WO2008107146A1 - Pre-accelerated resin composition - Google Patents
Pre-accelerated resin composition Download PDFInfo
- Publication number
- WO2008107146A1 WO2008107146A1 PCT/EP2008/001668 EP2008001668W WO2008107146A1 WO 2008107146 A1 WO2008107146 A1 WO 2008107146A1 EP 2008001668 W EP2008001668 W EP 2008001668W WO 2008107146 A1 WO2008107146 A1 WO 2008107146A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- resin
- resin composition
- composition according
- component
- mmol
- Prior art date
Abstract
Description
Claims