WO2008065454A1 - Film - Google Patents

Film Download PDF

Info

Publication number
WO2008065454A1
WO2008065454A1 PCT/GB2007/050733 GB2007050733W WO2008065454A1 WO 2008065454 A1 WO2008065454 A1 WO 2008065454A1 GB 2007050733 W GB2007050733 W GB 2007050733W WO 2008065454 A1 WO2008065454 A1 WO 2008065454A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
film according
cavitated
glass microspheres
microspheres
Prior art date
Application number
PCT/GB2007/050733
Other languages
English (en)
Inventor
Christopher Stewart Konkel
Original Assignee
Innovia Films Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from GB0624049A external-priority patent/GB2444242A/en
Priority claimed from GB0624050A external-priority patent/GB0624050D0/en
Priority claimed from GB0717566A external-priority patent/GB0717566D0/en
Priority claimed from GB0717670A external-priority patent/GB0717670D0/en
Application filed by Innovia Films Limited filed Critical Innovia Films Limited
Priority to EP07824943A priority Critical patent/EP2097335A1/fr
Publication of WO2008065454A1 publication Critical patent/WO2008065454A1/fr

Abstract

La présente invention concerne un film polymère pourvu de cavités qui renferme des microsphères creuses en verre en une quantité ne dépassant par environ 40 % en poids du film.
PCT/GB2007/050733 2006-12-01 2007-11-30 Film WO2008065454A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP07824943A EP2097335A1 (fr) 2006-12-01 2007-11-30 Film

Applications Claiming Priority (8)

Application Number Priority Date Filing Date Title
GB0624049.3 2006-12-01
GB0624050.1 2006-12-01
GB0624049A GB2444242A (en) 2006-12-01 2006-12-01 Innerseal laminate containing voided biaxially stretched polypropylene
GB0624050A GB0624050D0 (en) 2006-12-01 2006-12-01 Film
GB0717566.4 2007-09-10
GB0717566A GB0717566D0 (en) 2007-09-10 2007-09-10 Film
GB0717670A GB0717670D0 (en) 2007-09-11 2007-09-11 Film
GB0717670.4 2007-09-11

Publications (1)

Publication Number Publication Date
WO2008065454A1 true WO2008065454A1 (fr) 2008-06-05

Family

ID=39205278

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2007/050733 WO2008065454A1 (fr) 2006-12-01 2007-11-30 Film

Country Status (2)

Country Link
EP (1) EP2097335A1 (fr)
WO (1) WO2008065454A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140072743A1 (en) * 2012-09-11 2014-03-13 Baxter Healthcare S.A. Polymer films containing microspheres
WO2019089535A3 (fr) * 2017-10-30 2019-06-13 Eastman Chemical Company Films contenant des vides à faible densité
IT201800005317A1 (it) * 2018-05-14 2019-11-14 Film di copertura ad uso agricolo ad elevato effetto termico, e ad effetto schermante alle radiazioni n.i.r., conseguiti mediante utilizzo di microsfere cave di vetro , e relativo metodo di realizzazione
US11097508B2 (en) 2016-12-02 2021-08-24 3M Innovative Properties Company Polymeric multilayer material and method of making the same

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4403048A (en) * 1980-08-08 1983-09-06 T C Manufacturing Company Corrosion-resistant coating composition containing hollow microballoons
US5885721A (en) * 1996-10-03 1999-03-23 Mobil Oil Corporation Multilaminar high density polyethylene film with high biaxial orientation
US20020182435A1 (en) * 2001-05-30 2002-12-05 Migliorini Robert A. Monoweb metallized film suitable for direct surface printing
EP1306403A1 (fr) * 2001-10-25 2003-05-02 Agriplast S.r.l. Film transparent pour l'agriculture, contenant des microsphères de verre
WO2004094141A2 (fr) * 2003-04-18 2004-11-04 Exxonmobil Oil Corporation Films en polypropylene multicouches orientes, a partie centrale modifiee

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1428747A (en) * 1973-08-07 1976-03-17 Ici Ltd Polymeric films
US5252632A (en) * 1992-11-19 1993-10-12 Savin Roland R Low cost cathodic and conductive coating compositions comprising lightweight hollow glass microspheres and a conductive phase

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4403048A (en) * 1980-08-08 1983-09-06 T C Manufacturing Company Corrosion-resistant coating composition containing hollow microballoons
US5885721A (en) * 1996-10-03 1999-03-23 Mobil Oil Corporation Multilaminar high density polyethylene film with high biaxial orientation
US20020182435A1 (en) * 2001-05-30 2002-12-05 Migliorini Robert A. Monoweb metallized film suitable for direct surface printing
EP1306403A1 (fr) * 2001-10-25 2003-05-02 Agriplast S.r.l. Film transparent pour l'agriculture, contenant des microsphères de verre
WO2004094141A2 (fr) * 2003-04-18 2004-11-04 Exxonmobil Oil Corporation Films en polypropylene multicouches orientes, a partie centrale modifiee

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
See also references of EP2097335A1 *

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140072743A1 (en) * 2012-09-11 2014-03-13 Baxter Healthcare S.A. Polymer films containing microspheres
US11097508B2 (en) 2016-12-02 2021-08-24 3M Innovative Properties Company Polymeric multilayer material and method of making the same
WO2019089535A3 (fr) * 2017-10-30 2019-06-13 Eastman Chemical Company Films contenant des vides à faible densité
CN111295284A (zh) * 2017-10-30 2020-06-16 伊士曼化工公司 低密度含有空隙的膜
KR20200070379A (ko) * 2017-10-30 2020-06-17 이스트만 케미칼 컴파니 저밀도 공극-함유 필름
JP2021501238A (ja) * 2017-10-30 2021-01-14 イーストマン ケミカル カンパニー 低密度の空隙含有フィルム
KR102470432B1 (ko) * 2017-10-30 2022-11-23 이스트만 케미칼 컴파니 저밀도 공극-함유 필름
IT201800005317A1 (it) * 2018-05-14 2019-11-14 Film di copertura ad uso agricolo ad elevato effetto termico, e ad effetto schermante alle radiazioni n.i.r., conseguiti mediante utilizzo di microsfere cave di vetro , e relativo metodo di realizzazione
EP3569410A1 (fr) * 2018-05-14 2019-11-20 Agriplast S.r.l. Film de couverture agricole pour des serres à haute efficacité ir et un effet de blindage à n.i.r. rayonnements, obtenus par l'utilisation de microsphères de verre creuses et son procédé de production associé

Also Published As

Publication number Publication date
EP2097335A1 (fr) 2009-09-09

Similar Documents

Publication Publication Date Title
WO2008065453A1 (fr) Film
AU715460B2 (en) High density polyethylene film with high biaxial orientation
US6150013A (en) Low thermal conductivity in-mold label films
CA2741448C (fr) Films thermoretractables multicouches, etiquettes fabriquees a partir de ceux-ci et leur utilisation
EP3405344B1 (fr) Film bi-orienté, à cavités, linéaire à faible densité ayant de bonnes propriétés de scellement
HUT76514A (en) Multi-layered, oriented, weldable film structure wit a better processability
EP2195255A1 (fr) Films d'emballage et procédés pour les fabriquer
KR20080094730A (ko) 폴리에스테르 필름
AU692026B2 (en) Heat sealable multilayer film containing polyvinyl alcohol layer
KR20090101354A (ko) 열수축성 폴리올레핀계 필름 및 그의 제조방법
EP1519835B1 (fr) Etiquette en papier synthetique
CA2226770C (fr) Pellicules polymeriques
WO2001038434A1 (fr) Film etire a base de resine et son procede de fabrication
WO2008065454A1 (fr) Film
TW574100B (en) EVOH and EVM in single- or multilayer products
US20140295076A1 (en) Low seal initiation lid for rigid substrates
EP3057718A1 (fr) Substrats revêtus de poly(chlorure de vinylidène)
AU722889B2 (en) Voided uniaxially oriented films
JP2001214013A (ja) 樹脂延伸フィルムおよびその製造方法
JP2001192470A (ja) 樹脂延伸フィルムおよびその製造方法
WO1994024171A1 (fr) Procede de production d'une solution polymere oxydee et procede de production d'un stratifie au moyen de ladite solution
JPH0153184B2 (fr)
EP2323834A1 (fr) Film

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07824943

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2007824943

Country of ref document: EP