WO2011006942A1 - Procédé et appareil pour la fabrication d'un stratifié comprenant un film orienté et à ondulation fine et produits résultants - Google Patents

Procédé et appareil pour la fabrication d'un stratifié comprenant un film orienté et à ondulation fine et produits résultants Download PDF

Info

Publication number
WO2011006942A1
WO2011006942A1 PCT/EP2010/060168 EP2010060168W WO2011006942A1 WO 2011006942 A1 WO2011006942 A1 WO 2011006942A1 EP 2010060168 W EP2010060168 W EP 2010060168W WO 2011006942 A1 WO2011006942 A1 WO 2011006942A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
nip
orientation
rollers
angle
Prior art date
Application number
PCT/EP2010/060168
Other languages
English (en)
Inventor
Ole-Bendt Rasmussen
Nikolaj Rasmussen
Original Assignee
Ole-Bendt Rasmussen
Nikolaj Rasmussen
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ole-Bendt Rasmussen, Nikolaj Rasmussen filed Critical Ole-Bendt Rasmussen
Priority to AU2010272530A priority Critical patent/AU2010272530A1/en
Priority to EP10743063A priority patent/EP2454079A1/fr
Priority to CN2010800378655A priority patent/CN102548733A/zh
Priority to JP2012520030A priority patent/JP2012533444A/ja
Publication of WO2011006942A1 publication Critical patent/WO2011006942A1/fr

Abstract

L'invention porte sur un procédé de fabrication d'un stratifié d'un film orienté et ondulé (A) et d'un film ou bande (B), au moins le film (A) étant constitué par un matériau polymère cristallin apte à être orienté, le film (A) étant étiré sous une configuration angulaire en étant saisi par un pincement linéaire (D-F) formé entre des rouleaux ou des barres, tout en étant transporté vers ce pincement dans une direction qui forme un angle aigu (u) avec un plan perpendiculaire au pincement linéaire, et en étant ensuite tiré par des moyens de traction (1 et 2) sous un angle aigu (v) par rapport audit plan perpendiculaire, mesuré sur le côté opposé de ce plan, (v) étant supérieur à (u), mais inférieur à 85°, de façon à produire ainsi un allongement et une orientation moléculaire uniaxiale, le rapport d'étirement (GD à FE) et les angles (u) et (v) étant sélectionnés de telle sorte que l'angle d'orientation du film étiré (A) s'écarte de moins de 15° par rapport à sa direction longitudinale, et qu'une réduction de largeur de film est établie, laquelle, mesurée en ligne directe est supérieure à la réduction de largeur provoquée par l'allongement longitudinal, de façon à former une ondulation s'étendant longitudinalement, et ladite ondulation étant stabilisée avant la rencontre des moyens de traction (1 et 2), et le film (B) étant stratifié sur le film (A) après que le film (A) a quitté le pincement (D-F), tout en maintenant les cannelures de (A). De façon appropriée, les films sont formés en polyéthylène.
PCT/EP2010/060168 2009-07-17 2010-07-14 Procédé et appareil pour la fabrication d'un stratifié comprenant un film orienté et à ondulation fine et produits résultants WO2011006942A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
AU2010272530A AU2010272530A1 (en) 2009-07-17 2010-07-14 Method of and apparatus for manufacture of a laminate comprising an oriented and fine-waved film, and resultant products
EP10743063A EP2454079A1 (fr) 2009-07-17 2010-07-14 Procédé et appareil pour la fabrication d'un stratifié comprenant un film orienté et à ondulation fine et produits résultants
CN2010800378655A CN102548733A (zh) 2009-07-17 2010-07-14 制造包括定向的细微波纹薄膜的层合体的方法与设备及生成的产品
JP2012520030A JP2012533444A (ja) 2009-07-17 2010-07-14 配向されかつ微細な波形が設けられたフィルムを含んでなる積層体を製造する方法及び装置及び結果として得られる製品

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GBGB0912449.6A GB0912449D0 (en) 2009-07-17 2009-07-17 Method of an apparatus for manufacture of a laminate comprising an oriented and fine-waved film, and resultant products
GB0912449.6 2009-07-17

Publications (1)

Publication Number Publication Date
WO2011006942A1 true WO2011006942A1 (fr) 2011-01-20

Family

ID=41058121

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2010/060168 WO2011006942A1 (fr) 2009-07-17 2010-07-14 Procédé et appareil pour la fabrication d'un stratifié comprenant un film orienté et à ondulation fine et produits résultants

Country Status (7)

Country Link
EP (1) EP2454079A1 (fr)
JP (1) JP2012533444A (fr)
CN (1) CN102548733A (fr)
AU (1) AU2010272530A1 (fr)
GB (1) GB0912449D0 (fr)
TW (1) TW201107118A (fr)
WO (1) WO2011006942A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109910371A (zh) * 2019-04-09 2019-06-21 徐自立 Pe膜热封制袋机的热封装置

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2022107944A (ja) * 2021-01-12 2022-07-25 コニカミノルタ株式会社 斜め延伸フィルムの製造方法

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2505146A (en) 1946-12-14 1950-04-25 Polaroid Corp Process and apparatus for stretching continuous sheet materials
GB1078732A (en) 1963-08-08 1967-08-09 Rasmussen O B Method of and apparatus for stretching a material in the form of a film or band
US3491185A (en) * 1965-05-05 1970-01-20 Rasmussen O B Method and apparatus for orienting films made from thermoplastic polymers
US3491158A (en) 1965-11-26 1970-01-20 Huels Chemische Werke Ag Process for the preparation of saturated aliphatic alcohols
US5361469A (en) 1988-06-24 1994-11-08 Rasmussen O B Apparatus for helical cutting of a flexible tubular sheet of polymeric material
US6139938A (en) 1999-02-22 2000-10-31 Innovative Packaging Corp. High flute density, printable, corrugated paperboard
WO2002102592A1 (fr) 2001-06-15 2002-12-27 Ole-Bendt Rasmussen Complexe de films obtenu par lamination et procedes et appareil permettant sa fabrication
WO2004054793A1 (fr) 2002-12-13 2004-07-01 Ole-Bendt Rasmussen Stratifies de feuilles presentant une resistance amelioree a la flexion dans toutes les directions et procedes et dispositifs permettant de les produire

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB8815083D0 (en) * 1988-06-24 1988-08-03 Rasmussen O B Method & apparatus for helical cutting of lay-flat flexible tubular sheet of polymer material

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2505146A (en) 1946-12-14 1950-04-25 Polaroid Corp Process and apparatus for stretching continuous sheet materials
GB1078732A (en) 1963-08-08 1967-08-09 Rasmussen O B Method of and apparatus for stretching a material in the form of a film or band
US3491185A (en) * 1965-05-05 1970-01-20 Rasmussen O B Method and apparatus for orienting films made from thermoplastic polymers
US3491158A (en) 1965-11-26 1970-01-20 Huels Chemische Werke Ag Process for the preparation of saturated aliphatic alcohols
US5361469A (en) 1988-06-24 1994-11-08 Rasmussen O B Apparatus for helical cutting of a flexible tubular sheet of polymeric material
US6139938A (en) 1999-02-22 2000-10-31 Innovative Packaging Corp. High flute density, printable, corrugated paperboard
WO2002102592A1 (fr) 2001-06-15 2002-12-27 Ole-Bendt Rasmussen Complexe de films obtenu par lamination et procedes et appareil permettant sa fabrication
WO2004054793A1 (fr) 2002-12-13 2004-07-01 Ole-Bendt Rasmussen Stratifies de feuilles presentant une resistance amelioree a la flexion dans toutes les directions et procedes et dispositifs permettant de les produire

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109910371A (zh) * 2019-04-09 2019-06-21 徐自立 Pe膜热封制袋机的热封装置
CN109910371B (zh) * 2019-04-09 2024-02-27 浙江德力普智能制造有限公司 Pe膜热封制袋机的热封装置

Also Published As

Publication number Publication date
CN102548733A (zh) 2012-07-04
TW201107118A (en) 2011-03-01
GB0912449D0 (en) 2009-08-26
JP2012533444A (ja) 2012-12-27
EP2454079A1 (fr) 2012-05-23
AU2010272530A1 (en) 2012-03-08

Similar Documents

Publication Publication Date Title
KR100212163B1 (ko) 적층필름
JP6529543B2 (ja) 織物の特性を示すフィルム材料、その製造のための方法および装置
RU2457945C2 (ru) Способ и устройство для изготовления поперечно ориентированной пленки термопластичного полимерного материала и продукты, получаемые таким способом
US7132151B2 (en) Laminates of films and methods and apparatus for the manufacture
DK171395B1 (da) Fremgangsmåde og apparat til komprimeret tværgående strækning af polymer emner
US9120267B2 (en) Method for longitudinal stretching a film in solid state and apparatus to carry out the method
JP2011510835A5 (fr)
CA2703970C (fr) Procede et appareil pour l'orientation longitudinale d'un materiau de film thermoplastique
EP2454079A1 (fr) Procédé et appareil pour la fabrication d'un stratifié comprenant un film orienté et à ondulation fine et produits résultants

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201080037865.5

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10743063

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2010743063

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2012520030

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 1201000161

Country of ref document: TH

WWE Wipo information: entry into national phase

Ref document number: 2010272530

Country of ref document: AU

ENP Entry into the national phase

Ref document number: 2010272530

Country of ref document: AU

Date of ref document: 20100714

Kind code of ref document: A