WO2005058982A1 - Process for the (co)polymerization of ethylene - Google Patents
Process for the (co)polymerization of ethylene Download PDFInfo
- Publication number
- WO2005058982A1 WO2005058982A1 PCT/EP2004/013372 EP2004013372W WO2005058982A1 WO 2005058982 A1 WO2005058982 A1 WO 2005058982A1 EP 2004013372 W EP2004013372 W EP 2004013372W WO 2005058982 A1 WO2005058982 A1 WO 2005058982A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymerization
- ethylene
- process according
- molecular weight
- compound
- Prior art date
Abstract
Description
Claims