WO2008121337A1 - Polymer manufacturing process - Google Patents
Polymer manufacturing process Download PDFInfo
- Publication number
- WO2008121337A1 WO2008121337A1 PCT/US2008/004079 US2008004079W WO2008121337A1 WO 2008121337 A1 WO2008121337 A1 WO 2008121337A1 US 2008004079 W US2008004079 W US 2008004079W WO 2008121337 A1 WO2008121337 A1 WO 2008121337A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- pet
- polymer
- final polymer
- commercially available
- reaction
- Prior art date
Abstract
Description
Claims