WO2005121101A1 - Phenylnaphthylimidazoles for use on copper surfaces during soldering - Google Patents
Phenylnaphthylimidazoles for use on copper surfaces during soldering Download PDFInfo
- Publication number
- WO2005121101A1 WO2005121101A1 PCT/JP2005/010898 JP2005010898W WO2005121101A1 WO 2005121101 A1 WO2005121101 A1 WO 2005121101A1 JP 2005010898 W JP2005010898 W JP 2005010898W WO 2005121101 A1 WO2005121101 A1 WO 2005121101A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- copper
- treating agent
- surface treating
- compound
- zinc
- Prior art date
Abstract
Description
Claims