WO2011070135A1 - Article polyester composite - Google Patents
Article polyester composite Download PDFInfo
- Publication number
- WO2011070135A1 WO2011070135A1 PCT/EP2010/069340 EP2010069340W WO2011070135A1 WO 2011070135 A1 WO2011070135 A1 WO 2011070135A1 EP 2010069340 W EP2010069340 W EP 2010069340W WO 2011070135 A1 WO2011070135 A1 WO 2011070135A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyester
- reinforcing
- semi
- aromatic
- temperature
- Prior art date
Links
- 229920000728 polyester Polymers 0.000 title claims abstract description 75
- 239000002131 composite material Substances 0.000 title claims abstract description 39
- 239000004744 fabric Substances 0.000 claims abstract description 44
- 230000003014 reinforcing effect Effects 0.000 claims abstract description 23
- 238000000034 method Methods 0.000 claims abstract description 22
- 239000000203 mixture Substances 0.000 claims abstract description 20
- 238000004519 manufacturing process Methods 0.000 claims abstract description 17
- 238000002844 melting Methods 0.000 claims abstract description 15
- 230000008018 melting Effects 0.000 claims abstract description 15
- 239000000155 melt Substances 0.000 claims abstract description 7
- 229920001707 polybutylene terephthalate Polymers 0.000 claims description 26
- 229920000139 polyethylene terephthalate Polymers 0.000 claims description 25
- 239000005020 polyethylene terephthalate Substances 0.000 claims description 25
- -1 aromatic diol Chemical class 0.000 claims description 15
- 238000005470 impregnation Methods 0.000 claims description 11
- 238000001816 cooling Methods 0.000 claims description 9
- 239000000835 fiber Substances 0.000 claims description 9
- 230000008569 process Effects 0.000 claims description 9
- 239000000843 powder Substances 0.000 claims description 6
- 239000011521 glass Substances 0.000 claims description 5
- 238000006068 polycondensation reaction Methods 0.000 claims description 5
- 229920002215 polytrimethylene terephthalate Polymers 0.000 claims description 5
- 238000000465 moulding Methods 0.000 claims description 4
- 244000198134 Agave sisalana Species 0.000 claims description 3
- 244000025254 Cannabis sativa Species 0.000 claims description 3
- 235000012766 Cannabis sativa ssp. sativa var. sativa Nutrition 0.000 claims description 3
- 235000012765 Cannabis sativa ssp. sativa var. spontanea Nutrition 0.000 claims description 3
- 240000000491 Corchorus aestuans Species 0.000 claims description 3
- 235000011777 Corchorus aestuans Nutrition 0.000 claims description 3
- 235000010862 Corchorus capsularis Nutrition 0.000 claims description 3
- 240000000797 Hibiscus cannabinus Species 0.000 claims description 3
- 240000006240 Linum usitatissimum Species 0.000 claims description 3
- 235000004431 Linum usitatissimum Nutrition 0.000 claims description 3
- 239000004642 Polyimide Substances 0.000 claims description 3
- 229920003235 aromatic polyamide Polymers 0.000 claims description 3
- 125000003118 aryl group Chemical group 0.000 claims description 3
- 235000009120 camo Nutrition 0.000 claims description 3
- 235000005607 chanvre indien Nutrition 0.000 claims description 3
- 239000011487 hemp Substances 0.000 claims description 3
- 229920006267 polyester film Polymers 0.000 claims description 3
- 229920001721 polyimide Polymers 0.000 claims description 3
- 125000001931 aliphatic group Chemical group 0.000 claims description 2
- 239000011112 polyethylene naphthalate Substances 0.000 claims description 2
- 229920000049 Carbon (fiber) Polymers 0.000 claims 1
- 239000004917 carbon fiber Substances 0.000 claims 1
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 17
- LYCAIKOWRPUZTN-UHFFFAOYSA-N Ethylene glycol Chemical compound OCCO LYCAIKOWRPUZTN-UHFFFAOYSA-N 0.000 description 12
- 230000002787 reinforcement Effects 0.000 description 9
- KKEYFWRCBNTPAC-UHFFFAOYSA-N Terephthalic acid Chemical compound OC(=O)C1=CC=C(C(O)=O)C=C1 KKEYFWRCBNTPAC-UHFFFAOYSA-N 0.000 description 7
- WOZVHXUHUFLZGK-UHFFFAOYSA-N dimethyl terephthalate Chemical compound COC(=O)C1=CC=C(C(=O)OC)C=C1 WOZVHXUHUFLZGK-UHFFFAOYSA-N 0.000 description 7
- 230000007062 hydrolysis Effects 0.000 description 7
- 238000006460 hydrolysis reaction Methods 0.000 description 7
- 229920000642 polymer Polymers 0.000 description 7
- 238000012360 testing method Methods 0.000 description 7
- 230000035882 stress Effects 0.000 description 6
- 239000000654 additive Substances 0.000 description 5
- 239000000463 material Substances 0.000 description 5
- 239000000178 monomer Substances 0.000 description 5
- 150000002009 diols Chemical class 0.000 description 4
- 230000032050 esterification Effects 0.000 description 4
- 238000005886 esterification reaction Methods 0.000 description 4
- 238000006116 polymerization reaction Methods 0.000 description 4
- 229920005989 resin Polymers 0.000 description 4
- 239000011347 resin Substances 0.000 description 4
- 230000006641 stabilisation Effects 0.000 description 4
- 238000011105 stabilization Methods 0.000 description 4
- 239000004952 Polyamide Substances 0.000 description 3
- DNIAPMSPPWPWGF-UHFFFAOYSA-N Propylene glycol Chemical compound CC(O)CO DNIAPMSPPWPWGF-UHFFFAOYSA-N 0.000 description 3
- 230000008901 benefit Effects 0.000 description 3
- 230000015572 biosynthetic process Effects 0.000 description 3
- 150000005690 diesters Chemical class 0.000 description 3
- MTHSVFCYNBDYFN-UHFFFAOYSA-N diethylene glycol Chemical compound OCCOCCO MTHSVFCYNBDYFN-UHFFFAOYSA-N 0.000 description 3
- 229920002647 polyamide Polymers 0.000 description 3
- 238000002360 preparation method Methods 0.000 description 3
- 239000012783 reinforcing fiber Substances 0.000 description 3
- 238000003786 synthesis reaction Methods 0.000 description 3
- 229920001169 thermoplastic Polymers 0.000 description 3
- 229920001187 thermosetting polymer Polymers 0.000 description 3
- 238000005809 transesterification reaction Methods 0.000 description 3
- 102100020895 Ammonium transporter Rh type A Human genes 0.000 description 2
- 101100301844 Arabidopsis thaliana RH50 gene Proteins 0.000 description 2
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 2
- 101150015738 Fev gene Proteins 0.000 description 2
- 102100037681 Protein FEV Human genes 0.000 description 2
- 101150107345 Rhag gene Proteins 0.000 description 2
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 2
- 229910052799 carbon Inorganic materials 0.000 description 2
- 238000012512 characterization method Methods 0.000 description 2
- 238000006243 chemical reaction Methods 0.000 description 2
- 230000000052 comparative effect Effects 0.000 description 2
- 230000003750 conditioning effect Effects 0.000 description 2
- 125000004122 cyclic group Chemical group 0.000 description 2
- 230000007423 decrease Effects 0.000 description 2
- 238000007872 degassing Methods 0.000 description 2
- 238000001035 drying Methods 0.000 description 2
- 239000012765 fibrous filler Substances 0.000 description 2
- 239000012530 fluid Substances 0.000 description 2
- 239000003365 glass fiber Substances 0.000 description 2
- 238000010438 heat treatment Methods 0.000 description 2
- WGCNASOHLSPBMP-UHFFFAOYSA-N hydroxyacetaldehyde Natural products OCC=O WGCNASOHLSPBMP-UHFFFAOYSA-N 0.000 description 2
- QQVIHTHCMHWDBS-UHFFFAOYSA-N isophthalic acid Chemical compound OC(=O)C1=CC=CC(C(O)=O)=C1 QQVIHTHCMHWDBS-UHFFFAOYSA-N 0.000 description 2
- 239000011159 matrix material Substances 0.000 description 2
- 238000005259 measurement Methods 0.000 description 2
- YZPOQCQXOSEMAZ-UHFFFAOYSA-N pbt2 Chemical compound ClC1=CC(Cl)=C(O)C2=NC(CN(C)C)=CC=C21 YZPOQCQXOSEMAZ-UHFFFAOYSA-N 0.000 description 2
- 238000013001 point bending Methods 0.000 description 2
- 239000012763 reinforcing filler Substances 0.000 description 2
- 239000000126 substance Substances 0.000 description 2
- 239000004416 thermosoftening plastic Substances 0.000 description 2
- PUPZLCDOIYMWBV-UHFFFAOYSA-N (+/-)-1,3-Butanediol Chemical compound CC(O)CCO PUPZLCDOIYMWBV-UHFFFAOYSA-N 0.000 description 1
- WSQZNZLOZXSBHA-UHFFFAOYSA-N 3,8-dioxabicyclo[8.2.2]tetradeca-1(12),10,13-triene-2,9-dione Chemical compound O=C1OCCCCOC(=O)C2=CC=C1C=C2 WSQZNZLOZXSBHA-UHFFFAOYSA-N 0.000 description 1
- HSSYVKMJJLDTKZ-UHFFFAOYSA-N 3-phenylphthalic acid Chemical compound OC(=O)C1=CC=CC(C=2C=CC=CC=2)=C1C(O)=O HSSYVKMJJLDTKZ-UHFFFAOYSA-N 0.000 description 1
- BJLUCDZIWWSFIB-UHFFFAOYSA-N 5-tert-butylbenzene-1,3-dicarboxylic acid Chemical compound CC(C)(C)C1=CC(C(O)=O)=CC(C(O)=O)=C1 BJLUCDZIWWSFIB-UHFFFAOYSA-N 0.000 description 1
- 239000005995 Aluminium silicate Substances 0.000 description 1
- 239000005046 Chlorosilane Substances 0.000 description 1
- 229920001634 Copolyester Polymers 0.000 description 1
- LFQSCWFLJHTTHZ-UHFFFAOYSA-N Ethanol Chemical compound CCO LFQSCWFLJHTTHZ-UHFFFAOYSA-N 0.000 description 1
- KLDXJTOLSGUMSJ-JGWLITMVSA-N Isosorbide Chemical compound O[C@@H]1CO[C@@H]2[C@@H](O)CO[C@@H]21 KLDXJTOLSGUMSJ-JGWLITMVSA-N 0.000 description 1
- 239000004698 Polyethylene Substances 0.000 description 1
- 206010063493 Premature ageing Diseases 0.000 description 1
- 208000032038 Premature aging Diseases 0.000 description 1
- 239000012963 UV stabilizer Substances 0.000 description 1
- 208000021017 Weight Gain Diseases 0.000 description 1
- YIMQCDZDWXUDCA-UHFFFAOYSA-N [4-(hydroxymethyl)cyclohexyl]methanol Chemical compound OCC1CCC(CO)CC1 YIMQCDZDWXUDCA-UHFFFAOYSA-N 0.000 description 1
- 239000002253 acid Substances 0.000 description 1
- 238000004026 adhesive bonding Methods 0.000 description 1
- 238000006136 alcoholysis reaction Methods 0.000 description 1
- 235000012211 aluminium silicate Nutrition 0.000 description 1
- 238000007098 aminolysis reaction Methods 0.000 description 1
- 239000003963 antioxidant agent Substances 0.000 description 1
- 238000009954 braiding Methods 0.000 description 1
- 239000003795 chemical substances by application Substances 0.000 description 1
- KOPOQZFJUQMUML-UHFFFAOYSA-N chlorosilane Chemical compound Cl[SiH3] KOPOQZFJUQMUML-UHFFFAOYSA-N 0.000 description 1
- 150000001875 compounds Chemical class 0.000 description 1
- 230000006835 compression Effects 0.000 description 1
- 238000007906 compression Methods 0.000 description 1
- 239000007822 coupling agent Substances 0.000 description 1
- 238000002425 crystallisation Methods 0.000 description 1
- 230000008025 crystallization Effects 0.000 description 1
- 230000032798 delamination Effects 0.000 description 1
- 150000004985 diamines Chemical class 0.000 description 1
- 150000001991 dicarboxylic acids Chemical class 0.000 description 1
- VNGOYPQMJFJDLV-UHFFFAOYSA-N dimethyl benzene-1,3-dicarboxylate Chemical compound COC(=O)C1=CC=CC(C(=O)OC)=C1 VNGOYPQMJFJDLV-UHFFFAOYSA-N 0.000 description 1
- OVPXRLUTUWRYEY-UHFFFAOYSA-N dimethyl naphthalene-1,8-dicarboxylate Chemical class C1=CC(C(=O)OC)=C2C(C(=O)OC)=CC=CC2=C1 OVPXRLUTUWRYEY-UHFFFAOYSA-N 0.000 description 1
- BTVWZWFKMIUSGS-UHFFFAOYSA-N dimethylethyleneglycol Natural products CC(C)(O)CO BTVWZWFKMIUSGS-UHFFFAOYSA-N 0.000 description 1
- 239000012153 distilled water Substances 0.000 description 1
- 230000009977 dual effect Effects 0.000 description 1
- 239000000975 dye Substances 0.000 description 1
- 238000009950 felting Methods 0.000 description 1
- 239000011152 fibreglass Substances 0.000 description 1
- 239000000945 filler Substances 0.000 description 1
- 239000006260 foam Substances 0.000 description 1
- 230000006870 function Effects 0.000 description 1
- 239000008187 granular material Substances 0.000 description 1
- 239000012761 high-performance material Substances 0.000 description 1
- 239000011872 intimate mixture Substances 0.000 description 1
- 229960002479 isosorbide Drugs 0.000 description 1
- NLYAJNPCOHFWQQ-UHFFFAOYSA-N kaolin Chemical compound O.O.O=[Al]O[Si](=O)O[Si](=O)O[Al]=O NLYAJNPCOHFWQQ-UHFFFAOYSA-N 0.000 description 1
- 238000009940 knitting Methods 0.000 description 1
- 239000007788 liquid Substances 0.000 description 1
- 239000000314 lubricant Substances 0.000 description 1
- 238000012423 maintenance Methods 0.000 description 1
- 238000010128 melt processing Methods 0.000 description 1
- 239000002184 metal Substances 0.000 description 1
- 239000010445 mica Substances 0.000 description 1
- 229910052618 mica group Inorganic materials 0.000 description 1
- 238000002156 mixing Methods 0.000 description 1
- 230000004048 modification Effects 0.000 description 1
- 238000012986 modification Methods 0.000 description 1
- 150000002762 monocarboxylic acid derivatives Chemical group 0.000 description 1
- 150000002763 monocarboxylic acids Chemical class 0.000 description 1
- 239000002245 particle Substances 0.000 description 1
- 238000005192 partition Methods 0.000 description 1
- 239000000049 pigment Substances 0.000 description 1
- 239000004014 plasticizer Substances 0.000 description 1
- 229920000573 polyethylene Polymers 0.000 description 1
- 238000012545 processing Methods 0.000 description 1
- 230000002035 prolonged effect Effects 0.000 description 1
- 239000012779 reinforcing material Substances 0.000 description 1
- 230000000717 retained effect Effects 0.000 description 1
- 230000002441 reversible effect Effects 0.000 description 1
- 238000007142 ring opening reaction Methods 0.000 description 1
- 238000007493 shaping process Methods 0.000 description 1
- 230000035939 shock Effects 0.000 description 1
- FZHAPNGMFPVSLP-UHFFFAOYSA-N silanamine Chemical compound [SiH3]N FZHAPNGMFPVSLP-UHFFFAOYSA-N 0.000 description 1
- 239000000377 silicon dioxide Substances 0.000 description 1
- 238000002791 soaking Methods 0.000 description 1
- 238000007711 solidification Methods 0.000 description 1
- 230000008023 solidification Effects 0.000 description 1
- 239000002904 solvent Substances 0.000 description 1
- 238000003860 storage Methods 0.000 description 1
- 238000001308 synthesis method Methods 0.000 description 1
- 239000000454 talc Substances 0.000 description 1
- 229910052623 talc Inorganic materials 0.000 description 1
- 239000004753 textile Substances 0.000 description 1
- 239000003017 thermal stabilizer Substances 0.000 description 1
- 238000012546 transfer Methods 0.000 description 1
- 238000001721 transfer moulding Methods 0.000 description 1
- 230000009466 transformation Effects 0.000 description 1
- 238000009941 weaving Methods 0.000 description 1
- 230000004584 weight gain Effects 0.000 description 1
- 235000019786 weight gain Nutrition 0.000 description 1
- 239000000080 wetting agent Substances 0.000 description 1
- 239000010456 wollastonite Substances 0.000 description 1
- 229910052882 wollastonite Inorganic materials 0.000 description 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
- B29B17/00—Recovery of plastics or other constituents of waste material containing plastics
- B29B17/04—Disintegrating plastics, e.g. by milling
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C43/00—Compression moulding, i.e. applying external pressure to flow the moulding material; Apparatus therefor
- B29C43/003—Compression moulding, i.e. applying external pressure to flow the moulding material; Apparatus therefor characterised by the choice of material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
- B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
- B29C70/28—Shaping operations therefor
- B29C70/40—Shaping or impregnating by compression not applied
- B29C70/42—Shaping or impregnating by compression not applied for producing articles of definite length, i.e. discrete articles
- B29C70/46—Shaping or impregnating by compression not applied for producing articles of definite length, i.e. discrete articles using matched moulds, e.g. for deforming sheet moulding compounds [SMC] or prepregs
- B29C70/465—Shaping or impregnating by compression not applied for producing articles of definite length, i.e. discrete articles using matched moulds, e.g. for deforming sheet moulding compounds [SMC] or prepregs and impregnating by melting a solid material, e.g. sheets, powders of fibres
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
- B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
- B29C70/28—Shaping operations therefor
- B29C70/40—Shaping or impregnating by compression not applied
- B29C70/42—Shaping or impregnating by compression not applied for producing articles of definite length, i.e. discrete articles
- B29C70/46—Shaping or impregnating by compression not applied for producing articles of definite length, i.e. discrete articles using matched moulds, e.g. for deforming sheet moulding compounds [SMC] or prepregs
- B29C70/48—Shaping or impregnating by compression not applied for producing articles of definite length, i.e. discrete articles using matched moulds, e.g. for deforming sheet moulding compounds [SMC] or prepregs and impregnating the reinforcements in the closed mould, e.g. resin transfer moulding [RTM], e.g. by vacuum
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
- C08J5/04—Reinforcing macromolecular compounds with loose or coherent fibrous material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C45/00—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor
- B29C45/14—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor incorporating preformed parts or layers, e.g. injection moulding around inserts or for coating articles
- B29C45/14778—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor incorporating preformed parts or layers, e.g. injection moulding around inserts or for coating articles the article consisting of a material with particular properties, e.g. porous, brittle
- B29C45/14786—Fibrous material or fibre containing material, e.g. fibre mats or fibre reinforced material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2067/00—Use of polyesters or derivatives thereof, as moulding material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
- B29K2105/06—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts
- B29K2105/08—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts of continuous length, e.g. cords, rovings, mats, fabrics, strands or yarns
- B29K2105/0809—Fabrics
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2367/00—Characterised by the use of polyesters obtained by reactions forming a carboxylic ester link in the main chain; Derivatives of such polymers
- C08J2367/02—Polyesters derived from dicarboxylic acids and dihydroxy compounds
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02W—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO WASTEWATER TREATMENT OR WASTE MANAGEMENT
- Y02W30/00—Technologies for solid waste management
- Y02W30/50—Reuse, recycling or recovery technologies
- Y02W30/62—Plastics recycling; Rubber recycling
Definitions
- the impregnation of the fabric by the polyester composition being carried out either:
- Polyesters according to the invention can also be obtained by mixing, in particular melt, polyesters with chain length-changing monomers, such as especially diols, dicarboxylic acids, monoalcohol and / or mono carboxylic acids or with water. , diamines or monoamines.
- composition of the invention may also comprise the copolyesters derived in particular from the above polyesters, or mixtures of these polyesters or (co) polyesters.
- Reinforcing fillers may be incorporated into the semiaromatic polyester composition. These fillers may be chosen from fibrous fillers, such as short glass fibers, for example, or non-fibrous fillers such as kaolin, talc, silica, mica or wollastonite. Their size is generally between 1 and 50 ⁇ . Sub-micron or even nanometric charges may also be used, alone or in addition to other charges.
- Polymers of different viscosities were prepared by controlled hydrolysis. After measuring the water content of the products as received, a very small amount of distilled water was added to achieve the target water levels: 1000 ppm, 2000 ppm, and 3000 ppm. The products were then stored in sealed bottles, and heated at 50 ° C. for 12 hours, then mixed to homogenize the assembly. A measurement of the water content is then carried out by thermo-manometry at 200 ° C. in order to verify that the level attained is the target level (PET 2: 920 ppm, PET 3: 1990 ppm, PET 4: 2710 ppm; PBT 2: 1020 ppm, PBT 3: 1990 ppm, PBT 4: 2800 ppm).
- the 3-point bending tests at room temperature are carried out on parallelepiped test pieces (150x20x2 mm), according to ISO standard No. 14125, on a ZWICK 1478 machine: 64 mm center distance, 5 mm / min crosshead speed. Young's elastic modulus E (GPa) and maximum stress ⁇ max (MPa) values are measured and calculated.
Landscapes
- Engineering & Computer Science (AREA)
- Chemical & Material Sciences (AREA)
- Mechanical Engineering (AREA)
- Composite Materials (AREA)
- Health & Medical Sciences (AREA)
- Materials Engineering (AREA)
- Manufacturing & Machinery (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Environmental & Geological Engineering (AREA)
- Reinforced Plastic Materials (AREA)
- Compositions Of Macromolecular Compounds (AREA)
Priority Applications (3)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| CN201080056372.6A CN102656005B (zh) | 2009-12-11 | 2010-12-10 | 复合材料聚酯制品 |
| US13/514,928 US9283694B2 (en) | 2009-12-11 | 2010-12-10 | Composite polyester article |
| EP20100790765 EP2509776B1 (fr) | 2009-12-11 | 2010-12-10 | Procédé de fabrication d'un article polyester composite |
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| FR0958872 | 2009-12-11 | ||
| FR0958872A FR2953846B1 (fr) | 2009-12-11 | 2009-12-11 | Article polyester composite |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| WO2011070135A1 true WO2011070135A1 (fr) | 2011-06-16 |
Family
ID=42309661
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| PCT/EP2010/069340 WO2011070135A1 (fr) | 2009-12-11 | 2010-12-10 | Article polyester composite |
Country Status (5)
| Country | Link |
|---|---|
| US (1) | US9283694B2 (zh) |
| EP (1) | EP2509776B1 (zh) |
| CN (1) | CN102656005B (zh) |
| FR (1) | FR2953846B1 (zh) |
| WO (1) | WO2011070135A1 (zh) |
Families Citing this family (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| KR102337396B1 (ko) * | 2017-05-18 | 2021-12-10 | 도레이 카부시키가이샤 | 복합 시트상물 |
| EP3569645A1 (en) * | 2018-05-18 | 2019-11-20 | SABIC Global Technologies B.V. | Reinforced dynamically crosslinked polyester network |
| US20230002570A1 (en) * | 2019-12-05 | 2023-01-05 | Dsm Ip Assets B.V. | Compression limiter |
Citations (6)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US5019450A (en) * | 1981-01-21 | 1991-05-28 | Imperial Chemical Industries Plc | Fiber reinforced compositions and method of producing such compositions |
| GB2313312A (en) * | 1996-05-02 | 1997-11-26 | British United Shoe Machinery | Orthopeadic splint board |
| DE102005057181A1 (de) * | 2005-11-29 | 2007-06-06 | Lanxess Deutschland Gmbh | Verbinden von faserverstärktem Material mit einem Spritzgussmaterial |
| EP1892072A1 (en) * | 2006-08-22 | 2008-02-27 | HONDA MOTOR CO., Ltd. | Recycling fibres reinforced plastics (FRP) in injection moulding process |
| EP1990369A1 (en) * | 2006-02-27 | 2008-11-12 | Asahi Kasei Chemicals Corporation | Glass-fiber-reinforced thermoplastic resin composition and molded article |
| US20090246468A1 (en) * | 2008-03-30 | 2009-10-01 | Iq Tec Switzerland Gmbh | Apparatus and method for making reactive polymer pre-pregs |
Family Cites Families (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| EP1880833A1 (en) * | 2006-07-19 | 2008-01-23 | National University of Ireland, Galway | Composite articles comprising in-situ-polymerisable thermoplastic material and processes for their construction |
-
2009
- 2009-12-11 FR FR0958872A patent/FR2953846B1/fr not_active Expired - Fee Related
-
2010
- 2010-12-10 EP EP20100790765 patent/EP2509776B1/fr not_active Not-in-force
- 2010-12-10 CN CN201080056372.6A patent/CN102656005B/zh not_active Expired - Fee Related
- 2010-12-10 WO PCT/EP2010/069340 patent/WO2011070135A1/fr active Application Filing
- 2010-12-10 US US13/514,928 patent/US9283694B2/en not_active Expired - Fee Related
Patent Citations (7)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US5019450A (en) * | 1981-01-21 | 1991-05-28 | Imperial Chemical Industries Plc | Fiber reinforced compositions and method of producing such compositions |
| US5019450B1 (en) * | 1981-01-21 | 1996-10-29 | Kawasaki Chem Holding | Fibre reinforced compositions and methods for producing such compositions |
| GB2313312A (en) * | 1996-05-02 | 1997-11-26 | British United Shoe Machinery | Orthopeadic splint board |
| DE102005057181A1 (de) * | 2005-11-29 | 2007-06-06 | Lanxess Deutschland Gmbh | Verbinden von faserverstärktem Material mit einem Spritzgussmaterial |
| EP1990369A1 (en) * | 2006-02-27 | 2008-11-12 | Asahi Kasei Chemicals Corporation | Glass-fiber-reinforced thermoplastic resin composition and molded article |
| EP1892072A1 (en) * | 2006-08-22 | 2008-02-27 | HONDA MOTOR CO., Ltd. | Recycling fibres reinforced plastics (FRP) in injection moulding process |
| US20090246468A1 (en) * | 2008-03-30 | 2009-10-01 | Iq Tec Switzerland Gmbh | Apparatus and method for making reactive polymer pre-pregs |
Also Published As
| Publication number | Publication date |
|---|---|
| CN102656005A (zh) | 2012-09-05 |
| US9283694B2 (en) | 2016-03-15 |
| FR2953846B1 (fr) | 2012-03-02 |
| EP2509776B1 (fr) | 2014-03-05 |
| CN102656005B (zh) | 2015-03-25 |
| US20130001822A1 (en) | 2013-01-03 |
| FR2953846A1 (fr) | 2011-06-17 |
| EP2509776A1 (fr) | 2012-10-17 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| CA2852997C (fr) | Materiau composite thermoplastique renforce de fibres synthetiques et procede de fabrication | |
| EP2155474B1 (fr) | Article polyamide composite | |
| EP2326487B1 (fr) | Article polyamide composite | |
| FR2947823A1 (fr) | Article polyamide composite | |
| FR2947822A1 (fr) | Article polyamide composite | |
| EP2571925A1 (fr) | Article polyamide composite | |
| EP2513203B1 (fr) | Article composite a base de resines polyamides de faibles masses moleculaires | |
| CN107109054B (zh) | 具有改进的流动性的聚酰胺混合物 | |
| EP2509776B1 (fr) | Procédé de fabrication d'un article polyester composite | |
| EP3237182B1 (fr) | Procede de fabrication continu d'un profile en materiau composite a base de polymere thermoplastique a haute fluidite | |
| EP3237544B1 (fr) | Composition thermoplastique a haute fluidite | |
| CN117757232A (zh) | 一种聚酯合金材料及其制备方法与应用 |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| WWE | Wipo information: entry into national phase |
Ref document number: 201080056372.6 Country of ref document: CN |
|
| 121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 10790765 Country of ref document: EP Kind code of ref document: A1 |
|
| 121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 10790765 Country of ref document: EP Kind code of ref document: A1 |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 2010790765 Country of ref document: EP |
|
| NENP | Non-entry into the national phase |
Ref country code: DE |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 13514928 Country of ref document: US |