WO2006093949A1 - Two-component epoxy adhesive composition - Google Patents
Two-component epoxy adhesive composition Download PDFInfo
- Publication number
- WO2006093949A1 WO2006093949A1 PCT/US2006/007053 US2006007053W WO2006093949A1 WO 2006093949 A1 WO2006093949 A1 WO 2006093949A1 US 2006007053 W US2006007053 W US 2006007053W WO 2006093949 A1 WO2006093949 A1 WO 2006093949A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- epoxy
- weight percent
- adhesive composition
- epoxy resin
- Prior art date
Abstract
Description
Claims