WO2011137565A1 - Procédé pour le revêtement de textiles - Google Patents

Procédé pour le revêtement de textiles Download PDF

Info

Publication number
WO2011137565A1
WO2011137565A1 PCT/CN2010/000641 CN2010000641W WO2011137565A1 WO 2011137565 A1 WO2011137565 A1 WO 2011137565A1 CN 2010000641 W CN2010000641 W CN 2010000641W WO 2011137565 A1 WO2011137565 A1 WO 2011137565A1
Authority
WO
WIPO (PCT)
Prior art keywords
dispersion
alkaline
acid
process according
alkali metal
Prior art date
Application number
PCT/CN2010/000641
Other languages
English (en)
Inventor
Rolf Irnich
Xuehui Zhao
Original Assignee
Bayer Materialscience Ag
Bayer Materialscience (China) Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bayer Materialscience Ag, Bayer Materialscience (China) Co., Ltd. filed Critical Bayer Materialscience Ag
Priority to PCT/CN2010/000641 priority Critical patent/WO2011137565A1/fr
Priority to ES11716943T priority patent/ES2458426T3/es
Priority to BR112012028562A priority patent/BR112012028562A2/pt
Priority to MX2012012918A priority patent/MX2012012918A/es
Priority to AU2011249947A priority patent/AU2011249947A1/en
Priority to PL11716943T priority patent/PL2567019T3/pl
Priority to US13/696,451 priority patent/US20130288551A1/en
Priority to EP20110716943 priority patent/EP2567019B1/fr
Priority to JP2013508459A priority patent/JP5730988B2/ja
Priority to KR1020127031976A priority patent/KR101810267B1/ko
Priority to PT117169433T priority patent/PT2567019E/pt
Priority to PCT/EP2011/056971 priority patent/WO2011138284A1/fr
Priority to DK11716943.3T priority patent/DK2567019T3/da
Priority to TW100115867A priority patent/TWI507584B/zh
Publication of WO2011137565A1 publication Critical patent/WO2011137565A1/fr
Priority to ZA2012/08196A priority patent/ZA201208196B/en
Priority to HK13109549.2A priority patent/HK1182150A1/xx
Priority to HRP20140366AT priority patent/HRP20140366T1/hr

Abstract

La présente invention porte sur un procédé pour la fabrication de textiles revêtus dans lequel un substrat textile est tout d'abord mis en contact avec une dispersion aqueuse comprenant au moins un sel inorganique et au moins une cellulose modifiée.
PCT/CN2010/000641 2010-05-07 2010-05-07 Procédé pour le revêtement de textiles WO2011137565A1 (fr)

Priority Applications (17)

Application Number Priority Date Filing Date Title
PCT/CN2010/000641 WO2011137565A1 (fr) 2010-05-07 2010-05-07 Procédé pour le revêtement de textiles
EP20110716943 EP2567019B1 (fr) 2010-05-07 2011-05-02 Procédé de revêtement de textiles
PT117169433T PT2567019E (pt) 2010-05-07 2011-05-02 Processo para o revestimento de têxteis
MX2012012918A MX2012012918A (es) 2010-05-07 2011-05-02 Procedimiento para el recubrimiento de productos textiles.
AU2011249947A AU2011249947A1 (en) 2010-05-07 2011-05-02 Process for the coating of textiles
PL11716943T PL2567019T3 (pl) 2010-05-07 2011-05-02 Proces powlekania materiałów włókienniczych
US13/696,451 US20130288551A1 (en) 2010-05-07 2011-05-02 Process for the coating of textiles
ES11716943T ES2458426T3 (es) 2010-05-07 2011-05-02 Procedimiento de recubrimiento de materiales textiles
JP2013508459A JP5730988B2 (ja) 2010-05-07 2011-05-02 織物の被覆方法
KR1020127031976A KR101810267B1 (ko) 2010-05-07 2011-05-02 텍스타일의 코팅 방법
BR112012028562A BR112012028562A2 (pt) 2010-05-07 2011-05-02 processo para o revestimento de tecidos
PCT/EP2011/056971 WO2011138284A1 (fr) 2010-05-07 2011-05-02 Procédé pour l'enduction de textiles
DK11716943.3T DK2567019T3 (da) 2010-05-07 2011-05-02 Fremgangsmåde til coating af tekstiler
TW100115867A TWI507584B (zh) 2010-05-07 2011-05-06 用於塗佈織物之方法
ZA2012/08196A ZA201208196B (en) 2010-05-07 2012-10-31 Process for the coating of textiles
HK13109549.2A HK1182150A1 (en) 2010-05-07 2013-08-15 Process for the coating of textiles
HRP20140366AT HRP20140366T1 (hr) 2010-05-07 2014-04-18 Postupak za prevlaäśenje tekstila

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/CN2010/000641 WO2011137565A1 (fr) 2010-05-07 2010-05-07 Procédé pour le revêtement de textiles

Publications (1)

Publication Number Publication Date
WO2011137565A1 true WO2011137565A1 (fr) 2011-11-10

Family

ID=44903562

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2010/000641 WO2011137565A1 (fr) 2010-05-07 2010-05-07 Procédé pour le revêtement de textiles

Country Status (1)

Country Link
WO (1) WO2011137565A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020037487A1 (fr) 2018-08-21 2020-02-27 Dow Global Technologies Llc Procédé de formation de cuir synthétique
WO2020037486A1 (fr) 2018-08-21 2020-02-27 Dow Global Technologies Llc Procédé de formation d'un cuir synthétique

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1480585A (zh) * 2002-08-05 2004-03-10 �����ɷ� 类皮革片及其制备方法
CN1714193A (zh) * 2002-12-20 2005-12-28 陶氏环球技术公司 制造合成皮革的方法及由此制造的合成皮革

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1480585A (zh) * 2002-08-05 2004-03-10 �����ɷ� 类皮革片及其制备方法
CN1714193A (zh) * 2002-12-20 2005-12-28 陶氏环球技术公司 制造合成皮革的方法及由此制造的合成皮革

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020037487A1 (fr) 2018-08-21 2020-02-27 Dow Global Technologies Llc Procédé de formation de cuir synthétique
WO2020037486A1 (fr) 2018-08-21 2020-02-27 Dow Global Technologies Llc Procédé de formation d'un cuir synthétique
EP3841242A4 (fr) * 2018-08-21 2022-07-13 Dow Global Technologies Llc Procédé de formation d'un cuir synthétique
US11746465B2 (en) 2018-08-21 2023-09-05 The Dow Chemical Company Process for forming a synthetic leather
US11834780B2 (en) 2018-08-21 2023-12-05 Dow Global Technologies Llc Process for forming synthetic leather

Similar Documents

Publication Publication Date Title
EP2567019B1 (fr) Procédé de revêtement de textiles
US9783926B2 (en) Process for the coating of textiles
US20070259984A1 (en) Microporous coating based on polyurethane polyurea
KR20140059855A (ko) 방수 통기성 코팅물을 위한 수성 폴리우레탄 분산액
MX2008012956A (es) Revestimiento microporoso a base de poliuretano-poliurea.
US9624621B2 (en) Process for the production of coated textiles
CN112513122A (zh) 涂料组合物
WO2011137565A1 (fr) Procédé pour le revêtement de textiles
CN103003486B (zh) 织物涂布方法
US20220325027A1 (en) Acid-resistant and alkali-resistant composition

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10850935

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10850935

Country of ref document: EP

Kind code of ref document: A1