-ci
US10632585B2 (en) 2015-04-23 2020-04-28 University Of Florida Research Foundation, Inc. Hybrid tool with both fixed-abrasive and loose-abrasive phases
WO2017074773A1 (fr) 2015-10-30 2017-05-04 Applied Materials, Inc. Appareil et procédé de formation d'article de polissage ayant un potentiel zêta souhaité
US10593574B2 (en) 2015-11-06 2020-03-17 Applied Materials, Inc. Techniques for combining CMP process tracking data with 3D printed CMP consumables
US10391605B2 (en) 2016-01-19 2019-08-27 Applied Materials, Inc. Method and apparatus for forming porous advanced polishing pads using an additive manufacturing process
US11471999B2 (en) 2017-07-26 2022-10-18 Applied Materials, Inc. Integrated abrasive polishing pads and manufacturing methods
USD850041S1 (en) * 2017-07-31 2019-05-28 3M Innovative Properties Company Scouring pad
WO2019032286A1 (fr) 2017-08-07 2019-02-14 Applied Materials, Inc. Tampons à polir à distribution abrasive et leurs procédés de fabrication
MX2020003717A (es) 2017-10-04 2020-12-09 Saint Gobain Abrasives Inc Artículo abrasivo y método para elaborarlo.
CN112654655A (zh) 2018-09-04 2021-04-13 应用材料公司 先进抛光垫配方
US11331767B2 (en) 2019-02-01 2022-05-17 Micron Technology, Inc. Pads for chemical mechanical planarization tools, chemical mechanical planarization tools, and related methods
US11851570B2 (en) * 2019-04-12 2023-12-26 Applied Materials, Inc. Anionic polishing pads formed by printing processes
USD934573S1 (en) * 2019-12-19 2021-11-02 3M Innovative Properties Company Sponge with surface pattern
US11813712B2 (en) 2019-12-20 2023-11-14 Applied Materials, Inc. Polishing pads having selectively arranged porosity
US11806829B2 (en) 2020-06-19 2023-11-07 Applied Materials, Inc. Advanced polishing pads and related polishing pad manufacturing methods
US11878389B2 (en) 2021-02-10 2024-01-23 Applied Materials, Inc. Structures formed using an additive manufacturing process for regenerating surface texture in situ

Citations (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5152917A (en) 1991-02-06 1992-10-06 Minnesota Mining And Manufacturing Company Structured abrasive article
US5435816A (en) 1993-01-14 1995-07-25 Minnesota Mining And Manufacturing Company Method of making an abrasive article
US5454844A (en) 1993-10-29 1995-10-03 Minnesota Mining And Manufacturing Company Abrasive article, a process of making same, and a method of using same to finish a workpiece surface
US5672097A (en) 1993-09-13 1997-09-30 Minnesota Mining And Manufacturing Company Abrasive article for finishing
US5681217A (en) 1994-02-22 1997-10-28 Minnesota Mining And Manufacturing Company Abrasive article, a method of making same, and a method of using same for finishing
US5692950A (en) 1996-08-08 1997-12-02 Minnesota Mining And Manufacturing Company Abrasive construction for semiconductor wafer modification
US5851247A (en) 1997-02-24 1998-12-22 Minnesota Mining & Manufacturing Company Structured abrasive article adapted to abrade a mild steel workpiece
US5958794A (en) 1995-09-22 1999-09-28 Minnesota Mining And Manufacturing Company Method of modifying an exposed surface of a semiconductor wafer
US6139594A (en) 1998-04-13 2000-10-31 3M Innovative Properties Company Abrasive article with tie coat and method
US20020026752A1 (en) * 1996-09-11 2002-03-07 Minnesota Mining And Manufacturing Company Abrasive article and method of making
WO2006112909A1 (fr) * 2005-04-14 2006-10-26 Saint-Gobain Abrasives, Inc. Méthode de formation d'un article abrasif structuré
US7497885B2 (en) 2006-12-22 2009-03-03 3M Innovative Properties Company Abrasive articles with nanoparticulate fillers and method for making and using them
US20090176443A1 (en) * 2006-12-22 2009-07-09 Kollodge Jeffrey S Structured fixed abrasive articles including surface treated nano-ceria filler, and method for making and using the same
WO2011034635A1 (fr) * 2009-09-16 2011-03-24 3M Innovative Properties Company Article abrasif structuré et procédé d'utilisation de celui-ci

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3732267B2 (ja) * 1996-01-29 2006-01-05 大日本印刷株式会社 研磨テープの製造方法
US5876268A (en) * 1997-01-03 1999-03-02 Minnesota Mining And Manufacturing Company Method and article for the production of optical quality surfaces on glass
US5833724A (en) * 1997-01-07 1998-11-10 Norton Company Structured abrasives with adhered functional powders
FR2766106B1 (fr) * 1997-07-18 2001-09-07 Coatex Sa Utilisation d'un copolymere a structure tensio-active comme agent dispersant et/ou d'aide au broyage
US6458018B1 (en) * 1999-04-23 2002-10-01 3M Innovative Properties Company Abrasive article suitable for abrading glass and glass ceramic workpieces
US20030017797A1 (en) * 2001-03-28 2003-01-23 Kendall Philip E. Dual cured abrasive articles
US7150771B2 (en) * 2004-06-18 2006-12-19 3M Innovative Properties Company Coated abrasive article with composite tie layer, and method of making and using the same

Patent Citations (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5152917B1 (en) 1991-02-06 1998-01-13 Minnesota Mining & Mfg Structured abrasive article
US5152917A (en) 1991-02-06 1992-10-06 Minnesota Mining And Manufacturing Company Structured abrasive article
US5435816A (en) 1993-01-14 1995-07-25 Minnesota Mining And Manufacturing Company Method of making an abrasive article
US5672097A (en) 1993-09-13 1997-09-30 Minnesota Mining And Manufacturing Company Abrasive article for finishing
US5454844A (en) 1993-10-29 1995-10-03 Minnesota Mining And Manufacturing Company Abrasive article, a process of making same, and a method of using same to finish a workpiece surface
US5681217A (en) 1994-02-22 1997-10-28 Minnesota Mining And Manufacturing Company Abrasive article, a method of making same, and a method of using same for finishing
US5958794A (en) 1995-09-22 1999-09-28 Minnesota Mining And Manufacturing Company Method of modifying an exposed surface of a semiconductor wafer
US5692950A (en) 1996-08-08 1997-12-02 Minnesota Mining And Manufacturing Company Abrasive construction for semiconductor wafer modification
US6007407A (en) 1996-08-08 1999-12-28 Minnesota Mining And Manufacturing Company Abrasive construction for semiconductor wafer modification
US20020026752A1 (en) * 1996-09-11 2002-03-07 Minnesota Mining And Manufacturing Company Abrasive article and method of making
US5851247A (en) 1997-02-24 1998-12-22 Minnesota Mining & Manufacturing Company Structured abrasive article adapted to abrade a mild steel workpiece
US6139594A (en) 1998-04-13 2000-10-31 3M Innovative Properties Company Abrasive article with tie coat and method
WO2006112909A1 (fr) * 2005-04-14 2006-10-26 Saint-Gobain Abrasives, Inc. Méthode de formation d'un article abrasif structuré
US7497885B2 (en) 2006-12-22 2009-03-03 3M Innovative Properties Company Abrasive articles with nanoparticulate fillers and method for making and using them
US20090176443A1 (en) * 2006-12-22 2009-07-09 Kollodge Jeffrey S Structured fixed abrasive articles including surface treated nano-ceria filler, and method for making and using the same
WO2011034635A1 (fr) * 2009-09-16 2011-03-24 3M Innovative Properties Company Article abrasif structuré et procédé d'utilisation de celui-ci

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014047014A1 (fr) * 2012-09-21 2014-03-27 3M Innovative Properties Company Incorporation d'additifs dans des bandes abrasives fixes pour de meilleures performances cmp
WO2014189086A1 (fr) * 2013-05-24 2014-11-27 Jsr株式会社 Tampon de polissage chimio-mécanique et procédé de polissage chimio-mécanique l'utilisant
US11926780B2 (en) 2014-12-23 2024-03-12 Saint-Gobain Ceramics & Plastics, Inc. Shaped abrasive particles and method of forming same

Also Published As

Publication number Publication date
CN102892553B (zh) 2016-04-27
JP2013526777A (ja) 2013-06-24
SG185523A1 (en) 2012-12-28
CN102892553A (zh) 2013-01-23
US20130059506A1 (en) 2013-03-07
TW201213121A (en) 2012-04-01
KR20130081229A (ko) 2013-07-16
TWI532597B (zh) 2016-05-11

Similar Documents

Publication Publication Date Title
US20130059506A1 (en) Fixed abrasive pad with surfactant for chemical mechanical planarization
EP2327088B1 (fr) Article abrasif structuré, son procédé de fabrication et utilisation dans la planarisation de plaquettes
US8083820B2 (en) Structured fixed abrasive articles including surface treated nano-ceria filler, and method for making and using the same
US20150217424A1 (en) Incorporating additives into fixed abrasive webs for improved cmp performance
US7497885B2 (en) Abrasive articles with nanoparticulate fillers and method for making and using them
KR100777846B1 (ko) 폴리싱 패드 및 그의 사용 방법
KR100491452B1 (ko) 웨이퍼 표면 개질용 플루오로화합물을 포함하는 연마 용품
EP1954446A1 (fr) Article abrasif et procede de modification de la surface d'une piece de fabrication
KR20140018880A (ko) 복제된 미세구조화 배킹을 갖는 연마재 물품 및 그것을 이용하는 방법
TW491758B (en) Printing of polishing pads

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201180023624.X

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11719721

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 13696908

Country of ref document: US

ENP Entry into the national phase

Ref document number: 2013510126

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20127031934

Country of ref document: KR

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 11719721

Country of ref document: EP

Kind code of ref document: A1