WO2010057502A2 - Aube d’éolienne comprenant une matière de liaison renforcée avec des particules - Google Patents

Aube d’éolienne comprenant une matière de liaison renforcée avec des particules Download PDF

Info

Publication number
WO2010057502A2
WO2010057502A2 PCT/DK2009/050311 DK2009050311W WO2010057502A2 WO 2010057502 A2 WO2010057502 A2 WO 2010057502A2 DK 2009050311 W DK2009050311 W DK 2009050311W WO 2010057502 A2 WO2010057502 A2 WO 2010057502A2
Authority
WO
WIPO (PCT)
Prior art keywords
particles
bonding material
wind turbine
turbine blade
layers
Prior art date
Application number
PCT/DK2009/050311
Other languages
English (en)
Other versions
WO2010057502A3 (fr
Inventor
Srikanth Narasimalu
Erwin Merijn Wouterson
Original Assignee
Vestas Wind Systems A/S
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Vestas Wind Systems A/S filed Critical Vestas Wind Systems A/S
Publication of WO2010057502A2 publication Critical patent/WO2010057502A2/fr
Publication of WO2010057502A3 publication Critical patent/WO2010057502A3/fr

Abstract

La présente invention est relative à une aube d’éolienne comprenant au moins deux régions liées l’une à l’autre par une matière de liaison, dans laquelle la matière de liaison contient des particules (6) qui présentent des propriétés de distribution de taille, de rigidité et de résistance qui donnent une matière de liaison qui est plus résistante qu’une matière de liaison correspondante qui ne contient pas de particules. Les aubes d’éolienne peuvent être partiellement ou entièrement constituées de couches de fibres pré-imprégnées de résine (4), également appelées des pré-imprégnés, la résine constituant la matière de liaison entre les couches. Dans un procédé de fabrication selon la présente invention, des particules (6) sont disposées entre au moins plusieurs des pré-imprégnés (4) pendant la fabrication. Les particules (6) sont utilisées pour améliorer les propriétés mécaniques, telles que la résistance au cisaillement ou la ténacité à la fracture, et réduisent de ce fait le risque de décollement. On obtient ainsi une aube d’éolienne plus fiable. L’invention est en outre relative à un procédé de fabrication d’une aube d’éolienne de ce type.
PCT/DK2009/050311 2008-11-24 2009-11-23 Aube d’éolienne comprenant une matière de liaison renforcée avec des particules WO2010057502A2 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US20017908P 2008-11-24 2008-11-24
DKPA200801649 2008-11-24
DKPA200801649 2008-11-24
US61/200,179 2008-11-24

Publications (2)

Publication Number Publication Date
WO2010057502A2 true WO2010057502A2 (fr) 2010-05-27
WO2010057502A3 WO2010057502A3 (fr) 2010-07-22

Family

ID=42169468

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/DK2009/050311 WO2010057502A2 (fr) 2008-11-24 2009-11-23 Aube d’éolienne comprenant une matière de liaison renforcée avec des particules

Country Status (1)

Country Link
WO (1) WO2010057502A2 (fr)

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012113966A1 (fr) * 2011-02-25 2012-08-30 Francisco Javier Garcia Castro Procédé de fabrication de pales d'éoliennes, de pales d'hélices, d'ailes ou de structures similaires et de structure en forme de pale obtenue au moyen dudit procédé
CN103350515A (zh) * 2013-07-08 2013-10-16 广东明阳风电产业集团有限公司 玻璃纤维纱预浸润法制作叶片后缘增强件工艺
US9897065B2 (en) 2015-06-29 2018-02-20 General Electric Company Modular wind turbine rotor blades and methods of assembling same
WO2018114123A1 (fr) * 2016-12-21 2018-06-28 Siemens Wind Power A/S Procédé d'application d'une couche de protection sur une pale de rotor d'éolienne
US10072632B2 (en) 2015-06-30 2018-09-11 General Electric Company Spar cap for a wind turbine rotor blade formed from pre-cured laminate plates of varying thicknesses
US10077758B2 (en) 2015-06-30 2018-09-18 General Electric Company Corrugated pre-cured laminate plates for use within wind turbine rotor blades
US10107257B2 (en) 2015-09-23 2018-10-23 General Electric Company Wind turbine rotor blade components formed from pultruded hybrid-resin fiber-reinforced composites
US10113532B2 (en) 2015-10-23 2018-10-30 General Electric Company Pre-cured composites for rotor blade components
US10337490B2 (en) 2015-06-29 2019-07-02 General Electric Company Structural component for a modular rotor blade
US10422316B2 (en) 2016-08-30 2019-09-24 General Electric Company Pre-cured rotor blade components having areas of variable stiffness
US10954169B2 (en) * 2015-10-05 2021-03-23 Safran Aircraft Engines Process for manufacturing a ceramic composite material part by pressurized injection of a loaded slurry into a porous mould
WO2023024003A1 (fr) * 2021-08-26 2023-03-02 远景能源有限公司 Matériau de noyau renforcé pour pale de ventilateur et son procédé de préparation

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5925275A (en) * 1993-11-30 1999-07-20 Alliedsignal, Inc. Electrically conductive composite heater and method of manufacture
WO2004106420A2 (fr) * 2003-05-22 2004-12-09 Zyvex Corporation Nanocomposites et procedes
GB2410458A (en) * 2004-01-27 2005-08-03 David Irving A moulded fibre reinforced composite product with a core
EP1880833A1 (fr) * 2006-07-19 2008-01-23 National University of Ireland, Galway Articles composites comprenant des matériaux thermoplastiques polymerisables in-situ et méthodes de fabrication associées
GB2456484A (en) * 2009-06-10 2009-07-22 Vestas Wind Sys As Wind turbine blade incorporating nanoclay

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5925275A (en) * 1993-11-30 1999-07-20 Alliedsignal, Inc. Electrically conductive composite heater and method of manufacture
WO2004106420A2 (fr) * 2003-05-22 2004-12-09 Zyvex Corporation Nanocomposites et procedes
GB2410458A (en) * 2004-01-27 2005-08-03 David Irving A moulded fibre reinforced composite product with a core
EP1880833A1 (fr) * 2006-07-19 2008-01-23 National University of Ireland, Galway Articles composites comprenant des matériaux thermoplastiques polymerisables in-situ et méthodes de fabrication associées
GB2456484A (en) * 2009-06-10 2009-07-22 Vestas Wind Sys As Wind turbine blade incorporating nanoclay

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012113966A1 (fr) * 2011-02-25 2012-08-30 Francisco Javier Garcia Castro Procédé de fabrication de pales d'éoliennes, de pales d'hélices, d'ailes ou de structures similaires et de structure en forme de pale obtenue au moyen dudit procédé
ES2387432A1 (es) * 2011-02-25 2012-09-21 Francisco Javier Garcia Castro Procedimiento para la fabricación de palas eólicas, palas para hélices, alas o estructuras similares y estructura en forma de pala obtenida mediante dicho procedimiento
CN103350515A (zh) * 2013-07-08 2013-10-16 广东明阳风电产业集团有限公司 玻璃纤维纱预浸润法制作叶片后缘增强件工艺
CN103350515B (zh) * 2013-07-08 2015-11-11 广东明阳风电产业集团有限公司 玻璃纤维纱预浸润法制作叶片后缘增强件工艺
US9897065B2 (en) 2015-06-29 2018-02-20 General Electric Company Modular wind turbine rotor blades and methods of assembling same
US10337490B2 (en) 2015-06-29 2019-07-02 General Electric Company Structural component for a modular rotor blade
US10072632B2 (en) 2015-06-30 2018-09-11 General Electric Company Spar cap for a wind turbine rotor blade formed from pre-cured laminate plates of varying thicknesses
US10077758B2 (en) 2015-06-30 2018-09-18 General Electric Company Corrugated pre-cured laminate plates for use within wind turbine rotor blades
US10107257B2 (en) 2015-09-23 2018-10-23 General Electric Company Wind turbine rotor blade components formed from pultruded hybrid-resin fiber-reinforced composites
US10954169B2 (en) * 2015-10-05 2021-03-23 Safran Aircraft Engines Process for manufacturing a ceramic composite material part by pressurized injection of a loaded slurry into a porous mould
US10113532B2 (en) 2015-10-23 2018-10-30 General Electric Company Pre-cured composites for rotor blade components
US10422316B2 (en) 2016-08-30 2019-09-24 General Electric Company Pre-cured rotor blade components having areas of variable stiffness
WO2018114123A1 (fr) * 2016-12-21 2018-06-28 Siemens Wind Power A/S Procédé d'application d'une couche de protection sur une pale de rotor d'éolienne
CN110073101A (zh) * 2016-12-21 2019-07-30 西门子歌美飒可再生能源公司 将保护层施加到风力涡轮机转子叶片的方法
US11067058B2 (en) 2016-12-21 2021-07-20 Siemens Gamesa Renewable Energy A/S Method of applying a protective layer to a wind turbine rotor blade
CN110073101B (zh) * 2016-12-21 2024-01-23 西门子歌美飒可再生能源公司 将保护层施加到风力涡轮机转子叶片的方法
WO2023024003A1 (fr) * 2021-08-26 2023-03-02 远景能源有限公司 Matériau de noyau renforcé pour pale de ventilateur et son procédé de préparation

Also Published As

Publication number Publication date
WO2010057502A3 (fr) 2010-07-22

Similar Documents

Publication Publication Date Title
WO2010057502A2 (fr) Aube d’éolienne comprenant une matière de liaison renforcée avec des particules
EP1940610B1 (fr) Système de tissu hybride stable dans l'environnement servant à protéger l'extérieur d'un aéronef
AU2014203585B2 (en) Laminated composite radius filler with geometric shaped filler element and method of forming the same
EP2605902B1 (fr) Structures composites ayant des joints composite-métal et procédé pour leur fabrication
KR101846592B1 (ko) 초단 섬유 재료로 된 갭 필러를 가지는 복합 구조체의 제조 방법 및 시스템
Soutis Introduction: Engineering requirements for aerospace composite materials
US20030037867A1 (en) Paste-bond clevis joint
EP3083395B1 (fr) Élément de raidissement et structure renforcée
Wanhill Carbon fibre polymer matrix structural composites
US20200223194A1 (en) Method for limiting interlaminar fatigue in composite laminate and a component incorporating the same
US20230415448A1 (en) Honeycomb core sandwich panels
CN104340378B (zh) 一种复合材料主桨叶铰链力矩超差的修理方法
WO2008118649A1 (fr) Procédé pour lier une pellicule opposée à un noyau de composite de forme libre
Mills et al. Investigation, manufacture, and testing of damage-resistant airframe structures using low-cost carbon fibre composite materials and manufacturing technology
EP3375712A1 (fr) Structures composites possédant des lignes de jointure à impédance électrique correspondante
CA2919440A1 (fr) Materiau composite incorporant une barriere contre l'entree d'eau
US9243407B2 (en) Structure repair with polymer matrix composites
US10125617B2 (en) Composite structure and a method of fabricating the same
Lu Materials and Process Modeling of Aerospace Composites
Ranabhat Magnetic Compaction Force Assisted Additive Manufacturing of Continuous Carbon Fiber Reinforced Polymer Composites and System Architecture Investigation Using System Modeling Language (SYSML)
US11633881B1 (en) Heated composite tool and method for building and use
Rajamanickam Study of delamination of composite hat skin stringer interface failure
Karuppannan et al. Composites for reinforcement of damaged metallic aircraft wings
Kumar Adhesive bonding in composite structures for aerospace applications
Zafar Study of composite wind turbine spars

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09756411

Country of ref document: EP

Kind code of ref document: A2

122 Ep: pct application non-entry in european phase

Ref document number: 09756411

Country of ref document: EP

Kind code of ref document: A2