WO2007136382A1 - Formulation d'encre pour impression à jet d'encre conductrice - Google Patents

Formulation d'encre pour impression à jet d'encre conductrice Download PDF

Info

Publication number
WO2007136382A1
WO2007136382A1 PCT/US2006/020093 US2006020093W WO2007136382A1 WO 2007136382 A1 WO2007136382 A1 WO 2007136382A1 US 2006020093 W US2006020093 W US 2006020093W WO 2007136382 A1 WO2007136382 A1 WO 2007136382A1
Authority
WO
WIPO (PCT)
Prior art keywords
inkjet ink
weight
ink
ink composition
inkjet
Prior art date
Application number
PCT/US2006/020093
Other languages
English (en)
Inventor
Edward J. Stancik
Steven Dale Ittel
Original Assignee
E.I. Du Pont De Nemours And Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by E.I. Du Pont De Nemours And Company filed Critical E.I. Du Pont De Nemours And Company
Priority to CNA2006800546993A priority Critical patent/CN101448904A/zh
Priority to GB0819023A priority patent/GB2450656A/en
Priority to PCT/US2006/020093 priority patent/WO2007136382A1/fr
Publication of WO2007136382A1 publication Critical patent/WO2007136382A1/fr

Abstract

La présente invention concerne des compositions d'encre destinées à l'impression à jet d'encre présentant une formation réduite de gouttelettes satellites et une diffusion réduite sur des substrats non poreux, ainsi qu'un procédé pour imprimer des images avec une encre pour impression à jet d'encre présentant une formation réduite de gouttelettes satellites et une diffusion réduite sur des substrats non poreux.
PCT/US2006/020093 2006-05-24 2006-05-24 Formulation d'encre pour impression à jet d'encre conductrice WO2007136382A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CNA2006800546993A CN101448904A (zh) 2006-05-24 2006-05-24 导电喷墨油墨制剂
GB0819023A GB2450656A (en) 2006-05-24 2006-05-24 Condutive inkjet ink formulation
PCT/US2006/020093 WO2007136382A1 (fr) 2006-05-24 2006-05-24 Formulation d'encre pour impression à jet d'encre conductrice

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2006/020093 WO2007136382A1 (fr) 2006-05-24 2006-05-24 Formulation d'encre pour impression à jet d'encre conductrice

Publications (1)

Publication Number Publication Date
WO2007136382A1 true WO2007136382A1 (fr) 2007-11-29

Family

ID=37478843

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2006/020093 WO2007136382A1 (fr) 2006-05-24 2006-05-24 Formulation d'encre pour impression à jet d'encre conductrice

Country Status (3)

Country Link
CN (1) CN101448904A (fr)
GB (1) GB2450656A (fr)
WO (1) WO2007136382A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8511813B2 (en) 2010-12-21 2013-08-20 Hewlett-Packard Development Company, L.P. Oil-based ink jet inks

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0452118A1 (fr) * 1990-04-12 1991-10-16 Matsushita Electric Industrial Co., Ltd. Composition d'encre conductrice et méthode pour former un dessin conducteur en couche épaisse
WO2003106573A1 (fr) * 2002-06-13 2003-12-24 Nanopowders Industries Ltd. Procede de fabrication de nano-revetements, de nano-encres et de revetements et de nano-poudres conducteurs et transparents et encres ainsi produites
WO2005033799A2 (fr) * 2003-09-29 2005-04-14 E.I. Dupont De Nemours And Company Impression par filage de composants utilises en electronique et a des fins d'affichage
EP1561789A1 (fr) * 2004-02-09 2005-08-10 E.I. du Pont de Nemours and Company Compositions d'encres en couche épaisse imprimables par jet d'encre et méthodes
WO2006072959A1 (fr) * 2005-01-10 2006-07-13 Yissum Research Development Company Of The Hebrew University Of Jerusalem Dispersions aqueuses de nanoparticules de metal

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0452118A1 (fr) * 1990-04-12 1991-10-16 Matsushita Electric Industrial Co., Ltd. Composition d'encre conductrice et méthode pour former un dessin conducteur en couche épaisse
WO2003106573A1 (fr) * 2002-06-13 2003-12-24 Nanopowders Industries Ltd. Procede de fabrication de nano-revetements, de nano-encres et de revetements et de nano-poudres conducteurs et transparents et encres ainsi produites
WO2005033799A2 (fr) * 2003-09-29 2005-04-14 E.I. Dupont De Nemours And Company Impression par filage de composants utilises en electronique et a des fins d'affichage
EP1561789A1 (fr) * 2004-02-09 2005-08-10 E.I. du Pont de Nemours and Company Compositions d'encres en couche épaisse imprimables par jet d'encre et méthodes
WO2006072959A1 (fr) * 2005-01-10 2006-07-13 Yissum Research Development Company Of The Hebrew University Of Jerusalem Dispersions aqueuses de nanoparticules de metal

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8511813B2 (en) 2010-12-21 2013-08-20 Hewlett-Packard Development Company, L.P. Oil-based ink jet inks

Also Published As

Publication number Publication date
CN101448904A (zh) 2009-06-03
GB2450656A (en) 2008-12-31
GB0819023D0 (en) 2008-11-26

Similar Documents

Publication Publication Date Title
US20070276060A1 (en) Inkjet ink formulation
US10266715B2 (en) Liquid composition, especially ink composition, for printing with a binary deflected continuous jet, with non-charged drops, use of said composition, marking method and marked substrate
US7828888B2 (en) Inkjet-recording non-aqueous ink composition, inkjet recording method, and recorded matter
US7846500B2 (en) Latex-based overcoat for ink-jet printing applications
EP1544262B1 (fr) Systemes des vehicules liquides pour ameliorer la reponse frequencielle d'encres a base de latex pour imprimante a jet d'encre
JP3889099B2 (ja) インクジェット用インク及びインクジェット印刷におけるエーロゾルの低減法
US5395432A (en) Security jet ink
US7025817B2 (en) Ink, recording method, recording unit, ink cartridge, and recording apparatus
BRPI0608005B1 (pt) tinta e sistema para imprimir imagens sobre um substrato
KR20040018479A (ko) 플루오로화학 계면활성제를 함유하는 잉크 제트 잉크조성물
US10597546B2 (en) Liquid composition, especially ink composition, for printing with a binary deflected continuous jet, with non-charged drops, use of said composition, marking method and marked substrate
JP2006524269A (ja) インクジェットインク用途のための低バルク密度、低表面誘電率のラテックスポリマー
US5935308A (en) Latent image jet inks
KR101028934B1 (ko) 롤 프린팅용 잉크 조성물
JP5460608B2 (ja) 立体安定化ラテックス粒子
WO2007136382A1 (fr) Formulation d'encre pour impression à jet d'encre conductrice
US20070076021A1 (en) Processes for inkjet printing
JPS5964678A (ja) インクジエツト記録用インク
Kamyshny et al. Inkjet ink formulations
JP2004285356A (ja) インクジェットインク組成物および印刷方法
KR20200126977A (ko) 컨티뉴어스형 잉크젯 잉크 조성물
CN114686041A (zh) 一种uv固化字符油墨及其制备方法
JP2003327872A (ja) インクジェット記録用インク
JPH0735486B2 (ja) 記録液
JP2005072274A (ja) 液体吐出方法及び配線パターン形成方法

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 200680054699.3

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 06771076

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 0819023

Country of ref document: GB

Kind code of ref document: A

Free format text: PCT FILING DATE = 20060524

WWE Wipo information: entry into national phase

Ref document number: 0819023.3

Country of ref document: GB

WWE Wipo information: entry into national phase

Ref document number: 2009511991

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 06771076

Country of ref document: EP

Kind code of ref document: A1