WO2008151173A1 - Deposition of metal ions onto surfaces of conductive substrates - Google Patents
Deposition of metal ions onto surfaces of conductive substrates Download PDFInfo
- Publication number
- WO2008151173A1 WO2008151173A1 PCT/US2008/065602 US2008065602W WO2008151173A1 WO 2008151173 A1 WO2008151173 A1 WO 2008151173A1 US 2008065602 W US2008065602 W US 2008065602W WO 2008151173 A1 WO2008151173 A1 WO 2008151173A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- hydroxide
- solution
- metal
- water
- alkali metal
- Prior art date
Abstract
Description
Claims