WO2009153202A1 - Copolymer admixture system for workability retention of cementitious compositions - Google Patents
Copolymer admixture system for workability retention of cementitious compositions Download PDFInfo
- Publication number
- WO2009153202A1 WO2009153202A1 PCT/EP2009/057179 EP2009057179W WO2009153202A1 WO 2009153202 A1 WO2009153202 A1 WO 2009153202A1 EP 2009057179 W EP2009057179 W EP 2009057179W WO 2009153202 A1 WO2009153202 A1 WO 2009153202A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- copolymer
- monomer
- ethylenically unsaturated
- solution
- Prior art date
Abstract
Description
Claims