WO2007116778A1 - Water absorbing resin with improved internal structure and manufacturing method therefor - Google Patents
Water absorbing resin with improved internal structure and manufacturing method therefor Download PDFInfo
- Publication number
- WO2007116778A1 WO2007116778A1 PCT/JP2007/056528 JP2007056528W WO2007116778A1 WO 2007116778 A1 WO2007116778 A1 WO 2007116778A1 JP 2007056528 W JP2007056528 W JP 2007056528W WO 2007116778 A1 WO2007116778 A1 WO 2007116778A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- water absorbing
- absorbing resin
- water
- mass
- resin
- Prior art date
Abstract
Description
Claims