WO2005052082A1 - Structured paper release liner, adhesive-backed article assembly and method of making same - Google Patents
Structured paper release liner, adhesive-backed article assembly and method of making same Download PDFInfo
- Publication number
- WO2005052082A1 WO2005052082A1 PCT/US2004/038976 US2004038976W WO2005052082A1 WO 2005052082 A1 WO2005052082 A1 WO 2005052082A1 US 2004038976 W US2004038976 W US 2004038976W WO 2005052082 A1 WO2005052082 A1 WO 2005052082A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- paper
- release
- adhesive
- article
- pressure sensitive
- Prior art date
Abstract
Description
Claims