WO2006055652A2 - Solution based enhancements of fuel cell components and other electrochemical systems and devices - Google Patents
Solution based enhancements of fuel cell components and other electrochemical systems and devices Download PDFInfo
- Publication number
- WO2006055652A2 WO2006055652A2 PCT/US2005/041571 US2005041571W WO2006055652A2 WO 2006055652 A2 WO2006055652 A2 WO 2006055652A2 US 2005041571 W US2005041571 W US 2005041571W WO 2006055652 A2 WO2006055652 A2 WO 2006055652A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- solvent
- polymer
- electrode
- component
- membrane
- Prior art date
Abstract
Description
Claims