WO2005016856A1 - Production of olefins - Google Patents
Production of olefins Download PDFInfo
- Publication number
- WO2005016856A1 WO2005016856A1 PCT/EP2004/009142 EP2004009142W WO2005016856A1 WO 2005016856 A1 WO2005016856 A1 WO 2005016856A1 EP 2004009142 W EP2004009142 W EP 2004009142W WO 2005016856 A1 WO2005016856 A1 WO 2005016856A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- feedstock
- olefins
- crystalline silicate
- catalyst
- process according
- Prior art date
Abstract
Description
Claims