WO2011087883A1 - Glass-fiber containing composite materials for alkali metal-based batteries and methods of making - Google Patents
Glass-fiber containing composite materials for alkali metal-based batteries and methods of making Download PDFInfo
- Publication number
- WO2011087883A1 WO2011087883A1 PCT/US2010/062399 US2010062399W WO2011087883A1 WO 2011087883 A1 WO2011087883 A1 WO 2011087883A1 US 2010062399 W US2010062399 W US 2010062399W WO 2011087883 A1 WO2011087883 A1 WO 2011087883A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- glass
- substrate
- lithium
- battery
- particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Glass-fiber composites are described that include a substrate containing glass fibers and particles in contact with the glass fiber substrate. The particles may include an alkali-metal containing compound, in addition, batteries are described with an anode, a cathode, and an electrolyte. The cathode may include alkali-metal containing nanoparticles in contact with glass fibers. Also describe are methods of making a glass-fiber composite. The methods may include the steps of forming a wet laid non-woven glass fiber substrate, and contacting alkali-metal containing particles on the substrate.
Description
GLASS-FIBER CONTAINING COMPOSITE MATERIALS FOR ALKALI METAL-BASED BATTERIES AND METHODS OF MAKING BACKGROUND OF THE INVENTION
[0001] Lithium-ion batteries have gained widespread adoption in portable electronic devices, and are increasingly being used in larger-scale systems such as hybrid and electric vehicles and power generation systems. However, attempts to scale lithium-ion battery technology to these larger applications has exposed a number of problems.
[0002] First, the cost of lithium is high compared to conventional nickel, cadmium and lead based battery technologies, and these costs are magnified for larger sized batteries. Thus, there is a need for reducing or eliminating the about of lithium used in the battery. The relatively low proven reserves of lithium in the United States may also limit Li-based battery development and production in that country.
[0003] Second, there are safety concerns with some types of lithium battery technology that may be more prone to explosions and fires when scaled to larger sizes. For example, lithium-based batteries that use lithium-cobalt (LiCo02) cathodes can sometimes experience a release of oxygen during intense and/or frequent electrical charging and discharging cycles. The released oxygen is combustible, and can react with other components in the battery to create a fire or explosion.
[0004] Partly in response to the safety concerns with lithium-cobalt technology, other lithium-based materials have been examined for battery applications. One of these compounds is lithium iron phosphate {LiFeP04}. However, bulk LiFeP04 has proven to have relatively slow mass and charge transport properties, resulting in relatively poor battery power output. Sol-gel processes used to make LiFeP04 materials for batteries are also inefficient and expensive, further increasing the cost of these batteries. Thus, there is a need for new approaches to making Li-based batteries and their components with improved performance and reduced cost. BRIEF SUMMARY OF THE INVENTION
[0005] Materials are described that can improve the performance and reduce the cost of Li-based batteries. These materials include glass-fibers that can be fashioned into a non-woven mat that acts as a substrate for Li-containing nanoparticles. The mat provides strong, dimensionally-stable, a high-surface area scaffold for the nanoparticles, which provides a large surface area of active sites while reducing the amount of lithium left in the bulk. This means less lithium is required for an equivalent energy density, power
density, etc., than used in conventional Li-ion materials. They may also enhance the mass and charge transport properties of Li-based compounds such as LiFePO4.
[0006] Also described are sodium glass fibers that may eliminate the need for lithium altogether in specific battery components such as the cathode electrode. Sodium-based compounds such as sodium iron flourophosphate (Na2FePO4F) have been discovered that have ion transport rates comparable or exceeding Li-based compounds. Some of these sodium-based compounds can be incorporated into sodium glass fibers, which makes the fibers themselves the active material for ion transport and eliminates the need for additional nanoparticies to be added (although there is no prohibition against adding nanoparticies, which in some instances may further enhance the material's performance). These sodium glass fibers may be used to make a lithium free cathode.
[0007] Embodiments of the invention include glass-fiber composites that include a substrate containing glass fibers and particles in contact with the glass fiber substrate. The particles may include an alkali-metal containing compound, such as a iithium- containing compound.
[0008] Embodiments of the invention further include substrates having glass fibers made from sodium-containing materials, such as Na2FePO4F. The glass fibers may be microfibers and/or nanofibers.
[0009] Embodiments of the invention may also include batteries having an anode, a cathode, and an electrolyte. The cathode may include alkali-metal containing
nanoparticies in contact with glass fibers.
[0010] Embodiments of the invention may also further include batteries having a cathode that includes glass microfibers which include Na2FePO4F,
[0011] Embodiments of the invention may still further include methods of making a glass-fiber composite. The methods may include the steps of forming a wet laid non- woven glass fiber substrate, and contacting alkali-metal containing particles on the substrate.
[0012] Additional embodiments and features are set forth in part in the description that follows, and in part will become apparent to those skilled in the art upon examination of the specification or may be learned by the practice of the invention. The features and advantages of the invention may be realized and attained by means of the
instrumentalities, combinations, and methods described in the specification.
DETAILED DESCRIPTION OF THE INVENTION
[0013] Glass fiber composites are described that may be used as electrodes in electrical storage batteries, among other devices and applications. Examples of the
composites include non-woven glass microfibers that provide a durable, dimensionaily stable, microporous substrate for alkali-metal containing nanoparticles, such as lithium and/or sodium-containing nanoparticles. Specific examples of these nanoparticles may include lithium iron phosphate (LiFePO4,) and sodium iron fluorophosphate {Na2FePO 4F} nanoparticles.
[0014] Also described are glass fiber substrates made from glass fibers that incorporate sodium iron fluorophosphates. Making the glass fibers out of Na2FePO4F may obviate the need to introduce nanoparticles to the fibers when forming an electrode. These fibers may have micro- and/or nano-sized diameters that are similar or the same as the scale of the nanoparticles.
[0015] The composites may be made by combining a wet laid non-woven gas-fiber substrate with the nanoparticles. The nanoparticles may be introduced to the substrate by among other methods, coating, embedding, or saturating the nanoparticles in the substrate.
[0018] Both the above-described materials may be formed into a cathode electrode of an electrical storage battery. The cathode may be separated from the anode electrode by an electrolyte. The electrolyte may be, for example, a micro-porous separator membrane that contains LiPF6, and the anode electrode may be a metallic anode such as a lithium metal anode or an alloy of two or more metals.
[0017] Structural cathodes made from the composite materials have increased surface area for holding the nanoparticles, and may be incorporated into larger, more reliable cells having reduced winding costs. The high-surface area glass fiber substrates may include substrates with surface areas ranging from about 20 m2/g to about 300 m2/g or more.
[0018] Increasing the accessible surface area of the cathode can increase the ion mass transfer through the cathode as well as the total energy density of the cathode and battery. The present cathodes may include hierarchically porous structures that combine micro- and nanoscale pores to increase the structural integrity and surface area of the cathode material. Batteries that include the present cathodes may achieve power outputs of 760 W/kg or more, and energy densities of about 100 mAh/g or more. The batteries can also have improved cycle performance with losses of about 3% or less over about 700 cycles.
[0019] The composite materials have high-surface area produced by forming the glass mircofibers and/or nanofibers into strong, durable, non-woven mats. The fiberglass mats may be fashioned into a micro- and/or nanoporous substrate. They may provide improved mechanical and thermal properties, as well as improved dimensional stability
during electrical charging and discharging. This can increase the overall life span of batteries made with these materials. The increased strength of these composite materials also allows more rapid winding of cells and can increase the size of the cells, both of which can lower manufacturing costs of the batteries.
[0020] Batteries made with the present glass fiber materials (either with or without nanoparticles) may have a number of advantages over current lithium-ion battery technology. These advantages may include:
[0021] Specific Energy Density (Wh/kg) - The present batteries can meet or exceed about 200 Wh/kg (system) and about 400 Wh/kg (cell).
[0022] Volumetric Energy Density (Wh/i) - The increased strength provided by the glass fiber substrate allow tighter packing of the battery electrodes and separator. The nanoporous electrodes allow the electrolyte to penetrate into the electrodes, thus creating an efficient utilization of space. Sodium glass (e.g., Na2FePO4F) cathodes may have a lower intrinsic power density than cathodes using lithium-containing nanoparticles, but because active areas of the sodium glass cathodes include the fibers themselves, there is less inactive area for these cathodes.
[0023] System Cost (kWh/$) - For sodium glass cathodes, cost reductions may be realized due to the decreased use of lithium. These cathodes can reduce costs to about US$250/kWh or less. For cathodes that include Li-containing nanoparticles cost reductions of about 20% to about 40% compared to conventional Li-ion batteries may be realized from the reduction in cell windings and increased cell size.
[0024] Specific Power Density (W/kg) - Nanoscale systems can increase power density at high discharge rates owing to their increased ion mass transfer. The present batteries may have power densities of about 760 W/kg and energy density of about 100 mAh/g. The present materials may also be incorporated into system features such as
ultracapacitors that can boost power in pulses.
[0025] Volumetric Power Density (W/l) - Cathodes made from the present materials can have improved high-drain performance. [0026] Cycle Life (#) - Batteries may achieve about 1000 or more cycles. Binding materials and techniques are employed to reduce the unbinding of nanoparticles from the glass-fiber substrate in those embodiments where nanoparticles are used. For sodium- glass cathodes that do not have bound nanoparticles, even larger numbers of cycles may be achieved.
[0027] Round Trip Efficiency - The present batteries may have discharge capacity losses of about 3% or less over 700 cycles at a rate of 1.5C. At C/3, the capacity loss may be significantly lower,
[0028] Temperature Tolerance - The present composites, substrates, cathodes, and batteries may have maximum operating temperatures of about 65 °C or more.
[0029] Self Discharge - The present materials may be optimized to reduce the self discharge rate to what is comparable in conventional Li-ion batteries.
[0030] Safety - The present materials include phosphate containing active electrode materials. Phosphates (-P04) typically have more tightly bound oxygen groups than other conventional electrode materials (e.g., LiCoO2). This reduces the risk of oxygen liberation that can contribute to fires and explosions in the phosphate-containing batteries and systems. The strength and stability of the glass-fiber substrate can also reduce the incidents of short circuits in the battery and other catastrophic failure modes.
[0031] Calendar Life (Years) - The glass fiber substrates do not interfere with battery operation and iron-phosphate systems have significantly lower degradation rates than conventional Li-ion batteries and systems. The present batteries may have an increased lifetime compared to the average lifetime for a conventional system.
[0032] Having described several embodiments, it will be recognized by those of skill in the art that various modifications, alternative constructions, and equivalents may be used without departing from the spirit of the invention. Additionally, a number of well-known processes and elements have not been described in order to avoid unnecessarily obscuring the present invention. Accordingly, the above description should not be taken as limiting the scope of the invention.
[0033] Where a range of values is provided, it is understood that each intervening value, to the tenth of the unit of the lower limit unless the context clearly dictates otherwise, between the upper and lower limits of that range is also specifically disclosed.
Each smaller range between any stated value or intervening value in a stated range and any other stated or intervening value in that stated range is encompassed. The upper and lower limits of these smaller ranges may independently be included or excluded in the range, and each range where either, neither or both limits are included in the smaller ranges is also encompassed within the invention, subject to any specifically excluded limit in the stated range. Where the stated range includes one or both of the limits, ranges excluding either or both of those included limits are also included.
[0034] As used herein and in the appended claims, the singular forms "a", "an", and "the" include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to "a process" includes a plurality of such processes and reference to
"the elecirode" includes reference to one or more electrodes and equivalents thereof known to those skilled in the art, and so forth.
[0035] Also, the words "comprise," "comprising," "include," "including," and "includes" when used in this specification and in the following claims are intended to specify the presence of stated features, integers, components, or steps, but they do not preclude the presence or addition of one or more other features, integers, components, steps, acts, or groups.
Claims
1. A glass-fiber composite comprising:
a substrate comprising glass fibers; and
particles in contact with the substrate, wherein the particles comprise an alkali-metal containing compound.
2. The composite of claim 1 , wherein the non-woven glass fibers comprise non-woven glass microfibers.
3. The composite of claim 1 , wherein the particles comprise nanoparticies.
4. The composite of claim 1 , wherein the particles comprise a lithium- containing compound.
5. The composite of claim 4, wherein the lithium-containing compound is LiFePO4.
6. The composite of claim 1 , wherein the composite comprises a cathode of a battery.
7. A glass fiber substrate comprising glass fibers that include Na2FePO4F.
8. The glass fiber substrate of claim 7, wherein the glass fibers comprise nanofibers.
9. A battery comprising:
an anode;
a cathode comprising lithium-containing nanoparticies in contact with glass fibers; and
an electrolyte between the anode and the cathode.
10. The battery of claim 9, wherein the lithium-containing nanoparticies comprise LiFePO4.
1 1. The battery of claim 9. wherein the anode comprises lithium metal.
12. The battery of claim 9, wherein the electrolyte comprises a microporous separator membrane containing LiPF6.
13. A battery comprising:
an anode;
a cathode that includes glass fibers comprising Na2FePO4F; and an electrode.
14. The battery of claim 13, wherein the glass fibers comprise glass nanofibers.
15. A method οί making a glass-fiber composite, the method comprising the steps of:
forming a wet laid non-woven glass fiber substrate; and contacting alkali-metal containing particles on the substrate.
16. The method of claim 15, wherein the contacting of the alkali-metal containing particles on the substrate comprises coating, embedding, or saturating the substrate with the particles.
17. The method of claim 15, wherein the alkali-metal containing particles comprise lithium-containing nanoparticles.
18. The method of claim 17, wherein the lithium-containing nanoparticles comprise LiFePO4.
19. The method of claim 15, the glass fibers comprise Na2FePO4F.