WO2011038615A1 - 一体式陶瓷金卤灯电弧管的制造方法 - Google Patents

一体式陶瓷金卤灯电弧管的制造方法 Download PDF

Info

Publication number
WO2011038615A1
WO2011038615A1 PCT/CN2010/075455 CN2010075455W WO2011038615A1 WO 2011038615 A1 WO2011038615 A1 WO 2011038615A1 CN 2010075455 W CN2010075455 W CN 2010075455W WO 2011038615 A1 WO2011038615 A1 WO 2011038615A1
Authority
WO
WIPO (PCT)
Prior art keywords
arc tube
metal halide
blank
manufacturing
halide lamp
Prior art date
Application number
PCT/CN2010/075455
Other languages
English (en)
French (fr)
Inventor
邓湘凌
Original Assignee
Deng Xiangling
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Deng Xiangling filed Critical Deng Xiangling
Publication of WO2011038615A1 publication Critical patent/WO2011038615A1/zh

Description

一体式陶瓷金卤灯电弧管的制造方法 技术领域
本发明涉及电光源技术领域， 尤其涉及一种一体化多晶半透明氧化铝 陶瓷金属卤素灯（金卤灯） 电弧管的制造方法。 背景技术
由于陶瓷材料具有耐酸碱、 耐高温、 化学稳定性的特点， 用其制成的 金卤灯电弧管比用石英制成的金卤灯电弧管， 具有工作温度高、 光效高、 显色性好、 体积小、 寿命长等优点， 因此， 陶瓷金 灯近年来得到较大的 发展， 在照明领域中广泛推广， 是人类照明发展的方向。
目前， 陶瓷金卤灯电弧管主要采用半透明的多晶氧化铝陶瓷制造， 实 践证明， 一体式厚度均匀体积小的半透明多晶氧化铝陶瓷电弧管结构最为 完善。 中 国 专利 ZL97117991.3 , ZL00122245.7 , ZL03131897.5 , ZL200610035124.9, ZL200610232512.9公开的陶瓷金卤灯电弧管的制造方 法， 主要是 2件式， 3件式， 5件式等组合制成的陶瓷管， 由于厚度不均 匀， 容易在电弧管冷端处聚集高温的液态金属卤化物， 对电弧管的腐蚀性 很大， 导致灯的光衰与失效， 造成温度分布不均匀， 应力集中， 产生断 裂。 此外， 又由于几个部分粘接烧结在一起， 无法保证尺寸精度， 同心度 差， 连接重叠部分容易破碎， 生产效率低。
目前制造一体式陶瓷电弧管的技术途径有两种： 一是用可挥发的材料 做内芯， 然后用注浆、 注射等静压法制成陶瓷坯体， 再通过加热氧化的方 法去除内芯材料， 得到中空的陶瓷坯体， 如公开的发明专利 CN1251330A 和 CN1489558A所述。 这种方法的缺点是内芯材料的去除过程緩慢且要求 严格， 稍有炭质残留， 即会造成废品， 因此内芯的制造成本 4艮高， 且挥发 性材料也会造成环境污染。 另一种方法如美国专利 US6620272B2 所述： 先制造出两半轴线方向对称的空心坯体， 再用局部加热的方法将对接面的 粘合剂融化， 加压力粘接成一整体， 这种方法工艺比较复杂， 很难确保粘 接牢固。 发明内容
本发明的目的在于， 提供一种一体式陶瓷金卤灯电弧管的制造方法， 其工艺筒单， 生产效率高， 成品率高， 降低生产成本。 本发明的又一目的在于， 提供一种一体式陶瓷金卤灯电弧管的制造方 法， 其工艺筒单， 减少环境污染。
本发明的另一目的在于， 提供一种一体式陶瓷金卤灯电弧管的制造方 法， 其制得的产品尺寸精度高， 使用寿命长。
本发明提供的一种一体式陶瓷金卤灯电弧管的制造方法， 包括如下步 骤：
步骤 1 , 调制原料成浆料；
步骤 2, 制作毛坯管， 用模具将已调制好的浆料采用挤压成型方式或 注塑成型方式制得毛坯管；
步骤 3 , 制作坯体， 将毛坯管放入电弧管模具中， 采用热液压方式制 成一个圓滑过渡的一体式电弧管坯体；
步骤 4, 将坯体脱脂、 排塑；
步骤 5, 预烧结， 预烧温度控制在 1200°C-1400°C之间；
步骤 6, 氢气烧结， 氢气烧结的温度控制在 1850°C-1950°C之间； 步骤 7 , 冷却， 制得一体式陶瓷金卤灯电弧管。
所述原料的组成及含量如下， 按重量份计： 石蜡 11 - 17 份； 微晶蜡 11 - 17份； 硬脂蜡 1 - 3份； 塑胶 65 - 75份； 高纯氧化铝 500 - 1000份。
所述塑胶选用 PE、 PP、 HIPS, PET其中的一种或其组合， 高纯氧化 铝为 99.99%纯度的平均粒径为 0.5um的氧化铝粉末。
所述步骤 2 中， 毛坯管内径为圓形， 且该毛坯管的中部 5mm范围内 较管外径有 1.2倍的凸起。
所述步骤 3 中， 液体的温度为 150 °C - 200 °C , 压力为 O.OlMPa - 0.03MPa, 坯体在压力的作用下， 按电弧管模具的形状、 尺寸， 形成中空 电弧管坯体， 经冷却硬化后， 打开电弧管模具取出一体化金 灯电弧管坯 体。
所述电弧管模具的形状尺寸按陶瓷电弧管的形状尺寸设计， 该电弧管 模具上下开模合模、 左右密封， 局部可控制温度。
所述一体化金 灯电弧管坯体中部为球形或橢球形。
所述预烧结在氧气炉中烧结。
所述步骤 6中， 经过氢气烧结后， 坯体变为半透明。
本发明的有益效果： 本发明与现有技术相比， 不使用挥发性材料做内 芯， 降低了成本， 且避免了对环境的污染； 该发明的一体化陶瓷金 灯电 弧管无联接缝， 电弧管壳体厚度均匀、 圓滑， 无应力集中， 不易断裂； 该 一体式陶瓷金卤灯电弧管的制造方法， 其根据功率不同可方便的制作成各 种形状、 尺寸的电弧壳， 且该发明的制作工艺筒单可靠， 降低了生产成 本、 成品率高， 有利于工业化大批量生产。
为了能更进一步了解本发明的特征以及技术内容， 请参阅以下有关本 发明的详细说明与附图， 然而附图仅提供参考与说明用， 并非用来对本发 明加以限制。 附图说明
下面结合附图， 通过对本发明的具体实施方式详细描述， 将使本发明 的技术方案及其它有益效果显而易见。
附图中，
图 1为本发明一体式陶瓷金卤灯电弧管的制造方法流程图；
图 2为本发明方法中注射成型的毛坯管剖面示意图；
图 3为本发明方法中一体化金卤灯电弧管坯体剖面示意图。 具体实施方式 参阅以下有关本发明的详细说月与附图， 相^ ^本发明的目的、 特征与特 点， 应当可由此得到深入且具体的了解， 然而附图仅提供参考与说明用， 并非用来对本发明加以限制。
如图 1所示， 本发明一体式陶瓷金卤灯电弧管的制造方法， 包括： 步骤 1 , 调制原料成浆料， 该原料的组成及含量 （按重量份计） 如 下： 石蜡 11 - 17 份； 微晶蜡 11 - 17份； 硬脂蜡 1 - 3 份； 塑胶 65 - 75 份； 高纯氧化铝 500 - 1000份。 塑胶选用 PE、 PP、 HIPS, PET其中的一 种或其组合。 该高纯氧化铝为 99.99%纯度的平均粒径为 0.5um的氧化铝粉 末。
步骤 2, 制作毛坯管， 用模具将已调制好的浆料采用挤压成型方式或 注塑成型方式制得毛坯管 （图 2所示） ， 其内径为圓形， 且该毛坯管的中 部 5mm范围内较管外径有 1.2倍的凸起。
步骤 3 , 制作坯体， 将毛坯管放入电弧管模具中， 采用热液压方式制 成一个圓滑过渡的一体式电弧管坯体（图 3 所示） 。 此电弧管模具的形状 尺寸按陶瓷电弧管的形状尺寸设计； 液体的温度为 150°C _ 200°C , 压力为 O.OlMPa - 0.03MPa, 坯体在压力的作用下， 按电弧管模具的形状、 尺寸， 形成中空电弧管坯体， 经冷却硬化， 达到一定的机械强度， 打开电弧管模 具取出一体化金 灯电弧管坯体。 该一体化金 灯电弧管坯体中部可为球 形或橢球形。 作为一种选择性实施例， 所述电弧管模具上下开模合模、 左 右密封， 局部可控制温度。
步骤 4, 将坯体脱脂、 排塑， 加热坯体到 500°C , 其中坯体在温度达 到 100 °C之前脱脂， 在温度达到 200 °C之后排塑， 从而实现分阶段排气， 避免坯体中产生气泡。
步骤 5 , 预烧结， 预烧温度控制在 1200°C-1400°C之间， 其可在氧气炉 中烧结。
步骤 6, 氢气烧结， 氢气烧结的温度控制在 1850°C-1950°C之间， 经过 氢气烧结， 使得坯体变成半透明。
步骤 7 , 冷却， 制得一体式陶瓷金卤灯电弧管。
本发明制得的一体式陶瓷金卤灯电弧管， 其中部可为球形、 或橢球形 等， 两端为圓柱形细管， 该电弧管中空， 其壁厚均匀， 该壁厚在 0.5mm- 1.8mm 之间， 无接缝， 表面圓滑， 无应力集中， 不易断裂， 密度为 3.99g/cm3 , 平均晶粒尺寸为 20微米， 抗弯强度为 370MPa, 直线透光率为 30-40%。
综上所述， 本发明与现有技术相比， 不使用挥发性材料做内芯， 降低 了成本， 且避免了对环境的污染； 该发明的一体化陶瓷金 灯电弧管无联 接缝， 电弧管壳体厚度均匀、 圓滑， 无应力集中， 不易断裂； 该一体式陶 瓷金卤灯电弧管的制造方法， 其根据功率不同可方便的制作成各种形状、 尺寸的电弧壳， 且该发明的制作工艺筒单可靠， 降低了生产成本、 成品率 高， 有利于工业化大批量生产。
以上所述， 仅为本发明的较佳实施例， 对于本领域的普通技术人员来 说， 可以根据本发明的技术方案和技术构思作出其他各种相应的改变和变 形， 而所有这些改变和变形都应属于本发明权利要求的保护范围。

Claims

权 利 要 求
1、 一种一体式陶瓷金卤灯电弧管的制造方法， 包括如下步骤： 步骤 1 , 调制原料成浆料；
步骤 2, 制作毛坯管， 用模具将已调制好的浆料采用挤压成型方式或 注塑成型方式制得毛坯管；
步骤 3 , 制作坯体， 将毛坯管放入电弧管模具中， 采用热液压方式制 成一个圓滑过渡的一体式电弧管坯体；
步骤 4, 将坯体脱脂、 排塑；
步骤 5, 预烧结， 预烧温度控制在 1200°C-1400°C之间；
步骤 6, 氢气烧结， 氢气烧结的温度控制在 1850°C-1950°C之间； 步骤 7, 冷却， 制得一体式陶瓷金 灯电弧管。
2、 如权利要求 1 所述的一体式陶瓷金卤灯电弧管的制造方法， 其 中， 所述原料的组成及含量如下， 按重量份计： 石蜡 11 - 17 份； 微晶蜡 11 - 17份； 硬脂蜡 1 - 3份； 塑胶 65 - 75份； 高纯氧化铝 500 - 1000份。
3、 如权利要求 2 所述的一体式陶瓷金卤灯电弧管的制造方法， 其 中， 所述塑胶选用 PE、 PP、 HIPS, PET其中的一种或其组合， 高纯氧化 铝为 99.99%纯度的平均粒径为 0.5um的氧化铝粉末。
4、 如权利要求 1 所述的一体式陶瓷金卤灯电弧管的制造方法， 其 中， 所述步骤 2 中， 毛坯管内径为圓形， 且该毛坯管的中部 5mm范围内 较管外径有 1.2倍的凸起。
5、 如权利要求 1 所述的一体式陶瓷金卤灯电弧管的制造方法， 其 中， 所述步骤 3 中， 液体的温度为 150 °C - 200 °C , 压力为 O.OlMPa - 0.03MPa, 坯体在压力的作用下， 按电弧管模具的形状、 尺寸， 形成中空 电弧管坯体， 经冷却硬化后， 打开电弧管模具取出一体化金 灯电弧管坯 体。
6、 如权利要求 5 所述的一体式陶瓷金卤灯电弧管的制造方法， 其 中， 所述电弧管模具的形状尺寸按陶瓷电弧管的形状尺寸设计， 该电弧管 模具上下开模合模、 左右密封， 局部可控制温度。
7、 如权利要求 5 所述的一体式陶瓷金卤灯电弧管的制造方法， 其 中， 所述一体化金 灯电弧管坯体中部为球形或橢球形。
8、 如权利要求 1 所述的一体式陶瓷金卤灯电弧管的制造方法， 其 中， 所述预烧结在氧气炉中烧结。
9、 如权利要求 i 所述的一体式陶瓷金 灯电弧管的制造方法， 且 所述步骤 6中， 经过氢气烧结后， 坯体变为半透明。
PCT/CN2010/075455 2009-09-29 2010-07-26 一体式陶瓷金卤灯电弧管的制造方法 WO2011038615A1 (zh)