WO2008140480A1 - Armure transparente anti-fissure - Google Patents

Armure transparente anti-fissure Download PDF

Info

Publication number
WO2008140480A1
WO2008140480A1 PCT/US2007/023551 US2007023551W WO2008140480A1 WO 2008140480 A1 WO2008140480 A1 WO 2008140480A1 US 2007023551 W US2007023551 W US 2007023551W WO 2008140480 A1 WO2008140480 A1 WO 2008140480A1
Authority
WO
WIPO (PCT)
Prior art keywords
armor
transparent
index
crack
transparent armor
Prior art date
Application number
PCT/US2007/023551
Other languages
English (en)
Inventor
Michael L. Genier
Linda R Pinckney
Paul J Shustack
Jian-Zhi J Zhang
Original Assignee
Corning Incorporated
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Corning Incorporated filed Critical Corning Incorporated
Publication of WO2008140480A1 publication Critical patent/WO2008140480A1/fr

Abstract

La présente invention concerne une armure en verre transparente qui possède une pluralité d'éléments anti-fissure. L'armure peut être monolithique, stratifiée ou segmentée. Les éléments anti-fissure optimisent la capacité d'une armure transparente à absorber de multiples impacts de projectile sans rupture catastrophique ou perte de transparence optique. Les éléments anti-fissure limitent la propagation de fissures, et peuvent être à des angles non orthogonales par rapport à la face d'impact.
PCT/US2007/023551 2006-11-30 2007-11-08 Armure transparente anti-fissure WO2008140480A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US86192506P 2006-11-30 2006-11-30
US60/861,925 2006-11-30

Publications (1)

Publication Number Publication Date
WO2008140480A1 true WO2008140480A1 (fr) 2008-11-20

Family

ID=40002498

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2007/023551 WO2008140480A1 (fr) 2006-11-30 2007-11-08 Armure transparente anti-fissure

Country Status (1)

Country Link
WO (1) WO2008140480A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20150377595A1 (en) * 2014-06-27 2015-12-31 Ppg Industries Ohio, Inc. Reduced weight armor systems and methods of manufacturing the same
WO2019038720A1 (fr) * 2017-08-23 2019-02-28 Agp America S.A. Blindage multi-coup transparent
WO2019064277A1 (fr) * 2017-09-29 2019-04-04 Agp America S.A. Stratifié blindé transparent constitué de tuiles avec des articulations non perpendiculaires
EP3536440A1 (fr) * 2014-07-14 2019-09-11 Corning Incorporated Article en verre avec un cheminement de defauts
US10415936B2 (en) 2013-12-31 2019-09-17 Ppg Industries Ohio, Inc. Armor mounting system and armor incorporating the same

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3380406A (en) * 1965-04-28 1968-04-30 Whittaker Corp Composite design for transparent armour
US3516898A (en) * 1963-03-28 1970-06-23 Goodyear Aerospace Corp Hard faced plastic armor
US5315952A (en) * 1991-05-07 1994-05-31 Jackson Jr Curtiss E Method of making and apparatus of a view window

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3516898A (en) * 1963-03-28 1970-06-23 Goodyear Aerospace Corp Hard faced plastic armor
US3380406A (en) * 1965-04-28 1968-04-30 Whittaker Corp Composite design for transparent armour
US5315952A (en) * 1991-05-07 1994-05-31 Jackson Jr Curtiss E Method of making and apparatus of a view window

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10415936B2 (en) 2013-12-31 2019-09-17 Ppg Industries Ohio, Inc. Armor mounting system and armor incorporating the same
US10895439B2 (en) 2013-12-31 2021-01-19 Ppg Industries Ohio, Inc. Armor mounting system and armor incorporating the same
US11353296B2 (en) 2013-12-31 2022-06-07 Ppg Industries Ohio, Inc. Armor mounting system and armor incorporating the same
US11788821B2 (en) 2013-12-31 2023-10-17 Ppg Industries Ohio, Inc. Armor mounting system and armor incorporating the same
US20150377595A1 (en) * 2014-06-27 2015-12-31 Ppg Industries Ohio, Inc. Reduced weight armor systems and methods of manufacturing the same
US9803959B2 (en) * 2014-06-27 2017-10-31 Ppg Industries Ohio, Inc. Reduced weight armor systems and methods of manufacturing the same
EP3536440A1 (fr) * 2014-07-14 2019-09-11 Corning Incorporated Article en verre avec un cheminement de defauts
WO2019038720A1 (fr) * 2017-08-23 2019-02-28 Agp America S.A. Blindage multi-coup transparent
WO2019064277A1 (fr) * 2017-09-29 2019-04-04 Agp America S.A. Stratifié blindé transparent constitué de tuiles avec des articulations non perpendiculaires

Similar Documents

Publication Publication Date Title
EP1888996B1 (fr) Composite ceramique transparent
EP2244988B1 (fr) Vitre armée transparente légère
US8028612B2 (en) Transparent ballistic resistant armor
US9194663B2 (en) Transparent glass/polymer composite
KR20070107678A (ko) 광투과성 장갑 복합재료
EP2652433B1 (fr) Composites de fibres en sandwich pour applications balistiques
US20090263651A1 (en) Optically transparent resilient laminate materials and methods of manufacture
WO2009011951A2 (fr) Armure transparente en mosaïque
JP2011504992A (ja) マルチヒット対応透明積層装甲システム
WO2008140480A1 (fr) Armure transparente anti-fissure
US4879183A (en) Method to manufacture a blindaged glass
US20120174755A1 (en) Optically transmissive armor composite and method of manufacture
US20100126336A1 (en) Optically transmissive armor composite and method of manufacture
WO2019064277A1 (fr) Stratifié blindé transparent constitué de tuiles avec des articulations non perpendiculaires
WO2019038720A1 (fr) Blindage multi-coup transparent
CN115923264B (zh) 一种冲击后保持高能见度的防弹防爆玻璃
AU2012244085B2 (en) Transparent ceramic composite
WO2004055468A1 (fr) Plaque transparente pare-balles

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07874116

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 07874116

Country of ref document: EP

Kind code of ref document: A1