WO2005083483A1 - Fibre optique birefringente - Google Patents

Fibre optique birefringente Download PDF

Info

Publication number
WO2005083483A1
WO2005083483A1 PCT/DK2005/000128 DK2005000128W WO2005083483A1 WO 2005083483 A1 WO2005083483 A1 WO 2005083483A1 DK 2005000128 W DK2005000128 W DK 2005000128W WO 2005083483 A1 WO2005083483 A1 WO 2005083483A1
Authority
WO
WIPO (PCT)
Prior art keywords
fibre
stress
optical fibre
regions
tie
Prior art date
Application number
PCT/DK2005/000128
Other languages
English (en)
Inventor
Ole Sigmund
Andreas Hvidtfeld Nielsen
Original Assignee
Danmarks Tekniske Universitet (Dtu)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Danmarks Tekniske Universitet (Dtu) filed Critical Danmarks Tekniske Universitet (Dtu)
Publication of WO2005083483A1 publication Critical patent/WO2005083483A1/fr

Abstract

L'invention concerne des fibres optiques biréfringentes, utilisées par exemple comme fibres à maintien de polarisation. L'invention concerne plus particulièrement la répartition de différentes compositions de matériaux dans une fibre afin d'améliorer la biréfringence dans son noyau. La mise en oeuvre de procédés d'optimisation de topologie basés sur une analyse par éléments finis permet d'obtenir des conceptions de fibres à trois phases de matériaux différentes, ce qui augmente considérablement la biréfringence dans le noyau de la fibre. Une de ces phases présente un module d'élasticité d'Young inférieur à celui des autres et peut présenter des vides, tels que des trous d'air. La présente invention apporte des modifications aux dispositions standard, telles que le noeud papillon et le double noeud papillon. L'invention peut également être appliquée aux fibres à cristal optique ou aux fibres à bande interdite photonique.
PCT/DK2005/000128 2004-02-27 2005-02-25 Fibre optique birefringente WO2005083483A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US54780004P 2004-02-27 2004-02-27
US60/547,800 2004-02-27

Publications (1)

Publication Number Publication Date
WO2005083483A1 true WO2005083483A1 (fr) 2005-09-09

Family

ID=34910943

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/DK2005/000128 WO2005083483A1 (fr) 2004-02-27 2005-02-25 Fibre optique birefringente

Country Status (1)

Country Link
WO (1) WO2005083483A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009104010A1 (fr) * 2008-02-19 2009-08-27 University Of Kent Fibre optique
CN109655434A (zh) * 2019-02-22 2019-04-19 东北大学 一种多参数测量的光纤lmr传感器
CN110320591A (zh) * 2019-07-04 2019-10-11 山东大学 一种基于表面微结构的单晶激光光纤及其制作方法与应用

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2096788A (en) * 1981-01-17 1982-10-20 Nippon Telegraph & Telephone Single polarization single-mode optical fibers
US4478489A (en) * 1981-04-13 1984-10-23 Corning Glass Works Polarization retaining single-mode optical waveguide
JPS6067908A (ja) * 1983-09-26 1985-04-18 Nippon Telegr & Teleph Corp <Ntt> 光フアイバとその製造方法
US4709986A (en) * 1984-06-18 1987-12-01 Polaroid Corporation Ensheathed optical fiber and coupling method
EP0540386A1 (fr) * 1991-10-29 1993-05-05 Thomson-Csf Fibre optique et procédé de fabrication
WO2000037974A1 (fr) * 1998-12-21 2000-06-29 Corning Incorporated Fibre a cristal photonique
WO2003029854A1 (fr) * 2001-09-27 2003-04-10 Nippon Telegraph And Telephone Corporation Fibre optique a maintien de polarisation et fibre optique a polarisation unique absolue

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2096788A (en) * 1981-01-17 1982-10-20 Nippon Telegraph & Telephone Single polarization single-mode optical fibers
US4478489A (en) * 1981-04-13 1984-10-23 Corning Glass Works Polarization retaining single-mode optical waveguide
JPS6067908A (ja) * 1983-09-26 1985-04-18 Nippon Telegr & Teleph Corp <Ntt> 光フアイバとその製造方法
US4709986A (en) * 1984-06-18 1987-12-01 Polaroid Corporation Ensheathed optical fiber and coupling method
EP0540386A1 (fr) * 1991-10-29 1993-05-05 Thomson-Csf Fibre optique et procédé de fabrication
WO2000037974A1 (fr) * 1998-12-21 2000-06-29 Corning Incorporated Fibre a cristal photonique
WO2003029854A1 (fr) * 2001-09-27 2003-04-10 Nippon Telegraph And Telephone Corporation Fibre optique a maintien de polarisation et fibre optique a polarisation unique absolue

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
J.R. FOLKENBERG, M.D. NIELSEN, N.A. NORTENSEN, C. JAKOBSEN H.R. SIMONSEN, OPTICS EXPRESS, vol. 12, no. 5, 8 March 2004 (2004-03-08), pages 956 - 960, XP002307643 *
KUN-HSIEH TSAI ET AL: "GENERAL SOLUTIONS FOR STRESS-INDUCED POLARIZATION IN OPTICAL FIBERS", JOURNAL OF LIGHTWAVE TECHNOLOGY, IEEE. NEW YORK, US, vol. 9, no. 1, January 1991 (1991-01-01), pages 7 - 17, XP000204991, ISSN: 0733-8724 *
PATENT ABSTRACTS OF JAPAN vol. 0092, no. 03 (P - 381) 21 August 1985 (1985-08-21) *

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009104010A1 (fr) * 2008-02-19 2009-08-27 University Of Kent Fibre optique
CN109655434A (zh) * 2019-02-22 2019-04-19 东北大学 一种多参数测量的光纤lmr传感器
CN109655434B (zh) * 2019-02-22 2024-01-26 东北大学 一种多参数测量的光纤lmr传感器
CN110320591A (zh) * 2019-07-04 2019-10-11 山东大学 一种基于表面微结构的单晶激光光纤及其制作方法与应用
CN110320591B (zh) * 2019-07-04 2020-08-25 山东大学 一种基于表面微结构的单晶激光光纤及其制作方法与应用

Similar Documents

Publication Publication Date Title
US7532798B2 (en) Optical waveguide
Saitoh et al. Photonic bandgap fibers with high birefringence
US6954574B1 (en) Photonic crystal fibres
US20060291789A1 (en) Photonic crystal fibres comprising stress elements
KR101500819B1 (ko) 복굴절 미세구조 광섬유 제조 방법
CN104111493A (zh) 一种高双折射平坦色散双芯光子晶体光纤及其制备方法
Becker et al. Laser-drilled free-form silica fiber preforms for microstructured optical fibers
US11079536B2 (en) Suppressing surface modes in fibers
US7805038B2 (en) Birefringent photonic bandgap optical waveguide
JP2024012204A (ja) 空芯微細構造光ファイバプリフォーム、光ファイバ及びその製造方法
WO2005083483A1 (fr) Fibre optique birefringente
WO2003058309A1 (fr) Procede et appareil concernant des fibres optiques microstructurees
RU2606796C1 (ru) Чирпированный микроструктурный волновод и способ его изготовления
Chen All-solid silica-based photonic crystal fibers
Buczynski et al. Double-core photonic crystal fiber with square lattice
Li et al. Bow-tie holes-aided elliptical-core polarization-maintaining fiber with high birefringence
JP4447528B2 (ja) フォトニックバンドギャップファイバとその製造方法
Pysz et al. Comparing characteristics and prospects of fabrication of multicomponent photonic crystal fibers with different lattice structures
JP2007041166A (ja) フォトニックバンドギャップファイバとその製造方法
JP4447529B2 (ja) フォトニックバンドギャップファイバとその製造方法
Guan Finite element analysis of propagation characteristics for an Octagonal Photonic Crystal Fiber (O-PCF)
Qing et al. Properties of all-solid square-lattice photonic bandgap fibres
Mohammad-Nejad et al. Design of a Photonic Crystal Fiber with Improved Dispersion and Confinement Loss Over All Telecommunication Bands
Sharma et al. Proposed novel design of silica PCF to minimizing the dispersion using OptiFDTD
Kujawa et al. Double glass and glass-air photonic crystal fibers

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SM SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DPEN Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed from 20040101)
122 Ep: pct application non-entry in european phase