WO2008000824A1 - Elastic roll cover, covered roll and method of manufacturing a covered roll - Google Patents
Elastic roll cover, covered roll and method of manufacturing a covered roll Download PDFInfo
- Publication number
- WO2008000824A1 WO2008000824A1 PCT/EP2007/056589 EP2007056589W WO2008000824A1 WO 2008000824 A1 WO2008000824 A1 WO 2008000824A1 EP 2007056589 W EP2007056589 W EP 2007056589W WO 2008000824 A1 WO2008000824 A1 WO 2008000824A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- roll
- rubber mixture
- manufacturing
- rubber
- powder
- Prior art date
Abstract
Description
Claims