WO2006026626A2 - Film multicouche comprenant au moins une couche ionomere et une couche de liaison adhesive et article produit a partir dudit film - Google Patents

Film multicouche comprenant au moins une couche ionomere et une couche de liaison adhesive et article produit a partir dudit film Download PDF

Info

Publication number
WO2006026626A2
WO2006026626A2 PCT/US2005/030873 US2005030873W WO2006026626A2 WO 2006026626 A2 WO2006026626 A2 WO 2006026626A2 US 2005030873 W US2005030873 W US 2005030873W WO 2006026626 A2 WO2006026626 A2 WO 2006026626A2
Authority
WO
WIPO (PCT)
Prior art keywords
layer
ionomeric
multilayer film
polyolefin
thermoplastic
Prior art date
Application number
PCT/US2005/030873
Other languages
English (en)
Other versions
WO2006026626A3 (fr
Inventor
Christopher J. Wawsczyk
Christian G. Mayville
Joseph Schulcz
Original Assignee
Mayco Plastics, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mayco Plastics, Inc. filed Critical Mayco Plastics, Inc.
Publication of WO2006026626A2 publication Critical patent/WO2006026626A2/fr
Publication of WO2006026626A3 publication Critical patent/WO2006026626A3/fr

Abstract

L'invention concerne un film multicouche et un article comprenant ledit film. Le film multicouche comprend une couche ionomère, une couche thermoplastique et une couche intermédiaire contenant au moins un matériau pouvant adhérer à la couche thermoplastique et au moins un promoteur d'adhésion ionomère. Au moins un matériau solide d'amélioration visuelle est dispersé dans la couche ionomère.
PCT/US2005/030873 2004-08-31 2005-08-31 Film multicouche comprenant au moins une couche ionomere et une couche de liaison adhesive et article produit a partir dudit film WO2006026626A2 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US60581104P 2004-08-31 2004-08-31
US60/605,811 2004-08-31

Publications (2)

Publication Number Publication Date
WO2006026626A2 true WO2006026626A2 (fr) 2006-03-09
WO2006026626A3 WO2006026626A3 (fr) 2006-10-05

Family

ID=36000693

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2005/030873 WO2006026626A2 (fr) 2004-08-31 2005-08-31 Film multicouche comprenant au moins une couche ionomere et une couche de liaison adhesive et article produit a partir dudit film

Country Status (1)

Country Link
WO (1) WO2006026626A2 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017189600A1 (fr) * 2016-04-28 2017-11-02 Coveris Holding Corp. Films à couches multiples et procédés associés
CN112244426A (zh) * 2018-01-24 2021-01-22 耐克创新有限合伙公司 包括聚烯烃板的鞋底结构和由其形成的鞋类物品
WO2022266361A1 (fr) * 2021-06-18 2022-12-22 Bixby International Corporation Stratifiés fonctionnels et esthétiques durables

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020055006A1 (en) * 2000-04-14 2002-05-09 Vogel Randall Allen Multilayer, co-extruded, ionomeric decorative surfacing
US20030100633A1 (en) * 2001-02-16 2003-05-29 Hitoshi Maki Process for producing colored resin composition and utilization thereof

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020055006A1 (en) * 2000-04-14 2002-05-09 Vogel Randall Allen Multilayer, co-extruded, ionomeric decorative surfacing
US20030100633A1 (en) * 2001-02-16 2003-05-29 Hitoshi Maki Process for producing colored resin composition and utilization thereof

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017189600A1 (fr) * 2016-04-28 2017-11-02 Coveris Holding Corp. Films à couches multiples et procédés associés
US11890839B2 (en) 2016-04-28 2024-02-06 Transcontinental Holding Corp. Multi-layer films and related methods
CN112244426A (zh) * 2018-01-24 2021-01-22 耐克创新有限合伙公司 包括聚烯烃板的鞋底结构和由其形成的鞋类物品
WO2022266361A1 (fr) * 2021-06-18 2022-12-22 Bixby International Corporation Stratifiés fonctionnels et esthétiques durables

Also Published As

Publication number Publication date
WO2006026626A3 (fr) 2006-10-05

Similar Documents

Publication Publication Date Title
US7335424B2 (en) Ionomer laminates and articles formed from ionomer laminates
JP4842491B2 (ja) アイオノマー系多層同時押出化粧仕上げ材
US7405008B2 (en) Ionomer laminates and articles formed from ionomer laminates
EP2177354B1 (fr) Structure de support laminée
AU2001253390A1 (en) Multilayer, co-extruded, ionomeric decorative surfacing
US7479327B2 (en) Tie-layer materials for use with ionomer-based films and sheets as skins on other materials
US20050288418A1 (en) Article having a multilayer film including at least one layer containing metallic components and method of making the same
WO2006026626A2 (fr) Film multicouche comprenant au moins une couche ionomere et une couche de liaison adhesive et article produit a partir dudit film
US20030099840A1 (en) Composite laminate structures especially useful for automotive trim components, and methods and tie layers employed to make the same
US8252424B2 (en) Article having a multilayer film outer skin including at least one layer containing a pigmented layer and method of making the same
US20050288419A1 (en) Polymeric article having a multilayer film including at least one pigmented layer, method of making the same, and pigment additive package and composition suitable for use therein
US20050077649A1 (en) Formable ionomer coated metal sheets
JP2001001368A (ja) 射出成形同時絵付用シート
AU2002250418A1 (en) Ionomer laminates and articles formed from ionomer laminates
AU2002305076A1 (en) Ionomer laminates and articles formed from ionomer laminates

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KM KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NG NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SM SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU LV MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase in:

Ref country code: DE

122 Ep: pct application non-entry in european phase