PATENT
PRIMING MIXTURES FOR SMALL ARMS
TECHNICAL FIELD The present invention generally relates to primer charges or mixes and more
particularly to priming mixes for small arms ammunition.
BACKGROUND
The smallest component in small arms ammunition, the primer, is the link
between the striking of the firing pin and the explosion of the projectile out of the cartridge casing. Generally, most common primer mixes are comprised of a primary
explosive, an oxiding agent and a fuel source. Percussion primers and/or primer mixes
have undergone relatively few gradual changes since their original development. In early
primers, mercury fulminate was the most commonly used primer mix. Since that time, alternate priming mixes have replaced mercury fulminate, as this latter composition was found to deteriorate rapidly under tropical conditions and cause potential health problems
or concerns such as lethargy and nausea to the shooter after firing. Such alternate mixes,
typically based on lead thiocyanate/potassium chlorate formulations, however, were
found to be detrimental to weapon barrels because of the formation of corrosive water
ATLANTA 432955vl 1
soluble potassium chloride salts upon combustion. More conventional primer mixes currently in use typically are based on the primary explosive lead styphnate, a substance which is much more stable than mercury fulminate and is in common use today.
Although more stable and less corrosive than earlier primer mixes, the use of lead
styphnate-based primers has become more of a concern recently due to increasing
awareness of the health hazards of lead. While considerable attention has been directed to removing lead from primer mixes, however, there has been less attention paid to the removal of the remaining toxic components from the primer mix. One of most common
oxidizing agents used in conventional primer mixes is barium nitrate. Unfortunately,
barium is highly toxic, and therefore poses a potential health hazard, particularly when
used within an enclosed shooting area where it can accumulate in the atmosphere and on surfaces. Generally, a typical small arms primer contains between 30% and 50% oxidizer, so replacing barium nitrate with a non-toxic oxidizer greatly reduces the post-
ignition airborne hazards.
Alternative oxidizers, such as potassium nitrate, have been found to perform as well as barium nitrate under certain circumstances or conditions. For example, inorganic
nitrate salts perform very well as oxidizing agents in pyrotechnic fonnulations because of their relatively low melting points, available oxygen, and their crystalline form; however,
such nitrate salts such as potassium nitrate, are hygroscopic, making them very
susceptible to the effects of atmospheric moisture and inappropriate for use in certain
storage conditions. Since priming formulations typically are assembled in high moisture
ATLANTA 432955vl 2
environments to escape unintended ignition by heat, shock, or impact, many oxidizers, such as inorganic nitrates, can cause deleterious side chemical reactions when combined with other ingredients under such high-moisture conditions. Such reactions produce an inferior product with reduced sensitivity to impact and thus ignition, consequently increasing potential failure rates for such primers.
Accordingly, there exists a need for a priming mixture for small arms ammunition
that addresses the foregoing and other related and unrelated problems in the art.
SUMMARY Briefly described, the present invention generally encompasses compositions and
methods of preparing priming mixtures for small arms ammunition comprising oxidizer systems containing bismuth oxide, as well as small arms ammunition cartridges that incorporate such priming mixtures. The oxidizer systems can include bismuth oxide alone or in combination with one or more other oxidizers. The priming mixtures further generally will include one or more primary explosives combined with oxidizer systems
containing bismuth oxide, hi one embodiment, the oxidizer systems containing bismuth
oxide are non-hygroscopic and non-corrosive. The priming mixtures of the present
invention further can be non-toxic and substantially free of lead, or can contain some lead compound, such as lead styphnate as a primary explosive charge while substantially
reducing the overall content of toxic materials in the priming mixture.
ATLANTA 432955 vl
In one embodiment, the priming mixtures of the present invention include a primary explosive and a non-hygroscopic, non-corrosive oxidizer system comprising bismuth oxide. The primary explosive may be selected from heavy metal salts of
trinitroresorcinol, dinitrobenzofuroxan, diazodinitrophenol and combinations thereof. The primary explosive also may include a lead-based compound such as lead styphnate. hi addition to bismuth oxide, the non-hygroscopic, non-corrosive oxidizer system may include one or more additional oxidizer compounds or elements, such as potassium
nitrate, zinc peroxide, manganese dioxide, molybdenum trioxide, strontium nitrate,
strontium peroxide, tin oxide, iron oxide and combinations thereof. Still further, the
priming mixtures containing a primary explosive and a non-hygroscopic, non-corrosive
oxidizer system comprising bismuth oxide also may include one or more reducing agents, gas producing agents and sensitizers to provide the desired or required performance characteristics for supplying a priming charge to a round of small arms ammunition.
hi another embodiment, the present invention includes priming mixtures for small
arms ammunition comprising approximately 20-70% by weight of a primary explosive, such as a lead-free explosive or a lead-based compound such as lead styphnate, and approximately 10-70% by weight of an oxidizer system comprising bismuth oxide. These
priming mixtures optionally may include approximately 0-25% by weight of a gas
producing agent, approximately 0-20% by weight of a sensitizer, and approximately 0-
20% by weight of a reducing agent. The oxidizer systems of these priming mixtures may
include, in addition to bismuth oxide, oxidizers selected from potassium nitrate, zinc
ATLANTA 432955vl 4
peroxide, manganese dioxide, molybdenum tiioxide, strontium nitrate, strontium peroxide, barium nitrate, tin oxide, iron oxide and combinations thereof. The gas producing agents may be selected from pentaerythritol tetranitrate, trinitrotoluene and/or
combinations thereof, while the reducing agents may be selected from aluminum, boron,
calcium suicide, magnesium, magnesium-aluminum alloy, silicon, titanium, tungsten,
zirconium and combinations thereof.
The priming mixtures typically are wet processed during production for safety,
and are formed by methods comprising combining and mixing water with a primary
explosive and an oxidizer system comprising bismuth oxide. In alternative embodiments,
one or more reducing agents, gas generating agents or sensitizers also can be added
during combination and mixing to form the priming mixtures of the present invention. In a further embodiment, water may be combined and mixed with, on a dry weight percent basis, approximately 20-70% by weight of a primary explosive, approximately 10-70% by
weight of an oxidizer system comprising bismuth oxide, approximately 0-25% by weight
of a gas producing agent, approximately 0-20% by weight of a sensitizer, and
approximately 0-20% by weight of a reducing agent. The wet formed priming mixture then can be rolled and charged into percussion cups.
These and other aspects of the present invention are set forth in greater detail
below.
DETAILED DESCRIPTION
ATLANTA 432955vl 5
The present invention generally is directed to priming mixtures containing bismuth oxide primarily for use in small amis ammunition. The priming mixtures generally include a primary explosive and an oxidizer system containing bismuth oxide
by itself or in combination with one or more other oxidizers. Other priming components,
such as gas producing agents, sensitizers, and reducing agents or fuels also may be included in the priming mixtures of the present invention. These priming mixtures can be
incorporated into small arms ammunition primers or cartridges, which also are encompassed by the present invention.
Bismuth oxide as used herein is also referred to as bismuth(iπ)oxide or Bi2O3. As used herein, the term "small arms ammunition" refers to ammunition for a firearm capable of being carried by a person and fired without mechanical support and typically having a bore diameter of about one inch or less. The term "priming mixture", as used
herein, refers to a combination of explosive and/or pyrotechnic type ingredients, which, when pressed into caseless ammunition or a primer cup or spun into the rim cavity of a
rimfire shell, will explode or deflagrate upon impact by a firing-pin with the round of
ammunition to ignite the propellant of the round and fire the bullet or slug of the round.
The term "primary explosive" generally refers to a sensitive explosive which nearly always detonates by simple ignition from an energy source of appropriate magnitude for a
small arm, such as spark, flame, impact and other primary heat sources. The term
"primary explosive" further generally includes, but is not limited to, mercury fulminate, lead azide, lead styphnate, silver azide, diazodinitrophenol (DDNP), tetrazene, potassium
ATLANTA 432955vl 6
dinitrobenzofhroxane (KDNBF), heavy metal salts of 5-nitrotetrazole and other compounds that exhibit performance characteristics of handling, storage or detonation similar to these example compounds.
As used herein, the term "non-corrosive primer" refers to a primer which does not contain chemical compounds that typically will produce corrosion or rust in a gun barrel. The term "substantially free of lead", as used herein, refers to the complete absence of
lead or the presence of lead in a trace amount or an amount that would not be considered
toxic. As used herein, the term "non-toxic" refers to a compound or mixture that contains
no more than trace amounts of lead, manganese, antimony and barium, or amounts of these compounds that are considered to be non- detrimental to human health. The term "non-hygroscopic", as used herein, generally refers to an article, compound, or system
that does not readily talcing up and retain moisture, especially when exposed to humidity.
Additionally, the term "cartridge", as used herein, refers to a round of ammunition comprising a case, as well as caseless ammunition, and having a priming mixture and
propellant with or without one or more projectiles.
The present invention generally is directed to priming mixtures comprising an
oxidizer system containing bismuth oxide. The oxidizer system can include bismuth
oxide alone or in combination with one or more other or secondary oxidizers, such as
potassium nitrate, zinc peroxide, manganese dioxide, molybdenum trioxide, strontium nitrate, strontium peroxide, barium nitrate, tin oxide, and iron oxide. These secondary oxidizers can be present in the oxidizer system in a range of generally about 0% to
ATLANTA 432955vl 7
particularly about 99% by weight, about 10% to about 90% by weight, and more particularly about 30% to about 60% by weight. Although bismuth oxide has a relatively
high melting point of 817°C as compared to other oxidizers commonly used in small
arms ammunition priming mixtures, bismuth oxide is substantially non-hygroscopic and
non-toxic, thereby providing certain advantages in storage, handling and use that are not found in other oxidizers. Bismuth oxide also has a texture that allows it flow with ease when blended in the traditional manner in which primer formulations are blended to thus
provide a substantially homogenous mixture without having to incorporate flowing agents
or implement strenuous particle size control procedures. Therefore, the oxidizer systems
of the present invention can be substantially free of flowing agents and can exhibit a range of particle sizes that is broader than those found in conventional homogenous oxidizer systems. A substantially homogeneous priming mixture generally is easier to
measure out into the primer cup and process than non-homogeneous mixtures that
commonly arise with traditional oxidizer systems. Furthermore, raw dry and wet priming
mixtures formed with bismuth oxide generally are less sensitive to external stimulus, such
as impact or friction, than those formed with traditional oxidizer systems, thus making the mixtures containing bismuth oxide generally safer to handle, process, and utilize.
In particular embodiments, the priming mixtures of the present invention can
include from about 10% to about 70% by weight of an oxidizer system comprising
bismuth oxide alone or in combination with one or more other oxidizers, although greater
or lesser amounts of the oxidizer can be used. In certain embodiments, the priming
ATLANTA 432955vl 8
mixtures can contain about 25% to about 55% by weight of an oxidizer system including bismuth oxide. This bismuth oxide can constitute anywhere from about 1% up to about
100% by weight of the oxidizer system, and particularly about 5% to about 100% by weight of the oxidizer system.
hi addition to a bismuth oxide oxidizer system, the priming mixtures of the present invention generally include one or more primary explosives, such as, for example, lead salts of trinitroresorcinol, diazodinitrophenol, or earth metal salts of
dinitrobenzofuroxan. hi one embodiment, the priming mixture includes DDNP as one of
the primary explosive constituents. DDNP can be used alone, or in combination with one or more other primary explosives, such as IODNBF, and derivatives and mixtures thereof, in the priming mixture. Alternatively, KDNBF may constitute the only primary explosive of the priming mixtures or comprise one of a combination of primary explosive
components, other than DDNP. While DDNP and KDNBF are substantially free of lead
and non-toxic, they can be used individually or together in combination with one or more
lead-based primary explosives, such as lead styphnate or the like, in the priming mixtures containing bismuth oxide. Generally, the primary explosive, whether composed of a
single compound or a combination of two or more compounds, will be selected or
designed to have ballistic properties similar to or better than those of lead styphnate.
The priming mixtures of the present invention typically will include one or more primary explosives in a range of about 20% to about 70% by weight of the priming
mixture, although it is also possible to utilize greater or lesser percentages by weight of
ATLANTA 432955vl 9
the primary explosive in the primary mixture as well, hi one embodiment, the primary explosive constitutes about 25% to about 50% by weight of the priming mixture, hi a
more particular embodiment, the priming mixture generally comprises about 40% to
about 45% by weight of a primary explosive, such as KDNBF or DDNP.
The priming mixtures of the present invention also can include one or more secondary explosives, which typically act as sensitizers that accelerate or otherwise
modify the rate of conversion of the pyrotechnic system. There are a variety of sensitizers
capable of being included in the present priming mixture, hi the present case, the sensitizer is selected, in part, for its compatibility with the chosen primary explosive. The sensitizer can enhance the sensitivity of the primary explosive to the percussion mechanism, hi one embodiment, tetrazene is selected as a secondary explosive to be
combined with a primary explosive, such as DDNP or KDNBF. Tetrazene, also known
as tetracene, tetrazolyl guanyltetrazene hydrate or tetrazene- l-carboxamidine-4-(l -H-
tetrazol-5-yl) monohydrate, also can be added to the priming mixture, in combination
with DDNP or KDNBF, to increase the sensitivity of the charge.
The priming mixtures also can include sensitizers, typically in an amount from
about 0% to about 30% by weight of the priming mixture. The sensitizer can include one
or more secondary explosives, such as tetrazene, friction agents, such as ground glass, or
other inert substances, hi one embodiment, the priming mixture contains about 5% to about 20% by weight of such materials, and in one particular embodiment, tetrazene
ATLANTA 432955vl 10
typically is added to the mix in an amount between about 4 to 11% by weight. For
example, tetrazene can comprise about 5% by weight of the priming mixture.
Gas producing agents also can be included in the priming mixtures of the present invention. Single or double based propellants, such as pentaerythritol tetranitrate or
trinitrotoluene, can be included to provide sources of expanding gas when the priming mixture is activated. Generally, the priming mixtures can include about 0% to about 25% by weight of one or more gas producing agents. In one particular embodiment, the
priming mixture comprises about 5% to about 25% by weight of a gas producing agent.
The priming mixtures further can include one or more fuels or reducing agents. The fuel can be either a metallic fuel or reducing agent, nonmetallic fuel, or combinations thereof. The fuel can constitute from about 0% to about 20% by weight of the priming mixture. Examples of potential fuels or reducing agents include aluminum, boron,
calcium suicide, magnesium, magnesium-aluminum alloy, silicon, titanium, tungsten,
zirconium and nitrocellulose, hi one embodiment, the priming mixture includes about
5% to about 20% by weight of a fuel or reducing agent.
The primer mixtures also can contain a binder that is generally included up to
about 2% by weight to minimize dusting. The binder typically can constitute about 0.5 to
about 1.5% by weight of the priming mixture although other, varying amounts also can be
used. The binder generally is chosen for maximum compatibility with the explosive formulation prepared, and typically will be selected from a variety of gum materials, such
ATLANTA 432955vl 11
as gum arabics, and particularly acacia gum arabic, as well as carboxy methylcellulose,
ethyl cellulose, and guar tragacanth, polyvinyl alcohol with guar gum.
The disclosed components of the priming mixtures can be combined and wet
mixed by the use of standard low shear mixers, using customary techniques for blending explosives. The components typically are wet-mixed for safety since the explosive compounds are desensitized when mixed with water. Also, the components can be dry mixed using a technique called diapering, which is done behind a barricade. With these techniques, the explosive components are generally blended first, followed by the fuels, and finally the oxidizer components.
By way of example and illustration, and not by limitation, the mixing and
preparation of the priming mixture is illustrated below by the following steps. Other
components may be added to the mixture as described above, and the recited priming
mixture is not to be limited by any one proscribed process, but only by the appended
claims.
The priming mixture may be prepared and applied by the following steps:
1. Within the above-described ranges, primary and secondary explosives are added in a kettle mixer with an amount of water and then mixed for approximately 2
minutes. When added to the kettle, the primary and secondary explosives generally are
wet with water. This moisture generally is sufficient to wet the entire mixture.
2. Within the above-described ranges, fuels or other sensitizers are added to the wet mix of explosives and then mixed for approximately 2 minutes.
ATLANTA 432955vl 12
3. Within the above-described ranges, the oxidizer system containing
bismuth oxide is added to the wet mix of explosives and fuel and then mixed for about 2
minutes. Subsequently, the entire mixture is mixed for about 3 minutes to form the wet
mix primer. 4. The resulting wet priming mixture is rolled onto plates having holes or recesses wherein the wet mixture is formed into pellets and then punched and charged into primer cups. The resulting charged priming mixture is then covered with a paper foil
and an anvil is inserted. The charged priming mixture is then typically allowed to dry for approximately 5 days at about 50°C. The present invention also encompasses small arms ammunition cartridges that
incorporated the priming mixtures described herein. The cartridges typically will include
a case in which the priming mixture is disposed, although the primer mixture also could
be used for caseless ammunition as well. The cartridge may include projectiles, such as
shot or bullets. The cartridge also can be a centerfire cartridge for rifles, pistols and
revolvers in which the primer is centrally aligned within the head of the cartridge or a rimfire cartridge having a flanged head with the priming mixture disposed in the rim
cavity.
Examples: Example 1 A standard primer contains a mixture conventional formulation of 35.6% lead styphnate, 5% tetrazene, 40.6% barium nitrate, 11.9% antimony sulfide, and 6.9%
ATLANTA 432955vl 13
aluminum with an additional 0.5% of binder (Conventional Formulation). To demonstrate
the ability of bismuth oxide to act as a direct replacement for more common oxidizers, in this case barium nitrate, an alternative mixture was prepared by substituting bismuth
oxide for barium nitrate in the conventional formulation. This alternative mixture is referred to as BIOl. Both mixes were prepared by mixing water- wet explosives with the mentioned dry ingredients in a production fashion. Once mixed these were then assembled into small arms primers. After drying, these primers were then tested
according to the SAAMI specification for small arms ammunition sensitivity. The
accepted performance standard requires that no sample fires when a 1.94 ounce test
weight is dropped from a height of 1 inch into the priming mixture and that all samples must fire when the weight is dropped from a height of 11 inches. When the priming
mixture was tested in 38 Special shells, the results of Table 1 were obtained.
TABLE l
50 samples tested at each level
Conventional Formulation BIOl all fire height, in. 6 6 all no-fire height, in. 2 2
X-bar 3.62 4.16
X-bar + 4σ 6.35 7.11
X-bar - 2σ 2,2(5 2M_
From the results of the sensitivity test shown in Table 1, it is apparent that
although there is some difference in sensitivity between the two, both samples are well
ATLANTA 432955v1 14
within the SAAMI guidelines, and it can be seen that the bismuth oxide in BIOl meets the
SAMMI performance standards.
An additional comparison was performed by using the above two primer samples and loading them into 9mm rounds of ammunition using 115 grain metal case bullet and Bullseye® propellant. The loaded 9mm rounds of ammunition were then fired at various temperatures while measuring peak chamber pressure and muzzle velocity. Table 2 indicates the results when tested in 9mm ammunition.
TABLE 2 average of 50 rounds sample storage peak pressure, standard muzzle standard lOOpsi deviation velocity, ft/sec deviation
Conventional 7O0F 313 20 1137 27
BIOl 7O0F 325 13 1215 19
Conventional 15O0F 356 17 1162 28
BIOl 15O0F 353 11 1267 16
Conventional -2O0F 304 25 1104 38
BIOl -2O0F 339 23 1202 29
The results of Table 2 indicate that the BIOl formulation containing bismuth oxide
as the main oxidant performed equal to or better than the Conventional Formulation on peak pressure and exhibited higher muzzle velocity after every storage condition. The
performance of the bismuth oxide primer formulation is consistent over a wide range of
temperatures. In each of case, the equilibrium time was 48 hours. Also, 50 rounds were
ATLANTA 432955vl 15
fired at each condition. Although this example was performed in 9mm, it can be inferred
that this improvement will transfer to all small arms ammunition.
Example 2
To illustrate the compatibility of bismuth oxide with other primer components and the versatility of bismuth oxide in various primer mixes, four different mixes were
prepared using bismuth oxide in combination with various oxidizers. Mix descriptions are found in Table 3.
TABLE 3
percent by weight dry ingredients
BI02 BI03 BI04 BI05
KDNBF 45 45 45 45
Tetrazene 5 5 5 5
Bismuth Oxide 15 15 15 15
Zinc Peroxide 30
Potassium 30
Nitrate
Strontium 30
Peroxide
Molybdenum 30
Oxide
Titanium 5 5 5 5
After these mixes were charged into primers, they were dried and primed into 38
Special casings, and tested according to the SAAMI specification for small pistol
ATLANTA 432955vl 16
sensitivity. The results of the sensitivity testing are presented in Table 4.
TABLE 4
50 samples tested at each level
BI02 BI03 BI04 BI05 all fire height, 7 9 5 7 in. all no-fire 3 3 2 5 height, in.
X-bar 3.86 5.52 3.28 5.04
X-bar + 4σ 7.14 11.09 5.29 7.47
X-bar - 2σ 2.22 2.73 2.28 3.83
From Table 4, it is evident that secondary oxidizers can affect the overall
sensitivity of the mixture. All but one, BI03, meet the SAAMI specification- for X-bar +
4σ all-fire sensitivity. This does not mean that the bismuth oxide/potassium nitrate formulation will not perform satisfactorily; a simple alteration to the ratio of the two
components can change the sensitivity to meet the specification.
Additional information about each formulation was gathered when each was fired
in a semi-closed primer bomb. The results of semi-closed primer bomb are found in Table
5.
ATLANTA 432955vl 17
TABLE 5 average of 10 primers fired for each sample
BI02 BI03 BI04 BI05 time-to- lst-rise, 0.273 0.295 0.366 0.434 μs rise time, μs 0.106 0.117 0.200 0.293 peak pressure, 242 271 138 171 psi temperature, K 1464 1675 1494 1453
The data set forth in Table 5 reveals performance variations linked to the selected
primary oxidant. This data shows the efficiency of the inorganic nitrate as an oxidizer. To determine how these outputs affected the ballistics properties of loaded ammunition, the
above primers were loaded into 9mm cartridges using a 101 grain frangible bullet with
6.2 grains of HPC-33 propellant. The internal ballistics peak pressure and muzzle
velocity for each was obtained. Ballistics data is found in Table 6.
TABLE 6 average of 10 rounds
BI02 BI03 BI04 BI05 peak pressure, lOOpsi 382 388 363 342 peak pressure extreme variation, 60 39 55 57 lOOpsi peak pressure standard deviation 15 12 17 20 muzzle velocity, ft/sec 1306 1317 1287 1278 muzzle velocity extreme variation, 69 57 62 70 ft/sec muzzle velocity standard deviation 18 15 22 23
ATLANTA 432955vl 18
Holding the mass of propellant constant allows the evaluation of the primers ability to ignite the charge. The comparison in Table 6 reveals the effects of changing the dominate oxidant has on ballistics performance. When comparing the effect the different combinations have on primer bomb output, it appears the use of strontium peroxide or molybdenum trioxide drastically decreased the output. However the decreased output
was not detrimental to propellant ignition. In any event, the above example demonstrates
bismuth oxide's capacity to function in combination with other oxidizers in small arms
ammunition. Furthermore, it must be understood that only one type of propellant was used in this example, it maybe the case that the strontium peroxide or molybdenum
trioxide containing primers may perform better when using alternative propellant.
Although, this is just a few of the unlimited number of possible combinations, it
highlights bismuth oxide's capacity to be used in combination with other oxidizers to tailor primer performance.
Example 3
Again the versatility of bismuth oxide is demonstrated in this example where its
use as the sole oxidizer in combination with a variety of fuels is presented. As shown in
Table 7, eight formulations were produced in which all components and their percentages were kept constant, except that the type of fuel was varied.
ATLANTA 432955vl 19
TABLE 7 percent dry ingredients by weight
BI06 BI07 BI08 BI09 BIlO Bill BI12 BI13
KDNBF 45 45 45 45 45 45 45 45
Tetrazene 5 5 5 5 5 5 5 5
Bi2O3 45 45 45 45 45 45 45 45
Al 5
B 5
CaSi2 5
Mg 5
MgAl Alloy 5
Si 5
Ti 5
Zr 5
Once the primer formulations were produced, they were tested for sensitivity in 38 Special casings according to SAAMI specifications. The results of the sensitivity testing
are presented in Table 8.
TABLE 8
50 samples tested at each level
BI06 BI07 BI08 BI09 BIlO Bill BI12 BI13 all fire height, in. 7 7 7 6 7 5 5 6 all no-fire height, in. 3 3 3 2 2 2 2 2
X-bar 4.92 4.84 4.26 3.44 3.58 3.50 3.34 3.66
X-bar + 4σ 8.03 8.81 7.10 5.30 5.64 5.10 5.19 5.39
X-bar - 2σ 3.37 2.86 2.84 2.51 2.20 2.70 2.41 2.5
ATLANTA 432955vl 20
Each primer formulation met or exceeded the SAAMI specifications for primer sensitivity. Consequently, it is evident that bismuth oxide performs well with a variety of fuels. However, sensitivity is just one of the criteria that a primer must meet. Therefore,
the ballistic characteristics of the primer formulations were tested by loading the primers
into 9 mm 101 frangible rounds using 6.2 grains of HPC-33. The results are set forth in Table 9.
TABLE 9 average of 10 samples
BI06 BI07 BI08 BI09 BIlO Bill BI12 BI13 peak pressure, lOOpsi 368 407 395 385 389 407 397 385 peak pressure extreme 33 67 45 84 50 82 64 56 variation, lOOpsi peak pressure standard 11 19 13 26 16 22 23 21 deviation muzzle velocity, ft/sec 1297 1283 1278 1273 1285 1284 1279 1309 muzzle velocity extreme 37 47 45 37 34 11 46 38 variation, ft/sec muzzle velocity standard 12 16 14 13 11 4 14 13 deviation
The results illustrate the versatility and compatibility of bismuth oxide in a variety
of primer formulations that can be used in small arms ammunition.
While various embodiments have been set forth as illustrated and described
above, it is recognized that numerous variations may be made with respect to relative weight percentages of various constituents in the composition. Therefore, while the
invention has been disclosed in various forms only, it will be obvious to those skilled in
ATLANTA 432955vl 21
the art that many additions, deletions and modifications can be made without departing from the spirit and scope of this invention, and no undue limits should be imposed,
except as to those set forth in the following claims.