WO2006056102A1 - Multi-ply type cloth cover paper - Google Patents

Multi-ply type cloth cover paper

Info

Publication number
WO2006056102A1
WO2006056102A1 PCT/CN2004/001351 CN2004001351W WO2006056102A1 WO 2006056102 A1 WO2006056102 A1 WO 2006056102A1 CN 2004001351 W CN2004001351 W CN 2004001351W WO 2006056102 A1 WO2006056102 A1 WO 2006056102A1
Authority
WO
WIPO (PCT)
Prior art keywords
paper
layer
composite type
cloth
thickness
Prior art date
Application number
PCT/CN2004/001351
Other languages
French (fr)
Chinese (zh)
Inventor
Linping Zhang
Original Assignee
Linping Zhang
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Linping Zhang filed Critical Linping Zhang
Priority to CN2004800436871A priority Critical patent/CN1993222B/en
Priority to PCT/CN2004/001351 priority patent/WO2006056102A1/en
Publication of WO2006056102A1 publication Critical patent/WO2006056102A1/en

Abstract

The invention relates to a multi-ply paper, especially relates to a multi-ply type cloth cover paper which the cloth is stuck to the paper by adhesive. It is characterized in that the multi-ply type cloth cover paper substantially consists of a cloth layer to be printed or written, a paper layer for supporting and an adhesive layer which is placed between the cloth layer and the paper layer and bonds them together. The multi-ply type cloth cover paper can be used for print paper or artwork paper directly. Therefore, the printing photo or document is provided with additional art impression and high durability.

Description

复合型布面纸 技术领域  Composite fabric paper
本发明涉及一种复合型纸， 尤其涉及一种由布和纸通过粘结剂复合 而成的复合型布面纸。 背景技术  The present invention relates to a composite type paper, and more particularly to a composite type paper which is formed by laminating cloth and paper through an adhesive. Background technique
以前， 照片通常是利用一般的照相机拍摄， 然后取出胶卷进行冲洗 并用相纸洗印上照片。 如今， 数码相机已被人们普遍使用， 此时人们不 必使用传统的照片冲印技术来冲洗照片， 而只需使用打印机将数码相机 拍摄的照片直接打印在相纸或普通纸上即可， 此时， 为了使打印出的照 片具有好的质量， 一般要求所使用的打印纸具有好的质量， 例如使用高 质量的相片纸。  Previously, photos were usually taken with a normal camera, then the film was taken out for rinsing and the photo was washed with photo paper. Nowadays, digital cameras have been widely used. At this time, people do not have to use traditional photo printing technology to wash photos. Instead, they can use the printer to directly print photos taken by digital cameras on photo paper or plain paper. In order for the printed photograph to have good quality, it is generally required that the printed paper used has good quality, for example, using high quality photo paper.
此外， 人们还经常需要使用打印机从计算机中打印出例如风景画、 油画、 广告、 名片以及宣传资料等等， 此时也希望所使用的打印纸具有 较好的质量以使打印出的文件具有好的效果。  In addition, people often need to use a printer to print out, for example, landscapes, oil paintings, advertisements, business cards, promotional materials, etc. from the computer. At this time, it is also desirable that the printing paper used has better quality so that the printed documents have good quality. Effect.
使用的相片纸一般比较光滑， 打印出的照片或文件也比较清晰、 真 实。 但无论是使用亮光的相片纸还是使用哑光的相片纸， 打印出的照片 或文件一般与原照片或文件完全相同， 不具备附加的艺术效果。 因此如 果人们希望打印出的照片或文件与原照片或文件相比具有更高品质的附 加的艺术效果， 尚需开发出更好的打印用材料。  The photo paper used is generally smooth, and the printed photos or documents are clearer and more realistic. However, whether you use glossy photo paper or matte photo paper, the printed photos or documents are generally identical to the original photo or file, and have no additional artistic effects. Therefore, if people want to print a photo or document with a higher quality additional artistic effect than the original photo or document, it is necessary to develop a better printing material.
在制作灯箱广告时， 人们有时使用布料作为广告用材料， 因为有些 布料能透光， 且比较经久耐用， 但此时布料上的文字一般是通过印刷机 械印刷上的， 因为布匹非常柔软， 当其较薄时很难用一般的打印机来打 印。 发明内容 When making lightbox advertisements, people sometimes use fabrics as advertising materials, because some fabrics are light-transmissive and durable, but the text on the fabric is usually printed by printing machinery because the fabric is very soft. It is difficult to print with a normal printer when it is thin. Summary of the invention
为了使打印出的照片或文件具有附加的艺术效果， 本发明人突发奇 想： 布料由于其具有布紋， 如果能将照片或文件打印在布上， 肯定会产 生附加的艺术效果。 但由于布匹非常柔软， 根本不可能用一般的喷墨打 印机或照片打印机将照片或文件打印在布上， 为此本发明人考虑到将布 料与纸张进行复合， 开发出复合型布面纸， 其可直接用作打印机用纸， 从而使打印出的照片或文件具有附加的艺术效果。  In order to make the printed photograph or document have an additional artistic effect, the inventor has a whimsy: Since the cloth has a cloth pattern, if the photo or the document can be printed on the cloth, an additional artistic effect is surely produced. However, since the cloth is very soft, it is impossible to print a photo or a document on a cloth by a general inkjet printer or a photo printer. For this reason, the inventors considered that the fabric and the paper are combined to develop a composite type paper. Can be used directly as printer paper, so that printed photos or documents have additional artistic effects.
因此， 本发明的目的是提供一种新颖的复合型布面纸， 其可直接用 作打印机用纸， 从而使打印出的照片或文件具有附加的艺术效果。  Accordingly, it is an object of the present invention to provide a novel composite type of facing paper which can be used directly as a printer paper to provide an additional artistic effect to printed photographs or documents.
本发明提供的复合型布面纸基本上由作为打印或书写面的布料层、 作为支承层的纸质层、 和位于二者之间并使二者复合在一起的粘结剂层 所组成。  The composite type paper provided by the present invention basically consists of a cloth layer as a printing or writing surface, a paper layer as a supporting layer, and an adhesive layer interposed therebetween and which are combined together.
所述复合型布面纸的厚度优选为 0.05-3毫米。 如果该复合型布面纸 的厚度小于 0.05毫米， 则其可能太柔软， 用于打印机打印时进纸和出纸 较困难， 打印出的照片或文件质量不高， 并且这样的复合型布面纸在制 备时复合难度较大， 废品率高， 成本高。 如果该复合型布面纸的厚度大 于 3毫米， 则其难以在打印机上使用。 该复合型布面纸的厚度更优选为 0.08-2毫米。  The composite type paper preferably has a thickness of from 0.05 to 3 mm. If the composite type paper has a thickness of less than 0.05 mm, it may be too soft, it is difficult to feed and eject paper when printing, and the quality of printed photographs or documents is not high, and such a composite type paper In the preparation, the compounding difficulty is high, the scrap rate is high, and the cost is high. If the composite type paper has a thickness of more than 3 mm, it is difficult to use on a printer. The thickness of the composite type paper is more preferably 0.08 - 2 mm.
所述复合型布面纸的宽度没有特别的限制， 可以根据需要确定， 例 如可以为 9-1800毫米。  The width of the composite type paper is not particularly limited and may be determined as needed, for example, 9 to 1800 mm.
只要能使所述复合型布面纸的厚度满足上述范围， 所述布料层、 纸 质层及粘结剂层的厚度没有特别的限制。 一般来说， 只要能使所述布料 层和纸质层有效地复合在一起， 所述粘结剂层的厚度应越小越好。 为了 能使所述复合型布面纸的厚度满足上述范围， 所述布料层的厚度优选为 0.02-1.8毫米， 所述纸质层的厚度优选为 0.03-1.8毫米。 所述布料层所采用的布料没有特别的限制， 例如可以采用化纤布料、 棉布料、 或丝绸料， 但特别优选的是采用化纤布料， 因为化纤布料厚度 可以较薄并且较为经久耐用。 所述布料的颜色一般为白色， 但也可根据 需要采用其它色彩， 甚至可采用带有花边、 艺术边框等的布料以产生进 一步的艺术效果。 The thickness of the cloth layer, the paper layer and the binder layer is not particularly limited as long as the thickness of the composite type paper can be made to satisfy the above range. In general, as long as the cloth layer and the paper layer can be effectively compounded together, the thickness of the adhesive layer should be as small as possible. In order to make the thickness of the composite type cloth paper satisfy the above range, the thickness of the cloth layer is preferably 0.02 to 1.8 mm, and the thickness of the paper layer is preferably 0.03 to 1.8 mm. The cloth to be used for the cloth layer is not particularly limited, and for example, a chemical fiber cloth, a cotton cloth, or a silk material can be used, but it is particularly preferable to use a chemical fiber cloth because the chemical fiber cloth can be thin and durable. The color of the fabric is generally white, but other colors may be used as needed, and even fabrics with lace, artistic borders, etc. may be used to produce further artistic effects.
所述纸质层所采用的材料没有特别的限制， 可以根据需要选用； 例 如， 当需要较高的打印质量时， 可选用目前常用的相片纸作为纸质层， 或者当所需打印质量要求不很高时， 也可选用一般的打印纸作为纸质层。  The material used for the paper layer is not particularly limited and may be selected as needed; for example, when higher print quality is required, the currently used photo paper may be selected as the paper layer, or when the required print quality is not required. When it is very high, a general printing paper can also be used as the paper layer.
所述粘结剂层所采用的粘结剂没有特别的限制， 一般来说， 能用于 粘贴纸张的粘结剂都可以用于制作本发明的复合型布面纸。  The binder used in the adhesive layer is not particularly limited. Generally, an adhesive which can be used for sticking paper can be used to produce the composite type paper of the present invention.
本发明的复合型布面纸一般通过机械复合而制作， 在复合时应尽量 使所述布料层和所述支承用纸质层紧密复合， 避免在二者之间产生气泡。  The composite type paper of the present invention is generally produced by mechanical compounding, and the cloth layer and the supporting paper layer should be closely combined as much as possible during the compounding to avoid generation of air bubbles between the two.
由于本发明的复合型布面纸其打印面具有布料的紋理， 利用这种复 合型布面纸打印出的照片或文件具有与原始照片或文件不同的附加的艺 术效果， 并且其表面的手感完全不同于普通的相纸或打印纸。 另外， 用 本发明的复合型布面纸打印出的照片或文件不易被撕裂， 可长时间保存。  Since the composite type paper of the present invention has a printed surface with a texture of the cloth, the photograph or document printed by the composite type paper has an additional artistic effect different from the original photograph or document, and the surface feel is completely Different from ordinary photo paper or printing paper. Further, the photograph or document printed on the composite type paper of the present invention is not easily torn and can be stored for a long period of time.
除上述用途外， 本发明的复合型布面纸还可用于制作名片、 手工艺 品或其它高档艺术品， 还可供书法家在其上直接创作书法作品或供画家 创作绘画作品而不需裱糊。 附图说明  In addition to the above-mentioned uses, the composite type paper of the present invention can also be used for making business cards, handicrafts or other high-end art works, and it is also possible for a calligrapher to directly create a calligraphy work or a painter to create a painting without being confused. DRAWINGS
图 1是本发明的复合型布面纸的示意图。 具体实施方式  BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a schematic view of a composite type of paper of the present invention. Detailed ways
参照图 1，根据本发明的一种实施方式，所提供的复合型布面纸由作 为打印或书写面的布料层 2、 作为支承层的纸质层 1、 和位于二者之间并 使二者复合在一起的粘结剂层 3所组成。 在本实施方式中， 纸质层 1采 用厚度约为 0.2mm 的相片纸如柯达相片纸等， 布料层 2采用厚度约为 0.1mm的普通的化纤白布， 粘结剂采用普通液体胶水， 所有这些都可以 从市场上购买到。 其制作方法可以是： 采用滚轴复合机， 将一定尺寸的 布料和纸张分别由二个送料辊送入由相向旋转的一对或多对滚轴组成的 复合机构中， 在进入所述复合机构之前通过涂浆机构在所述纸张的复合 面上均匀涂敷一层粘结剂， 通过调整滚轴之间的间隙大小而使所述布料 和纸张紧密复合在一起， 然后经自然干燥， 得到本发明的复合型布面纸， 其厚度约为 0.3mm。 Referring to Figure 1, in accordance with an embodiment of the present invention, a composite type of paper is provided It is composed of a cloth layer 2 for printing or writing a surface, a paper layer 1 as a supporting layer, and an adhesive layer 3 interposed therebetween and which are combined together. In the present embodiment, the paper layer 1 is made of a photo paper having a thickness of about 0.2 mm, such as Kodak photo paper, etc., the cloth layer 2 is made of a common chemical fiber white cloth having a thickness of about 0.1 mm, and the binder is a common liquid glue, all of which are used. Can be purchased from the market. The manufacturing method may be: using a roller laminating machine, feeding a certain size of cloth and paper from two feeding rollers into a composite mechanism consisting of one or more pairs of rotating rollers that are opposite to each other, and entering the composite mechanism Previously, a layer of adhesive is uniformly applied to the composite surface of the paper by a sizing mechanism, and the cloth and the paper are closely combined by adjusting the size of the gap between the rollers, and then naturally dried to obtain the present. The composite type of paper of the invention has a thickness of about 0.3 mm.

Claims

权利要求书 Claim
1、 一种复合型布面纸， 其特征在于基本上由作为打印或书写面的布 料层、 作为支承层的纸质层、 和位于二者之间并使二者复合在一起的粘 结剂层所组成。 A composite type of cloth paper characterized by substantially a cloth layer as a printing or writing surface, a paper layer as a supporting layer, and a binder interposed therebetween and combining the two The composition of the layers.
2、 根据权利要求 1所述的复合型布面纸， 其特征在于该复合型布面 纸的厚度为 0.05-3毫米。  The composite type paper according to claim 1, wherein the composite type paper has a thickness of from 0.05 to 3 mm.
3、根据权利要求 2所述的复合型布面纸， 其特征在于该复合型布面 纸的厚度为 0.08-2毫米。  A composite type paper according to claim 2, wherein the composite type paper has a thickness of 0.08 - 2 mm.
4、根据权利要求 1所述的复合型布面纸， 其特征在于所述布料层的 厚度为 0.02-1.8毫米。  A composite type paper according to claim 1, wherein said cloth layer has a thickness of from 0.02 to 1.8 mm.
5、 根据权利要求 1所述的复合型布面纸， 其特征在于所述纸质层的 厚度为 0.03-1.8毫米。  The composite type paper according to claim 1, wherein the paper layer has a thickness of from 0.03 to 1.8 mm.
6、根据权利要求 1所述的复合型布面纸， 其特征在于所述布料层为 化纤布料层、 棉布料层、 或丝绸料层。  The composite type paper according to claim 1, wherein the cloth layer is a chemical fiber cloth layer, a cotton cloth layer, or a silk material layer.
7、 根据权利要求 1所述的复合型布面纸， 其特征在于所述布料层为 带有花边或艺术边框的布料层。  The composite type paper according to claim 1, wherein the cloth layer is a cloth layer with a lace or an artistic border.
8、 根据权利要求 1所述的复合型布面纸， 其特征在于所述纸质层为 相片纸层或铜版纸层。  The composite type paper according to claim 1, wherein the paper layer is a photo paper layer or a coated paper layer.
9、 根据权利要求 1所述的复合型布面纸， 其特征在于所述纸质层为 普通打印纸层。  The composite type paper according to claim 1, wherein the paper layer is a plain printing paper layer.
PCT/CN2004/001351 2004-11-25 2004-11-25 Multi-ply type cloth cover paper WO2006056102A1 (en)