WO2011134423A1 - 一种改良盐碱地的方法及盐碱地的种植方法 - Google Patents

一种改良盐碱地的方法及盐碱地的种植方法 Download PDF

Info

Publication number
WO2011134423A1
WO2011134423A1 PCT/CN2011/073512 CN2011073512W WO2011134423A1 WO 2011134423 A1 WO2011134423 A1 WO 2011134423A1 CN 2011073512 W CN2011073512 W CN 2011073512W WO 2011134423 A1 WO2011134423 A1 WO 2011134423A1
Authority
WO
WIPO (PCT)
Prior art keywords
saline
aggregate
soil
layer
planting
Prior art date
Application number
PCT/CN2011/073512
Other languages
English (en)
French (fr)
Inventor
秦升益
Original Assignee
北京仁创科技集团有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 北京仁创科技集团有限公司 filed Critical 北京仁创科技集团有限公司
Publication of WO2011134423A1 publication Critical patent/WO2011134423A1/zh

Description

一种改良盐碱地的方法及盐碱地的种植方法 技术领域
本发明涉及一种改良盐碱地的方法以及盐碱地的种植方法。 背景技术
目前， 国内外对盐碱地的处理方法一般包括排盐法和压盐法等， 但它们都存在着 许多不足之处， 例如， 排盐法是靠使用大量的淡水对盐碱地进行长期冲洗而使盐碱地表 面的含盐量降低， 压盐法是利用自然降水或人工大水灌溉， 促使部分盐碱沿着土壤的孔 隙、 裂缝等向下渗透， 将表层土壤的盐分随水带到底层。 上述方法虽然能够使盐碱地表 层的含盐量降低， 但不能够保持长久， 而且需要大量的水源。
因此， 迫切地需要开发一种用水量小并且能够长期有效地改良盐碱地的方法及盐 碱地的种植方法。 发明内容
本发明的目的是为了克服现有的改良盐碱地的方法及盐碱地的种植方法存在的用 水量大且效果保持不长久的缺点，提供一种用水量小并且能够长期有效地改良盐碱地的 方法及盐碱地的种植方法。
本发明提供了一种改良盐碱地的方法， 其中， 该方法包括： 在盐碱地上设置透气 性防渗骨料层， 在所述透气性防渗骨料层上设置种植土层。
此外， 本发明还提供了一种盐碱地的种植方法， 其中， 该方法包括： 将植物和 /或 植物种子栽种于改良后的盐碱地中， 其中， 该改良后的盐碱地是经过本发明提供的方法 处理的。
本发明提供的改良盐碱地的方法及盐碱地的种植方法在种植土层下设置透气性防 渗骨料层， 该透气性防渗骨料层既能够透气， 又能够有效地防止盐碱地的盐碱渗透到种 植土层中， 从而防止表层种植土层被盐渍化， 使种植土层能够长久地适于进行种植， 并 且所述透气性防渗骨料层还能防止种植土层中的水分渗透到盐碱地中，从而有利于种植 土层的保墒。 此外， 本发明提供的方法无需大量的淡水资源进行冲洗， 从而有效地降低 了用水量并扩大了该方法的使用范围。 具体实施方式
本发明提供了一种改良盐碱地的方法， 其中， 该方法包括： 在盐碱地上设置透气 性防渗骨料层， 在所述透气性防渗骨料层上设置种植土层。
根据本发明， 所述透气性防渗骨料层的透气性和渗流系数可以在很大范围内改变， 只要能够防止透气性防渗骨料层上的种植土层被盐渍化并具有一定的透气性以满足种 植土层中的植物生长即可，优选情况下，所述透气性防渗骨料层的透气度可以为 10-100， 所述透气度 k是反映材料透过气体能力的参数。通过一定形状试样的空气量 Q (厘米 3) 与通气时间 （分钟）、 试样前后的压力差 P (厘米 ·水柱高）、 试样的截面积 F (厘米 2) 成正比， 与试样高度 h (厘米） 成反比。
t - P F
即 Q = κ
h
Q h
则 K =
F · P t
式中: κ- -透气度 （厘米 3·厘米 /厘米 2·厘米水柱，分钟）
Q- -气体透过量 （厘米 3)
F- -试样截面积 （厘米 2)
h- -试样高度 （厘米）
ρ -压力差 （厘米水柱）
t—时间 （分钟）
所述渗流系数可以为 10—4-10— 7厘米 /秒，所述渗流系数是达西定律中表示常温下水在材料 中渗透力的量度 （厘米 /秒， cm/s )
本发明的发明人发现， 将含有骨料主体和位于骨料主体上的疏水性树脂膜的复合 颗粒铺设在盐碱地上之后能够有效地防止盐碱地的盐碱渗透到种植土层中。 因此， 优选 情况下， 所述透气性防渗骨料层由透气性防渗骨料颗粒铺设而成， 所述透气性防渗骨料 颗粒含有骨料主体和位于骨料主体上的疏水性树脂膜， 所述骨料主体可以为石英砂、 矿 渣、陶粒和玻璃微珠中的一种或几种。按照该优选实施方式，可以实现以下良好的效果： 所述透气性防渗骨料颗粒的主体为石英砂、矿渣、陶粒或玻璃微珠，具有良好的耐候性， 因此可以更长期有效地改良盐碱地； 石英砂、 矿渣、 陶粒或玻璃微珠的成本较低， 有利 于大规模地利用； 由所述透气性防渗骨料颗粒铺设成的所述透气性防渗骨料层的强度很 大， 不易被损坏， 能够长期地发挥防渗效果 < 所述骨料主体的大小可以在很大范围内改变， 优选情况下， 所述骨料主体的平均 粒子直径可以为 20-3500微米， 更优选为 100-1000微米。
所述透气性防渗骨料中， 位于骨料主体上的所述疏水性树脂膜的量可以在很大范 围内改变， 优选情况下， 以所述透气性防渗骨料的总重量为基准， 所述骨料主体的含量 可以为 90-99重量％， 所述疏水性树脂膜的含量可以为 1-10重量％。
根据本发明， 所述疏水性树脂膜的材料可以为疏水性环氧树脂、 疏水性酚醛树脂、 疏水性聚氨酯树脂以及疏水性硅树脂中的一种或几种。所述疏水性环氧树脂、 疏水性酚 醛树脂、 疏水性聚氨酯和疏水性硅树脂的种类为本领域技术人员所公知， 例如， 所述疏 水性环氧树脂可以为縮水甘油醚类环氧树脂、 縮水甘油酯类环氧树脂、 縮水甘油胺 类环氧树脂、线型脂肪族类环氧树脂、脂环族类环氧树脂、聚硫橡胶改性环氧树脂、 聚酰胺树脂改性环氧树脂、 聚乙烯醇叔丁醛改性环氧树脂、 丁腈橡胶改性环氧树脂、 酚醛树脂改性环氧树脂、 聚酯树脂改性环氧树脂、 尿醛三聚氰胺树脂改性环氧树脂、 糠 醛树脂改性环氧树脂、 乙烯树脂改性环氧树脂、 异氰酸酯改性环氧树脂和硅树脂改性环 氧树脂中的一种或几种。
例如， 所述疏水性酚醛树脂可以为二甲苯改性酚醛树脂、 环氧树脂改性酚醛树脂 和有机硅改性酚醛树脂中的一种或几种。
此外， 优选情况下， 所述所述疏水性树脂膜还可以含有固化剂， 所述固化剂的含 量可以在很大范围内改变， 优选情况下， 以所述疏水性树脂膜的总重量为基准， 所述固 化剂的含量为 20-25重量％。
本发明中， 所述固化剂的种类没有特别的限制， 只要能够使在所述骨料主体上形 成疏水性树脂膜即可。 例如， 所述固化剂可以为六次甲基四胺、 二丁基二月桂酸锡、
Ν,Ν,Ν',Ν'-四甲基胍盐、 过氧化酮、 环烷酸钴、 过氧化苯甲酸叔丁酯、 过氧化二碳酸酯、 二烷基过氧化物、 过氧化辛酸叔己酯和过氧化二碳酸双酯、 甲苯二异氰酸酯 （TDI) 和 三羟甲基丙烷（ΤΜΡ) 的加成物以及甲苯二异氰酸酯（TDI)的三聚体中的一种或几种。
根据本发明的一个优选的实施方式， 当使用二甲苯改性酚醛树脂、 环氧树脂改性 酚醛树脂和有机硅改性酚醛树脂中的一种或几种作为疏水性树脂膜的材料时，优选使用 六次甲基四胺作为固化剂。
根据本发明的另一个优选实施方式， 当使用疏水性有机硅树脂作为疏水性树脂膜 的材料时， 优选使用甲苯二异氰酸酯 （TDI)和三羟甲基丙烷 （ΤΜΡ) 的加成物和 /或甲 苯二异氰酸酯 （TDI) 的三聚体作为固化剂。 根据本发明的另一个优选实施方式， 当使用疏水性聚氨酯树脂作为疏水性树脂膜的 材料时， 当在常温下加入的固化剂优选为过氧化酮和 /或环烷酸钴，在加热状态下加入的 固化剂优选为过氧化苯甲酸叔丁酯、 过氧化二碳酸酯、 二烷基过氧化物、 过氧化辛酸叔 己酯和过氧化二碳酸双酯中的一种或几种。
符合上述要求的透气性防渗骨料颗粒可以商购得到， 例如， 北京仁创科技集团有限 公司生产的透气性防水砂， STS-303。
优选情况下， 本发明的方法还可以包括： 在设置透气性防渗骨料层之前， 对盐碱 地进行整平处理。
根据需要， 本发明的方法还可以包括： 在盐碱地上设置透气性防渗骨料层之前， 将盐碱地表层土去除掉。 例如， 当待改良的盐碱地的地势较高时， 可以直接铺设透气性 防渗骨料层； 当待改良的盐碱地的地势较高时， 可以先去除掉一定深度的表层土。 去除 掉的盐碱地表层土的深度可以根据所要种植的植物而在很大范围内改变， 优选情况下， 所述去除掉的盐碱地表层土的深度可以为为 20-100厘米， 更优选为 40-60厘米。
所述透气性防渗骨料层的厚度没有特别的限制， 只要能够防止透气性防渗骨料层 上的种植土层被盐渍化并具有一定的透气性以满足种植土层中的植物生长即可，优选情 况下， 所述透气性防渗骨料层的厚度可以为为 1-10厘米， 更优选为 3-5厘米。
所述种植土层的厚度可以根据所要种植的植物而在很大范围内改变， 优选情况下， 所述种植土层的厚度可以为 20-100厘米， 更优选为 40-60厘米。
本发明还提供了一种盐碱地的种植方法， 其中， 该方法包括： 将植物和 /或植物种 子栽种于改良后的盐碱地中，其中，该改良后的盐碱地是经过本发明提供的方法处理的。
所述栽种植物和 /或植物种子的方法为本领域技术人员所公知， 可以根据所要种植 的物种， 而选择各种常规的农业种植方式。所述植物可以为粮食作物、蔬菜作物、林木、 果树、 观赏植物和草类中的一种或几种， 例如， 可以为大葱、 茄子、 菠菜、 白菜、 萝卜、 辣椒、 圣女果等， 所述植物种子可以为上述植物的繁殖材料。
下面通过以下实施例对本发明进行更加详细的说明。 实施例 1
在花盆 （直径为 40厘米， 高为 90厘米） 内装填盐碱土 （填满）， 以模拟盐碱地。 将盐碱地表层土 （深度为 18厘米） 去除掉， 在去除了表层土的盐碱地上铺设厚度 为 2厘米的透气防水砂 （北京仁创科技集团有限公司， STS-303 ) 形成透气性防渗骨料 层， 在所述透气性防渗骨料层上铺设厚度为 16厘米的种植土层。 实施例 2
在花盆 （直径为 40厘米， 高为 90厘米） 内装填盐碱土 （填满）， 以模拟盐碱地。 将盐碱地表层土（深度为 40厘米）去除掉，将去除表层土后的土层进行平整处理， 在整平后的土层上铺设厚度为 3 厘米的透气防水砂 （北京仁创科技集团有限公司， STS-303 )形成透气性防渗骨料层， 在所述透气性防渗骨料层上铺设厚度为 37厘米的种 植土层。 实施例 3
在花盆 （直径为 40厘米， 高为 90厘米） 内装填盐碱土 （填满）， 以模拟盐碱地。 将盐碱地表层土（深度为 50厘米）去除掉，将去除表层土后的土层进行平整处理， 在整平后的土层上铺设厚度为 4 厘米的透气防水砂 （北京仁创科技集团有限公司， STS-303 )形成透气性防渗骨料层， 在所述透气性防渗骨料层上铺设厚度为 46厘米的种 植土层。 实施例 4
在花盆 （直径为 40厘米， 高为 90厘米） 内装填盐碱土 （装填高度为 45厘米）， 以模拟盐碱地。
在盐碱地上铺设厚度为 8 厘米的透气防水砂 （北京仁创科技集团有限公司，
STS-303 )形成透气性防渗骨料层， 在所述透气性防渗骨料层上铺设厚度为 37厘米的种 植土层。 实施例 5
在花盆 （直径为 40厘米， 高为 90厘米） 内装填盐碱土， 以模拟盐碱地。
将盐碱地表层土（深度为 30厘米）去除掉，将去除表层土后的土层进行平整处理， 在整平后的土层上铺设厚度为 5 厘米的透气防水砂 （北京仁创科技集团有限公司， STS-303 )形成透气性防渗骨料层， 在所述透气性防渗骨料层上铺设厚度为 25厘米的种 植土层。 对比例 1
在花盆 （直径为 40厘米， 高为 90厘米） 内装填盐碱土 （装填高度为 45厘米）， 以模拟盐碱地。
在盐碱地上铺设 45厘米的种植土层。 实施例 6-10
通过 STZ直读式透气性测定仪和柱状有机玻璃管内放水试验， 检测实施例 1-5中 铺设的透气性防渗骨料层的透气度和渗流系数， 结果如表 1所示。
表 1
Figure imgf000008_0001
实施例 15-20
在实施例 1-5中的改良后的盐碱地上移栽大葱，并在与实施例 1-5中添加的种植土 相同的正常的种植土中也移栽同样的植物， 作为对照。
分别在移栽后 1个月、 2个月、 3个月后观察移栽大葱的株高， 结果如表 2所示。 对比例 2
在与实施例 15-20相同的条件下移栽大葱， 不同的是， 使用对比例 1的土壤。 表 2
Figure imgf000008_0002
实施例 21-25
在实施例 1-5中的改良后的盐碱地上播种尖椒种子 （北京縁东方农业技术研究所， 尖椒王牌）， 并在正常的种植土中也播种同样的植物种子， 作为对照。
分别在种植后 1个月、 2个月、 3个月后观察尖椒的株高以及 6个月后单株尖椒上 结尖椒的数量对比， 结果分别见表 3、 表 4所示。
对比例 3
在与实施例 21-25相同的条件下播种尖椒， 不同的是， 使用对比例 1的土壤。 表 3 实施例 实施例 实施例 实施例 实施例 正常种植土 对比例 1 l(cm) 2(cm) 3(cm) 4(cm) 5(cm) (cm) (cm)
1月 4.7 4.8 5 5.1 5.1 5.1 3.2
2月 28 28 28 29 29.2 29 15
3月 49 49 49 50 50 51 18 (叶面有干 枯） 表 4
Figure imgf000009_0001
从表 2、 表 3和表 4中的数据可以看出， 在对比例 1中， 虽然在盐碱地土壤上铺设 了 45厘米的种植土层， 在种植 1个月时植物的生长情况与在正常的栽培土上的生长基 本保持一致， 但是随着时间推移， 2个月和 3个月时的生长效果很差， 尖椒没有结果实。 与此相反， 在经过本发明的方法改良的盐碱土上进行栽培和播种， 植物和种子的生长与 在正常的栽培土上的生长保持一致，说明本发明提供的改良盐碱地的方法和种植方法能 够有效地防止表层种植土层被盐渍化， 从而使种植土层能够长久地适于进行种植， 并且 本发明提供的方法无需大量的淡水资源进行冲洗，从而有效地降低了用水量并扩大了该 方法的使用范围。

Claims

权利要求
1、 一种改良盐碱地的方法， 其中， 该方法包括： 在盐碱地上设置透气性防渗骨料 层， 在所述透气性防渗骨料层上设置种植土层。
2、根据权利要求 1所述的方法，其中，所述透气性防渗骨料层的透气度为 10-100， 渗流系数为 10— 4-10— 7厘米 /秒。
3、 根据权利要求 1或 2所述的方法， 其中， 所述透气性防渗骨料层由透气性防渗 骨料颗粒铺设而成，所述透气性防渗骨料颗粒含有骨料主体和位于骨料主体上的疏水性 树脂膜， 所述骨料主体为石英砂、 矿渣、 陶粒或玻璃微珠中的一种或几种， 所述骨料主 体的平均粒子直径为 20-3500微米。
4、 根据权利要求 3所述的方法， 其中， 以所述透气性防渗骨料颗粒的总重量为基 准， 所述骨料主体的含量为 90-99重量％， 所述疏水性树脂膜的含量为 1-10重量％。
5、 根据权利要求 3所述的方法， 其中， 所述疏水性树脂膜的材料为疏水性环氧树 月旨、 疏水性酚醛树脂、 疏水性聚氨酯树脂以及疏水性硅树脂中的一种或几种， 并且所述 疏水性树脂膜还含有固化剂， 以所述疏水性树脂膜的总重量为基准， 所述固化剂的含量 为 20-25重量％。
6、根据权利要求 1所述的方法，其中，所述透气性防渗骨料层的厚度为 1-10厘米， 所述种植土层的厚度为 15-100厘米。
7、根据权利要求 6所述的方法， 其中， 所述透气性防渗骨料层的厚度为 3-5厘米， 所述种植土层的厚度为 40-60厘米。
8、 根据权利要求 1所述的方法， 其中， 该方法还包括： 在盐碱地上设置透气性防 渗骨料层之前， 将盐碱地表层土去除掉。
9、 根据权利要求 1 所述的方法， 其中， 去除掉的盐碱地表层土的深度为 15-100 厘米。
10、 一种盐碱地的种植方法， 其中， 该方法包括： 将植物和 /或植物种子栽种于改 良后的盐碱地中， 其中， 所述盐碱地的改良方法为权利要求 1-9中的任意一项所述的方 法。
PCT/CN2011/073512 2010-04-30 2011-04-29 一种改良盐碱地的方法及盐碱地的种植方法 WO2011134423A1 (zh)