WO2009120511A2 - Hydrogel intraocular lens and method of forming same - Google Patents
Hydrogel intraocular lens and method of forming same Download PDFInfo
- Publication number
- WO2009120511A2 WO2009120511A2 PCT/US2009/036925 US2009036925W WO2009120511A2 WO 2009120511 A2 WO2009120511 A2 WO 2009120511A2 US 2009036925 W US2009036925 W US 2009036925W WO 2009120511 A2 WO2009120511 A2 WO 2009120511A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- alkyl
- ophthalmic device
- phenyl
- lens
- chromophore
- Prior art date
Abstract
Description
Claims